CN101709492B - 一种化学镀镍液 - Google Patents
一种化学镀镍液 Download PDFInfo
- Publication number
- CN101709492B CN101709492B CN2009102632325A CN200910263232A CN101709492B CN 101709492 B CN101709492 B CN 101709492B CN 2009102632325 A CN2009102632325 A CN 2009102632325A CN 200910263232 A CN200910263232 A CN 200910263232A CN 101709492 B CN101709492 B CN 101709492B
- Authority
- CN
- China
- Prior art keywords
- nickel
- chemical nickel
- brightening agent
- plating solution
- plating liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种化学镀镍液，其组分包括硫酸镍20-30g/L、氯化镍52-58g/L、次磷酸钠30-35g/L、柠檬酸钠10-15g/L、硫酸铝0.5-0.8g/L、光亮剂3-5mL/L和氨水90-100ml/L。本发明的优点是能使镀液的覆盖能力好，能提高镀层的耐腐蚀性。
Description
技术领域
本发明涉及一种电镀液，具体说是一种化学镀镍液。
背景技术
电镀镍主要用作防护装饰性镀层，镍镀层对铁基体而言，属于阴极性镀层，其孔隙率高，因此要用镀铜层作底层或采用多层镍电镀。由于化学镀镍层具有优秀的均匀性、硬度、耐磨和耐蚀性等综合物理化学性能，它广泛用于汽车、自行车、钟表、医疗器械、仪器仪表和日用五金等方面。普通镀镍溶液的主要成分为硫酸镍、氯化钠和硼酸，虽然在普通镀镍溶液加入光亮剂可获得镜面光亮的镍层，但是镀液覆盖能力差、耐蚀性低。
发明内容
发明目的：本发明的目的是为了克服现有技术的不足，提供一种覆盖能力好、耐蚀性高的化学镀镍液。
技术方案：为了解决上述技术问题，本发明的技术方案为：一种化学镀镍液，其组分包括硫酸镍20-30g/L、氯化镍52-58g/L、次磷酸钠30-35g/L、柠檬酸钠10-15g/L、硫酸铝0.5-0.8g/L、光亮剂3-5mL/L和氨水90-100ml/L。
所述光亮剂的组分为氯化亚锡和盐酸。
按照上述配方进行配制，配制过程中，温度为30-40度，用氨水来调整PH值使得PH值在8.5-9.5之间，配好后溶液为深绿色。
有益效果：与现有技术相比，本发明的优点是能使镀液的覆盖能力好，能提高镀层的耐腐蚀性。
具体实施方式
下面结合具体实施例进一步阐明本发明，应理解这些实施例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
实施例1：本发明一种化学镀镍液，其组分包括硫酸镍20g/L、氯化镍52g/L、次磷酸钠30g/L、柠檬酸钠10g/L、硫酸铝0.5g/L、光亮剂3mL/L和氨水90ml/L。所述光亮剂的组分为氯化亚锡和盐酸。在30-40度按照上述配方进行配制，然后用氨水来调整PH值使得PH值为8.5-9.5之间，即得到所述镀镍液。
实施例2：本发明一种化学镀镍液，其组分包括硫酸镍30g/L、氯化镍58g/L、次磷酸钠35g/L、柠檬酸钠15g/L、硫酸铝0.8g/L、光亮剂5mL/L和氨水100ml/L。所述光亮剂的组分为氯化亚锡和盐酸。在30-40度按照上述配方进行配制，然后用氨水来调整PH值使得PH值在8.5-9.5之间，即得到所述镀镍液。
实施例3：本发明一种化学镀镍液，其组分包括硫酸镍25g/L、氯化镍55g/L、次磷酸钠33g/L、柠檬酸钠13g/L、硫酸铝0.6g/L、光亮剂4mL/L和氨水95ml/L。所述光亮剂的组分为氯化亚锡和盐酸。在30-40度按照上述配方进行配制，然后用氨水来调整PH值使得PH值在8.5-9.5之间，即得到所述镀镍液。
Claims (1)
1.一种化学镀镍液，其特征在于：其组分包括硫酸镍20-30g/L、氯化镍52-58g/L、次磷酸钠30-35g/L、柠檬酸钠10-15g/L、硫酸铝0.5-0.8g/L、光亮剂3-5mL/L和氨水90-100ml/L；所述光亮剂的组分为氯化亚锡和盐酸；在温度为30-40度按照所述各组分的配方进行配制，然后用氨水来调整PH值使得PH值在8.5-9.5之间即得所述化学镀镍液。