CN101735705B - 一种自干型镜背保护涂料 - Google Patents
一种自干型镜背保护涂料 Download PDFInfo
- Publication number
- CN101735705B CN101735705B CN2010100313686A CN201010031368A CN101735705B CN 101735705 B CN101735705 B CN 101735705B CN 2010100313686 A CN2010100313686 A CN 2010100313686A CN 201010031368 A CN201010031368 A CN 201010031368A CN 101735705 B CN101735705 B CN 101735705B
- Authority
- CN
- China
- Prior art keywords
- protective coating
- self
- back protective
- mirror back
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种自干型镜背保护涂料，其组成成分及重量百分比为：油基树脂40-50％，颜料5-15％，填料25-48％，溶剂3-5％，助剂2-5％。本发明涉及的自干型镜背保护涂料以可再生的植物油为原料，以对人体无害的非苯类溶剂为稀释用溶剂，颜料、填料以及催干剂均不含对环境有害的铅、铬等重金属，各原料环保无毒、使用安全。
Description
技术领域
本发明属于涂料领域，尤其是一种超快自干型镜背保护涂料。
背景技术
传统的自干型镜背保护涂料多选用醇酸树脂为基料，通过Co、Mn、Pb、Zn、Ca等催干剂作用于树脂中植物油所含的双健氧化干燥成膜，一般需要18-24h才能达到实际干燥，若达到可装箱的程度则需要72h，这就要求用户必须配备有相当大的干燥场地，给用户生产带来极大不便，因此迫切要求提高镜背保护涂料的干燥速度，以节省干燥时间和企业生产场地。近年来铝镜的使用范围越来越广，对铝镜保护涂料的要求也逐渐提高，尤其是在苛刻条件下使用的铝镜各项指标要求也相对提高，不仅需要高硬度、高耐水、高耐盐雾的性能，而且增加了耐二甲苯擦拭的指标，目前的溶剂自干型镜背保护涂料已远远不能满足这些要求。
发明内容
本发明的目的在于克服现有技术的不足，提供一种相对安全环保、干燥速度快、耐二甲苯擦拭、单组份的超快自干型镜背保护涂料。
本发明的目的是通过以下技术方案实现的：
一种超快自干型镜背保护涂料，其组成成分及重量百分比为：
油基树脂 40-50％
颜料 5-15％
填料 25-48％
溶剂 3-5％
助剂 2-5％。
而且，所述颜料包括钛白粉、炭黑、酞青蓝之一或者混合物。
而且，所述填料包括碳酸钙、滑石粉、硫酸钡之一或者混合物。
而且，所述溶剂松节油、200#溶剂油或芳烃类溶剂。
而且，所述助剂的种类包括防沉剂、催干剂、防结皮剂。
而且，所述油基树脂的制备方法：其特征在于：制备的主要步骤是：将含共扼双键的植物油和含酚树脂在催化剂的存在下，隔绝空气，经275-285℃反应1-3h，控制聚合粘度为6#涂杯80S-100S，反应结束后降 温至120-150℃，除去催化剂，即得油基树脂，经有机溶剂稀释后过滤备用。
而且，所述油基树脂的制备方法中各物质的重量百分比为：
植物油 25-30％
含酚树脂 35-45％
催化剂 0.001-0.005％
有机溶剂 30-40％。
而且，所述含共扼双键的植物油为梓油、桐油、脱水蓖麻油其中一种或其混合物。
而且，所述含酚树脂包括纯酚醛树脂。
而且，所述含酚树脂还包括对叔丁基酚树脂、特辛酚树脂、松香改性苹果酸酐或苯酚树脂其中一种。
本发明的优点和积极效果是：
1、本发明涉及的超快自干型镜背保护涂料以可再生的植物油为原料，以对人体无害的非苯类溶剂为稀释用溶剂，颜料、填料以及催干剂均不含对环境有害的铅、铬等重金属，各原料环保无毒、使用安全。
2、本镜背保护涂料的干燥速度较自干型醇酸树脂、丙烯酸改性醇酸树脂、丙烯酸改性环氧脂、单组份聚氨脂等靠氧化交联干燥的基料要快一倍以上，涂料面干15min，实际干燥仅8-12h，24h后即可装箱运输，在满足超快干燥的同时还具有较强的机械性能和防腐性能以及耐二甲苯擦拭能力。
3、本镜背保护涂料为单组分涂料，使用方便，储存和运输更加容易，符合国家节能环保的要求。
具体实施方式
下面通过具体实施例对本发明作进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
本实施例中按照生产1000kg的自干型镜背保护涂料得到以下各原料的重量。
实施例1：
一种超快自干型镜背保护涂料，其组成成分及重量百分比范围为：
油基树脂 40-50％
颜料 5-15％
填料 25-48％
溶剂 3-5％
防沉剂 2-3％
催干剂 0.5-1％
防结皮剂 0.1-0.5％。
其中具体用量以及具体原料名称与重量为：
油基树脂 500kg
颜料(钛白粉∶炭黑∶酞青蓝＝0.9∶0.02∶0.08) 110kg
填料(碳酸钙∶滑石粉∶硫酸钡＝4∶2∶4) 300kg
溶剂(松节油) 50kg
防沉剂(有机膨润土) 30kg
催干剂(多种金属羧酸盐) 5kg
防结皮剂(甲乙酮肟) 5kg
制备方法为：将各组分按照配比要求均匀混合经研磨分散至规定细度，再调整粘度经过过滤即得本超快自干型镜背保护涂料。
所述油基树脂的制备步骤是：将含共扼双键的植物油(梓油)125kg和含酚树脂(纯酚醛树脂)200kg在催化剂(PbO+LiOH)25g的催化下，隔绝空气如氮气保护条件下，经275-285℃反应1-3h，控制聚合粘度为6#涂杯80S-100S，反应结束后降温至120-150℃，除去催化剂，即得油基树脂，用有机溶剂(松节油)175kg稀释后过滤得到500kg油基树脂液备用，其含量约为60％。
其中含共扼双键的植物油包括梓油、桐油、脱水蓖麻油；
含酚树脂包括：纯酚醛树脂及酚醛树脂改性物如对叔丁基酚树脂、特辛酚树脂、松香改性苹果酸酐树脂、苯酚树脂；
催化剂为ZnO、Ca(CH3COO)2、PbO、LiOH中的至少一种；
有机溶剂还可以是松节油、200#溶剂油以及芳烃类溶剂。
纯酚醛树脂(pure phenolic resin)，以甲醛与某些对位和邻位的芳基或C3以上的烷基(如对位叔丁基苯酚或对位苯基苯酚)取代苯酚或甲酚缩聚制得的酚醛树脂，不需用松香改性就可溶于植物油。因不含松香，故称为纯酚醛树脂。为硬而脆的透明固体，软化点一般比松香高30～40℃，不需经过改性，无论碱催化或酸催化，都具有良好的油溶性。不论反应介质pH值的大小，均将生成线性树脂。主要用于涂料工业，并且用对位取代酚制造的树脂，比苯酚制造的树脂保色性更好，形成的漆膜干燥性能、硬度、耐化学药品性、耐水性、绝缘性等都优于松香改性酚醛树脂。
实施例2
一种超快自干型镜背保护涂料，其组成成分及重量分别为：
油基树脂 450kg
颜料(钛白粉∶炭黑∶酞青蓝＝0.9∶0.02∶0.08) 100kg
填料(碳酸钙∶滑石粉∶硫酸钡＝4∶2∶4) 340kg
溶剂(200#溶剂) 50kg
防沉剂(有机膨润土) 45kg
催干剂(多种金属羧酸盐) 10kg
防结皮剂(甲乙酮肟) 5kg
制备方法为：将各组分按照配比要求均匀混合经研磨分散至规定细度，再调整粘度经过过滤即得本超快自干型镜背保护涂料。
所述油基树脂的制备步骤是：将含共扼双键的植物油(桐油)135kg和含酚树脂(对叔丁基酚树脂)157.5kg在催化剂(PbO+LiOH)22.5g的催化下，隔绝空气或氮气保护条件下，经275-285℃反应1-3h，控制聚合粘度为6#涂杯80S-100S，反应结束后降温至120-150℃，除去催化剂，即得油基树脂，再将本树脂经175有机溶剂(200#溶剂)稀释后过滤得到450kg油基树脂备用，其固体含量约为60％。
超快自干型镜背保护涂料的性能检测结果如下：
1、漆膜外观：平整光滑；
2、固体含量：≥60％；
3、粘度：涂4#杯25C°测≥200s；
4、细度：≤30微米；
5、附着力：一级；
6、硬度：HB-H；
7、光泽：8-10；
8、耐水性：≥400h；
9、耐盐雾性：≥400h；
10、干燥性能：面干15分钟，实干8小时；
11、耐二甲苯擦拭：≥30次；
12、储存稳定性：无结皮和严重沉淀。
Claims (8)
1.一种自干型镜背保护涂料，其特征在于：其组成成分及重量百分比为：
所述油基树脂的制备方法为：将含共轭双键的植物油和含酚树脂在催化剂的存在下，隔绝空气，经275-285℃反应1-3h，控制聚合粘度为6#涂杯80S-100S，反应结束后降温至120-150℃，除去催化剂，即得油基树脂，经有机溶剂稀释后过滤备用。
2.根据权利要求1所述的一种自干型镜背保护涂料，其特征在于：所述颜料包括钛白粉、炭黑、酞青蓝之一或者混合物。
3.根据权利要求1所述的一种自干型镜背保护涂料，其特征在于：所述填料包括碳酸钙、滑石粉、硫酸钡之一或者混合物。
4.根据权利要求1所述的一种自干型镜背保护涂料，其特征在于：所述助剂的种类包括防沉剂、催干剂和防结皮剂。
5.根据权利要求1所述的一种自干型镜背保护涂料：其特征在于：所述油基树脂的制备方法中各物质的重量百分比为：
6.根据权利要求1所述的一种自干型镜背保护涂料，其特征在于：所述含共轭双键的植物油为桐油、脱水蓖麻油其中一种或其混合物。
7.根据权利要求1所述的一种自干型镜背保护涂料，其特征在于：所述含酚树脂包括纯酚醛树脂。
8.根据权利要求1所述的一种自干型镜背保护涂料，其特征在于：所述含酚树脂包括对叔丁基酚树脂、特辛酚树脂、松香改性苹果酸酐树脂或苯酚树脂其中一种。