CN101805992B - 一种用于制造潜水衣的彩色涂布 - Google Patents
一种用于制造潜水衣的彩色涂布 Download PDFInfo
- Publication number
- CN101805992B CN101805992B CN201010126423XA CN201010126423A CN101805992B CN 101805992 B CN101805992 B CN 101805992B CN 201010126423X A CN201010126423X A CN 201010126423XA CN 201010126423 A CN201010126423 A CN 201010126423A CN 101805992 B CN101805992 B CN 101805992B
- Authority
- CN
- China
- Prior art keywords
- curing agent
- colorized
- butanone
- diving suit
- silica gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种用于制造潜水衣的彩色涂布,所述的彩色涂布由以下重量百分比的原料制成:聚氨酯涂层胶40~60,丁酮25~35,硅胶8~12,固化剂4~6,色母4~7。本发明采用聚氨酯涂层胶、丁酮、硅胶、固化剂及色母进行恰当的配比组合,这样所制得的胶水具有不易分层、涂刷性好、韧性好、耐水性强、不易剥离及毒性小等特点,同时可根据需要印刷相应的图案,且可以使被涂覆的潜水衣外表达到色彩艳丽、光滑且容易擦干水分等效果,非常方便实用,推广价值高。
Description
技术领域
本发明涉及潜水衣制造技术领域,具体来说是一种制造潜水衣所用的彩色涂布。
背景技术
目前,市面上所销售的潜水衣种类非常多,其布料一般采用针纹布,由于针纹布在潜水后难于擦干水分,而且容易出现硬化分层、色彩艳丽光亮不足等缺点,因而本发明就应此缺点而改进。
发明内容
本发明的目的是克服上述现有技术的缺点,提供一种不容易硬化分层、可根据需要印刷相应的图案且可以达到色彩艳丽、光滑且容易擦干水分的潜水衣彩色涂布。
本发明可以通过以下技术方案来实现:
本发明公开了一种用于制造潜水衣的彩色涂布,所述的彩色涂布由以下重量百分比的原料制成:
聚氨酯涂层胶40~60 丁酮25~35 硅胶8~12
固化剂4~6 色母4~7。
根据上述配比,该彩色涂布各原料之间的最佳重量百分比如下:
聚氨酯涂层胶50 丁酮30 硅胶10 固化剂5
色母5。
所述的固化剂为环氧树脂胶。
上述原料的采用的聚氨酯涂层胶,其英文名称为:Polyurethane,简称PU,聚氨酯全称为聚氨基甲酸酯,是分子结构中含有-NHCOO-单元的高分子化合物,该单元由异氰酸基和羟基反应而成。它的优势在于:涂层柔软并有弹性;涂层强度好,可用于很薄的涂层;涂层多孔性,具有透湿和通气性能;可以达到耐磨,耐湿,耐干洗等优点。PU涂层胶具有良好的强伸度和耐水性,从组分上来说,它还分为双组分类和单组分类,双组分产品由预聚物和交联剂组成,预聚物是将异氰酸酯与低聚多元醇反应生成的末端为羟基的预聚物,交联剂则是含有多个(三个以上)异氰酸酯基的化合物。在涂层整理时,预聚物与交联剂反应,形成热固性网状薄膜,赋予纺织品优良的性能。为了达到防水透湿的效果,溶剂型涂层整理剂一般采用湿法涂层工艺加工织物。
丁酮,又称甲乙酮,是干馏木材的蒸出液(木醇油)的重要组分,工业上可用二级丁醇脱氢或用丁烯加水氧化法生产。其可以有效用作为溶剂、脱蜡剂,也用于多种有机合成,以及作为合成香料和医药的原料。本发明采用丁酮稀释聚氨酯涂层胶、硅胶原料,使之达到互相溶解的最佳效果。
本发明生产的工艺流程大概如下:
首先,先将聚氨酯涂层胶(PU胶粒)用丁酮进行稀释,然后,稀释后再与硅胶进行接枝配合,使之相互溶解;各胶水溶合后再根据相应比例的色母进行调色;调色准确后再添加适量的固化剂,使胶水更有较好耐湿性、耐折性等,同时达到光亮的色彩效果;最后将胶水涂覆于潜水衣表面上即可,这样胶水可以牢固地覆盖于产品的表面,达到光亮彩艳、光滑、不吸水、有弹性、不易分层等优点。
本发明与现有技术相比有如下优点:
本发明采用聚氨酯涂层胶、丁酮、硅胶、固化剂及色母进行恰当的配比组合,这样所制得的胶水具有不易分层、涂刷性好、韧性好、耐水性强、不易剥离及毒性小等特点,同时可根据需要印刷相应的图案,且可以使被涂覆的潜水衣外表达到色彩艳丽、光滑且容易擦干水分等效果,非常方便实用,推广价值高。
具体实施方式
下面将对本发明作进一步描述:
本发明公开了一种用于制造潜水衣的彩色涂布,所述的彩色涂布由以下重量百分比的原料制成:
聚氨酯涂层胶40~60 丁酮25~35 硅胶8~12
固化剂4~6 色母4~7。
根据上述配比,该彩色涂布各原料之间的最佳重量百分比如下:
聚氨酯涂层胶50 丁酮30 硅胶10 固化剂5
色母5。
所述的固化剂为环氧树脂胶。
上述原料的采用的聚氨酯涂层胶,其英文名称为:Polyurethane,简称PU,聚氨酯全称为聚氨基甲酸酯,是分子结构中含有-NHCOO-单元的高分子化合物,该单元由异氰酸基和羟基反应而成。它的优势在于:涂层柔软并有弹性;涂层强度好,可用于很薄的涂层;涂层多孔性,具有透湿和通气性能;可以达到耐磨,耐湿,耐干洗等优点。PU涂层胶具有良好的强伸度和耐水性,从组分上来说,它还分为双组分类和单组分类,双组分产品由预聚物和交联剂组成,预聚物是将异氰酸酯与低聚多元醇反应生成的末端为羟基的预聚物,交联剂则是含有多个(三个以上)异氰酸酯基的化合物。在涂层整理时,预聚物与交联剂反应,形成热固性网状薄膜,赋予纺织品优良的性能。为了达到防水透湿的效果,溶剂型涂层整理剂一般采用湿法涂层工艺加工织物。
丁酮,又称甲乙酮,是干馏木材的蒸出液(木醇油)的重要组分,工业上可用二级丁醇脱氢或用丁烯加水氧化法生产。其可以有效用作为溶剂、脱蜡剂,也用于多种有机合成,以及作为合成香料和医药的原料。本发明采用丁酮稀释聚氨酯涂层胶、硅胶原料,使之达到互相溶解的最佳效果。
本发明生产的工艺流程大概如下:
首先,先将聚氨酯涂层胶(PU胶粒)用丁酮进行稀释,然后,稀释后再与硅胶进行接枝配合,使之相互溶解;各胶水溶合后再根据相应比例的色母进行调色;调色准确后再添加适量的固化剂,使胶水更有较好耐湿性、耐折性等,同时达到光亮的色彩效果;最后将胶水涂覆于潜水衣表面上即可,这样胶水可以牢固地覆盖于产品的表面,达到光亮彩艳、光滑、不吸水、有弹性、不易分层等优点。
本发明采用聚氨酯涂层胶、丁酮、硅胶、固化剂及色母进行恰当的配比组合,这样所制得的胶水具有不易分层、涂刷性好、韧性好、耐水性强、不易剥离及毒性小等特点,同时可根据需要印刷相应的图案,且可以使被涂覆的潜水衣外表达到色彩艳丽、光滑且容易擦干水分等效果,非常方便实用,推广价值高。
除上最佳实施例外,还可以采用以下实施例:
潜水衣彩色涂布的各原料之间也可以采用以下重量百分比原料制成:
聚氨酯涂层胶55 丁酮31 硅胶8 固化剂4
色母2。
或者也可以采用其它实施例,如下:
聚氨酯涂层胶40 丁酮35 硅胶12 固化剂6
色母7。
所述的固化剂为环氧树脂胶固化剂。
以上所述,仅为本发明的若干实施例而已,并非对本发明作任何形式上的限制;凡本行业的普通技术人员均可按说明书内容而顺畅地实施本发明;但是,凡熟悉本专业的技术人员在不脱离本发明技术方案范围内,可利用以上所揭示的技术内容而作出的些许更动、修饰与演变的等同变化,均为本发明的等效实施例;同时,凡依据本发明的实质技术对以上实施例所作的任何等同变化的更动、修饰与演变等,均仍属于本发明的技术方案的保护范围之内。
Claims (3)
1.一种用于制造潜水衣的彩色涂布,其特征在于:所述的彩色涂布由以下重量百分比的原料制成:
聚氨酯涂层胶40~60 丁酮25~35 硅胶8~12
固化剂4~6 色母4~7。
2.根据权利要求1所述的彩色涂布,其特征在于:所述的彩色涂布由以下重量百分比的原料制成:
聚氨酯涂层胶50 丁酮30 硅胶10 固化剂5
色母5。
3.根据权利要求2所述的彩色涂布,其特征在于:所述的固化剂为环氧树脂胶固化剂。