CN101275222B - 镍-磷-聚四氟乙烯复合镀液 - Google Patents
镍-磷-聚四氟乙烯复合镀液 Download PDFInfo
- Publication number
- CN101275222B CN101275222B CN2007100207647A CN200710020764A CN101275222B CN 101275222 B CN101275222 B CN 101275222B CN 2007100207647 A CN2007100207647 A CN 2007100207647A CN 200710020764 A CN200710020764 A CN 200710020764A CN 101275222 B CN101275222 B CN 101275222B
- Authority
- CN
- China
- Prior art keywords
- nickel
- phosphorus
- plating solution
- polytetrafluorethylecomposite
- composite plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种镍-磷-聚四氟乙烯复合镀液，每升该镍-磷-聚四氟乙烯复合镀液中包含25-40g硫酸镍、20-36g柠檬酸纳、5-12g乙酸钠、15-40g次磷酸钠、0.5-2g的OP-10以及0.4-0.6g的N，N二甲基酰氨溶于水，还包含7-18g铁氟龙乳化液。将NAK-80钢浸泡在该配方中令钢表面镀上一层镍-磷-聚四氟乙烯镀层，该镀层中沉积较多聚四氟乙烯粒子且这些聚四氟乙烯粒子均匀分布，又，该镀层还具有附着良好的优点；另外，该镀液中的聚四氟乙烯粒子稳定不易沉降，可多次重复使用。
Description
【技术领域】
本发明属于金属表面处理领域，具体涉及钢表面的复合镀配方。
【背景技术】
化学复合镀是金属自催化还原过程中，惰性微粒与金属共同沉积在金属表面，形成复合材料镀层的新型工艺技术，特别是化学镀镍磷合金基础上发展的化学复合镀，可以获得各种特殊功能的复合镀层，如高耐磨性、高硬度、减摩自润滑以及梯度材料镀层等等。镍基化学复合镀既具有非晶态合金的优良性能，又具有分散微料的特殊性能，从而满足了现代工业对零件表面性能的特殊要求。
目前镍-磷-聚四氟乙烯(Ni-P-PTFE)复合镀工艺步骤如下：脱脂→水洗→酸洗→水洗→复合镀镍→水洗→热处理，其中复合镀镍步骤使用的镀液由于PTFE粒子的憎液性而在该镀液中易于团聚和沉降，这不仅影响PTFE粒子在镀层中的均匀分布，进而影响镀层的附着效果，而且使得镀液不能多次重复使用。
因此，实有必要提出一种镍-磷-聚四氟乙烯复合镀液，可以改善上述PTFE粒子的沉降特性。
【发明内容】
因此，本发明的目的在于提供一种镍-磷-聚四氟乙烯复合镀液，用以改善其中聚四氟乙烯粒子的沉降特性，进而提高镀层的附着力以及令镀液可重复使用。
为达成上述目的，本发明的镍-磷-聚四氟乙烯复合镀液，其中每升该镍-磷-聚四氟乙烯复合镀液中包含以下物质溶于水：
硫酸镍 25-40g；
柠檬酸钠 20-36g；
乙酸钠 5-12g；
次磷酸钠 15-40g；
OP-10 0.5-2g；
N，N二甲基酰氨 0.4-0.6g；
且每升该镍-磷-聚四氟乙烯复合镀液还包含7-18g铁氟龙乳化液。
使用该镍-磷-聚四氟乙烯复合镀液的步骤如下：
将经过酸洗以及水洗的NAK-80钢在浓度分别为25-40g/L硫酸镍、20-36g/L柠檬酸纳、5-12g/L乙酸钠、15-40g/L次磷酸钠、7-18g/L铁氟龙乳化液、0.5-2g/L的OP-10以及0.4-0.6g/L的N，N二甲基酰氨的该镍-磷-聚四氟乙烯复合镀液中浸泡60-120分钟，工作温度70-95℃，取出后再经一水洗以及一次热处理步骤，则钢表面获得一附着良好的镍-磷-聚四氟乙烯防护膜。
相较于现有技术，将NAK-80钢浸泡在该配方中令钢表面镀上一层镍-磷-聚四氟乙烯镀层，该镀层中沉积较多聚四氟乙烯粒子且这些聚四氟乙烯粒子均匀分布，又，该镀层还具有附着良好的优点；另外，该镀液中的聚四氟乙烯粒子稳定不易沉降，可多次重复使用。
【具体实施方式】
较优地，每升该镍-磷-聚四氟乙烯复合镀液中包含以下物质溶于水，最好为纯水：
硫酸镍 25-40g；
柠檬酸钠 20-36g；
乙酸钠 5-12g；
次磷酸钠 15-40g；
表面活性剂 0.5-2g；
助剂 0.4-0.6g；
且每升该镍-磷-聚四氟乙烯复合镀液还包含7-18g铁氟龙乳化液。
优选地，该表面活性剂为OP-10，该助剂为N，N二甲基酰氨。
优选地，该镍-磷-聚四氟乙烯复合镀液的PH值介于4.8至5.3之间，主要通过添加磷酸水溶液或氢氧化钠水溶液对PH值进行控制。
使用该镍-磷-聚四氟乙烯复合镀液的二较佳实施例如下：
实施例1：
将经过酸洗以及水洗的钢，优选为NAK-80钢在浓度分别为25g/L硫酸镍、20g/L柠檬酸纳、5g/L乙酸钠、15g/L次磷酸钠、7g/L铁氟龙乳化液、0.5g/L的OP-10以及0.4g/L的N，N二甲基酰氨的该镍-磷-聚四氟乙烯复合镀液中浸泡120分钟，工作温度70℃，取出后再经一水洗以及一次热处理步骤，则钢表面获得一附着良好的镍-磷-聚四氟乙烯防护膜。
实施例2：
将经过酸洗以及水洗的钢，优选为NAK-80钢在浓度分别为40g/L硫酸镍、36g/L柠檬酸纳、12g/L乙酸钠、40g/L次磷酸钠、18g/L铁氟龙乳化液、2g/L的OP-10以及0.6g/L的N，N二甲基酰氨的该镍-磷-聚四氟乙烯复合镀液中浸泡60分钟，工作温度95℃，取出后再经一水洗以及一次热处理步骤，则钢表面获得一附着良好的镍-磷-聚四氟乙烯防护膜。
以上NAK-80钢在该镍-磷-聚四氟乙烯复合镀液的浸泡时间以及工作温度不仅限于上述范围，因为它还取决于该镍-磷-聚四氟乙烯复合镀液中各物质的浓度配比以及欲形成防护膜的厚度。
Claims (4)
1.一种镍-磷-聚四氟乙烯复合镀液，其特征在于：每升该镍-磷-聚四氟乙烯复合镀液中还包含以下物质溶于水：
硫酸镍 25-40g；
柠檬酸钠 20-36g；
乙酸钠 5-12g；
次磷酸钠 15-40g；
表面活性剂 0.5-2g；
助剂 0.4-0.6g；
且每升该镍-磷-聚四氟乙烯复合镀液还包含7-18g铁氟龙乳化液；
其中，该表面活性剂为OP-10，该助剂为N，N二甲基酰氨。
2.如权利要求1所述的镍-磷-聚四氟乙烯复合镀液，其特征在于：该镍-磷-聚四氟乙烯复合镀液的PH值介于4.8至5.3之间。
3.如权利要求1所述的镍-磷-聚四氟乙烯复合镀液，其特征在于：该镍-磷-聚四氟乙烯复合镀液的工作温度为70-95℃。
4.如权利要求1所述的镍-磷-聚四氟乙烯复合镀液，其特征在于：溶剂为纯水。