CN101774782A - Processing method of marble - Google Patents
Processing method of marble Download PDFInfo
- Publication number
- CN101774782A CN101774782A CN200810154255A CN200810154255A CN101774782A CN 101774782 A CN101774782 A CN 101774782A CN 200810154255 A CN200810154255 A CN 200810154255A CN 200810154255 A CN200810154255 A CN 200810154255A CN 101774782 A CN101774782 A CN 101774782A
- Authority
- CN
- China
- Prior art keywords
- marble
- stone grain
- stone
- working method
- hydrochloric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of stone processing, relating to a processing method of marble. The invention has the technical method that marble scraps are smashed and dipped in hydrochloric acid so as to passivate corners; then the marble scraps are washed and dried, adhesive is added to be evenly stirred, and the mixture is filled in a die; the mixture is shaped after dried; and the surface is polished and burnished to obtain marble stone with different decorative patterns. The method solves the problem of reuse of marble scraps, saves raw materials and reduces waste pollution; meanwhile, the obtained new stone has different decorative pattern models and structures, so that the stone can be used for decoration, building and the like.
Description
Technical field
The invention belongs to field of stone processing, relate to a kind of processing method of marble.
Background technology
Marble is a kind of architectural decoration stone material commonly used, because of itself having mixed color, forms the pattern that differs from one another, and therefore often is used as finishing material.According to the difference of decorated style etc., marble often is cut into different shapes, to cooperate the main body effect.Yet after the cutting, a lot of building stones are a kind of waste of material owing to too small or the corner is lofty goes out of use, and also environment are caused certain pollution.
Summary of the invention
The present invention is directed to the problems referred to above, propose a kind of processing method of marble, what can solve the marble rejected material utilizes problem again.
Technical scheme of the present invention is: the marble waste material is smashed, soaked through persalt, make the corner be able to passivation; After flushing is dried, add adhesive glue, stir, pour in the mould, drying is handled aftershaping.The surface promptly obtains having the marble stone material of different decorative patterns through polishing, polished finish.
The marble waste material is smashed the stone grain into 0.5cm-2cm among the present invention.
The used salt acid concentration is at 5%-15% among the present invention, and soak time is 1-3 hour.
Used adhesive glue can be water glass or other industrial glue among the present invention, and addition is the 10%-20% of stone grain weight.
Mould can be made different thickness, row shape and size according to actual needs.
Usefulness of the present invention is to have solved the reuse of marble scraps problem, saves starting material, reduces waste pollution.Simultaneously, the new stone material that obtains has different tread patterns modelings and structure, can be used for decoration, building etc.
Embodiment
Present invention is described in conjunction with embodiment.
Embodiment one:
1, gets the marble waste material,, utilize mineral breaker to pulverize, make it to form size and be the stone grain of 0.5cm as cutting scrap stock etc.
2, the stone grain being placed concentration is 5% hydrochloric acid, soaks 1 hour, and carries out agitation as appropriate; To the corner passivation of stone grain, pull out, clean, dry with clear water.
3, adding weight ratio in the stone grain is 10% water glass, stirs, and pours in the mould, with the vibrator vibration fully.
4, mould is put into baking oven and slowly be heated to 120 ℃, be incubated 6 hours, the demoulding behind the naturally cooling.
5, the surface polish, polished finish, make it level and smooth, expose the marble primary colors, show decorative pattern.
Embodiment two
1, gets the marble waste material,, utilize mineral breaker to pulverize, make it to form size and be the stone grain of 2cm as cutting scrap stock etc.
2, the stone grain being placed concentration is 15% hydrochloric acid, soaks 3 hours, and carries out agitation as appropriate; To the corner passivation of stone grain, pull out, clean, dry with clear water.
3, adding weight ratio in the stone grain is 20% water glass, stirs, and pours in the mould, with the vibrator vibration fully.
4, mould is put into baking oven and slowly be heated to 120 ℃, be incubated 6 hours, the demoulding behind the naturally cooling.
5, the surface polish, polished finish, make it level and smooth, expose the marble primary colors, show decorative pattern.
In carrying out the course of processing, the product of making if desired has certain color, can when irritating mould pigment be added to wherein, makes it to form distinct colors.Can also add the intensity of raising products such as reinforcing bar therein according to size and intensity needs.
Claims (6)
1. processing method of marble is characterized in that comprising following steps:
(1), get the marble waste material, as the cutting scrap stock etc., utilize mineral breaker to pulverize, make it to form the stone grain;
(2), place hydrochloric acid to soak the stone grain, and carry out agitation as appropriate, to the corner passivation of stone grain, pull out, clean, dry with clear water;
(3), in the stone grain, add tackiness agent, stir, pour in the mould, fully with the vibrator vibration;
(4), mould put into baking oven slowly be heated to 120 ℃, be incubated 6 hours, the demoulding behind the naturally cooling;
(5), the surface polishes, polished finish, makes it level and smooth, exposes the marble primary colors, shows decorative pattern.
2. a kind of marble working method according to claim 1 is characterized in that stone grain size is 0.5cm-2cm.
3. a kind of marble working method according to claim 1 is characterized in that concentration of hydrochloric acid is 5%-15%.
4. a kind of marble working method according to claim 1 is characterized in that the hydrochloric acid soak time is 1-3 hour.
5. a kind of marble working method according to claim 1 is characterized in that tackiness agent is preferably water glass.
6. a kind of marble working method according to claim 1, the adding proportion that it is characterized in that tackiness agent is the 10%-20% of stone grain weight.