CN101760861A - Pattern painting fabric - Google Patents
Pattern painting fabric Download PDFInfo
- Publication number
- CN101760861A CN101760861A CN200810175748A CN200810175748A CN101760861A CN 101760861 A CN101760861 A CN 101760861A CN 200810175748 A CN200810175748 A CN 200810175748A CN 200810175748 A CN200810175748 A CN 200810175748A CN 101760861 A CN101760861 A CN 101760861A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fire
- retardant
- camouflage
- winder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multifunctional pattern painting fabric, which is prepared by weaving blended yarns of flame retardant vinyl chloride-acrylonitrile copolymer fibers and cotton fibers in a ratio of 70/30, and composite static wires arranged in the radial direction of the fabric at intervals. In order to overcome the phenomenon of cotton smoldering, the cotton fibers are subjected to flame retardant treatment; and the woven gray fabric is printed with anti-infrared pattern painting, and then subjected to flame retardant waterproofing treatment. The obtained product has good performance, and meets the requirements on function, strength, comfort and appearance.
Description
Technical field:
The present invention relates to a kind of camouflage fabric, relate in particular to multi-functional camouflage fabric.
Background technology:
Bring in constant renewal in along with defence equipment, army's field work in wartime protective clothing has proposed more and more higher requirement to fabric panel, need satisfy permanent fire-retardant, antistatic, waterproof and anti-infrared simultaneously and scout four big functional requirements.
Fire-retardant, the antistatic of existing cotton textiles, waterproof, Infrared Radiation Proof Camouflage Fabric in the prior art owing to adopt flame-retardant after-finishing method to handle fabric, it is powerful reduce too big, particularly tearing brute force is lower, do not reach and wear requirement, and feel is harder, influences wearing comfortableness.And when the multi-functional colour camoufague cloth that adopts polyester filament to develop as raw material, though function and brute force have reached requirement, terylene is met fire and is produced molten drop, and the gas permeability of dacron and hygroscopicity are poor, do not satisfy the requirement of wearing comfortableness and outward appearance.If select fire-retardant polyester filament yarn and yarn interweaving for use, embedding adds the composite conducting silk weaving makes, and fabric property is better, but appearance style is undesirable, does not still reach to wear requirement.
For addressing the above problem, the present invention selects the blended yarn of fire-retardant polyacrylic and polyester fiber and cotton fiber for use, and blending rate is 70/30, and is spaced composite conducting silk weaving system at the fabric warp-wise; For overcoming the cotton phenomenon of glowing, cotton fiber has been carried out flame treatment, the grey cloth of knitting system prints the anti-infrared camouflage color earlier, carries out the fire-resistant waterproof arrangement then.The product that obtains is every functional, satisfies function, intensity, comfortableness and appearance requirement.
Summary of the invention:
The invention discloses a kind of camouflage fabric, select the blended yarn of fire-retardant polyacrylic and polyester fiber and cotton fiber for use, blending rate is 70/30, and is spaced composite conducting silk weaving system at the fabric warp-wise.
Distance is 1-2cm between conductive filament.
Technical process is that strip mixes also → rove → spun yarn → winder → doubling → winder → twist thread → winder → warping → looming → weave → pre-treatment → seal camouflage color → soap → ginning fire retardant and waterproofing agent (fire-retardant, WATER REPELLENT TREATMENT) → preliminary drying → bake → wash → dry → stentering forming → finished product inspection
The fire-retardant polyacrylic and polyester fiber that adopts is the modification Vinyon N, copolymer by acrylonitrile and vinyl chloride or vinylidene chloride is made through wet method or dry spinning, the acrylonitrile proportion is 35%~85% in copolymer, except that monomers such as acrylonitrile, vinyl chloride or vinylidene chloride, generally select for use alkyl or alkenyl sulfonate as the 3rd monomer, to improve the dyeability of fiber.In addition, add 0.3%~10% Sb in the copolymer spinning fluid
2O
3, can play cooperative effect, improve its fire resistance greatly.On chemical constitution, the existing polyacrylonitrile chain link of Vinyon N the chlorofibre chain link is arranged again, thereby it has the feature performance benefit of two kinds of fibers concurrently, not only have the light weight of acrylic fiber, good textile performance such as high-strength, warming, and have the anti-flammability of chlorofibre.
The fire-retardant of Vinyon N mainly is that gas phase is fire-retardant, also has endothermic effect, diluting effect and skin effect to play a role jointly simultaneously.Contain Sb
2O
3The fire retardation of Vinyon N mainly realize Sb by halogen antimony synergistic effect
2O
3Itself is anti-flammability not, and it is the good synergist of halogenated flame retardant, can reduce the halogen flame consumption when share with halogen flame, improves its fire resistance greatly.
This fabric has adopted present state-of-the-art composite conducting silk, and they are spaced in fabric, plays anti-static electrification.Composite conducting fiber can make electric charge leak soon and disperse, and eliminates static by faint corona discharge simultaneously.Detailed process is: 1. the fabric of conductive fiber is owing to static is with in friction; 2. the electric charge that produces in the fabric compiles to conductive fiber, has induced in the conductive fiber and the electrically charged incompatible electric charge of fabric; 3. brought out the generation highfield near the conductive fiber, make its ambient air be subjected to this effect of electric field and ionization, i.e. corona discharge; 4. in the positive and negative ion that corona discharge produces, move to fabric,, thereby eliminate static with the electrically charged neutralization of fabric with the electrically charged incompatible ion of fabric.
Simultaneously can adopt present state-of-the-art organic fluorine waterproof agent, it has splendid water resistance and washability.The organic fluorine waterproof agent has extremely low surface tension, and the fabric face tension force of handling through this waterproofing agent also is lower than oil surface tension well below the surface tension of water, and therefore, this fabric has splendid waterproof and oil repellent energy.
Specific embodiment:
Raw material: fire-retardant Vinyon N and cotton fiber mixed yarn
Blending rate: Vinyon N/cotton proportioning is 70/30
Yarn wire size number: 19.7tex * 2
Warp density (finished product): 315/10cm
Weft density (finished product): 244/10cm
Fabric width (finished product): 120cm
Tissue: 2/1 ↑ or 3/1 ↑
Conductive filament spacing distance: 1.5cm
Technical process:
Strip mixes also → rove → spun yarn → winder → doubling → winder → twist thread → winder → warping → looming → weave → pre-treatment → seal camouflage color → soap → ginning fire retardant and waterproofing agent (fire-retardant, WATER REPELLENT TREATMENT) → preliminary drying → bake → wash → dry → stentering forming → finished product inspection
Dyeing and finishing technology:
Fire-retardant, waterproof prescription (1L dressing liquid)
Cotton fire retardant 100g
Organic fluorine waterproof agent 20g
Crosslinking agent 8g
Catalyst 0.5g
Two soak two roll (pick-up rate 75%) → preliminary drying (105 ℃, 1.5min) → bake (160 ℃, 3min) → washing neutralization → oven dry → stentering forming
Fabric bakes after padding fire retardant, should carry out the alkali cleaning neutralization after baking immediately, to reduce the strength damage of fabric.Flame-proof treatment is after the fabric of washing need be through stentering forming, to improve the waterproof effect of finished product.
Claims (5)
1. camouflage fabric, it is characterized in that: the blended yarn of fire-retardant polyacrylic and polyester fiber and cotton fiber, blending rate are 70/30, and are spaced composite conducting silk weaving system at the fabric warp-wise.
2. camouflage fabric as claimed in claim 1 is characterized in that: distance is 1-2cm between conductive filament.
3. camouflage fabric as claimed in claim 1, it is characterized in that: the fire-retardant polyacrylic and polyester fiber of employing is the modification Vinyon N, copolymer by acrylonitrile and vinyl chloride or vinylidene chloride is made through wet method or dry spinning, and the acrylonitrile proportion is 35%~85% in copolymer.
4. camouflage fabric as claimed in claim 3 is characterized in that: add 0.3%~10% Sb in the copolymer spinning fluid
2O
3
5. a manufacturing is characterized in that as the method for camouflage fabric as described in the claim 1-3: technical process is that strip mixes also → rove → spun yarn → winder → doubling → winder → twist thread → winder → warping → looming → weave → pre-treatment → seal camouflage color → soap → ginning fire retardant and waterproofing agent (fire-retardant, WATER REPELLENT TREATMENT) → preliminary drying → bake → wash → dry → stentering forming → finished product inspection.