CN101758009B - 紫外光固化涂料金属贴皮表面施工方法 - Google Patents

紫外光固化涂料金属贴皮表面施工方法 Download PDF

Info

Publication number
CN101758009B
CN101758009B CN 200810207681 CN200810207681A CN101758009B CN 101758009 B CN101758009 B CN 101758009B CN 200810207681 CN200810207681 CN 200810207681 CN 200810207681 A CN200810207681 A CN 200810207681A CN 101758009 B CN101758009 B CN 101758009B
Authority
CN
China
Prior art keywords
ultraviolet light
drying
roller coat
energy
metal skin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 200810207681
Other languages
English (en)
Other versions
CN101758009A (zh
Inventor
黄仕高
王向科
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuhai zhanchen New Material Co., Ltd
Original Assignee
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Zhanchen Paint Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Fuchen Chemical Co Ltd, Beijing Zhanchen Chemical Co Ltd, Zhanchen Paint Group Co Ltd filed Critical Shanghai Fuchen Chemical Co Ltd
Priority to CN 200810207681 priority Critical patent/CN101758009B/zh
Publication of CN101758009A publication Critical patent/CN101758009A/zh
Application granted granted Critical
Publication of CN101758009B publication Critical patent/CN101758009B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种紫外光固化涂料金属涂装的施工工艺。其特征在于有下列步骤组成：素材处理，烘干，用辊涂一道底漆，用紫外光干燥机将能量调整至350～400mj/cm2干燥，用辊涂二道底漆，用紫外光辊涂底漆，用紫外光干燥机将能量调整至250～300mj/cm2干燥，砂光，除尘，淋前辊涂，用紫外光淋涂亮光清面漆，流平，用紫外光干燥机将能量调整至300～500mj/cm2全干燥，成品。本发明的优点是生产效率高，涂装后在低温或高温下均不开裂，附着力佳，漆膜丰满度佳。

Description

紫外光固化涂料金属贴皮表面施工方法
技术领域
本发明涉及一种紫外光固化涂料金属涂装的施工工艺。
背景技术
目前在一些装潢业中需要在一些建筑物的表面包上金属贴皮，为了更加美化设计及与周围环境适合，有时要进行涂装，但是由于施工的工艺存在问题，涂装在外经风吹雨打，烈日爆晒，涂装容易起皮剥离，因此亟待发明一种新型的紫外光固化涂料金属贴皮表面施工方法。
发明内容
本发明的目的是解决现有技术中在金属贴皮表面进行涂装施工所存在的上述问题，提供一种紫外光固化涂料金属贴皮表面施工方法。本发明设计紫外光固化涂料金属贴皮表面施工方法，其特征在于有下列步骤组成：
(1)素材处理：用20％工业用盐酸擦试，去除金属贴皮表面油质、污质，
(2)烘干：用红外线对金属贴皮表面加温至100～120℃，10～15min烘干，
(3)用辊涂一道底漆：用紫外光辊涂底漆水浴加温在40～60℃均可，
(4)干燥：用紫外光干燥机将能量调整至350～400mj/cm2干燥，
(5)用辊涂二道底漆：用紫外光辊涂底漆，水浴加温在35～50℃均可，
(6)干燥：用紫外光干燥机将能量调整至250～300mj/cm2干燥，
(7)砂光：用320#～400#砂纸砂磨，
(8)除尘：用除尘机除去表面灰尘，
(9)淋前辊涂：用紫外光辊涂二道底漆，
(10)淋涂面漆：用紫外光淋涂亮光清面漆，
(11)流平：用40℃～60℃红外线流平机过10～15min，
(12)干燥：用紫外光干燥机将能量调整至300～500mj/cm2全干燥，成品。
本发明的优点是生产效率高，涂装后在低温或高温下均不开裂，附着力佳，漆膜丰满度佳。
下面结合实例对本发明作详细说明。
具体实施方式
实施例1：
(1)素材处理：用20％工业用盐酸擦试，去除表面油质、污质；
(2)烘干：用本领域通用设备红外线加温至100℃，10min烘干；
(3)辊涂一道底漆：用上海富臣化工生产的紫外光辊涂底漆FU2010M，水浴箱加温在40℃均可；
(4)干燥：用本领域通用紫外光干燥机将灯光能量调整至350mj/cm2干燥；
(5)辊涂二道底漆：用上海富臣化工生产的紫外光辊涂底漆FU2020MFC，水浴加温在35℃均可；
(6)干燥：用紫外光干燥机将能量调整至250mj/cm2干燥；
(7)砂光：用320#砂纸砂磨平整光滑；
(8)除尘：用除尘机除去表面灰尘；
(9)UV淋前辊涂：用本领域通用设备、单辊机或双辊机均可，油漆可用上海富臣化工生产的FU2020MFC二道底漆；
(10)淋涂UV亮光清面漆：用上海富臣化工生产的淋涂亮光清面漆FU3220；
(11)流平：用本领域通用设备红外线加温40℃流平机过10min；
(12)干燥：用紫外光干燥机将能量调整至300mj/cm2全干燥，成品。
实施例2：
(1)素材处理：用20％工业用盐酸擦试，去除表面油质、污质；
(2)烘干：用红外线加温至110℃，12min烘干；
(3)辊涂一道底漆：用上海富臣化工生产的紫外光辊涂底漆FU2010M，水浴加温在50℃均可；
(4)干燥：用紫外光干燥机将能量调整至380mj/cm2干燥；
(5)辊涂二道底漆：用上海富臣化工生产的紫外光辊涂底漆FU2020MFC，水浴加温在40℃均可；
(6)干燥：用紫外光干燥机将能量调整至280mj/cm2干燥；
(7)砂光：用400#砂纸砂磨平整光滑；
(8)除尘：用除尘机除去表面灰尘；
(9)淋前辊涂：用上海富臣化工生产的FU2020MFC二道底漆；
(10)淋涂面漆：用上海富臣化工生产的淋涂亮光清面漆FU3220；
(11)流平：用50℃红外线流平机过13min；
(12)干燥：用紫外光干燥机将能量调整至400mj/cm2全干燥，成品。
实施例3：
(1)素材处理：用20％工业用盐酸擦试，去除表面油质、污质；
(2)烘干：用红外线加温至120℃，15min烘干；
(3)辊涂一道底漆：用上海富臣化工生产的紫外光辊涂底漆FU2010M，水浴加温在60℃均可；
(4)干燥：用紫外光干燥机将能量调整至400mj/cm2干燥；
(5)辊涂二道底漆：用上海富臣化工生产的紫外光辊涂底漆FU2020MFC，水浴加温在50℃均可；
(6)干燥：用紫外光干燥机将能量调整至300mj/cm2干燥；
(7)砂光：用320#砂纸砂磨平整光滑；
(8)除尘：用除尘机除去表面灰尘；
(9)淋前辊涂：用上海富臣化工生产的FU2020MFC二道底漆；
(10)淋涂面漆：用上海富臣化工生产的淋涂亮光清面漆FU3220；
(11)流平：用60℃红外线流平机过13min；
(12)干燥：用紫外光干燥机将能量调整至500mj/cm2全干燥，成品。

Claims (1)

1.紫外光固化涂料金属贴皮表面施工方法，其特征在于由下列步骤组成：
(1)素材处理：用20％工业用盐酸擦试，去除金属贴皮表面油质、污质，
(2)烘干：用红外线对金属贴皮表面加温至100～120℃，10～15min烘干，
(3)用辊涂一道底漆：用紫外光辊涂底漆水浴加温在40～60℃均可，
(4)干燥：用紫外光干燥机将能量调整至350～400mj/cm2干燥，
(5)用辊涂二道底漆：用紫外光辊涂底漆，水浴加温在35～50℃均可，
(6)干燥：用紫外光干燥机将能量调整至250～300mj/cm2干燥，
(7)砂光：用320#～400#砂纸砂磨，
(8)除尘：用除尘机除去表面灰尘，
(9)淋前辊涂：用紫外光辊涂二道底漆，
(10)淋涂面漆：用紫外光淋涂亮光清面漆，
(11)流平：用40℃～60℃红外线流平机过10～15min，
(12)干燥：用紫外光干燥机将能量调整至300～500mj/cm2全干燥，成品。
CN 200810207681 2008-12-24 2008-12-24 紫外光固化涂料金属贴皮表面施工方法 Active CN101758009B (zh)