CN101638469A - 一种多元醇树脂乳液及其制备方法 - Google Patents
一种多元醇树脂乳液及其制备方法 Download PDFInfo
- Publication number
- CN101638469A CN101638469A CN200810142206A CN200810142206A CN101638469A CN 101638469 A CN101638469 A CN 101638469A CN 200810142206 A CN200810142206 A CN 200810142206A CN 200810142206 A CN200810142206 A CN 200810142206A CN 101638469 A CN101638469 A CN 101638469A
- Authority
- CN
- China
- Prior art keywords
- polyol resin
- water
- resin emulsion
- weight
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多元醇树脂乳液及其制备方法，组份包括有重量份数为40－80份的多元醇树脂，重量份数占多元醇树脂2－10％的非离子乳化剂，以及重量份数为30－52份的水。本发明的制备方法为：A.称取多元醇树脂，放入容器中加热至20－80℃，加入乳化剂A－3065；B.用乳化机将步骤A所得的多元醇树脂和乳化剂混合溶液分散均匀；C.用相转化点化，加水搅拌即得多元醇树脂乳液。本发明主要是与水性异氰酸酯固化剂搭配使用，可运用于地坪涂料、黏合剂、模具注塑、电器封装和化学灌浆等领域，具有良好的漆膜附着力，优良的耐化学药品性，高度的耐磨性及韧性，作为水性化产品，具有优异的环保性。
Description
技术领域
本发明涉及一种树脂乳液，尤其涉及一种应用于水性聚氨酯的多元醇树脂乳液。
本发明还涉及上述多元醇树脂乳液的制备方法。
背景技术
聚氨酯在各种行业应用广泛：如胶粘剂、发泡、弹性体、浇注、注塑、涂料及光油等，石油树脂时交通、建筑及其它一些行业不可或缺的基建材料，应用日益广泛，但由于它是一种不溶于水的油性聚合物，不能与亲水性的材料混合使用，近年来，随着聚氨酯的应用和研究的进展，人们对环境保护意识不断加强，有关的劳动保护，安全，消防，环境保护等法律法规的日益完善，水性聚氨酯正逐步取代溶剂型聚氨酯成为涂层和胶粘剂领域的一个重要组成部分，而应用于水性聚氨酯的多元醇树脂乳液及其制备也就成为人们急需解决的技术问题。
发明内容
本发明要解决的技术问题是为了克服以上的技术不足，提供一种能很好地应用于水性聚氨酯的多元醇树脂乳液，本发明还提供了这种多元醇树脂乳液的制备方法。
为了克服以上的技术缺陷，本发明采用如下的技术方案：
本发明提供一种多元醇树脂乳液，包括以下组份及其重量份数为：重量份数为40-80份的多元醇树脂，重量份数占多元醇树脂2-10％的非离子乳化剂，以及重量份数为30-52份的水。
其中，所述的多元醇树脂可以为SOVERMOL系列的多元醇树脂。所述的非离子乳化剂为乳化剂A-3065。所述的水一般采用热水，其温度为30-80℃。
本发明还提供一种如上所述的多元醇树脂乳液的制备方法，包括如下步骤：
包括如下步骤：称取设定重量份数的多元醇树脂、非离子乳化剂和水，
A、将多元醇树脂放入容器中，加热至20-80℃，加入非离子乳化剂；
B、用乳化机将步骤A所得的多元醇树脂和乳化剂混合溶液分散均匀；
C、向步骤B所得的混合溶液中加30-80℃的水，当混合溶液达到相转化临界点时停止加水，搅拌3-10分钟至混合溶液均匀，加入剩余的水，继续搅拌5-30分钟，得多元醇树脂乳液。
本发明所述的多元醇树脂乳液，主要是与水性异氰酸酯固化剂搭配使用，可运用于地坪涂料、黏合剂、模具注塑、电器封装和化学灌浆等领域，具有良好的漆膜附着力，优良的耐化学药品性，高度的耐磨性及韧性，作为水性化产品，具有优异的环保性。
具体实施方式
下面结合具体实施方式对本发明作进一步的说明：
(1)组份及重量份数组成如下：
序号 名称 投入量(份) 备注
1 SOVEMOL多元醇树脂 40-80
2 乳化剂A-3065 树脂的2-10％ 非离子型
3 热水 30-52 30-80℃
(2)制备工艺叙述：容器采用500ml的烧杯。
A、称取SOVERMOL多元醇树脂40-80份，放入500ml的烧杯中，加热至20-80℃，加入重量份数占多元醇树脂2-10％的乳化剂A-3065；
B、将乳化机分散头置于烧杯中，开启乳化机，预热分散头，同时将步骤A所得的多元醇树脂和乳化剂混合溶液分散均匀；
C、采用相转化点法乳化工艺，向步骤B所得的混合溶液中加30-80℃的水，当混合溶液达到相转化临界点时停止加水，搅拌3-10分钟至混合溶液均匀，加入剩余的水，继续搅拌5-30分钟，即得多元醇树脂乳液。
相转化点法是将水缓慢加入树脂中，在加水的过程中，乳液中两相开始为w/o(油包水)体系，随着加水量增加，最终完成w/o向o/w(水包油)型体系转换。
尽管本发明已作了详细说明并引证了实施例，但对于本领域的普通技术人员，显然可以按照上述说明而做出的各种方案、修改和改动，都应该包括在权利要求的范围之内。
Claims (5)
1、一种多元醇树脂乳液，其特征在于：包括以下组份及其重量份数为：重量份数为40-80份的多元醇树脂，重量份数占多元醇树脂2-10％的非离子乳化剂，以及重量份数为30-52份的水。
2、如权利要求1所述的多元醇树脂乳液，其特征在于：所述的多元醇树脂为SOVERMOL多元醇树脂。
3、如权利要求1所述的多元醇树脂乳液，其特征在于：所述的非离子乳化剂为乳化剂A-3065。
4、如权利要求1所述的多元醇树脂乳液，其特征在于：所述的水的温度为30-80℃。
5、如权利要求1-4任一所述的多元醇树脂乳液的制备方法，其特征在于：包括如下步骤：称取设定重量份数的多元醇树脂、非离子乳化剂和水，
A、将多元醇树脂放入容器中，加热至20-80℃，加入非离子乳化剂；
B、用乳化机将步骤A所得的多元醇树脂和乳化剂混合溶液分散均匀；
C、向步骤B所得的混合溶液中加30-80℃的水，当混合溶液达到相转化临界点时停止加水，搅拌3-10分钟至混合溶液均匀，加入剩余的水，继续搅拌5-30分钟，得多元醇树脂乳液。