CN101781493A - 聚氨酯复合水性油墨链接料以及水性油墨的生产方法 - Google Patents
聚氨酯复合水性油墨链接料以及水性油墨的生产方法 Download PDFInfo
- Publication number
- CN101781493A CN101781493A CN 200910205636 CN200910205636A CN101781493A CN 101781493 A CN101781493 A CN 101781493A CN 200910205636 CN200910205636 CN 200910205636 CN 200910205636 A CN200910205636 A CN 200910205636A CN 101781493 A CN101781493 A CN 101781493A
- Authority
- CN
- China
- Prior art keywords
- raw material
- water
- temperature
- reaction
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种聚氨酯复合水性油墨链接料以及水性油墨的生产方法。该方法先将原料A加入反应釜内加温120℃脱水后，待原料A温度降至70℃以下时，再按一定比例和顺序将B和C加入A的反应釜内，升温至60℃-100℃时控温2-15个小时，之后降温80℃以下加入D和E，再升温至60℃-100℃控温2-15个小时，再降温80℃以下加入F和E，这次加料后不再升温，反应2-5个小时，加入G和E，搅拌30-50分钟加入一定量的水和H，再搅拌10-30分钟即成链接料。这时将50％左右的链接料、37％左右的水和助剂以及13％左右的有机颜料经分散研磨后，得到水性油墨(水占总量的70％)，生产成本非常低，用途广泛。
Description
技术领域
本发明涉及聚氨酯复合水性油墨链接料及水性油墨的生产方法，特别涉及一种用水做溶剂的水性油墨(水占总量的70％)，有利于环保，成本低，用途广泛的一种水性油墨的生产方法。
背景技术
现在印刷厂家通常用的是传统的溶剂油墨，这种油墨易挥发、易燃、有毒，污染环境，损害工人身体健康。即使国内有些油墨厂家生产出的水性油墨，里面有一定比例的醇和酯，它仅仅是使用在纸箱、纸袋等纸张方面的印刷，有一定的局限性。在国际市场上没有竞争力。
发明内容
本发明涉及的水性油墨不仅能印刷食品、药品、饮料等纸张方面，还能印刷在以PET、PE为主的塑料包装上，用途非常广泛。
本发明提供一种用水做溶剂的水性油墨成本非常低，用途广泛的一种水性油墨的生产方法。
为了实现上述目的，本发明是先将原料A加入反应釜中，搅拌升温至120℃抽真空脱水1.5小时，再按一定比例和顺序，将B和C加入A的反应釜内升温，当温度升至60℃-100℃时计算时间，反应2-15个小时后降温80℃以下，加入D和E，再升温至60℃-100℃继续反应2-15个小时，再降温80℃以下，按比例和顺序加入F和E，这次加料后不再升温，反应2-5个小时，加入G和E，搅拌30-50分钟加入一定量的水和H，再搅拌10-30分钟既成链接料。将50％左右的链接料、37％左右的水和助剂以及13％左右的有机颜料混合分散后，再经研磨分散得到水性油墨。
加料后反应时间控制在5-7个小时之间，温度控制在60℃-100℃之间；
反应料A、B、C、D、E、F、G、H可以是其他原料；
加反应料时，先降低温度，再按顺序加料，然后升温；
效果比较好的反应时间与反应温度的控制：第一次升温至70℃-90℃，第一次加料时降温70℃以下；第二次升温至70℃-90℃，第二次加料降温还是70℃以下。反应时间都是5-7小时。第二次加料后不再升温，反应2-3个小时加入G和E，搅拌30-50分钟加入一定量的水和H，再搅拌10-30分钟既成链接料。
用50％左右生产好的链接料，再用37％左右的水和助剂以及13％左右的有机颜料，混合后经分散研磨得到水性油墨(水占总量的70％)。
采用上述方法后，使聚氨酯复合水性油墨链接料及水性油墨成本非常低，用途广，经过印刷厂家使用验证，得到客户的好评，确实具备了国际市场的竞争力。
具体实施方式
以下结合实施例对本发明作进一步详细说明。
(1)、称原料A50-150加入反应釜中边搅拌边升温，加温120℃抽真空1.5小时后，停止加温和抽空，待原料A温度降至70℃以下时用；
(2)、按顺序将B原料80-180和C原料1-100加入步骤(1)的反应釜中，升温70℃-90℃控温反应5-7个小时，然后降温70℃以下；
(3)、按顺序将D原料0.01-10和E原料1-50加入步骤(1)的反应釜中，再升温至70℃-90℃继续反应5-7个小时，再降温70℃以下；
(4)、按顺序将F原料1-100和E原料1-50加入步骤(1)的反应釜中，这次加料后不再升温，反应2-3个小时；
(5)、按顺序将G原料50-150和E原料100-200加入步骤(1)的反应釜中，搅拌30-50分钟加料；
(6)、按顺序将水1000-3000和H原料1-50加入步骤(1)的反应釜中，再搅拌10-30分钟既成链接料；
(7)、用连接料30-100加水和助剂10-50，再加有机颜料1-50，混合后经分散研磨包装得到水性油墨(水占总量的70％)。
Claims (5)
1.聚氨酯复合水性油墨链接料以及水性油墨的生产方法，其特点在于：先将原料A加入反应釜内加温120℃抽真空脱水1.5小时，停止加温和抽空，待原料A温度降至70℃以下时，再按一定比例和顺序将B和C加入原料A的反应釜内，边搅拌边升温，当温度升至60℃-100℃时计算时间，反应2-15个小时后降温80℃以下，加入D和E，再升温至60℃-100℃继续反应2-15个小时，再降温80℃以下，按比例和顺序加入F和E，这次加料后不再升温，反应2-5个小时，加入G和E，搅拌30-50分钟加入一定量的水和H，再搅拌10-30分钟既成链接料。将50％左右的链接料、37％左右的水和助剂以及13％左右的有机颜料混合分散后，再经研磨分散得到水性油墨(水占总量的70％)。
2.根据权利要求1所述，其特点在于：先将原料A脱水后再加入B和C反应4-7个小时。
3.根据权利要求1所述，其特点在于：加反应料按比例和顺序加入后再升温。
4.根据权利要求1所述，其特点在于：第一次和第二次升温都是60℃-100℃，第一次和第二次降温都是80℃以下加料，第二次降温加料后不再升温，继续反应2-5个小时，加入G和E，搅拌30-50分钟后，加入一定量的水和H，再搅拌10-30分钟既成链接料。
5.根据权利要求1所述，其特点在于：将50％左右的链接料、37％左右的水和助剂以及13％左右的有机颜料混合分散后，再经研磨分散得到水性油墨(水占总量的70％)。