CN101734897A - 一种石膏粘结剂的配方 - Google Patents

一种石膏粘结剂的配方 Download PDF

Info

Publication number
CN101734897A
CN101734897A CN200810230953A CN200810230953A CN101734897A CN 101734897 A CN101734897 A CN 101734897A CN 200810230953 A CN200810230953 A CN 200810230953A CN 200810230953 A CN200810230953 A CN 200810230953A CN 101734897 A CN101734897 A CN 101734897A
Authority
CN
China
Prior art keywords
favorable
parts
mpa
strength
gypsum binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200810230953A
Other languages
English (en)
Inventor
李耕伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Flying Space Building Materials Science And Technology Co ltd
Original Assignee
Henan Flying Space Building Materials Science And Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan Flying Space Building Materials Science And Technology Co ltd filed Critical Henan Flying Space Building Materials Science And Technology Co ltd
Priority to CN200810230953A priority Critical patent/CN101734897A/zh
Publication of CN101734897A publication Critical patent/CN101734897A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种石膏粘结剂的配方，原料按重量调配比例为：脱硫石膏100份，聚乙烯醇0-5份，甲基纤维素0.1-0.7份，柠檬酸钠0-0.2份，干粉搅拌，混匀即成产品。测试报告显示，初凝时间30-100min，终凝时间：45-115min，抗折强度：2.3-2.9MPa，抗压强度：5.5-6.5MPa，粘接(压剪)强度：0.40-0.9MPa。本发明具有以下效果：具有良好的稳定性，保水性和流滑性；粘接性能强、具有良好的亲和力，具有界面活性作用，大幅度提高产品与基材得附着力；具有pH值稳定，良好的润滑性，抗收缩性和抗霉变等性能，不需要再接缝处使用纱布，粘接牢靠，具有微膨胀性，杜绝了开裂现象。

Description

一种石膏粘结剂的配方
技术领域：
本发明涉及一种石膏粘结剂的配方，特别适用于各类石膏板，石膏装饰艺术制品的粘接。
背景技术：
现有的石膏条板之间的接缝处大都采用涂有胶水的纱布进行粘接，这种粘接方式费工、费时，稍有膨胀，就易出现开裂等现象。
发明内容：
本发明的任务是提出一种粘接牢靠，具有良好的亲和力，具有界面活性作用，大幅度提高产品与基材的附着力的一种石膏粘结剂的配方。本发明的任务是这样完成的，一种石膏粘结剂的配方，其特征在于：原料按重量调配比例为：脱硫石膏100份，聚乙烯醇0-5份，甲基纤维素0.1-0.7份，柠檬酸钠0-0.2份，干粉搅拌，混匀即成产品。测试报告显示，初凝时间30-100min，终凝时间：45-115min，抗折强度：2.3-2.9MPa，抗压强度：5.5-6.5MPa，粘接(压剪)强度：0.40-0.9MPa。本发明具有以下效果：具有良好的稳定性，保水性和流滑性；粘接性能强、具有良好的亲和力，具有界面活性作用，大幅度提高产品与基材得附着力；具有PH值稳定，良好的润滑性，抗收缩性和抗霉变等性能，不需要再接缝处使用纱布，粘接牢靠，具有微膨胀性，杜绝了开裂现象。
具体实施方式：
实施例1：
脱硫石膏100份；聚乙烯醇0.01份；甲基纤维素0.1份；柠檬酸0.01份；干粉搅拌，混匀即成产品。
测试报告如下：初凝时间：30min
终凝时间：45min
抗折强度：2.3MPa
抗压强度：5.5MPa
粘接(压剪)强度：0.40MPa
实施例2：
脱硫石膏100份；聚乙烯醇5份；甲基纤维素0.7份；柠檬酸0.2份；干粉搅拌，混匀即成产品。
测试报告如下：初凝时间：100min
终凝时间：115min
抗折强度：2.5MPa
抗压强度：6.5MPa
粘接(压剪)强度：0.60MPa
实施例3：
脱硫石膏100份；聚乙烯醇3份；甲基纤维素0.3份；柠檬酸0.1份；干粉搅拌，混匀即成产品。
测试报告如下：初凝时间：85min
终凝时间：105min
抗折强度：2.90MPa
抗压强度：6.5MPa
粘接(压剪)强度：0.9MPa

Claims (2)

1.一种石膏粘结剂的配方，其特征在于：原料按重量调配比例为：脱硫石膏100份，聚乙烯醇0-5份，甲基纤维素0.1-0.7份，柠檬酸钠0-0.2份，干粉搅拌，混匀即成产品。
2.根据权利要求1所述的一种石膏粘结剂的配方，其特征在于：测试报告显示，初凝时间30-100min，终凝时间：45-115min，抗折强度：2.3-2.9MPa，抗压强度：5.5-6.5MPa，粘接(压剪)强度：0.40-0.9MPa。
CN200810230953A 2008-11-10 2008-11-10 一种石膏粘结剂的配方 Pending CN101734897A (zh)