CN101591492B - 一种氯醚树脂防火涂料及其制备方法 - Google Patents
一种氯醚树脂防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN101591492B CN101591492B CN2009100867383A CN200910086738A CN101591492B CN 101591492 B CN101591492 B CN 101591492B CN 2009100867383 A CN2009100867383 A CN 2009100867383A CN 200910086738 A CN200910086738 A CN 200910086738A CN 101591492 B CN101591492 B CN 101591492B
- Authority
- CN
- China
- Prior art keywords
- weight part
- chlorinated polyether
- polyether resin
- fire
- retardant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种氯醚树脂防火涂料，由1重量份的氯醚树脂、0.01～0.2重量份的环氧树脂、0.21～0.6重量份的聚磷酸铵、0.1～0.4重量份的三聚氰胺、0.15～0.31重量份的季戊四醇、0.01～0.06重量份的三氧化二锑、0.005～0.01重量份的硅油、0.01～0.25重量份的氯化石蜡、0.01～0.7重量份的氢氧化铝、0.05～0.31重量份的硼酸锌、0.05～0.25重量份的钛白粉、0.03～0.19重量份的陶瓷粉、0.01～0.16重量份的滑石粉、0.1～2.0重量份的二甲苯、0.3～2.2重量份的重芳烃溶剂组成，具有涂层薄、干燥快、施工方便及装饰性良好的特点，涂膜有良好的附着力、耐水、耐酸碱腐蚀及耐候性能，遇火膨胀发泡，形成均匀致密的防火隔热层。
Description
技术领域
本发明涉及一种用于室内外钢结构及砼表面保护的氯醚树脂防火涂料及其制备方法。
背景技术
现有的膨胀型钢结构防火涂料的涂层不足之处是耐候性能和附着力不佳，需要涂刷另外的面漆，且涂层易粉化，使涂层失去阻燃性能，其涂层附着力一般为0.2MPa。
发明内容
本发明的目的是提供一种氯醚树脂防火涂料，制造方法简便、涂料具有涂层薄、干燥快、施工方便及装饰性良好的特点，其涂膜具有良好的附着力、耐水、耐酸碱腐蚀及耐候性能，涂层在高温作用下不脱落，遇火膨胀发泡，形成均匀致密的防火隔热层。适用于工矿企业、炼油厂、体育场馆、仓储库房、大型超市、宾馆等室内外钢结构的防火阻燃工程。另一个目的是提供氯醚树脂防火涂料和制备方法。
本发明采用的技术方案：本发明的氯醚树脂防火涂料，其特征是由1重量份的氯醚树脂、0.01～0.2重量份的环氧树脂、0.21～0.6重量份的聚磷酸铵、0.1～0.4重量份的三聚氰胺、0.15～0.31重量份的季戊四醇、0.01～0.06重量份的三氧化二锑、0.005～0.01重量份的硅油、0.01～0.25重量份的氯化石蜡、0.01～0.7重量份的氢氧化铝、0.05～0.31重量份的硼酸锌、0.05～0.25重量份的钛白粉、0.03～0.19重量份的陶瓷粉、0.01～0.16重量份的滑石粉、0.1～2.0重量份的二甲苯、0.3～2.2重量份的重芳烃溶剂组成。
氯醚树脂涂料的制造方法，其特征是：将1重量份的氯醚树脂、0.01～0.2重量份的环氧树脂、0.1～2.0重量份的二甲苯、0.3～2.2重量份的重芳烃、0.005～0.01重量份的硅油，放入不锈钢的料桶中或反应釜中，在常温下低速搅拌均匀，高速分散1～3h后，在高速搅拌的情况下加入0.21～0.6重量份的聚磷酸铵、0.1～0.4重量份的三聚氰胺、0.15～0.31重量份的季戊四醇、0.01～0.06重量份的三氧化二锑、0.01～0.25重量份的氯化石蜡、0.01～0.7重量份的氢氧化铝、0.05～0.31重量份的硼酸锌、0.05～0.25重量份的钛白粉、0.03～0.19重量份的陶瓷粉、0.01～0.16重量份的滑石粉，分散0.5h后用球磨机研磨，控制细度≤70μm，制成氯醚树脂防火涂料。
氯醚树脂是中顺集团汇通公司生产的氯醚树脂MP45。
环氧树脂是山东天茂化工有限公司生产的环氧树脂618或软化点为30～55℃的液态双酚A型环氧树脂。
钛白粉采用的是R972金红石型。
陶瓷粉采用的是粒径为35～50μm。
滑石粉采用的是325～800目。
重芳烃溶剂，可以采用三甲苯或S-1000#或S-1500#。
本发明的氯醚树脂防火涂料，由氯醚树脂、环氧树脂及氯化石蜡，加入一定量的有机发泡体系、一定量的无机发泡体系、一定量的混合溶剂、一定量的助剂、一定量的颜填料配制而成。氯醚树脂是氯乙烯-乙烯基异丁基醚树脂的简称，是由75％氯乙烯和25％乙烯基异丁基醚共聚而成的聚合物。氯醚树脂聚合物高分子的链结构，决定了其本身特有的性能，共聚物中的乙烯基异丁基醚长链基团作为高分子链支链的存在，使得聚合物高分子不易堆砌紧密，结晶度降低，宏观表现为聚合物的柔韧性增强，说明乙烯基异丁基醚组分具有内增塑作用，使得聚合物形成的涂膜有足够的柔韧性。高分链中大量醚键的存在，使聚合物涂膜与底材有良好的附着力。共聚物中不含可皂化的酯键，并因结合的氯原子十分稳定，使涂料具有优良的阻燃、耐化学品腐蚀性。氯醚树脂中不含反应性的双键，因此不易为大气氧化而降解，其制成的涂层耐大气老化性优良、耐光稳定性优异、不易泛黄及粉化。故由氯醚树脂制成的涂层具有良好的阻燃、耐水解性、耐光性、耐侯性和耐化学腐蚀性。在氯醚树脂涂料中加入一定量的环氧树脂，进一步提高了涂膜的附着力。使用的硅油有助于减少气泡的形成及气泡的逸出。使用的有机、无机发泡体系协同作用，使遇火膨胀形成具有一定高度、均匀致密的防火隔热层。使用的钛白粉、陶瓷粉增加了防火隔热层的强度，提高了耐火性能。
本发明与现有技术相比的有益效果
1、本发明的氯醚树脂防火涂料，具有常温干燥成膜的特点，其涂层具有良好的阻燃性能、附着力、耐化学品性、耐盐雾性、耐候性、耐光老化性，其中耐火极限达到2h(涂层厚度3.1mm)，涂层粘接强度达到1.2MPa。能应用于室内外钢结构及砼表面的防火阻燃工程。
2、本发明的氯醚树脂防火涂料及其制备方法，工艺简单，无须特殊设备。
3、本发明的氯醚树脂防火涂料的性能价格比高。
具体实施方式
实施例1
本发明的氯醚树脂防火涂料的制造方法。在不锈钢的料桶中，将1重量份的氯醚树脂、0.06重量份的环氧树脂、0.6重量份的二甲苯、1重量份的重芳烃溶剂、0.006重量份的硅油，在常温下低速搅拌均匀，高速分散2h后，在高速搅拌的情况下加入0.41重量份的聚磷酸铵、0.22重量份的三聚氰胺、0.2重量份的季戊四醇、0.05重量份的三氧化二锑、014重量份的氯化石蜡、0.6重量份的氢氧化铝、0.2重量份的硼酸锌、0.18重量份的钛白粉、0.07重量份的陶瓷粉、0.05重量份的滑石粉，分散0.5h后用球磨机研磨，控制细度≤70μm，将其分散均匀制成氯醚树脂防火涂料。
该涂料具有单组分包装、常温干燥成膜的特点，其涂层粘接强度1.2MPa；耐曝热性720h；耐湿热性720h；耐化学品浸泡性(3％氨水、3％盐酸)360h涂层完好；耐盐雾性40次涂层完好；耐火性能2.0h(涂层厚度3.1mm)。
实施例2
本发明的氯醚树脂防火涂料的制造方法。放入反应釜中，将1重量份的氯醚树脂MP45、0.1重量份的环氧树脂618、1.5重量份的二甲苯、0.5重量份的重芳烃溶剂S-1000#、0.007重量份的硅油，在常温下低速搅拌均匀，高速分散2h后，在高速搅拌的情况下加入0.52重量份的聚磷酸铵、0.3重量份的三聚氰胺、0.25重量份的季戊四醇、0.04重量份的三氧化二锑、0.1重量份的氯化石蜡、0.5重量份的氢氧化铝、0.16重量份的硼酸锌、0.15重量份的R972金红石型325目筛余的钛白粉、0.1重量份粒径为35～40μm的陶瓷粉、0.07重量份的600目滑石粉，分散0.5h后用球磨机研磨，控制细度≤70μm，制成氯醚树脂防火涂料。
该涂料具有单组分包装、常温干燥成膜的特点，其涂层粘接强度1.2MPa；耐曝热性720h；耐湿热性720h；耐化学品浸泡性(3％氨水、3％盐酸)360h涂层完好；耐盐雾性40次涂层完好；耐火性能2.0h(涂层厚度3.1mm)。
实施例3
本发明的氯醚树脂防火涂料的制造方法。在不锈钢的料桶中，将1重量份的氯醚树脂MP45、0.14重量份的软化点为30～55℃的液态双酚A型环氧树脂、1.7重量份的二甲苯、0.3重量份的重芳烃溶剂三甲苯、0.008重量份的硅油，在常温下低速搅拌均匀，高速分散2h后，在高速搅拌的情况下加入0.58重量份的聚磷酸铵、0.37重量份的三聚氰胺、0.29重量份的季戊四醇、0.03重量份的三氧化二锑、0.06重量份的氯化石蜡、0.4重量份的氢氧化铝、0.13重量份的硼酸锌、0.1重量份的R972金红石型325目筛余的钛白粉、0.15重量份粒径为35～40μm的陶瓷粉、0.1重量份的600目滑石粉，分散0.5h后用球磨机研磨，控制细度≤70μm，将其分散均匀制成氯醚树脂防火涂料。
该涂料具有单组分包装、常温干燥成膜的特点，其涂层粘接强度1.2MPa；耐曝热性720h；耐湿热性720h；耐化学品浸泡性(3％氨水、3％盐酸)360h涂层完好；耐盐雾性40次涂层完好；耐火性能2.0h(涂层厚度3.1mm)。
重芳烃溶剂S-1000#和S-1500#，淄博市临淄泽泉化工有限公司有产品销售。
Claims (8)
1.一种氯醚树脂防火涂料，其特征是由1重量份的氯醚树脂、0.01～0.2重量份的环氧树脂、0.21～0.6重量份的聚磷酸铵、0.1～0.4重量份的三聚氰胺、0.15～0.31重量份的季戊四醇、0.01～0.06重量份的三氧化二锑、0.005～0.01重量份的硅油、0.01～0.25重量份的氯化石蜡、0.01～0.7重量份的氢氧化铝、0.05～0.31重量份的硼酸锌、0.05～0.25重量份的钛白粉、0.03～0.19重量份的陶瓷粉、0.01～0.16重量份的滑石粉、0.1～2.0重量份的二甲苯、0.3～2.2重量份的重芳烃溶剂组成。
2.一种根据权利要求1所述的一种氯醚树脂防火涂料，其特征是：氯醚树脂是氯醚树脂MP45。
3.一种根据权利要求1所述的一种氯醚树脂防火涂料，其特征是：环氧树脂是环氧树脂618或液态双酚A型环氧树脂。
4.一种根据权利要求1所述的一种氯醚树脂防火涂料，其特征是：钛白粉采用的是金红石型钛白粉。
5.一种根据权利要求1所述的一种氯醚树脂防火涂料，其特征是：陶瓷粉采用的是粒径为35～50μm。
6.一种根据权利要求1所述的一种氯醚树脂防火涂料，其特征是：滑石粉采用的是325～800目。
7.一种根据权利要求1所述的一种氯醚树脂防火涂料，其特征是：重芳烃溶剂采用三甲苯或S-1000#或S-1500#。
8.一种根据权利要求1、2、3、4、5、6或7所述的一种氯醚树脂防火涂料的制备方法，其特征是：将1重量份的氯醚树脂、0.01～0.2重量份的环氧树脂、0.1～2.0重量份的二甲苯、0.3～2.2重量份的 重芳烃、0.005～0.01重量份的硅油，放入反应釜中，在常温下低速搅拌均匀，高速分散1～3h后，在高速搅拌的情况下加入0.21～0.6重量份的聚磷酸铵、0.1～0.4重量份的三聚氰胺、0.15～0.31重量份的季戊四醇、0.01～0.06重量份的三氧化二锑、0.01～0.25重量份的氯化石蜡、0.01～0.7重量份的氢氧化铝、0.05～0.31重量份的硼酸锌、0.05～0.25重量份的钛白粉、0.03～0.19重量份的陶瓷粉、0.01～0.16重量份的滑石粉，分散0.5h后，用球磨机研磨，控制细度≤70μm，制成氯醚树脂防火涂料。