CN101817935A - 一种再生橡胶增塑剂及其制备方法 - Google Patents
一种再生橡胶增塑剂及其制备方法 Download PDFInfo
- Publication number
- CN101817935A CN101817935A CN200910126124A CN200910126124A CN101817935A CN 101817935 A CN101817935 A CN 101817935A CN 200910126124 A CN200910126124 A CN 200910126124A CN 200910126124 A CN200910126124 A CN 200910126124A CN 101817935 A CN101817935 A CN 101817935A
- Authority
- CN
- China
- Prior art keywords
- reclaimed rubber
- coal tar
- naphthalene
- plasticizer
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种再生橡胶增塑剂及其制备方法属于环境保护领域、化工领域。本地区再生橡胶增塑剂全部使用的是高温煤焦油。由于焦化厂原材料、工艺的调整影响了再生橡胶的质量稳定。再生橡胶制成的橡胶制品，由于萘的升华，制品表面凝结一层白色的升华萘，影响产品质量。本地区焦化厂的焦油渣，作为拉圾倒在厂外，浪费资源，污染环境。为了解决上述几个问题，发明了一种再生橡胶增塑剂及其制备方法。用蒽油萃取工艺，将焦油渣中的煤焦油和焦炭粉分离，得到含萘更低的煤焦油。对含萘更低的煤焦油脱水，调粘度，制备成质量稳定的再生橡胶增塑剂。制备成的再生橡胶增塑剂，送多个再生橡胶生产厂使用，发现使用量少，质量稳定，制品表面没有白色的升华萘。
Description
技术领域
一种再生橡胶增塑剂及其制备方法属于环境保护领域、化工领域。
背景技术
废橡胶，如废橡胶轮胎数量大，堆积如山，如何处理是一个世界性环保难题。废橡胶，如废橡胶轮胎进行脱硫再生生产再生橡胶是比较成熟的技术。
再生橡胶是指用废橡胶，如废橡胶轮胎为原料加工成的、有一定可塑度、能重新使用的橡胶。
再生橡胶能部分地代替生橡胶用于橡胶制品，节约生橡胶及炭黑，也有利于改善环境。
再生过程是废橡胶在增塑剂、氧、热和机械剪切的综合作用下，使硫化橡胶的部分分子链和交联点断裂的过程。再生橡胶生产过程包括粉碎、再生(脱硫)和精炼3个工序。
橡胶增塑剂通常按照其极性和用途分为软化剂和增塑剂。目前业界统称增塑剂。
增塑剂在生产使用过程中应满足下列条件：增塑效果好，用量少，吸收速度快，与橡胶的相容性好，挥发性小，不迁移，耐寒性好，耐水、耐油和耐溶剂，耐热、耐光性好，电绝缘性好，耐燃性好，耐菌，价廉物美等。
增塑剂可以按来源分为石油系增塑剂、煤焦油系增塑剂、松油系增塑剂、脂肪系增塑剂及合成增塑剂。
再生橡胶增塑剂，常用的有煤焦油、松焦油、裂化渣油。
本地区是全国焦炭生产基地，焦化厂很多，高温煤焦油很多。由于高温煤焦油作为再生橡胶增塑剂使用，效果好，价格低，所以本地区再生橡胶生产厂，再生橡胶增塑剂全部使用的是高温煤焦油。
由于本地区焦化厂很多，使用的原材料、工艺不完全相同，所以高温煤焦油的质量也不完全相同。就是在一个厂，由于原材料、工艺的调整高温煤焦油的质量也经常变化。再生橡胶生产厂添加高温煤焦油的数量需要经常变化，影响了再生橡胶的质量稳定。
由于煤焦油中含有10％的萘，再生橡胶制成的橡胶制品，由于萘的升华，制品表面凝结一层白色的升华萘，影响产品质量。
另外，本地区焦化厂的焦油渣，作为拉圾倒在厂外，浪费资源，污染环境。
为了解决上述几个难以解决的问题，申请人经过多年研究，发明了一种再生橡胶增塑剂及其制备方法。
发明内容
为了解决再生橡胶增塑剂萘的升华问题，要选低萘高温煤焦油作为再生橡胶增塑剂。在研究中发现，高温煤焦油的焦油渣中含萘的含量最低，但是焦油渣中含有大量焦炭粉，不适用于作橡胶增塑剂。所以选择了用蒽油萃取工艺，将焦油渣中的煤焦油和焦炭粉分离，得到含萘更低的煤焦油。
为了解决再生橡胶增塑影响再生橡胶的质量稳定，对含萘更低的煤焦油脱水，调粘度，制备成质量稳定的再生橡胶增塑剂。
制备成的再生橡胶增塑剂，送多个再生橡胶生产厂使用，发现使用量少，质量稳定，制品表面没有白色的升华萘。
生产再生橡胶增塑剂副产的焦粉，由于还含有少量煤焦油，燃烧产生黑烟，污染环境，所以不适于作锅炉燃料。通过研究发现，生产再生橡胶增塑剂副产的焦粉挤压成型，烧结之后适用于炼铁炉使用。
具体实施方式
制造：蒽油罐1台、萃取罐2台、脱水罐1台。
在萃取罐中加焦油渣15吨，蒽油2吨，加热到80～90℃，搅拌30分钟，从出油口放出的是再生橡胶增塑剂半成品15吨。
在萃取罐中加蒽油2吨，对焦油渣进行洗涤，从出油口放洗涤液备用。
从出渣口放出焦炭粉2吨，用离心机脱蒽油。焦炭粉挤压成园柱型，600℃的炉温中加热30分钟，成高强度焦炭。
再生橡胶增塑剂加入脱水罐，脱水在4％以下，调节粘度到适当范围内，即成品再生橡胶增塑剂。
Claims (5)
1.为了解决再生橡胶增塑剂萘的升华问题，要选低萘高温煤焦油作为再生橡胶增塑剂。
2.选择了用蒽油萃取工艺，将焦油渣中的煤焦油和焦炭粉分离，得到含萘更低的煤焦油。
3.对含萘更低的煤焦油脱水，调粘度，制备成质量稳定的再生橡胶增塑剂。
4.制备成的再生橡胶增塑剂，送多个再生橡胶生产厂使用，发现使用量少，质量稳定，制品表面没有白色的升华萘。
5.生产再生橡胶增塑剂副产的焦粉挤压成型，烧结之后适用于炼铁炉使用。