CN101666064B - 沥青裂纹路面的施工方法 - Google Patents
沥青裂纹路面的施工方法 Download PDFInfo
- Publication number
- CN101666064B CN101666064B CN 200910144388 CN200910144388A CN101666064B CN 101666064 B CN101666064 B CN 101666064B CN 200910144388 CN200910144388 CN 200910144388 CN 200910144388 A CN200910144388 A CN 200910144388A CN 101666064 B CN101666064 B CN 101666064B
- Authority
- CN
- China
- Prior art keywords
- asphalt
- pattern
- crack
- crackle
- pavement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
沥青裂纹路面的施工方法，其特征是首先完成路基和基层的施工，在基层上摊铺面层以下部分，再摊铺沥青形成沥青面层，继而将表面制有裂纹纹样的钢模板以其裂纹纹样所在一侧垂直扣压在沥青面层上；使用压路机在钢模板上进行振动压实，使沥青面层上的裂纹纹样的缝隙达到设定的深度和宽度；提起钢模板后向沥青面层上已形成的裂纹纹样缝隙中均匀撒入砂子，用砂子填满裂纹纹样缝隙，再次使用压路机对路面终压；最后用水冲洗沥青面层，并使用混凝土打磨机对沥青面层上裂纹纹样的边缘进行修整，使成型的裂纹纹样准确清晰。本发明方法极大地提高了路面施工质量，有效保证了沥青裂纹路的成型标准性。
Description
技术领域
本发明涉及一种沥青路面的施工方法，更具体地说是应用在特殊场合中的沥青裂纹路面的施工方法。
背景技术
沥青裂纹路面是一些特殊场合中对路面的要求，比如，昆山正新轮胎汽车试验场为提高研发能力需要建造沥青裂纹路面，路面上的裂纹纹样有0.9m宽和1.1m宽两种，裂纹类型有图1a所示的A类，其中A1的长度1000mm、宽为800mm，A2的长和宽均为800mm，以及图1b所示B类，其中B1的长度为1000mm、宽为800mm，B2的长和宽均为800mm，经组合形成有四种排列方式，分别如图2a、图2b、图2c和图2d所示。
图2a是以A1和A2沿长度方向排布，A1与A2之间的距离为900mm。
图2b是以A2和B1沿长度方向排布，A2与B1之间的距离为900mm。
图2c是以B2和A1沿长度方向排布，B2与A1之间的距离为900mm。
图2d是以B2和B1沿长度方向排布，B2与B1之间的距离为900mm。
但是，迄今尚无有关沥青裂纹路面施工方法的公开报导。
若是按照沥青路面的常规铺设方式，在对已形成裂纹纹样的沥青面直接进行终压时，压路机的碾压会使裂纹纹样严重变形，不能保证施工质量。
发明内容
本发明是为避免上述现有技术所存在的不足之处，提供一种沥青裂纹路面的施工方法，以较为简单的方式保证沥青裂纹路面的施工质量。
本发明解决技术问题采用如下技术方案。
1、沥青裂纹路面的施工方法，其特征是按如下步骤操作：
a、首先完成路基和基层的施工，在基层上摊铺面层以下部分，再摊铺沥青形成沥青面层，继而将表面制有裂纹纹样的钢模板以其裂纹纹样所在一侧垂直扣压在沥青面层上；
b、使用压路机在钢模板上进行振动压实，使沥青面层上的裂纹纹样的缝隙达到设定的深度和宽度；
c、垂直提起钢模板，利用漏斗向沥青面层上已形成的裂纹纹样缝隙中均匀撒入砂子，用砂子填满裂纹纹样缝隙，再次使用压路机，对路面进行终压，使路面及砂子表面平整；
d、用水冲洗沥青面层，再使用混凝土打磨机对沥青面层上裂纹纹样的边缘进行修整，使成型的裂纹纹样准确清晰。
2、根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述钢模板是以钢条按照裂纹纹样的线形焊接在平面钢板上，钢条的端面打磨出2mm的光滑导角。
3、根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述步骤a中，在钢模板扣压沥青面层之前，钢模板的表面涂刷有脱模剂。
4、根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述沥青面层采用AC-10型沥青混合料。
5、根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述步骤b中，使用压路机在钢模板上进行振动压实先静压再振动压实。
与已有技术相比，本发明有益效果体现在：
1、本发明在裂纹纹样的缝隙内撒入砂子，可以保证在对沥青路面实施终压时，保持裂纹纹样缝隙的完好，极大地提高了路面施工质量，有效保证了沥青裂纹路的成型标准性。
2、本发明方法施工完成的路面能用于测试轮胎的摩擦性能，能对车辆进行操纵稳定性试验。
3、本发明方法具体可以应用在特殊的沥青道路中，如复合式跳动路、人孔路和凸起路等类似的特殊路面。
附图说明
图1a、图1b为不同类型裂纹纹样示意图。
图2a、图2b、图2c和图2d为两种裂纹纹样的有效组合形状。
以下通过具体实施方式，对本发明作进一步说明。
具体实施方式
本实施例中沥青裂纹路面的施工方法是按如下步骤操作：
1、按常规方法完成道路路基和基层的施工，在道路基层的表面摊铺沥青形成沥青面层，随即在指定区域的沥青面层上放置具有裂纹纹样的钢模板，以钢模板上裂纹纹样所在一侧垂直扣压在沥青面层上；
2、使用压路机在钢模板上进行初压，要注意防止钢板的推移，使沥青面层上的裂纹纹样的缝隙达到设定的深度和宽度；
3、垂直提起钢模板，利用漏斗在沥青面层上已形成的裂纹纹样缝隙中均匀撒入砂子，要避免砂子撒到裂缝以外的沥青面层上，用砂子填满缝隙并刮平砂子表面，使砂子在缝隙中密实，为了确保缝隙尺寸，可以使砂子表面高过缝隙2mm。
4、使用压路机在沥青面上进行终压，使沥青表面基本平整即终压完成；
5、用水冲洗路面，再用混凝土打磨机对沥青面上裂纹纹样的边缘进行修整，使成型的裂纹纹样准确清晰。
施工中，所用的钢模板是以钢条按照裂纹纹样的线形焊接在平面钢板上，钢条的端面打磨出2mm的光滑导角，钢条的厚度即为裂纹的宽度，钢条的宽度即为裂纹的深度。
为了便于钢模板的出模，可以在钢模板扣压沥青路面之前，在钢模板的表面涂刷脱模剂，脱模剂可以直接使用机油。
具体实施中，沥青面层可以按常规采用AC-10型沥青混合料。
所使用的砂子需经过筛网过滤，除去较大颗粒和杂质，保证砂子粒径为0.3～0.6mm。
Claims (4)
1.沥青裂纹路面的施工方法，其特征是按如下步骤操作：
a、首先完成路基和基层的施工，在基层上摊铺面层以下部分，再摊铺沥青形成沥青面层，继而将表面制有裂纹纹样的钢模板以其裂纹纹样所在一侧垂直扣压在沥青面层上；
b、使用压路机在钢模板上进行振动压实，使沥青面层上的裂纹纹样的缝隙达到设定的深度和宽度；
c、垂直提起钢模板，利用漏斗向沥青面层上已形成的裂纹纹样缝隙中均匀撒入砂子，用砂子填满裂纹纹样缝隙，再次使用压路机，对路面进行终压，使路面及砂子表面平整；
d、用水冲洗沥青面层，再使用混凝土打磨机对沥青面层上裂纹纹样的边缘进行修整，使成型的裂纹纹样准确清晰。
2.根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述步骤a中，在钢模板扣压沥青面层之前，钢模板的表面涂刷有脱模剂。
3.根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述沥青面层采用AC-10型沥青混合料。
4.根据权利要求1所述的沥青裂纹路面的施工方法，其特征是所述步骤b中，使用压路机在钢模板上先静压，再振动压实。