CN101816525A - 一种双面异体葡甘露聚糖海绵及其制造方法 - Google Patents
一种双面异体葡甘露聚糖海绵及其制造方法 Download PDFInfo
- Publication number
- CN101816525A CN101816525A CN 201010160374 CN201010160374A CN101816525A CN 101816525 A CN101816525 A CN 101816525A CN 201010160374 CN201010160374 CN 201010160374 CN 201010160374 A CN201010160374 A CN 201010160374A CN 101816525 A CN101816525 A CN 101816525A
- Authority
- CN
- China
- Prior art keywords
- sponge
- glucomannans
- colloid
- double
- glucomannan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种双面异体葡甘露聚糖海绵及其制造方法,包含第一海绵及第二海绵,制作步骤包括制备一葡甘露聚糖混合物,将其加热一定时间形成第一胶体,再将第一胶体覆盖在未经反应的葡甘露聚糖混合物上,两者进一步加热,未经反应的葡甘露聚糖混合物形成第二胶体,第一胶体与第二胶体于接合面粘合,使其相对地结合成一体成为双面异体葡甘露聚糖海绵。藉由第一海绵与第二海绵通过不同反应时间所制得,使其内部具有不同的孔密度,使得该双面异体葡甘露聚糖海绵具有2个不同粗糙程度的表面,能够适用于人体的不同肤质,达到清洁与保养的双重功效。
Description
技术领域
本发明是关于一种人体清洁用品,特别是指一种双面异体葡甘露聚糖海绵的制造方法及其用途。
背景技术
大多数人会在沐浴或洗脸过程中利用海绵或是毛巾等辅助工具,用以达到清洁肌肤、去除老化角质的功效。传统洗脸海绵或是沐浴海绵大多是使用橡胶材质或是由化学原料所制成,会散发一股刺鼻不舒服的味道,此外,其整体质地粗糙,外表面不平整,不仅无法达到清洁效果,反而因为过度摩擦会造成对皮肤角质层的伤害。
目前许多业者利用“魔芋”研发出一种新型海绵,该魔芋又称为蒟蒻,由于魔芋中含有大量的葡甘露聚糖达85%以上,因此其化学名又为葡甘露聚糖,它是来自amorphophallis植物的块根,因其是纯天然成分,所以对皮肤不会产生任何毒性和不良影响。由魔芋所制成的海绵具有极高的含水量,使用时能与皮肤间形成一层水膜,就算使用过程中使用清洁剂,其摩擦力仍比传统的海绵更加滑顺,并且可以更加有效地锁住肌肤水分。另外,魔芋中含有天然多糖纤维,能深入肌肤毛孔,深层清洁皮肤内的脏污与老化角质。
然而目前坊间业者所制作的魔芋海绵具有以下缺点:
1、制作时间过长:由于制作个过程繁琐,需要经过分散、膨润、碱化、蒸煮、冷冻、脱碱、漂洗等步骤,一般来说,完成上述步骤需要3~7天的制作时间。
2、无法适应各种肤质:由于制作时间与工艺温度一成不变,藉此形成的魔芋海绵仅仅具有单一预定粗糙程度的表面,适用范围过窄,倘若表面过于粗糙,该魔芋海绵无法应用于娇嫩的皮肤表面;倘若表面过于细致,又无法达到应有的清洁老化角质的效果。
本申请中,由于魔芋中主要成分为葡甘露聚糖,因此下文以葡甘露聚糖为重点论述。
发明内容
本发明主要目的在于提供一种双面异体葡甘露聚糖海绵的制造方法,它是由至少2个相异的葡甘露聚糖凝胶彼此结合,从而形成一块具有至少两种不同孔密度的海绵,亦即该海绵具有2个不同粗糙程度的表面,能够适用于人体的不同肤质,达到清洁与保养的双重功效。
上述中,2个凝胶的相异是通过不同的反应时间所形成的,并进一步藉由交联反应使两者彼此结合。
本发明所提供的一种双面异体葡甘露聚糖海绵的制造方法,其包含有下列步骤:
a、制备一葡甘露聚糖混合物;
b、将葡甘露聚糖混合物平均分成两份,其中一份葡甘露聚糖混合物倒入一预定形状的容器中;
c、将灌好模的葡甘露聚糖混合物,放入加热设备中加热至一预定温度,进行交联反应,经过一预定反应时间,形成第一胶体;
d、将第一胶体取出后覆盖于另一份未经反应的葡甘露聚糖混合物上,然后将第一胶体与未经反应的葡甘露聚糖混合物置入一预定形状的容器中,放入加热设备中加热至一预定温度,进行交联反应,经过一预定反应时间;
e、未经反应的葡甘露聚糖混合物形成第二胶体,并且该第二胶体及第一胶体于接合面相粘合成为一葡甘露聚糖冻状胶体;
f、冷却葡甘露聚糖冻状胶体,以针状工具于该葡甘露聚糖冻状胶体上扎小孔;
g、将葡甘露聚糖冻状胶体放入冷冻箱中冷冻,使水滴凝结于该葡甘露聚糖冻状胶体中,形成多孔状的海绵。
本发明进一步的技术方案还包括:步骤c所述的预定温度是介于80℃~100℃之间,步骤c所述的预定反应时间是介于30分钟~80分钟之间。
本发明进一步的技术方案还包括:步骤d所述的预定温度是介于80℃~100℃之间,步骤d所述的预定反应时间是介于30分钟~80分钟之间。
本发明方法将传统制作魔芋海绵的复杂程序大为简化,有效缩短了制作时间,提高了生产效率。
本发明的另一目的在于提供一种双面异体葡甘露聚糖海绵,包含有:
第一海绵,是具有第一孔密度的块体;
第二海绵,是具有第二孔密度的块体,而且与第一海绵彼此相对地结合成一体,其中,第一孔密度不同于第二孔密度。并且该双面异体葡甘露聚糖海绵具有2个不同粗糙程度的表面,作为人体清洁用品的用途,以适应人体的不同肤质。
本发明与现有技术相比,具有以下显著的进步和突出的特点:
第一、能够有效地将制作程序简化,缩短制作时间,提高产能,一般来说,只需要15~24小时即可完成。
第二、本发明方法可使2个经由不同反应时间的葡甘露聚糖凝胶彼此结合,从而形成具有两种不同孔密度的海绵。
第三、本发明方法制得的双面异体葡甘露聚糖海绵,具有2个不同粗糙程度的表面,能够适用于人体的不同肤质,达到清洁与保养的双重功效。
附图说明
下面结合附图和实施例对本发明作进一步说明。
图1是本发明以较佳实施例所制得的双面异体葡甘露聚糖海绵的外观图;
图2是图1沿2-2方向的剖面图。
图中:1是双面异体葡甘露聚糖海绵;2是第一海绵;201是第一孔密度;3是第二海绵;301是第二孔密度。
具体实施方式
参照图1及图2所示,本发明一种双面异体葡甘露聚糖海绵的制造方法,它是将2个经不同反应时间的葡甘露聚糖凝胶彼此结合,而形成一块具有两种不同孔密度的海绵,亦即该海绵具有2个不同粗糙程度的表面,用以适应人体的不同肤质。
具体而言,本实施例的操作步骤如下:
a、按食用碱∶热水=10g∶100g的重量配比,用热水将食用碱溶解为碱水;
b、按葡甘露聚糖∶水=5g∶100g的重量配比,将葡甘露聚糖混合至水中,经快速搅拌3分钟,使其成为粘稠状的葡甘露聚糖精粉液;
c、按碱水∶葡甘露聚糖精粉液=10g∶100g的重量配比,将碱水加入粘稠状的葡甘露聚糖精粉液中并混合均匀,以除去葡甘露聚糖精粉液中的乙酰基,形成葡甘露聚糖混合物;
d、将葡甘露聚糖混合物平均分成两份,其中一份葡甘露聚糖混合物倒入一预定形状的容器中,倒入量为容器容积的一半;
e、取灌好模的葡甘露聚糖混合物,放入加热设备中加热至90℃,进行交联反应,反应时间为50分钟,形成第一胶体。
f、将第一胶体取出后覆盖于另一份未经反应的葡甘露聚糖混合物上;
g、将第一胶体与未经反应的葡甘露聚糖混合物置入一预定形状的容器中,倒入量为容器容积的一倍,再次放入加热设备中加热至90℃,进行交联反应,反应时间为50分钟,未经反应的葡甘露聚糖混合物形成第二胶体,并且该第二胶体及第一胶体于接合面相粘合成为一葡甘露聚糖冻状胶体。
h、冷却该葡甘露聚糖冻状胶体至45℃后,以针状工具于该葡甘露聚糖冻状胶体上扎出若干个均匀分布的小孔。
i、将该葡甘露聚糖冻状胶体放入-6℃并具有干燥功能的冷冻箱中冷冻,使水滴凝结于该葡甘露聚糖冻状胶体中,从而形成多孔状的海绵。
j、将柠檬酸加入水中,调节ph值至4,将海绵置入其中并搅拌均匀,浸泡100分钟脱碱,再经漂洗后即得成品(参照图1所示)。
上述中,步骤d所述一预定形状的容器与步骤g所述一预定形状的容器,可以是相同容器,亦可以是不同容器。
更进一步而言,请参照图1及图2所示,以上述方法制得的双面异体葡甘露聚糖海绵1,其是由第一海绵2及第二海绵3所组成的,其中:
该第一海绵2是具有第一孔密度201的块体;
该第二海绵3是具有第二孔密度301的块体,而且与第一海绵2彼此相对地结合成一体,并且,第一孔密度201不同于第二孔密度301。
由于该第一海绵与第二海绵是由不同反应时间所制得,使其内部具有不同的孔密度,因此使得该双面异体葡甘露聚糖海绵具有2个不同粗糙程度的表面,可以藉由该双面异体葡甘露聚糖海绵适应人体不同的肤质状况,也就是,当使用者以该双面异体葡甘露聚糖海绵清洁乳脸部等肤质较细致的部位时,可选择孔密度较高而且具有较平滑表面的海绵,减少伤害皮肤角质层的情形发生;反之,倘若需要清洁如手肘等角质层较厚的部位时,则可选择孔密度较低而且具有较粗糙表面的海绵,达到有效去除老化角质的目的。
以上内容只是结合具体的主要实施方式所做的进一步详细说明,不能认定本发明的具体实施只局限于这些说明。本领域技术人员在不脱离本发明构思的前提下,所作出的其他若干技术精确、美化的推演或替换,都应当属于本发明的保护范围。
Claims (8)
1.一种双面异体葡甘露聚糖海绵的制造方法,其特征在于:其是由至少2个相异的葡甘露聚糖凝胶彼此结合,而形成一具有至少两种不同孔密度的海绵。
2.根据权利要求1所述的双面异体葡甘露聚糖海绵的制造方法,其特征在于:至少2个相异的葡甘露聚糖凝胶的不同是通过反应时间上的差异所造成的。
3.根据权利要求1所述的双面异体葡甘露聚糖海绵的制造方法,其特征在于:其是以交联反应使2个相异的葡甘露聚糖凝胶彼此结合的。
4.根据权利要求1所述的双面异体葡甘露聚糖海绵的制造方法,其特征在于:包括以下步骤:
a、制备一葡甘露聚糖混合物;
b、将步骤a中的葡甘露聚糖混合物平均分成两份,其中一份葡甘露聚糖混合物倒入一预定形状的容器中;
c、将灌好模的葡甘露聚糖混合物,放入加热设备中加热至一预定温度,进行交联反应,经过一预定反应时间,形成第一胶体;
d、将步骤c的第一胶体取出后覆盖于另一份未经反应的葡甘露聚糖混合物上,然后将第一胶体与未经反应的葡甘露聚糖混合物置入一预定形状的容器中,放入加热设备中加热至一预定温度,进行交联反应,经过一预定反应时间;
e、未经反应的葡甘露聚糖混合物形成第二胶体,并且该第二胶体及第一胶体于接合面相粘合成为一葡甘露聚糖冻状胶体;
f、冷却步骤e的葡甘露聚糖冻状胶体,以针状工具于该葡甘露聚糖冻状胶体上扎小孔;
g、将步骤f的葡甘露聚糖冻状胶体放入冷冻箱中冷冻,使水滴凝结于该葡甘露聚糖冻状胶体中,形成多孔状的海绵。
5.根据权利要求4所述的双面异体葡甘露聚糖海绵的制造方法,其特征在于:步骤c所述的预定温度是介于80℃~100℃之间,步骤c所述的预定反应时间是介于30分钟~80分钟之间。
6.根据权利要求4所述的双面异体葡甘露聚糖海绵的制造方法,其特征在于:步骤d所述的预定温度是介于80℃~100℃之间,步骤d所述的预定反应时间是介于30分钟~80分钟之间。
7.一种根据权利要求1的制造方法所制得的双面异体葡甘露聚糖海绵,其特征在于:包含有:
第一海绵,是具有第一孔密度的块体;
第二海绵,是具有第二孔密度的块体,而且与第一海绵彼此相对地结合成一体,其中,第一孔密度不同于第二孔密度。
8.一种根据权利要求1的制造方法所制得的双面异体葡甘露聚糖海绵,其特征在于:其是具有2个不同粗糙程度的表面,作为人体清洁用品,以适应人体的不同肤质。