CN101781414B - 微波硫化双复合胶管的内层胶配方 - Google Patents

微波硫化双复合胶管的内层胶配方 Download PDF

Info

Publication number
CN101781414B
CN101781414B CN2009103113392A CN200910311339A CN101781414B CN 101781414 B CN101781414 B CN 101781414B CN 2009103113392 A CN2009103113392 A CN 2009103113392A CN 200910311339 A CN200910311339 A CN 200910311339A CN 101781414 B CN101781414 B CN 101781414B
Authority
CN
China
Prior art keywords
parts
compound
rubber tube
microwave
vulcanized
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009103113392A
Other languages
English (en)
Other versions
CN101781414A (zh
Inventor
张洪起
王学荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Pengling Group Co ltd
Original Assignee
Tianjin Pengling Rubber Hose Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Pengling Rubber Hose Co Ltd filed Critical Tianjin Pengling Rubber Hose Co Ltd
Priority to CN2009103113392A priority Critical patent/CN101781414B/zh
Publication of CN101781414A publication Critical patent/CN101781414A/zh
Application granted granted Critical
Publication of CN101781414B publication Critical patent/CN101781414B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及微波硫化双复合胶管的内层胶配方。组份和质量份数配方为：丁腈橡胶100份，快压出炭黑80～100份，邻苯二甲酸二辛酯20～30份，除湿消泡剂20～30份，氧化锌4～6份，硬脂酸1～2份，N-苯基-α-奈胺1～2份，N-异丙基-N-对甲苯基对苯二胺2～3份，古马隆树脂5～15份，2-硫醇基苯并噻唑0.6～1份，二硫化二苯并噻唑1.4～1.8份，二烷基二硫化磷酸锌0.8～1.2份，硫磺1.6～2.0份。由于TP/S、除湿消泡剂的加入解决了内层胶微波硫化后出现微孔的问题，与传统蒸汽硫化罐硫化胶管对比，工序简单，节省人力，生产效率提高1倍，产品生产成本降低50％，材料的性能与传统蒸汽硫化罐硫化的相同。

Description

微波硫化双复合胶管的内层胶配方
技术领域
本发明涉及胶管技术领域，特别涉及微波硫化双复合胶管的内层胶配方。
背景技术
目前国际、国内普遍使用的NBR/CSM双复合胶管，内层胶选用丁腈橡胶(简称NBR)，颜色设计为黑色，外层胶选用氯磺化聚乙烯橡胶(简称CSM)，颜色设计为灰色。该胶管简称为NBR/CSM双复合胶管。均采用蒸汽硫化罐高温高压条件下硫化成型制备胶管。该方法首先使用双复合挤出机共挤出制备出半成品胶管，在其表面涂洒隔离剂，然后按规定的长度切割，切割后的半成品胶管堆放在一起，停放4～8小时后，将半成品胶管单层摆放在金属托盘上，最后将金属托盘推进蒸汽硫化罐中，在高温高压条件硫化成型，成型后的胶管使用清洗剂清洗干净。该方法经过了挤出-涂洒隔离剂-定长切割-堆放-停放-摆放-硫化-清洗八道工序，工序繁琐，人力消耗大，生产效率低。
微波硫化双复合胶管是指内层胶和外层胶通过双复合挤出机共挤出而复合在一起的全胶管，采用微波硫化工艺硫化成型。使用微波连续硫化工艺生产NBR/CSM双复合胶管，只需双复合挤出机挤出半成品胶管直接进入微波加热硫化箱中硫化成成品，将成品按定长切割。该方法经过了挤出-硫化-定长切割三道工序，工序简单，节省人力，生产效率高，产品的性能和外观能达到与蒸汽硫化罐硫化相同的效果。蒸汽硫化罐硫化胶管是在高温高压条件硫化，胶管内层胶内部不会出现微孔，但微波硫化产品是在高温常压条件下硫化，胶管内层胶内部容易出现微孔，影响产品的性能和外观。采用微波硫化工艺原有的蒸汽硫化罐硫化工艺的配方不能满足要求，需要设计新的配方，解决内层胶的微孔问题，在与原有工艺相同的材料性能和外观的同时，达到简化工序，节省人力、提高生产效率，降低成本的目的。
发明内容
本发明的目的就是提供一种微波硫化NBR/CSM双复合胶管的内层胶配方，通过合理的配方设计，解决内层胶硫化时产生的微孔，从而达到减少能源消耗，节省人力、提高生产效率，降低成本的效果。
本发明的微波硫化NBR/CSM双复合胶管的内层胶的组份和质量份数配方如下：
丁腈橡胶(NBR)                                  100份，
快压出炭黑(N550)                               80～100份，
邻苯二甲酸二辛酯(DOP)                          20～30份，
除湿消泡剂                                     20～30份，
氧化锌                                         4～6份，
硬脂酸                                         1～2份，
N-苯基-α-奈胺(防老剂甲)                       1～2份，
N-异丙基-N′-对甲苯基对苯二胺(防老剂4010NA)    2～3份，
古马隆树脂                                     5～15份，
2-硫醇基苯并噻唑(M)                            0.6～1份，
二硫化二苯并噻唑(DM)                           1.4～1.8份，
二烷基二硫化磷酸锌(TP/S)                       0.8～1.2份，
硫磺                                           1.6～2.0份。
本发明的胶管由内层胶(NBR)和外层胶(CSM)组成，采用双复合挤出机共挤出微波硫化成型，内层胶为黑色，外层胶为灰色。
内层胶主料是丁腈橡胶，门尼粘度ML1+4 100℃55，丙烯腈含量33％，耐油、耐热性能好
由于橡胶本身补强性差需加入补强剂炭黑，优选快压出炭黑N550，补强性中等，但挤出工艺性好。
快速硫化促进剂二烷基二硫化磷酸锌(TP/S)，TP/S的加入，可以使胶管硫化时进入微波段就能初定型，这样可抑制胶管由于高温常压硫化产生的挥发气体发出微孔。
除湿消泡剂，主要成分氧化钙，能均匀地分散，化合胶料中的水分，可避免因水分挥发造成微孔。
本发明的效果，由于TP/S、除湿消泡剂的加入解决了内层胶微波硫化后出现微孔的问题，与传统蒸汽硫化罐硫化胶管对比，工序简单，节省人力，生产效率提高1倍，产品生产成本降低50％.材料的性能与传统蒸汽硫化罐硫化的相同。
具体实施方式
实施例1：
丁腈橡胶(NBR)                                100份，
快压出炭黑(N550)                             80份，
邻苯二甲酸二辛酯(DOP)                        20份，
除湿消泡剂                                   20份，
氧化锌                                       4份
硬脂酸                                       1份，
N-苯基-α-奈胺(防老剂甲)                     1份，
N-异丙基-N′-对甲苯基对苯二胺(防老剂4010NA)  2份，
古马隆树脂                                   5份，
2-硫醇基苯并噻唑(M)                          0.6份，
二硫化二苯并噻唑(DM)                         1.4份，
二烷基二硫化磷酸锌(TP/S)                     0.8份
硫磺                                         1.6份。
实施例2：
丁腈橡胶(NBR)                                100份，
快压出炭黑(N550)                             90份，
邻苯二甲酸二辛酯(DOP)                        25份，
除湿消泡剂                                   25份，
氧化锌                                       5份
硬脂酸                                       1.5份，
N-苯基-α-奈胺(防老剂甲)                     1.5份，
N-异丙基-N′-对甲苯基对苯二胺(防老剂4010NA)  2.5份，
古马隆树脂                                   10份，
2-硫醇基苯并噻唑(M)                          0.8份，
二硫化二苯并噻唑(DM)                         1.6份，
二烷基二硫化磷酸锌(TP/S)                     1.0份
硫磺                                         1.8份。
实施例3：
丁腈橡胶(NBR)                                100份，
快压出炭黑(N550)                             100份，
邻苯二甲酸二辛酯(DOP)                        30份，
除湿消泡剂                                   30份，
氧化锌                                       6份
硬脂酸                                       2份，
N-苯基-α-奈胺(防老剂甲)                     2份，
N-异丙基-N′-对甲苯基对苯二胺(防老剂4010NA)  3份，
古马隆树脂                                   15份，
2-硫醇基苯并噻唑(M)                          1份，
二硫化二苯并噻唑(DM)                         1.8份，
二烷基二硫化磷酸锌(TP/S)                     1.2份
硫磺                                         2.0份。
采用上述实施例的内层胶配方，内层胶微波硫化后将其横向和纵向切割后目视观察内部无微孔，与传统蒸汽硫化罐硫化相同，材料性能也相同。但工序简单，节省人力，生产效率提高1倍，产品生产成本降低50％.

Claims (1)

1.一种微波硫化双复合胶管的内层胶，其特征是内层胶的组份和质量份数配方如下：
丁腈橡胶                                100份，
快压出炭黑                              80～100份，
邻苯二甲酸二辛酯                        20～30份，
除湿消泡剂                              20～30份，
氧化锌                                  4～6份，
硬脂酸                                  1～2份，
N-苯基-α-萘胺                          1～2份，
N-异丙基-N′-对甲苯基对苯二胺           2～3份，
古马隆树脂                              5～15份，
2-硫醇基苯并噻唑                        0.6～1份，
二硫化二苯并噻唑                        1.4～1.8份，
二烷基二硫化磷酸锌                      0.8～1.2份，
硫磺                                    1.6～2.0份。
CN2009103113392A 2009-12-12 2009-12-12 微波硫化双复合胶管的内层胶配方 Expired - Fee Related CN101781414B (zh)