CN101619192B - 一种环保型亮光地板油漆 - Google Patents
一种环保型亮光地板油漆 Download PDFInfo
- Publication number
- CN101619192B CN101619192B CN2009101607523A CN200910160752A CN101619192B CN 101619192 B CN101619192 B CN 101619192B CN 2009101607523 A CN2009101607523 A CN 2009101607523A CN 200910160752 A CN200910160752 A CN 200910160752A CN 101619192 B CN101619192 B CN 101619192B
- Authority
- CN
- China
- Prior art keywords
- component
- environment
- friendly
- floor paint
- luminous floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种环保型油漆，特别涉及一种植物油类环保型亮光地板油漆，是由甲、乙组分按1∶1比例配制而成，其中甲的配比如下为：大豆植物短油类醇酸树脂30-40％、蓖麻植物短油类醇酸树脂20-30％、消泡剂0.1-0.7％、流平剂0.1-0.5％、湿润剂0.1-1％、复合环保溶剂30-40％；乙组分为多异氰酸酯固化剂。本发明是一种成本低、性价比高，符合环保健康要求，具有丰满度佳，流平性好；附着力强，硬度高，耐撞击；耐磨、耐水、耐各种家庭清洁剂等特点的亮光地板油漆。
Description
【技术领域】
本发明涉及一种环保型油漆，特别涉及一种植物油类环保型亮光地板油漆。
【背景技术】
据不完全统计，每年因室内家居装修而发生的中毒死亡人数多达数十万，可见，选择健康的装饰材料，尤其是健康的油漆对家人的健康至关重要，但目前国内市场不少油漆中苯、VOC(挥发性有机化合物)的超标严重影响健康。苯、VOC超标将引起居室有机污染，严重的引起居住者头痛、咽喉痛等症状，危害人体健康。游离甲苯二异氰酸酯(TDI)是具有强烈刺激性气体的有机化合物。对皮肤、眼睛和呼吸道有强烈刺激作用，长期接触或高浓度的TDI蒸气可引起支气管炎、过敏性哮喘、肺炎、肺水肿。此外，现有的地板油漆高档的采用合成脂肪酸与丙稀酸体系性能好，但成本高，市场难于接收；其它体系价格有优势，但涂膜性能一般，施工问题较多。采用新的植物油体系，不仅符合环保健康的要求，而且具有高性能的涂膜性能，满足地板漆的施工要求。
【发明内容】
本发明的目的是提供一种成本低、性价比高，符合环保健康要求，具有丰满度佳，流平性好；附着力强，硬度高，耐撞击；耐磨、耐水、耐各种家庭清洁剂等特点的亮光地板油漆。
本发明是采用如下的配方来实现上述目的的，一种环保型亮光地板油漆，该油漆是由甲、乙组分按1∶1比例，以一般地板漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂 30-40％
蓖麻植物短油类醇酸树脂 20-30％
消泡剂 0.1-0.7％
流平剂 0.1-0.5％
湿润剂 0.1-1％
复合环保溶剂 30-40％
乙组分：多异氰酸酯固化剂。
其中消泡剂采用聚氨酯专用消泡剂，主要成份是改性硅酮类。
流平剂采用聚丙烯酸酯共聚体和氟碳改性聚丙烯酸酯类成份。
湿润剂采用聚醚改性二甲基硅氧烷共聚体溶液为主要成份。
复合环保溶剂采用醋酸丁酯、丙二醇甲醚醋酸脂、二价酸脂、混酸甲酯配制而成，其中各组分的配比为：醋酸丁酯60％，丙二醇甲醚醋酸脂10％，二价酸脂20％，混酸甲酯10％。
多异氰酸酯固化剂采用芳香族二异氰酸酯类。
本发明是针对现有地板油漆的缺陷而加以改进，从世界上最先进、最新的化工原料中经过大量的实验筛选出各种材料组配，采用多因素实验设计方法，正交试验设计法确定组分及其重量百分比，采用上述配方的其与现有技术相比，有如下优点：
1)采用的大豆植物短油类醇酸树脂的成本低、干燥速度快、好打磨；蓖麻植物短油类醇酸树脂的流平好、光泽高、柔韧性佳；两种树脂搭配涂膜质量更好，性能佳。
2)采用了世界上最先进消泡剂、流平剂、湿润剂助剂，满足了目前地板漆的生产及施工要求。
3)复合环保溶剂毒性低、气味小，无毒性，可完全生物降解，绝对无苯且voc含量符合健康要求。
4)乙组分：多异氰酸酯固化剂与甲组分按1∶1比例，保证了地板漆涂膜高性能。固化剂游离TDI含量≤0.2％，达到欧盟标准，高于国家GB18581-2001行业标准。
【具体实施方式】
下面对本发明作进一步的描述：
一种环保型亮光地板油漆，该油漆是由甲、乙组分按1∶1比例按一般地板漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂 30-40％
蓖麻植物短油类醇酸树脂 20-30％
消泡剂 0.1-0.7％
流平剂 0.1-0.5％
湿润剂 0.1-1％
复合环保溶剂 30-40％
乙组分：多异氰酸酯固化剂。
其中原料说明如下：
消泡剂采用聚氨酯专用消泡剂，主要成份是改性硅酮类。
流平剂采用聚丙烯酸酯共聚体和氟碳改性聚丙烯酸酯类成份。
湿润剂采用聚醚改性二甲基硅氧烷共聚体溶液为主要成份。
复合环保溶剂采用醋酸丁酯、丙二醇甲醚醋酸脂、二价酸脂、混酸甲酯配制而成，其中各组分的配比为：醋酸丁酯60％，丙二醇甲醚醋酸脂10％，二价酸脂20％，混酸甲酯10％。
多异氰酸酯固化剂采用芳香族二异氰酸酯类。
本发明的实施例一如下：
一种环保型亮光地板油漆，是由甲、乙组分按1∶1比例按一般地板油漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂A 30％
蓖麻植物短油类醇酸树脂B 29.1％
消泡剂 0.7％
流平剂 0.1％
湿润剂 0.1％
复合环保溶剂 40％
乙组分：多异氰酸酯固化剂。
本发明的实施例二如下：
一种环保型亮光地板油漆，该油漆是由甲、乙组分按1∶1比例按一般地板油漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂A 40％
蓖麻植物短油类醇酸树脂B 28.4％
消泡剂 0.1％
流平剂 0.5％
湿润剂 1％
复合环保溶剂 30％
乙组分：多异氰酸酯固化剂。
本发明的实施例三如下：
一种环保型亮光地板油漆，该油漆是由甲、乙组分按1∶1比例按一般地板油漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂A 37.8％
蓖麻植物短油类醇酸树脂B 20％
消泡剂 0.7％
流平剂 0.5％
湿润剂 1％
复合环保溶剂 40％
乙组分：多异氰酸酯固化剂。
本发明的实施例四如下：
一种环保型亮光地板油漆，该油漆是由甲、乙组分按1∶1比例按一般地板油漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂A 39.7％
蓖麻植物短油类醇酸树脂B 30％
消泡剂 0.1％
流平剂 0.1％
湿润剂 0.1％
复合环保溶剂 30％
乙组分：多异氰酸酯固化剂。
本发明的一个较佳实施例如下：
一种环保型亮光地板油漆，该油漆是由甲、乙组分按1∶1比例按一般地板油漆的制作工艺配制而成，其中甲、乙组分具体成分及配比如下(质量比)：
甲组分：
大豆植物短油类醇酸树脂A 40％
蓖麻植物短油类醇酸树脂B 24％
消泡剂 0.5％
流平剂 0.3％
湿润剂 0.15％
复合环保溶剂 35.05％
乙组分：多异氰酸酯固化剂。
该环保型亮光地板漆的各项性能指标和技术指标如下各表所示：
表一：环保型亮光地板漆性能指标
| 项目 | 单位 | HG/T2454-2006标准中的技术指标 | 实测值 |
| 在容器中状态 | 搅拌后均匀无硬块 | 符含 |
| 施工性 | 施涂无障碍 | 符合 | |
| 干燥时间 | H | 表干≤1H，实干≤24H | 表干≤1H，实干≤24H |
| 涂膜外观 | 正常 | 正常 | |
| 贮存稳定性(50℃/7d) | 无异常 | 无异常 | |
| 光泽(60°) | 商定 | 125 | |
| 铅笔硬度(擦伤)≥ | H | 3H | |
| 附着力(划格间距2mm)≤ | 1 | 1 | |
| 耐干热性((90±2〕℃，15min〕≤ | 级 | 2 | 2 |
| 耐磨性(750g/500r)≤ | g | 0.040 | 0.036 |
| 耐冲击性 | 涂膜无脱落、无开裂 | 正常 | |
| 耐水性(24h) | 无异常 | 无异常 | |
| 耐碱性(2h) | 无异常 | 无异常 | |
| 耐醇性(8h) | 无异常 | 无异常 | |
| 耐污染性(1h) 茶和醋 | 无异常 | 无异常 |
从表一可明显看出，本发明的各项性能均达到或高于国标标准，确认了本发明的高性能。
表二：环保型亮光地板漆技术要求
甲组分
| 项目 | 技术要求 |
| 固含量 | 43％ |
| 外观 | 浅黄全透明 |
| 粘度(涂-4，30℃) | 20秒 |
| 施工比例 | 甲组分∶乙组分＝1∶1 |
| 胶化时间(30℃，75％) | 4小时以上 |
乙组分
| 项目 | 技术要求 |
| 固含量 | 40％ |
| 外观 | 清澄透明 |
| 粘度(涂-4，30℃) | 10.8秒 |
| 游离TDI含量 | 0.1％ |
表二技术要求表明，VOC含量及游离TDI含量达到或优于GB18581-2001标准，符合环保健康要求，使用安全可靠。
尽管对本发明已作了详细的说明并提供了一些具体实例，但对本领域熟练技术人员来说，只要不离开本发明的精神和范围可作各种变化或修正是显然的。
Claims (6)
1.一种环保型亮光地板油漆，其特征在于：该油漆是由甲、乙组分按1:1比例配制而成，其中甲、乙组分具体成分及配比按质量计如下：
甲组分 :
大豆植物短油类醇酸树脂 30-40%
蓖麻植物短油类醇酸树脂 20-30%
消泡剂 0.1-0.7%
流平剂 0.1-0.5%
湿润剂 0.1-1%
复合环保溶剂 30-40%
乙组分为多异氰酸酯固化剂；
其中，所述复合环保溶剂采用醋酸丁酯、丙二醇甲醚醋酸脂、二价酸脂、混酸甲酯配制而成，其中各组分的配比为：醋酸丁酯60%，丙二醇甲醚醋酸脂10%，二价酸脂20%，混酸甲酯10%。
2..根据权利要求1所述的环保型亮光地板油漆，其特征在于：其中甲组分具体成分及配比按质量计如下：
大豆植物短油类醇酸树脂 30%
蓖麻植物短油类醇酸树脂 29.1%
消泡剂 0.7%
流平剂 0.1%
湿润剂 0.1%
复合环保溶剂 40%。
3.根据权利要求1所述的环保型亮光地板油漆，其特征在于：所述消泡剂采用聚氨酯专用消泡剂，主要成份是改性硅酮类。
4.根据权利要求1所述的环保型亮光地板油漆，其特征在于：所述流平剂采用聚丙烯酸酯共聚体和氟碳改性聚丙烯酸酯类成份。
5.根据权利要求1所述的环保型亮光地板油漆，其特征在于：所述湿润剂采用聚醚改性二甲基硅氧烷共聚体溶液为主要成份。
6.根据权利要求1所述的环保型亮光地板油漆，其特征在于：所述多异氰酸酯固化剂采用芳香族二异氰酸酯类。