CN101643255A - Micro-electrolysis water-activating material and preparation method thereof - Google Patents
Micro-electrolysis water-activating material and preparation method thereof Download PDFInfo
- Publication number
- CN101643255A CN101643255A CN200910170188A CN200910170188A CN101643255A CN 101643255 A CN101643255 A CN 101643255A CN 200910170188 A CN200910170188 A CN 200910170188A CN 200910170188 A CN200910170188 A CN 200910170188A CN 101643255 A CN101643255 A CN 101643255A
- Authority
- CN
- China
- Prior art keywords
- powder
- micro
- electrolysis water
- activating material
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a micro-electrolysis water-activating material and a preparation method thereof. The micro-electrolysis water-activating material comprises the following components by weight:10%-60% of tourmaline, 10%-70% of medical stone, 1%-20% of mica, 1%-20% of selenium powder, 1%-20% of zinc powder, 1%-20% of calcium ion powder, 1%-20% of ferromagnetic powder, 1%-20% of copper powder and 1%-10% of food grade adhesive. The micro-electrolysis water-cleaning material is simple to use, has the functions of delivering extreme infrared, activating water, cleaning water and absorbing and separating harmful gas and impurities of the tobacco and can dissolve out trace elements which are beneficial to human health and release negative ions. The micro-electrolysis water-activating material has simple preparation method and easy operation, and can be widely used in industries such as environmental protection, daily cosmetics, drinking water treatment, tobacco and liquor devices andcontainers and the like.
Description
Technical field
The present invention relates to a kind of micro-electrolysis water-activating material and preparation method thereof, belong to the healthy drinking-water of daily life field.
Background technology
Medical research shows that the potential of hydrogen of human body environment should that is to say between 7.35 to 7.45 that human body presents weakly alkaline could keep normal physiological function and substance metabolism.But, find at urbanite's health survey that at one the inside, city has the person more than 80% often to present in various degree acidic constitution.The human body fluid meta-acid, the vigor of cell will die down, and the metabolism of human body will be slowed down, and will cause heavy burden this time to the internal organs of human body.After time grown, disease will be following, when the body fluid pH value of human body is lower than 7, will produce major disease.Correlative study shows: the tumour patient of chance 100% all is an acidic constitution.In American-European-Japanese area and national of waiting, medical circle has begun to adopt the mode of alkalescent water to treat the disease that various acidic constitutions cause.And the Japan that just begins this research as far back as the thirties in last century, the then undisputed the longest country of the whole world average life span that becomes.So, how to make people's daily life tap water be tending towards weakly alkaline gradually, improve the quality of daily life tap water, become one of problem demanding prompt solution.
Summary of the invention
The present invention provides a kind of micro-electrolysis water-activating material and preparation method thereof in order to improve the quality of people's daily life tap water.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of micro-electrolysis water-activating material comprises following composition by its weight percent meter: 10%～60% tourmalinite, 10%～70% medical stone, 1%～20% Muscovitum, 1%～20% selenium powder, 1%～20% zinc powder, 1%～20% calcium ion powder, 1%～20% ferromagnetic powder, 1%～20% copper powder and 1%～10% food-grade adhesive.
On the basis of technique scheme, the present invention can also do following improvement.
Further, described tourmalinite comprises one or more the mixture in iron tourmaline, dravite and the elbaite, and described ferromagnetic powder comprises in ferric oxide and the Z 250 one or both mixture.
Further, described zinc powder comprises in zinc oxide and the zinc oxide one or both mixture.
Further, the preparation method of described calcium ion powder is as follows: after natural shellfish or animal bone are put into boiling water and boiled, pull out and dry, naturally cool to room temperature after heating again again, take out and make after grinding and screening.
Further, described copper powder comprises in Red copper oxide or the cupric oxide one or both mixture.
Further, described food-grade adhesive comprises in polyvinylpyrrolidone, dextrin and the pregelatinized Starch one or more mixture.
Further, the particle diameter of described food-grade adhesive is less than 20 microns.
Further, the particle diameter of described tourmalinite, medical stone and Muscovitum is less than 20 microns.
Further, the particle diameter of described selenium powder, zinc powder, iodine powder, calcium ion powder, ferromagnetic powder and copper powder is less than 50 microns.
The present invention also provides a kind of technical scheme that solves the problems of the technologies described above as follows: a kind of preparation method of micro-electrolysis water-activating material comprises that to grind to form particle diameter behind the copper powder separated pulverizing that micro-electrolysis water-activating material weight is 10%～60% tourmalinite, 10%～70% medical stone, 1%～20% Muscovitum, 1%～20% selenium powder, 1%～20% zinc powder, 1%～20% calcium ion powder, 1%～20% ferromagnetic powder and 1%～20% be micron order or nano level powder with accounting for; In mixed powder, add the food-grade adhesive that accounts for micro-electrolysis water-activating material weight 1%～10% again and carry out uniform mixing; Then cause granular or strike out irregularly shaped or form filtrable material and get final product by equipment by manufacturing process.
The invention has the beneficial effects as follows: micro-electrolysis water-activating material of the present invention is easy to use, have far infrared rays, activated water, purify waste water, obnoxious flavour and impurity function in the adsorption filtration tobacco, stripping is to the HUMAN HEALTH beneficial trace elements, discharge negative ion, can effectively improve acidic constitution and reduce acidic substance in the tobacco and wine the injury of HUMAN HEALTH.The preparation method of micro-electrolysis water-activating material of the present invention is simple, and processing ease can be widely used in the industries such as environmental protection, daily makeup, drinking water treatment, tobacco and wine equipment and container.
Embodiment
Below principle of the present invention and feature are described, institute gives an actual example and only is used to explain the present invention, is not to be used to limit scope of the present invention.
Micro-electrolysis water-activating material of the present invention comprises following composition by its weight percent meter: 10%～60% tourmalinite, 10%～70% medical stone, 1%～20% Muscovitum, 1%～20% selenium powder, 1%～20% zinc powder, 1%～20% calcium ion powder, 1%～20% ferromagnetic powder, 1%～20% copper powder and 1%～10% food-grade adhesive.
Described tourmalinite comprises one or more the mixture in iron tourmaline, dravite and the elbaite.Described ferromagnetic powder comprises one or both the mixture in ferric oxide and the Z 250.Described zinc powder comprises in zinc oxide and the zinc oxide one or both mixture, use machinery to prepare the micron order zinc powder by lash method, utilize to grind and in the cylindrical shell of certain amplitude vibrations to the zinc particle impact, effect such as friction and make the particle pulverizing, in process of lapping, utilize the hard of high speed rotating to grind, make mutual friction mutually between medium and the particle, collision, particle slippage under enough reactive forces, make the particle fracture, by recrystallize behind the particle repeated deformation, the continuous refinement of powder reaches technical requirements.Described selenium powder is by being precipitated out selenium smart cupric electrolysis, is made into to grind after the particulate state and screening gets final product again.The preparation method of described calcium ion powder is as follows: after natural shellfish or animal bone are put into 80 ℃～90 ℃ boiling water and boiled 10 minutes～15 minutes, pull out and dry, naturally cool to room temperature again after heating 1 hour～2 hours under 200 ℃～250 ℃ in going into again, take out and make after grinding and screening.Described copper powder comprises in Red copper oxide or the cupric oxide one or both mixture.Described food-grade adhesive comprises one or more the mixture in polyvinylpyrrolidone, dextrin and the pregelatinized Starch.The bonding composition of described food-grade adhesive all meets the requirement of state food level, has stopped the use clay and might contain chromic problem as tackiness agent.The particle diameter of described tourmalinite, medical stone and Muscovitum is less than 20 microns.The particle diameter of described selenium powder, zinc powder, iodine powder, calcium ion powder, ferromagnetic powder and copper powder is less than 50 microns.The particle diameter of described food-grade adhesive is less than 20 microns
The 18 kinds of trace elements such as potassium, calcium, magnesium major element and zinc, iron, selenium, copper, iodine that contain needed by human in the described medical stone, but also contain a large amount of zircons, can discharge infrared rays, the water of decomposition molecule also comes activated water by increasing oxonium ion, if in the filter tip of tobacco, add the particle of medical stone, can be when not changing the tobacco flavour and effectively filter Nicotine and tar, and filter effect is good for water filtration and activated carbon filtration.
Described Muscovitum has effects such as the lung of returning, liver, the spleen channel, kidney tonifying, astringing to arrest bleeding, can be used for hindering that labor is deficient, dizzy, palpitation with fear etc.
Described selenium powder is referred to as " anticancer king " in the body trace element by the expert; selenium can prevent that Regular Insulin β cellular oxidation from destroying; promote the sugar metabolism; lowering blood glucose and glucose in urine; also can protect retina; increase Vitrea smooth finish; improve eyesight and prevent cataractous effect; still keep the important element of heart normal function, to the effect that the heart human body has protection and repairs, its bonding force to metal is very strong; can resist the murder by poisoning of cadmium to kidney and sexual gland and nervus centralis; with intravital mercury; tin; thallium; heavy metal combinations such as lead, it is compound and detoxify to form metallic selenium albumen; toxin expelling, the male sex needs more selenium.
Described zinc powder can promote growing of human body, scarce zinc can cause sense of taste decline, apocleisis, partial eclipse, also can increase body immunity, promote the healing of wound and wound, and can keep the male sex's normal spermatogenesis, the male sex can cause sperm quantity minimizing, vigor decline, seminal fluid to liquefy bad in case lack zinc.
Described iodine powder can be used for replenishing the iodine of human body needs, and the grownup is as if iodine deficiency, and Tiroidina can enlargement also produce complication, and hypothyroidism causes dysnoesia.
Described calcium ion powder can be used for replenishing the calcium of human body needs, and calcium deficiency can cause irritated insomnia, slow in reacting.The calcium ion of positively charged allows the inside and outside potential difference that takes place of cell, allows heart is rhythmic beats, sperm DNA foremost, so the acrosome of being made up of calcium is the maturation of the adjustable sexual cell of calcium.
Described ferromagnetic powder can be used for replenishing the iron of human body needs, and owing to the phosphoric acid salt that exists in the meals, carbonate, phytic acid, oxalic acid etc. can form the absorption that insoluble molysite stops iron with nonheme iron, gastric acid secretion also influences the absorption of iron.
Described copper powder can be used for replenishing the copper of human body needs, copper is the indispensable trace element of HUMAN HEALTH, for blood, nervus centralis and immunity system, the growth and the function of hair, skin and bone tissue and brain and liver, heart have material impact, and scarce copper can cause anaemia, skeleton change, coronary heart disease and few hair.
The preparation method of micro-electrolysis water-activating material of the present invention comprises tourmalinite, medical stone, Muscovitum, selenium powder, zinc powder, the iodine powder, calcium ion powder, grinding to form particle diameter behind ferromagnetic powder and the copper powder separated pulverizing is micron order or nano level powder, in mixed powder, add food-grade adhesive again and carry out uniform mixing, then cause granular by manufacturing process or strike out irregularly shaped or form filtrable material by equipment to get final product, described micro-electrolysis water-activating material comprises 10%～60% tourmalinite by its weight percent meter, 10%～70% medical stone, 1%～20% Muscovitum, 1%～20% selenium powder, 1%～20% zinc powder, 1%～20% calcium ion powder, 1%～20% ferromagnetic powder, 1%～20% copper powder and 1%～10% food-grade adhesive.
With three embodiment micro-electrolysis water-activating material of the present invention and preparation method thereof is done further detailed description below.
Embodiment 1
Micro-electrolysis water-activating material in the present embodiment comprises by its weight percent meter: 50% iron tourmaline, 35% medical stone, 2% Muscovitum, 1% selenium powder, 1% oxide powder and zinc, 1% calcium ion powder, 1% ferric oxide powder, 1% cuprous oxide powder and 8% polyvinylpyrrolidone.
Earlier with each component starting material separated pulverizing and be ground to micron or the nano level powder footpath that needs, wherein the particle diameter of iron tourmaline, medical stone, Muscovitum and polyvinylpyrrolidone is less than 20 microns, the particle diameter of selenium powder, oxide powder and zinc, iodine powder, calcium ion powder, ferric oxide powder and cuprous oxide powder is less than 50 microns, after then above-mentioned each component being mixed, cause granular or strike out irregularly shaped by equipment by manufacturing process.Or form filtrable material.
Embodiment 2
Micro-electrolysis water-activating material in the present embodiment comprises by its weight percent meter: 60% dravite, 30% medical stone, 3% Muscovitum, 1% selenium powder, 1% oxide powder and zinc, 1% calcium ion powder, 1% Z 250 powder, 1% cuprous oxide powder and 2% dextrin.
Earlier with each component starting material separated pulverizing and be ground to micron or the nano level powder footpath that needs, wherein the particle diameter of dravite, medical stone, Muscovitum and dextrin is less than 20 microns, the particle diameter of selenium powder, oxide powder and zinc, iodine powder, calcium ion powder, Z 250 powder and cuprous oxide powder is less than 50 microns, after then above-mentioned each component being mixed, cause granular or strike out irregularly shaped by equipment by manufacturing process.Or form filtrable material.
Embodiment 3
Micro-electrolysis water-activating material in the present embodiment comprises by its weight percent meter: 20% elbaite, 70% medical stone, 1% Muscovitum, 2% selenium powder, 2% titanium dioxide zinc powder, 1% calcium ion powder, 1% ferric oxide powder, 1% cupric oxide powder and 2% pregelatinized Starch.
Earlier with each component starting material separated pulverizing and be ground to micron or the nano level powder footpath that needs, wherein the particle diameter of elbaite, medical stone, Muscovitum and pregelatinized Starch is less than 20 microns, the particle diameter of selenium powder, titanium dioxide zinc powder, iodine powder, calcium ion powder, ferric oxide powder and cupric oxide powder is less than 50 microns, after then above-mentioned each component being mixed, cause granular or strike out irregularly shaped by equipment by manufacturing process.Or form filtrable material.
The above only is preferred embodiment of the present invention, and is in order to restriction the present invention, within the spirit and principles in the present invention not all, any modification of being done, is equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. micro-electrolysis water-activating material, it is characterized in that, comprise following composition: 10%～60% tourmalinite, 10%～70% medical stone, 1%～20% Muscovitum, 1%～20% selenium powder, 1%～20% zinc powder, 1%～20% calcium ion powder, 1%～20% ferromagnetic powder, 1%～20% copper powder and 1%～10% food-grade adhesive by its weight percent meter.
2. micro-electrolysis water-activating material according to claim 1, it is characterized in that, described tourmalinite comprises one or more the mixture in iron tourmaline, dravite and the elbaite, and described ferromagnetic powder comprises in ferric oxide and the Z 250 one or both mixture.
3. micro-electrolysis water-activating material according to claim 1 is characterized in that, described zinc powder comprises in zinc oxide and the zinc oxide one or both mixture.
4. micro-electrolysis water-activating material according to claim 1, it is characterized in that the preparation method of described calcium ion powder is as follows: after natural shellfish or animal bone are put into boiling water and boiled, pull out and dry, naturally cool to room temperature after heating again again, make after taking-up is ground and screened.
5. micro-electrolysis water-activating material according to claim 1 is characterized in that, described copper powder comprises in Red copper oxide or the cupric oxide one or both mixture.
6. micro-electrolysis water-activating material according to claim 1 is characterized in that, described food-grade adhesive comprises in polyvinylpyrrolidone, dextrin and the pregelatinized Starch one or more mixture.
7. micro-electrolysis water-activating material according to claim 1 is characterized in that the particle diameter of described food-grade adhesive is less than 20 microns.
8. micro-electrolysis water-activating material according to claim 1 is characterized in that the particle diameter of described tourmalinite, medical stone and Muscovitum is less than 20 microns.
9. micro-electrolysis water-activating material according to claim 1 is characterized in that, the particle diameter of described selenium powder, zinc powder, iodine powder, calcium ion powder, ferromagnetic powder and copper powder is less than 50 microns.
10. the preparation method of a micro-electrolysis water-activating material, it is characterized in that described preparation method comprises that to grind to form particle diameter behind the copper powder separated pulverizing that micro-electrolysis water-activating material weight is 10%～60% tourmalinite, 10%～70% medical stone, 1%～20% Muscovitum, 1%～20% selenium powder, 1%～20% zinc powder, 1%～20% calcium ion powder, 1%～20% ferromagnetic powder and 1%～20% be micron order or nano level powder with accounting for; In mixed powder, add the food-grade adhesive that accounts for micro-electrolysis water-activating material weight 1%～10% again and carry out uniform mixing; Then cause granular or strike out irregularly shaped or form filtrable material and get final product by equipment by manufacturing process.