CN101760800A - 一种增韧性降解纤维 - Google Patents
一种增韧性降解纤维 Download PDFInfo
- Publication number
- CN101760800A CN101760800A CN200910213572A CN200910213572A CN101760800A CN 101760800 A CN101760800 A CN 101760800A CN 200910213572 A CN200910213572 A CN 200910213572A CN 200910213572 A CN200910213572 A CN 200910213572A CN 101760800 A CN101760800 A CN 101760800A
- Authority
- CN
- China
- Prior art keywords
- percent
- toughened
- polyformaldehyde
- fiber
- maleic anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种增韧性降解纤维，为了使降解纤维的使用寿命增长，选用马来酸酐接枝聚甲醛和丙烯酸乙酯作为增韧改性添加剂，马来酸酐接枝聚甲醛接枝率为0.80％，添加量为0.5～0.8‰wt，丙烯酸乙酯，添加量为0.3～0.5‰wt，与聚丁二酸丁二醇酯进行混合，加入消光剂、阻燃剂等，将搅拌均匀的聚酯进入纺丝装置，经过挤压、喷丝、拉伸工序纺织成降解韧性纤维。
Description
技术领域
本发明涉及一种纤维的制备领域，特别涉及一种增韧性降解纤维。
背景技术
纺织用纤维多是化学纤维，纺织而成的布料被人们使用后很难处理，大多造成环境污染，人们越来越注重实用环保型面料，棉麻类的天然纤维难于赋予其各种各样的功能，所以聚酯型可降解纤维正成为开发热点。纯降解聚酯制备的纤维刚性强，但韧性不足，容易被折断。
发明内容
为了使降解纤维的使用寿命增长，需对聚酯进行改性以提高降解纤维性能，增加其韧性。
一种增韧性降解纤维，选用马来酸酐接枝聚甲醛和丙烯酸乙酯作为增韧改性添加剂，马来酸酐接枝聚甲醛接枝率为0.80％，添加量为0.5～0.8‰wt，丙烯酸乙酯，添加量为0.3～0.5‰wt。
选用聚丁二酸丁二醇酯作为降解纤维原料，聚酯首先在50～60℃真空干燥24小时，再与增韧添加剂进行混合，加入消光剂、阻燃剂等，将搅拌均匀的聚酯进入纺丝装置，经过挤压、喷丝、拉伸工序纺织成纤维。
本发明的进步意义在于：
纺丝成的纤维能有效的提高降解纤维性能，增加其韧性，延长纤维使用寿命。
具体实施方式
为了使降解纤维的使用寿命增长，增韧改性添加剂提高降解纤维性能，增加其韧性。选用马来酸酐接枝聚甲醛和丙烯酸乙酯作为增韧改性添加剂，马来酸酐接枝聚甲醛接枝率为0.80％，添加量为0.5～0.8‰wt，丙烯酸乙酯，添加量为0.3～0.5‰wt。
实施例
选用马来酸酐接枝聚甲醛和丙烯酸乙酯作为增韧改性添加剂，马来酸酐接枝聚甲醛的接枝率为0.80％，添加量为0.6‰wt，丙烯酸乙酯，添加量为0.4‰wt。聚丁二酸丁二醇酯作为降解纤维原料，聚酯首先在50～60℃真空干燥24小时，在与增韧添加剂进行混合，加入消光剂、阻燃剂等，将共混后的聚酯进入纺丝装置，经过挤压、220℃喷丝、多道拉伸工序纺织成纤维。纤维的韧性明显提高，断裂伸长率可达300％。
Claims (1)
1.一种增韧性降解纤维，其特征在于：选用马来酸酐接枝聚甲醛和丙烯酸乙酯作为增韧改性添加剂，马来酸酐接枝聚甲醛接枝率为0.80％，添加量为0.5～0.8‰wt，丙烯酸乙酯，添加量为0.3～0.5‰wt，用聚丁二酸丁二醇酯作为降解纤维原料，聚酯首先在50～60℃真空干燥24小时，再与增韧添加剂进行混合，加入消光剂、阻燃剂等，将搅拌均匀的聚酯进入纺丝装置，经过挤压、喷丝、拉伸工序纺织成纤维。