CN101760088B - 纳米改性环保氧化铁机用色浆及制备方法 - Google Patents

纳米改性环保氧化铁机用色浆及制备方法 Download PDF

Info

Publication number
CN101760088B
CN101760088B CN2009100304843A CN200910030484A CN101760088B CN 101760088 B CN101760088 B CN 101760088B CN 2009100304843 A CN2009100304843 A CN 2009100304843A CN 200910030484 A CN200910030484 A CN 200910030484A CN 101760088 B CN101760088 B CN 101760088B
Authority
CN
China
Prior art keywords
water
color paste
ferric oxide
friendly
nanometer modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2009100304843A
Other languages
English (en)
Other versions
CN101760088A (zh
Inventor
杜长森
周华
孙贵生
肖维意
吴鹏
毕其兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Shiming Technology Co., Ltd.
Original Assignee
Kunshan Sunmun Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Sunmun Technology Development Co Ltd filed Critical Kunshan Sunmun Technology Development Co Ltd
Priority to CN2009100304843A priority Critical patent/CN101760088B/zh
Publication of CN101760088A publication Critical patent/CN101760088A/zh
Application granted granted Critical
Publication of CN101760088B publication Critical patent/CN101760088B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种纳米改性环保氧化铁机用色浆，由氧化铁颜料、水性纳米浓缩浆、水性研磨树脂、润湿分散剂、pH值调节剂、保湿助溶剂、消泡剂和水组成，按原料总重量百分比计：氧化铁颜料：30～50％、水性纳米浓缩浆：10～15％、水性研磨树脂：3～7％、润湿分散剂：6～15％、pH值调节剂：0.1～0.5％、保湿助溶剂：10～12％、消泡剂：0.1～0.3％和余量为水。本发明所得的氧化铁色浆具环保、健康，使用方便之功能；又本发明所得的氧化铁色浆与大多数乳胶漆有良好的相溶性，推广面较广及本发明所得的氧化铁色浆放置二年不絮凝、不沉淀、不会严重分水，具有良好的储存稳定性。

Description

纳米改性环保氧化铁机用色浆及制备方法
技术领域
本发明涉及一种水性色浆，特别是一种用于机械调色的纳米改性环保氧化铁机用色浆。
背景技术
随着涂料工业的迅猛发展，人们选择涂料不仅看重其装饰与保护性，还尤其关注涂料色彩的搭配，为满足人们个性化配色的需要，各知名品牌涂料厂商不断扩大自己在民用市场的销售渠道，又快又准的现场配色服务成为零售店除品牌效益外的又一亮点，因此，建筑涂料民用市场电脑配色系统(POS调色系统)的发展前景越来越被看好。
调色系统是基于计算机仿真技术，利用电脑配色软件和调色机将色浆按一定体积比加入到基础白漆中，通过混匀而后得到与标准色卡颜色十分接近的色漆，这种调色系统中系统用色浆为其核心。
为引导建筑涂料向健康环保方向发展，各国法规都对涂料有明确要求：美国1999年执行的《建筑涂料和工业维护涂料管制条例》以及2008年7月1日颁布实施的1113法规规定对VOC有了越来越眼科的控制；在经济全球化的今天，我国也出台了相应的法规，如：国家标准GB18582-2008《室内装饰装修材料内墙涂料中有害物质限量》中规定水性墙面涂料VOC含量＜120g/L；环境标准HJ/T201-2005《环境标志产品技术要求水性涂料》则更加严格，要求内墙涂料VOC含量＜80g/L，外墙涂料VOC含量＜150g/L。在对涂料控制的同时，行业对机用色浆的环保要求和使用性能均提出了同样高的要求。
目前市售水性机用色浆的有机挥发份(VOC)、重金属、壬基酚聚氧乙烯醚(APEO)含量相对较高，多数涂料厂家开始推出低VOC、甚至零VOC的基础乳胶漆，而与之相配套用于调配低VOC、零VOC色漆的水性机用色浆成为市场的空缺。
发明内容
为了克服上述缺陷，本发明提供一种纳米改性环保氧化铁机用色浆及制备方法，该色浆为高环保、超低VOC产品，可以满足广大群众对健康、环保的需要。
本发明为了解决其技术问题所采用的技术方案是：一种纳米改性环保氧化铁机用色浆，由氧化铁颜料、水性纳米浓缩浆、水性研磨树脂、润湿分散剂、PH值调节剂、保湿助溶剂和水组成，按原料总重量百分比计：
氧化铁颜料：    30～50％
水性纳米浓缩浆：10～15％
水性研磨树脂：  3～7％
润湿分散剂：    6～15％
PH值调节剂：    0.1～0.5％
保湿助溶剂：    10～12％
消泡剂：        0.1～0.3％
余量为水。
本发明的进一步技术方案是：
所述的氧化铁颜料为氧化铁黄(Pigment yellow 42)、氧化铁红(Pigment red 101)和氧化铁黑(Pigment black11)中的任意一种。
所述的润湿分散剂至少为环保型不含VOC的聚丙烯酸铵盐、聚丙烯酸钠盐、脂肪醇聚氧乙烯醚、脂肪酸衍生物、聚丙烯酸酯、烷基硫酸盐、烷基磺酸盐、烷基磷酸盐和烷基苯磺酸盐等化合物中的一种。
所述的水性纳米浓缩浆至少为纳米级氧化锌、二氧化钛、二氧化硅、碳酸钙及硅酸盐矿物质制作成高浓度浆料中的一种。
所述的保湿助溶剂至少为聚乙二醇及其衍生物、聚丙二醇及其衍生物、三甘醇、丙三醇、1，2，4-丁三醇、二甘醇二丁醚、三甘醇一乙醚、四甘醇、四甘醇二甲醚、三乙醇胺、二乙醇胺、丁基二乙醇胺和硫二甘醇中的一种。
所述的PH值调节剂至少为氢氧化钠、氢氧化钾、氨水、尿素、三乙醇胺中的一种。
一种纳米改性环保氧化铁机用色浆的制备方法，按如下步骤进行：
a)将水、润湿分散剂、保湿助溶剂、PH值调节剂投入到分散容器中，分散机转数调至500～700r/min，15min后得一均匀溶液，其中预留总量10％的水备用；
b)将水性纳米颜料浆、水性研磨树脂、氧化铁颜料分别加入到上述混合液中，分散速度调至800～1000r/min，20分钟后研磨；
c)采用卧式砂磨机研磨，中间过程采用激光粒度仪控制色浆粒径分布达到d99小于1um，停止研磨，将预留的水清洗砂磨机；
d)加入0.1％的消泡剂，并在真空脱泡机中进行消泡，过滤包装即可。
本发明的有益效果是：本发明所得的氧化铁色浆具环保、健康，使用方便之功能；又本发明所得的氧化铁色浆与大多数乳胶漆有良好的相溶性，推广面较广及本发明所得的氧化铁色浆放置二年不絮凝、不沉淀、不会严重分水，具有良好的储存稳定性；最后本发明所涉及的氧化铁色浆生产步骤简单，生产综合成本低，节约了能源，提高了产品的商业价值。
具体实施方式
本发明实施例的配方参见表1：表1：(单位：重量百分比)
Figure GSB00000680600000041
纳米改性环保氧化铁机用色浆的制备方法，按如下步骤进行：
a)将水、润湿分散剂、保湿助溶剂、PH值调节剂投入到分散容器中，分散机转数调至500～700r/min，15min后得一均匀溶液，其中预留总量10％的水备用；
b)将水性纳米颜料浆、水性研磨树脂、氧化铁颜料分别加入到上述混合液中，分散速度调至800～1000r/min，20分钟后研磨；
c)采用卧式砂磨机研磨，中间过程采用激光粒度仪控制色浆粒径分布达到d99小于1um，停止研磨，将预留的水清洗砂磨机；
d)加入0.1％的消泡剂，并在真空脱泡机中进行消泡，过滤包装即可。
本发明所得的氧化铁色浆具环保、健康，使用方便之功能；又本发明所得的氧化铁色浆与大多数乳胶漆有良好的相溶性，推广面较广及本发明所得的氧化铁色浆放置二年不絮凝、不沉淀、不会严重分水，具有良好的储存稳定性；最后本发明所涉及的氧化铁色浆生产步骤简单，生产综合成本低，节约了能源，提高了产品的商业价值。

Claims (5)

1.一种纳米改性环保氧化铁机用色浆，其特征是：由氧化铁颜料、水性纳米浓缩浆、水性研磨树脂、润湿分散剂、pH值调节剂、保湿助溶剂、消泡剂和水组成，按原料总重量百分比计：
氧化铁颜料：30～50％
水性纳米浓缩浆：10～15％
水性研磨树脂：3～7％
润湿分散剂：6～15％
pH值调节剂：0.1～0.5％
保湿助溶剂：10～12％
消泡剂：0.1～0.3％
余量为水。
2.根据权利要求1所述的纳米改性环保氧化铁机用色浆，其特征是：所述的氧化铁颜料为氧化铁黄、氧化铁红和氧化铁黑中的任意一种。
3.根据权利要求1所述的纳米改性环保氧化铁机用色浆，其特征是：所述的润湿分散剂至少为环保型不含VOC的聚丙烯酸铵盐、聚丙烯酸钠盐、脂肪醇聚氧乙烯醚、聚丙烯酸酯、烷基硫酸盐、烷基磺酸盐、烷基磷酸盐和烷基苯磺酸盐化合物中的一种。
4.根据权利要求1所述的纳米改性环保氧化铁机用色浆，其特征是：所述的水性纳米浓缩浆至少为纳米级氧化锌、二氧化钛、二氧化硅、碳酸钙及硅酸盐矿物质制作成浆料中的一种。
5.根据权利要求1所述的纳米改性环保氧化铁机用色浆，其特征是：所述的保湿助溶剂至少为聚乙二醇、聚丙二醇、三甘醇、丙三醇、1，2，4-丁三醇、二甘醇二丁醚、三甘醇一乙醚、四甘醇、四甘醇二甲醚、三乙醇胺、二乙醇胺、丁基二乙醇胺和硫二甘醇中的一种。
CN2009100304843A 2009-04-13 2009-04-13 纳米改性环保氧化铁机用色浆及制备方法 Active CN101760088B (zh)