CN101612864B - 内彩砖制造工艺 - Google Patents

内彩砖制造工艺 Download PDF

Info

Publication number
CN101612864B
CN101612864B CN200810017154A CN200810017154A CN101612864B CN 101612864 B CN101612864 B CN 101612864B CN 200810017154 A CN200810017154 A CN 200810017154A CN 200810017154 A CN200810017154 A CN 200810017154A CN 101612864 B CN101612864 B CN 101612864B
Authority
CN
China
Prior art keywords
paint
brick
temperature
glass
lacquer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200810017154A
Other languages
English (en)
Other versions
CN101612864A (zh
Inventor
田文顺
张满营
李勇
刘景柱
李晓东
胡广海
邢化亭
董国竹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dezhou Zhenhua Decoration Glass Co Ltd
Original Assignee
Dezhou Zhenhua Decoration Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dezhou Zhenhua Decoration Glass Co Ltd filed Critical Dezhou Zhenhua Decoration Glass Co Ltd
Priority to CN200810017154A priority Critical patent/CN101612864B/zh
Publication of CN101612864A publication Critical patent/CN101612864A/zh
Application granted granted Critical
Publication of CN101612864B publication Critical patent/CN101612864B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种内彩砖制造工艺，涉及一种建筑材料制造方法。其特点是采用灵活工艺流程，几种原料的配比度要根据天气温度及空气中的湿度进行配比，当气温≤20℃度的天气，空气相对湿度≥40％，容量配比度为玻璃漆∶油漆稀料∶催化型定型剂＝4.5-5.5∶2.5-3.5∶0.4-0.6；当气温在≥20℃的天气，空气相对湿度≤40％，配比度为玻璃漆∶油漆稀料∶催化型定型剂＝4.5-55∶2-3∶0.4-0.6；其制造工艺主要包括以下工序：配漆、灌制、退火、吹气、喷漆、成品。本发明大大减小了工人的劳动强度，提高内彩砖的产量提高约2-3倍。节省了手工逛制的时间，降低了生产成本，避免了手工制作过程中玻璃砖内表面玻璃漆分布不均，漆面不干燥等问题，从而提高了产品质量。

Description

内彩砖制造工艺
技术领域
本发明涉及一种建筑材料制造方法。
背景技术
内彩砖作为玻璃砖行业中一种新型的玻璃砖产品，其生产工艺与通过窑炉玻璃工艺改变原料的颜色相比，可以随意变换色彩。内彩砖品种多样，属于手工艺产品，但手工制作存在产量低，效率低，成本高的不足。在制作流程中的手工逛砖工序和吹气工序会浪费大量的制作时间，制造工艺不成熟，不能掌握各种外界条件，并且手工逛制过程中玻璃漆在内表面附着不均匀，造成成品率低，产量底，成本高。
发明内容
为了克服现有技术的不足，本发明提供一种内彩砖制造工艺，以解决现有技术造成的产品内部附着漆不能均匀分布，人工逛制差异大，成品率低，产量低，成本高等问题。
本发明解决其技术问题所采用的技术方案是采用可调节工艺流程，几种原料的容量配比度要根据天气温度及空气中的湿度进行配比，主要是根据天气气温的变化调整油漆稀料的加入量；当气温在≥20℃的天气，空气相对湿度≤40％，容量配比度为玻璃漆∶油漆稀料∶催化型定型剂＝4.5-5.5∶2.5-3.5∶0.4-0.6；当气温≤20℃度的天气，空气相对湿度≥40％，容量配比度为玻璃漆∶油漆稀料∶催化型定型剂＝4.5-5.5∶2-3∶0.4-0.6；其制造工艺如下：
(1)配漆；按规定比例先将红色玻璃漆到入量杯中，再将油漆稀料倒入量杯中，最后将催化型定型剂加入，搅拌6-10分钟，用滤网进行过滤，备用；
(2)灌制：首先将调和好的玻璃漆倒入内彩砖，手工将两个内表面及四周逛制均匀；
(3)退火：退火时，退火炉最高温度在300-400℃，内彩砖出炉时温度控制在100-150℃。
(4)吹气：当砖温降到20-30℃时进行吹气。
(5)喷漆：将逛制好的内彩砖平放在输送带上，砖与砖之间保持8-15cm左右的距离，内彩砖通过输送带传送至喷漆机，自动喷漆。
(6)成品：成品检验、包装入库。
采用本发明的积极效果是大大减小了工人的劳动强度，实现了半自动化生产，内彩砖的产量提高约2-3倍。节省了手工逛制的时间，降低了生产成本，避免了手工制作过程中玻璃砖内表面玻璃漆分布不均，漆面不干燥等问题，从而提高了产品质量，降低了生产成本。
具体实施方式
实施例一
以生产46块红色内彩砖为例，气温在≥20℃，空气相对湿度≤40％的原料容量配比：玻璃漆∶油漆稀料∶催化型定型剂＝5∶3∶0.5；具体制造工艺：
1、配漆：：玻璃漆∶油漆稀料∶催化型定型剂＝5∶3∶0.5＝325ml∶195ml∶32ml＝552ml；552ml的混合液可用于生产46块内彩砖。
配漆时，应将量杯清洁干净，保证无尘无杂质和废旧漆料。
玻璃漆的加入--玻璃漆是基本的调色原料，开启漆盒时应注意防止杂物和粉尘落入，以免影响纯净度。将量杯水平放置在水平台面上，按规定比例将325ml的红色玻璃漆到入量杯中。
油漆稀料的加入--稀料作为一种稀释剂，起到稀释和调和的作用。将事先准备好的195ml油漆稀料倒入量杯中。
催化型定型剂的加入--最后将32ml的催化型定型剂加入，以保证漆的质量。
调和--用搅拌棒将混合体搅拌5分钟。
过滤--为了进一步保证漆的纯净度，要用滤网进行过滤。
2、灌制：首先向量杯内倒入每块内彩砖用量12ml调和好的玻璃漆，再将压孔砖倾斜45度，将量杯内的玻璃漆全部注入砖内，再手工进行逛制。首先将砖的两个内表面逛制均匀，再将四周逛匀。漆料均匀后，手工整体转动，直至均匀。
3、退火：退火时，退火炉的温度最高温度在380度左右，砖与砖之间留有一定的空间和距离。内彩砖出炉时温度在120度左右。
4、吹气：当砖温降到30度左右时进行吹气。
5、喷漆：将逛制好的内彩砖平放在输送带上，砖与砖之间保持10cm左右的距离，以免在输送过程中将砖碰坏，内彩砖通过输送带传送至喷漆机，自动喷漆。。
6、包装：由质检员检验合格后获得合格内彩砖产品，方可装箱，入库。
实施例二
以生产46块红色内彩砖为例，气温在≤20℃，空气相对湿度≥40％的原料容量配比：
1、配漆：玻璃漆∶油漆稀料∶催化型定型剂＝5∶2∶0.5＝370ml∶148ml∶42ml＝560ml，560ml的混合液可用于生产46块内彩砖。
配漆时，应将量杯清洁干净，保证无尘无杂质和废旧漆料。
玻璃漆的加入--玻璃漆是基本的调色原料，开启漆盒时应注意防止杂物和粉尘落入，以免影响纯净度。将量杯水平放置在水平台面上，按规定比例将370ml的红色玻璃漆到入量杯中。
油漆稀料的加入--稀料作为一种稀释剂，起到稀释和调和的作用。将事先准备好的148ml稀料倒入量杯中。
催化型定型剂的加入--最后将42ml的催化型定型剂加入，以保证漆的质量。
调和--用搅拌棒将混合体搅拌6分钟。过滤--为了进一步保证漆的纯净度，要用滤网进行过滤
2、灌制：首先向量杯内倒入每块内彩砖用量12ml调和好的玻璃漆，再将压孔砖倾斜45度，将量杯内的玻璃漆全部注入砖内，再手工进行逛制。首先将砖的两个内表面逛制均匀，再将四周逛匀。漆料均匀后，手工整体转动，直至均匀。
3、退火：退火时，退火炉的温度最高温度在380度左右，砖与砖之间留有一定的空间和距离。内彩砖出炉时温度在120度左右。
4、吹气：当砖温降到30度左右时进行吹气。
5、喷漆：将逛制好的内彩砖平放在输送带上，砖与砖之间保持10cm左右的距离，以免在输送过程中将砖碰坏，内彩砖通过输送带传送带喷漆机，自动喷漆。
6、成品：由质检员检验合格后获得合格内彩砖产品，方可装箱，入库。

Claims (1)

1.一种内彩砖制造工艺，其特征是采用灵活工艺流程，几种原料的容量配比度要根据天气温度及空气中的湿度进行配比，主要是根据天气气温的变化调整稀料的加入量；当气温在＞20℃的天气，空气相对湿度＜40％，容量配比度为玻璃漆∶油漆稀料∶催化型定型剂＝4.5-5.5∶2.5-3.5∶0.4-0.6；当气温＜20℃度的天气，空气相对湿度＞40％，容量配比度为玻璃漆∶油漆稀料∶催化型定型剂＝4.5-5.5∶2-3∶0.4-0.6；其制造工艺如下：
(1)配漆：按规定比例先将红色玻璃漆倒入量杯中，再将油漆稀料倒入量杯中，最后将催化型定型剂加入，搅拌6-10分钟，用滤网进行过滤，备用；
(2)灌制：首先将调和好的玻璃漆倒入内彩砖，手工将两个内表面及四周逛制均匀；
(3)退火：退火时，退火炉高温控制在300-400度，内彩砖出炉时温度控制在100-150℃；
(4)吹气：当砖温降到20-40℃时进行吹气；
(5)喷漆：将逛制好的内彩砖平放在输送带上，砖与砖之间保持8-15cm的距离，内彩砖通过输送带传送至喷漆机，自动喷漆，要保证喷漆均匀，砖面洁净；
(6)成品：成品检验、包装入库。 
CN200810017154A 2008-06-27 2008-06-27 内彩砖制造工艺 Expired - Fee Related CN101612864B (zh)