CN101586255B - 一种二水硫酸钙晶须制备方法 - Google Patents

一种二水硫酸钙晶须制备方法 Download PDF

Info

Publication number
CN101586255B
CN101586255B CN2009100327614A CN200910032761A CN101586255B CN 101586255 B CN101586255 B CN 101586255B CN 2009100327614 A CN2009100327614 A CN 2009100327614A CN 200910032761 A CN200910032761 A CN 200910032761A CN 101586255 B CN101586255 B CN 101586255B
Authority
CN
China
Prior art keywords
gram
filtrate
liter
crystal whisker
calcium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100327614A
Other languages
English (en)
Other versions
CN101586255A (zh
Inventor
朱伟长
郑翠红
俞海云
闫勇
韩甲兴
许苗苗
徐兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui University of Technology AHUT
Original Assignee
Anhui University of Technology AHUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui University of Technology AHUT filed Critical Anhui University of Technology AHUT
Priority to CN2009100327614A priority Critical patent/CN101586255B/zh
Publication of CN101586255A publication Critical patent/CN101586255A/zh
Application granted granted Critical
Publication of CN101586255B publication Critical patent/CN101586255B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种制备二水硫酸钙晶须的方法，其特征为：氯化钙溶液中加入十二烷基磷酸酯钾盐和壬基酚聚环氧乙烯醚(TX10)，搅拌中加入稀硫酸，反应液静置4-6小时，过滤，滤料为二水硫酸钙晶须。滤液与石灰石反应后重新生成氯化钙溶液，继续加入稀硫酸，再次生成二水硫酸钙晶须。本方法是以石灰石和稀硫酸为主要原料制备二水硫酸钙晶须，具有工艺简单，成本低廉的特点，适宜工业化生产。

Description

一种二水硫酸钙晶须制备方法
技术领域：
本发明涉及无机化工和无机材料领域，特别是一种二水硫酸钙晶须制备方法。
背景技术：
晶须是指以单晶形式生长的形状类似短纤维、而径向尺寸远小于短纤维的须状单晶体，它通常是具有均一的横截面、完整的外形、完善的内部结构。晶须是一种一维优势发育的单晶，晶格缺陷很少，强度接近理论值，是目前已知强度最大的固体，具有优良的力学性能。
硫酸钙晶须是一种对人体无害或危害极小的矿物纤维，和其他无机晶须相比，具有价格最廉、毒性最低的优势，并且具有耐高温、耐酸碱性、抗化学腐蚀、韧性好、电绝缘性好、强度高、易进行表面处理的特点，属于新型绿色环保材料。二水硫酸钙晶须应用广泛，特别适宜添加于涂料中。加入二水硫酸钙晶须的涂料和油漆不仅附着能力强、耐温、绝缘性好，而且具有抗菌作用。例如专利CN1806551A指出：内墙涂料添加2-3％的二水硫酸钙晶须具有抗菌作用，使用1-3年内抗菌率可达90-95％。
目前制备硫酸钙晶须的方法较多，例如专利CN1261624C、CN1317430C、CN1598083C所采用的水热法，专利CN1955345C、CN1324170C所采用熟石灰浆加硫酸的方法，这些方法各有特色，但都存在生产成本较高，工业生产废水量较大的不足之处。
发明内容
本发明采用氯化钙溶液与稀硫酸反应，在十二烷基磷酸酯钾盐和壬基酚聚环氧乙烯醚(TX10)存在时，缓慢生成二水硫酸钙晶须，溶液中同时生成盐酸。反应后的滤液与石灰石反应又重新生成氯化钙溶液，可以继续与稀硫酸反应再次生成二水硫酸钙晶须。本发明实际是以石灰石和稀硫酸为主要原料制备二水硫酸钙晶须，具有工艺简单，成本低廉的特点，并且生产过程中没有工业废水排放。
本发明的技术方案是：配制0.25-0.40mol/L氯化钙水溶液，每升溶液加入2.0-3.0克十二烷基磷酸酯钾盐和1.2-1.8克壬基酚聚环氧乙烯醚(TX10)搅拌溶解，溶液中十二烷基磷酸酯钾盐质量：壬基酚聚环氧乙烯醚(TX10)质量为1∶0.6。室温时，在保持搅拌中加入与氯化钙等物质的量的5-50％硫酸溶液，反应液静置4-6小时，过滤，滤料为二水硫酸钙晶须。滤液每升加入0.1克十二烷基磷酸酯钾盐、0.06克壬基酚聚环氧乙烯醚(TX10)和10％HCl 0.03升，再按每升滤液加入100-300目石灰石60克搅拌反应1-2小时后过滤，滤液搅拌中加入与氯化钙等物质的量的5-50％硫酸溶液，静置4-6小时后又继续生成二水硫酸钙晶须。
具体实施方式
实例1
配制0.25mol/L氯化钙水溶液10升，加入20克十二烷基磷酸酯钾盐和12克壬基酚聚环氧乙烯醚(TX10)搅拌溶解，在保持搅拌中加入50％硫酸溶液0.26升，反应液静置6小时，过滤，滤料为二水硫酸钙晶须，须长40-70微米，径比30-50。滤液加入1克十二烷基磷酸酯钾盐、0.6克壬基酚聚环氧乙烯醚(TX10)和10％HCl 0.3升，再加入300目石灰石600克搅拌反应1小时后过滤，滤液搅拌中加入50％硫酸溶液0.26升，静置4-6小时后又继续生成二水硫酸钙晶须。如此循环10次，所生成的二水硫酸钙晶须形貌保持不变，产品质量稳定。
实例2
配制0.4mol/L氯化钙水溶液10升，加入30克十二烷基磷酸酯钾盐和18克壬基酚聚环氧乙烯醚(TX10)搅拌溶解，在保持搅拌中加入10％硫酸溶液2.1升，反应液静置4小时，过滤，滤料为二水硫酸钙晶须，须长30-60微米，径比30-50。滤液加入1克十二烷基磷酸酯钾盐、0.6克壬基酚聚环氧乙烯醚(TX10)和10％HCl 0.3升，再加入100目石灰石600克搅拌反应2小时后过滤，滤液搅拌中加入10％硫酸溶液2.1升，静置4-6小时后又继续生成二水硫酸钙晶须。如此循环10次，所生成的二水硫酸钙晶须形貌保持不变，产品质量稳定。
实例3
配制0.33mol/L氯化钙水溶液10升，加入25克十二烷基磷酸酯钾盐和15克壬基酚聚环氧乙烯醚(TX10)搅拌溶解，在保持搅拌中加入20％硫酸溶液0.89升，反应液静置5小时，过滤，滤料为二水硫酸钙晶须，须长30-60微米，径比30-50。滤液加入1克十二烷基磷酸酯钾盐、0.6克壬基酚聚环氧乙烯醚(TX10)和10％HCl 0.3升，再加入200目石灰石600克搅拌反应2小时后过滤，滤液搅拌中加入20％硫酸溶液0.89升，静置4-6小时后又继续生成二水硫酸钙晶须。如此循环10次，所生成的二水硫酸钙晶须形貌保持不变，产品质量稳定。

Claims (1)

1.一种二水硫酸钙晶须制备方法，其步骤如下：配制0.25-0.40mol/L氯化钙水溶液，每升溶液加入2.0-3.0克十二烷基磷酸酯钾盐和1.2-1.8克壬基酚聚环氧乙烯醚(TX10)搅拌溶解，溶液中十二烷基磷酸酯钾盐质量∶壬基酚聚环氧乙烯醚(TX10)质量为1∶0.6；室温时，在保持搅拌中加入与氯化钙等物质的量的5-50％硫酸溶液，反应液静置4-6小时，过滤，滤料为二水硫酸钙晶须；滤液每升加入0.1克十二烷基磷酸酯钾盐、0.06克壬基酚聚环氧乙烯醚(TX10)和10％盐酸溶液0.03升，再按每升滤液加入100-300目石灰石60克搅拌反应1-2小时后过滤，滤液搅拌中加入与氯化钙等物质的量的5-50％硫酸溶液，静置4-6小时后又继续生成二水硫酸钙晶须。
CN2009100327614A 2009-06-08 2009-06-08 一种二水硫酸钙晶须制备方法 Expired - Fee Related CN101586255B (zh)