CN101812803A - 一种可降解的消毒用非织造布及其制备方法 - Google Patents
一种可降解的消毒用非织造布及其制备方法 Download PDFInfo
- Publication number
- CN101812803A CN101812803A CN 200910243014 CN200910243014A CN101812803A CN 101812803 A CN101812803 A CN 101812803A CN 200910243014 CN200910243014 CN 200910243014 CN 200910243014 A CN200910243014 A CN 200910243014A CN 101812803 A CN101812803 A CN 101812803A
- Authority
- CN
- China
- Prior art keywords
- disinfection
- woven fabric
- weaving cloth
- degradable
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种可降解的消毒用非织造布,特别是一种遇水即可释放二氧化氯的可降解的非织造布及其制备方法,其由可降解的吸水树脂和可降解的非织造布复合而成,所述的吸水树脂中混有亚氯酸盐和固体酸,遇水即可释放出具有杀菌消毒作用的二氧化氯。本发明的可降解的消毒用非织造布可广泛用于民用或医用杀菌消毒产品中,具有非常好的杀菌消毒效果,并且具有促进伤口愈合的作用。另外,本发明的可降解的消毒用非织造布由可生物降解的材料制备,制备工艺简单,成本低廉,绿色环保。
Description
技术领域
本发明涉及一种可降解的消毒用非织造布及其制备方法,具体地说,涉及一种遇水即可释放二氧化氯的可降解的非织造布及其制备方法。
背景技术
湿巾已经成为人们必备的清洁品之一,然而传统的湿巾大都是以聚乙烯,聚丙烯,聚酯和聚酰胺为材质的非织造布做为基质的,虽然造价低廉,但是其最大的缺点就是既无法生物降解,又难以回收,大量使用会造成白色污染。此外,为制造功能性湿巾,还需要配制包含许多化学成分的溶液,易污染水源。随着人们环保意识的增强,利用可生物降解材料制造环保湿巾已经成为人们的诉求,越来越多的国家、公司、企业正在大力开发各种可降解的纺织品。
生物可降解性非织造布是一种置于自然环境中在微生物的作用下能缓慢分解而最终消失的环境友好材料。纤维素,甲壳素,壳聚糖,聚乳酸,聚乙烯醇,海藻酸是目前研究最为广泛的生物可降解材料,已经应用与非织造布领域。
二氧化氯是目前公认的一种高效、低毒、快速、广谱的第四代新型杀菌消毒剂,以极强的杀菌力、不致癌、无二次污染的特性被世界卫生组织(WHO)列为A1级消毒剂。经美国环境保护署(EPA)和食品药物管理局(FDA)批准,用于食品保鲜、加工、饮用水的消毒、杀菌、除臭以及工业、农业及医疗卫生中。因其对细菌、真菌、病毒、芽孢有100%的杀菌率,国外已广泛用于医用消毒,但在我国还未推广应用。限制二氧化氯应用的主要原因是因为其不稳定性,受热或遇光易分解,常温下水溶液只能保存8小时,很难长期储存。目前市场上已在使用的缓释二氧化氯产品存在不同程度的缺陷,例如有效期短,释放量不平稳,释放速度难以控制等。
发明内容
本发明的目的是提供一种可降解的消毒用非织造布。
本发明的另一目的是提供上述可降解的消毒用非织造布的制备方法。
本发明进一步的目的是提供上述可降解的消毒用非织造布在民用或医用杀菌消毒产品中的应用。
本发明更进一步的目的是提供一种用上述可降解的消毒用非织造布制成的消毒湿巾。
为了实现本发明目的,本发明的一种可降解的消毒用非织造布,遇水即可进行杀菌消毒,其由可降解的吸水树脂和可降解的非织造布复合而成,所述的吸水树脂中混有亚氯酸盐和固体酸。
前述的可降解的消毒用非织造布,由以下方法制得:将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体酸5-20wt%,将混合后的物料在200-300℃的温度下熔融后喷涂在非织造布上,即得。
前述的可降解的消毒用非织造布,由以下方法制得:将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体酸5-20wt%,然后将混合后的物料均匀地分布在非织造布上;将涂有无甲醛的非水性粘合剂的非织造布覆盖在分布有物料的非织造布上,经滚压黏合后形成复合非织造布。
前述的可降解的消毒用非织造布,其中所述的吸水树脂中还含有0.5-2wt%的固体香料。
前述的可降解的消毒用非织造布,其中所述吸水树脂的原料选自可降解的天然原料,包括纤维素、甲壳素、淀粉、壳聚糖、海藻酸钠等中的一种或几种;或选自可降解的化学原料,包括聚乙烯醇、聚乳酸、聚己内酯、聚乙醇酸等中的一种或几种。
前述的可降解的消毒用非织造布,其中所述吸水树脂的原料优选为壳聚糖或甲壳素。
前述的可降解的消毒用非织造布,其中所述非织造布的材质选自可降解的天然原料或化学原料,天然原料包括纤维素、甲壳素、淀粉、壳聚糖、海藻酸钠等中的一种或几种;化学原料,包括聚乙烯醇、聚乳酸、聚己内酯、聚乙醇酸等中的一种或几种,优选为壳聚糖。
所述的可降解的吸水树脂和非织造布可以是自己合成的,也可以是市售商品。
前述的可降解的消毒用非织造布,其中所述亚氯酸盐优选为亚氯酸钠。
前述的可降解的消毒用非织造布,其中所述固体酸选自柠檬酸、酒石酸、硼酸、草酸、磷酸二氢盐、硫酸氢盐中的一种或几种,优选为柠檬酸或硼酸。
一种制备所述的可降解的消毒用非织造布的方法,包括以下步骤:1)将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体香料0.5-2wt%,固体酸5-20wt%;2)将步骤1)得到的混合物料在200-300℃的温度下熔融,然后喷涂在非织造布上,即得。
所述可降解的消毒用非织造布的另一种制备方法包括以下步骤:1)将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体香料0.5-2wt%,固体酸5-20wt%;2)将步骤1)得到的混合物料均匀地分布在非织造布上;3)将另一块涂有无甲醛的非水性粘合剂的非织造布覆盖在分布有物料的非织造布上,经滚压黏合后形成复合非织造布。
本发明的可降解的消毒用非织造布可广泛应用在民用或医用杀菌消毒产品中。如消毒湿巾、绷带底布、伤口敷布、伤口软垫、吸血布、创可贴等等。
一种用上述的可降解的消毒用非织造布制成的消毒湿巾,遇水即具有优异的杀菌消毒作用。将本发明的可降解的消毒用非织造布作为消毒湿巾使用时,只需要使上述的非织造布湿润即可。上述的非织造布遇水后,吸水树脂会迅速吸水,并将水份传递给亚氯酸盐和固体酸。亚氯酸盐和固体酸在水的作用下发生化学反应,释放出具有杀菌消毒作用的二氧化氯,并通过非织造布的空隙向外扩散。由于亚氯酸盐和固体酸是被混融在吸水树脂中的,吸水树脂的网状结构减慢了亚氯酸盐和固体酸的反应速率,也延缓了二氧化氯的释放速度,因此二氧化氯的释放速度不会因为吸水树脂吸收水分的多少而显著改变。
通常,二氧化氯浓度在0.1-10ppm即可以达到99%的杀菌率,而动物实验表明浓度在200ppm时也无任何副作用。经测定,本发明的可降解的消毒用非织造布遇水后在24h内可以维持二氧化氯浓度在1-15ppm,因此,当细菌、病毒接近非织造布的表面时,就会被二氧化氯迅速杀灭。
优选地,本发明的可降解的消毒用非织造布可作为民用柔巾机的原料,只需要在柔巾机的储液盒中放入清水即可获得现做现用的消毒湿巾。
借由上述技术方案,本发明至少具有下列优点及有益效果:
(1)本发明的可降解的消毒用非织造布由可生物降解的材料制备,在土壤中14天即可以开始降解,一般30-60天左右即可降解完毕,绿色环保。
(2)本发明优选壳聚糖作为非织造布的原料,具有促进伤口愈合的作用。
(3)本发明的可降解的消毒用非织造布遇水即具有杀菌消毒作用,可广泛用于民用或医用杀菌消毒产品中。
(4)本发明的可降解的消毒用非织造布,只需要用水湿润即可成为消毒湿巾,不需要像传统消毒湿巾必需要配制消毒液,防止了水源污染;避免了传统湿巾的塑料包装,避免了塑料对环境的污染,尤其方便家庭使用。
(5)本发明制备的二氧化氯消毒湿巾避免了现有二氧化氯消毒产品的不稳定或二元体系包装等问题,便于保存,现做现用,使用方便,且具有非常好的杀菌效果。
(6)本发明制备工艺简单,成本低廉。
具体实施方式
以下实施例用于说明本发明,但不用来限制本发明的范围。
实施例1可降解的消毒用非织造布的制备
本发明的具体应用实施例中的吸水树脂和非织造布均使用市售商品。
将粉状海藻酸钠吸水树脂72wt%,亚氯酸钠2wt%,固体香料0.5wt%,柠檬酸5wt%,混合均匀,所有物料的水份不超过0.5wt%,将混合后的粉末在260℃的温度下熔融后喷涂在壳聚糖非织造布上。
实施例2可降解的消毒用非织造布的制备
将粉状壳聚糖吸水树脂88wt%,亚氯酸钠0.5wt%,固体香料2wt%,硫酸氢钠10wt%,混合后研磨均匀,所有物料的水份不超过0.5wt%,然后均匀的分布在壳聚糖非织造布上;将另一块涂有无甲醛的醇溶型聚氨酯粘合剂的壳聚糖非织造布覆盖在这块制造布上,经滚压黏合后成复合非织造布。
实施例3用可降解的消毒用非织造布制造的消毒湿巾
将清水均匀喷洒在实施例1制造的可降解的消毒用非织造布上,每克非织造布上2-6ml,即可使用。
实施例4将可降解的消毒用非织造布作为民用柔巾机的原料制造消毒湿巾
将实施例2中制造的可降解的消毒用非织造布加工成柔巾机用卷筒状,放入柔巾机中,在柔巾机的储液盒中加入清水。按照柔巾机的正常操作制备湿巾。
试验例:
1、消毒用非织造布的可降解性观察
用土壤填埋的方法处理实施例1的可降解的消毒用非织造布,观察其降解程度,结果如表1所示:
表1
时间 | 5d | 10d | 15d | 30d | 60d |
降解率 | <1% | 2% | 5% | 30% | 90% |
2、可降解的消毒用非织造布制造的消毒湿巾内二氧化氯浓度测试
实施例3的消毒湿巾24h内二氧化氯浓度测试,结果如表2所示:
表2
时间 | 1min | 10min | 1h | 10h | 24h |
二氧化氯浓度 | 9.6ppm | 11.2ppm | 10.4ppm | 6.1ppm | 1.9ppm |
3、可降解的消毒用非织造布制造的消毒湿巾的杀菌效果
实施例3的消毒湿巾杀菌效果如表3所示:
表3
微生物 | 可能引起的疾病 | 杀灭率%(90秒) |
大肠杆菌 | 肠炎,腹泻,尿道炎,膀胱炎,肾盂肾炎,腹膜炎,阑尾炎,败血症 | >99.999 |
金黄色葡萄球菌 | 腹泻,急性肠炎,呕吐,发热 | >99.999 |
铜绿假单胞菌 | 化脓性病变 | >99.999 |
白色念球菌 | 鹅口疮,阴道炎 | >99.999 |
肺炎克雷伯氏菌 | 气管炎,肺炎,脑膜炎,泌尿系统炎症,创伤病变 | >99.999 |
白色葡萄球菌 | 呕吐,腹泻 | >99.999 |
黑曲霉 | 粮食霉变 | 96.111 |
虽然,上文中已经用一般性说明及具体实施方案对本发明作了详尽的描述,但在本发明基础上,可以对之作一些修改或改进,这对本领域技术人员而言是显而易见的。因此,在不偏离本发明精神的基础上所做的这些修改或改进,均属于本发明要求保护的范围。
Claims (10)
1.一种可降解的消毒用非织造布,其特征在于,其由可降解的吸水树脂和可降解的非织造布复合而成,所述的吸水树脂中混有亚氯酸盐和固体酸。
2.根据权利要求1所述的可降解的消毒用非织造布,由以下方法制得:将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体酸5-20wt%,将混合后的物料在200-300℃的温度下熔融后喷涂在非织造布上,即得。
3.根据权利要求1所述的可降解的消毒用非织造布,由以下方法制得:将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体酸5-20wt%,然后将混合后的物料均匀地分布在非织造布上;将涂有无甲醛的非水性粘合剂的非织造布覆盖在分布有物料的非织造布上,经滚压黏合后形成复合非织造布。
4.根据权利要求1-3任意一项所述的可降解的消毒用非织造布,其特征在于所述的吸水树脂中含有0.5-2wt%的固体香料。
5.根据权利要求1-3任意一项所述的可降解的消毒用非织造布,其中所述吸水树脂的原料选自纤维素、甲壳素、淀粉、壳聚糖、海藻酸钠、聚乙烯醇、聚乳酸、聚己内酯或聚乙醇酸中的一种或几种。
6.根据权利要求1-3任意一项所述的可降解的消毒用非织造布,其中所述非织造布的原料选自可降解的天然原料纤维素、甲壳素、淀粉、壳聚糖或海藻酸钠中的一种或几种以及化学原料聚乙烯醇、聚乳酸、聚己内酯或聚乙醇酸中的一种或几种。
7.根据权利要求1-3任意一项所述的可降解的消毒用非织造布,其中所述固体酸选自柠檬酸、酒石酸、硼酸、草酸、磷酸二氢盐或硫酸氢盐中的一种或几种。
8.一种制备如权利要求4-7任意一项所述的可降解的消毒用非织造布的方法,其特征在于其包括步骤:
1)将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体香料0.5-2wt%,固体酸5-20wt%;
2)将步骤1)得到的混合物料在200-300℃的温度下熔融,然后喷涂在非织造布上,即得。
9.一种制备如权利要求4-7任意一项所述的可降解的消毒用非织造布的方法,其特征在于其包括步骤:
1)将水份含量不超过0.5wt%的下述物料按比例混合均匀,其中吸水树脂70-90wt%,亚氯酸盐0.1-5wt%,固体香料0.5-2wt%,固体酸5-20wt%;
2)将步骤1)得到的混合物料均匀地分布在非织造布上;
3)将涂有无甲醛的非水性粘合剂的非织造布覆盖在分布有物料的非织造布上,经滚压黏合后形成复合非织造布。
10.如权利要求1-7任意一项所述的可降解的消毒用非织造布在民用或医用杀菌消毒产品中的应用。