CN101746964B - 一种钛合金玻璃封接工艺方法 - Google Patents

一种钛合金玻璃封接工艺方法 Download PDF

Info

Publication number
CN101746964B
CN101746964B CN2008102299582A CN200810229958A CN101746964B CN 101746964 B CN101746964 B CN 101746964B CN 2008102299582 A CN2008102299582 A CN 2008102299582A CN 200810229958 A CN200810229958 A CN 200810229958A CN 101746964 B CN101746964 B CN 101746964B
Authority
CN
China
Prior art keywords
glass
titanium alloy
sealing
temperature
glass sealing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008102299582A
Other languages
English (en)
Other versions
CN101746964A (zh
Inventor
姜岩
薛亮
韩继先
魏长有
高爽
周茹
景娜
王驰
高秀娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AVIC Shenyang Xinghua Aero Electrical Appliance Co Ltd
Original Assignee
AVIC Shenyang Xinghua Aero Electrical Appliance Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AVIC Shenyang Xinghua Aero Electrical Appliance Co Ltd filed Critical AVIC Shenyang Xinghua Aero Electrical Appliance Co Ltd
Priority to CN2008102299582A priority Critical patent/CN101746964B/zh
Publication of CN101746964A publication Critical patent/CN101746964A/zh
Application granted granted Critical
Publication of CN101746964B publication Critical patent/CN101746964B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种钛合金玻璃封接工艺方法，具体为用航空电连接器玻璃封接插座、钛合金壳体，与电封玻璃及玻封材料制成的插针，经热处理后制成能耐真空或其他介质的密封插座；工艺过程：抽真空到6.7*102～6.7*101Pa，并升温至320～330℃，保温8～12分钟；在保温结束后充入氩气气氛保护，压力≥0.08MPa，升温至500～600℃，保温18～22分钟；缓升温至960～970℃，保温18～22分钟。本发明的优点：保证玻璃与钛合金壳体的亲和性，封接过程中使炉内各部分温度均匀一致，熔融状态下的玻璃绝缘体与壳体和插针充分封接，获得良好的气密性，封接效果好，具有广泛的市场前景。

Description

一种钛合金玻璃封接工艺方法
技术领域
本发明涉及钛合金玻璃封接计数领域，特别提供了一种钛合金玻璃封接工艺方法。
背景技术
目前，钛合金玻璃封接工艺技术成本高，封接效果不好，迫切需要一种新的封接工艺解决封接效果不好的问题。
发明内容
本发明的目的是为了加强钛合金玻璃封接工艺的封接效果，特别提供了一种钛合金玻璃封接工艺。
本发明提供了一种钛合金玻璃封接工艺方法，其特征在于：所述的钛合金玻璃封接工艺方法具体为用航空电连接器玻璃封接插座1、钛合金壳体2，与电封玻璃及玻封材料制成的插针3，经热处理后制成能耐真空或其他介质的密封插座；
工艺过程：抽真空到6.7*102～6.7*101Pa，并升温至320～330℃，保温8～12分钟；作用：排气(壳体预氧化)。保证玻璃与钛合金壳体的亲和性，并在保温结束后充入氩气气氛保护，压力≥0.08MPa，采用氩气气氛保护可有效减少封接过程中氧气氛对钛合金壳体的污染；同时，氩气气氛对封接过程中所用的工装石墨模具有净化作用。升温至500～600℃，保温18～22分钟；作用：均温。使炉内各部分温度均匀一致。缓升温至960～970℃，保温18～22分钟；作用：使熔融状态下的玻璃绝缘体与壳体和插针充分封接，以获得良好的气密性。
所述的工艺过程中，抽真空到6.7*102～6.7*101Pa后，升温的温度优选为325℃。
所述的工艺过程中，在保温结束后充入氩气气氛保护，压力≥0.08MPa，升温的温度优选为550℃。
本发明的优点：
本发明所述的钛合金玻璃封接工艺方法保证玻璃与钛合金壳体的亲和性，有效减少封接过程中氧气氛对钛合金壳体的污染；同时，氩气气氛对封接过程中所用的工装石墨模具有净化作用。封接过程中使炉内各部分温度均匀一致，熔融状态下的玻璃绝缘体与壳体和插针充分封接，获得良好的气密性，封接效果好，具有广泛的市场前景。
附图说明
下面结合附图及实施方式对本发明作进一步详细的说明：
图1为密封插座结构示意图。
具体实施方式
实施例1
一种钛合金玻璃封接工艺方法，其特征在于：所述的钛合金玻璃封接工艺方法具体为用航空电连接器玻璃封接插座1、钛合金壳体2，与电封玻璃及玻封材料制成的插针3，经热处理后制成能耐真空或其他介质的密封插座；
工艺过程：抽真空到6.7*102～6.7*101Pa，并升温至320℃，保温8分钟；作用：排气(壳体预氧化)。保证玻璃与钛合金壳体的亲和性，并在保温结束后充入氩气气氛保护，压力≥0.08MPa，采用氩气气氛保护可有效减少封接过程中氧气氛对钛合金壳体的污染；同时，氩气气氛对封接过程中所用的工装石墨模具有净化作用。升温至500℃，保温18分钟；作用：均温。使炉内各部分温度均匀一致。缓升温至960℃，保温18分钟；作用：使熔融状态下的玻璃绝缘体与壳体和插针充分封接，以获得良好的气密性。
实施例2
一种钛合金玻璃封接工艺方法，其特征在于：所述的钛合金玻璃封接工艺方法具体为用航空电连接器玻璃封接插座1、钛合金壳体2，与电封玻璃及玻封材料制成的插针3，经热处理后制成能耐真空或其他介质的密封插座；
工艺过程：抽真空到6.7*102～6.7*101Pa，并升温至325℃，保温10分钟；作用：排气(壳体预氧化)。保证玻璃与钛合金壳体的亲和性，并在保温结束后充入氩气气氛保护，压力≥0.08MPa，采用氩气气氛保护可有效减少封接过程中氧气氛对钛合金壳体的污染；同时，氩气气氛对封接过程中所用的工装石墨模具有净化作用。升温至550℃，保温20分钟；作用：均温。使炉内各部分温度均匀一致。缓升温至965℃，保温20分钟；作用：使熔融状态下的玻璃绝缘体与壳体和插针充分封接，以获得良好的气密性。
实施例3
一种钛合金玻璃封接工艺方法，其特征在于：所述的钛合金玻璃封接工艺方法具体为用航空电连接器玻璃封接插座1、钛合金壳体2，与电封玻璃及玻封材料制成的插针3，经热处理后制成能耐真空或其他介质的密封插座；
工艺过程：抽真空到6.7*102～6.7*101Pa，并升温至330℃，保温12分钟；作用：排气(壳体预氧化)。保证玻璃与钛合金壳体的亲和性，并在保温结束后充入氩气气氛保护，压力≥0.08MPa，采用氩气气氛保护可有效减少封接过程中氧气氛对钛合金壳体的污染；同时，氩气气氛对封接过程中所用的工装石墨模具有净化作用。升温至600℃，保温22分钟；作用：均温。使炉内各部分温度均匀一致。缓升温至970℃，保温22分钟；作用：使熔融状态下的玻璃绝缘体与壳体和插针充分封接，以获得良好的气密性。

Claims (3)

1.一种钛合金玻璃封接工艺方法，其特征在于：所述的钛合金玻璃封接工艺方法具体为用航空电连接器玻璃封接插座(1)、钛合金壳体(2)，与电封玻璃及玻封材料制成的插针(3)，经热处理后制成能耐真空或其他介质的密封插座；
工艺过程：抽真空到6.7*102～6.7*101Pa，并升温至320～330℃，保温8～12分钟；在保温结束后充入氩气气氛保护，压力≥0.08MPa，升温至500～600℃，保温18～22分钟；缓升温至960～970℃，保温18～22分钟。
2.按照权利要求1所述的钛合金玻璃封接工艺方法，其特征在于：所述的工艺过程中，抽真空到6.7*102～6.7*101Pa后，升温的温度为325℃。
3.按照权利要求1所述的钛合金玻璃封接工艺方法，其特征在于：所述的工艺过程中，在保温结束后充入氩气气氛保护，压力≥0.08MPa，升温的温度为550℃。
CN2008102299582A 2008-12-19 2008-12-19 一种钛合金玻璃封接工艺方法 Active CN101746964B (zh)