CN101575485A - 一种用于纤维表面的pe保护膜压敏胶及其制备方法 - Google Patents
一种用于纤维表面的pe保护膜压敏胶及其制备方法 Download PDFInfo
- Publication number
- CN101575485A CN101575485A CNA2009100374070A CN200910037407A CN101575485A CN 101575485 A CN101575485 A CN 101575485A CN A2009100374070 A CNA2009100374070 A CN A2009100374070A CN 200910037407 A CN200910037407 A CN 200910037407A CN 101575485 A CN101575485 A CN 101575485A
- Authority
- CN
- China
- Prior art keywords
- pressure sensitive
- sensitive adhesive
- parts
- portions
- protective film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于纤维表面的PE保护膜压敏胶，由下述质量组成份数的原材料制成：丙烯酸2－乙基己酯：30～38份，乙酸乙烯酯：0～4份，丙烯酸羟乙酯：0.4～2份，丙烯酸：1.6～4份，溶剂：55～60份；通过本工艺制作出来的PE保护膜压敏胶，粘度好，使用时无须涂覆少量即可达到压敏效果，由于该压敏胶涂覆量少，所以在干燥过程中不会导致PE薄膜出现凸卷现象，而且当保护膜剥离的过程中不会在被保护的表面上残留有残胶，从而可以广泛应用于PE保护膜的制作上。
Description
技术领域
本发明涉及一种保护膜压敏胶，具体地说是一种用于纤维表面的PE保护膜压敏胶，本发明还涉及一种制备本保护膜压敏胶的制备方法。
背景技术
目前用于纤维表面的保护膜是以PE薄膜为基材，以橡胶或丙烯酸酯聚合物为压敏胶粘剂，经涂布干燥等方法加工而成。
由于现有的压敏胶的粘度较小，所以为了保证粘合质量，需要在PE薄膜上涂覆大量的压敏胶，但是由于PE薄膜的厚度较薄，当涂覆大量压敏胶以后，压敏胶在干燥过程中会出现收缩，从而使得PE薄膜出现凸卷现象，而且当保护膜剥离的过程中还会在被保护的表面上残留有残胶，所以开发一种使用效果好的PE保护膜压敏胶已经提上了人们的研究日程。
发明内容
为了克服现有技术的不足，本发明提供一种使用效果好的PE保护膜压敏胶。
本发明的另一个目的是要提供一种生产上述保护膜压敏胶的方法。
本发明解决其技术问题所采用的技术方案是：
一种用于纤维表面的PE保护膜压敏胶，由下述质量组成份数的原材料制成：丙烯酸2-乙基己酯：30～38份，乙酸乙烯酯：0～4份，丙烯酸羟乙酯：0.4～2份，丙烯酸：1.6～4份，溶剂：55～60份。
一种生产PE保护膜压敏胶的方法，其步骤如下：
1)：按比例称取各种原料；
2)：在溶剂内加入丙烯酸2-乙基己酯，乙酸乙烯酯，丙烯酸羟乙酯，丙烯酸后加热至80℃进行搅拌8小时即可。
本发明的有益效果是：通过本工艺制作出来的PE保护膜压敏胶，粘度好，使用时无须涂覆少量即可达到压敏效果，由于该压敏胶涂覆量少，所以在干燥过程中不会导致PE薄膜出现凸卷现象，而且当保护膜剥离的过程中不会在被保护的表面上残留有残胶，从而可以广泛应用于PE保护膜的制作上。
具体实施方式
一种用于纤维表面的PE保护膜压敏胶，由下述质量组成份数的原材料制成：丙烯酸2-乙基己酯：30～38份，乙酸乙烯酯：0～4份，丙烯酸羟乙酯：0.4～2份，丙烯酸：1.6～4份，溶剂：55～60份；
该PE保护膜压敏胶的最佳重量组成份数为：所述丙烯酸2-乙基己酯：35份，乙酸乙烯酯：2份，丙烯酸羟乙酯：1份，丙烯酸：3份，溶剂：60份。
一种生产上述PE保护膜压敏胶的方法，其步骤如下：
1)：按比例称取各种原料；
2)：在溶剂内加入丙烯酸2-乙基己酯，乙酸乙烯酯，丙烯酸羟乙酯，丙烯酸后加热至80℃进行搅拌，其内部发生聚合反应，8小时即可出料。
通过本工艺制作出来的PE保护膜压敏胶，粘度好，使用时无须涂覆少量即可达到压敏效果，由于该压敏胶涂覆量少，所以在干燥过程中不会导致PE薄膜出现凸卷现象，而且当保护膜剥离的过程中不会在被保护的表面上残留有残胶，从而可以广泛应用于PE保护膜的制作上。
Claims (3)
1.一种用于纤维表面的PE保护膜压敏胶，其特征在于：由下述质量组成份数的原材料制成：丙烯酸2-乙基己酯：30～38份，乙酸乙烯酯：0～4份，丙烯酸羟乙酯：0.4～2份，丙烯酸：1.6～4份，溶剂：55～60份。
2.根据权利要求1所述的一种用于纤维表面的PE保护膜压敏胶，其特征在于：所述丙烯酸2-乙基己酯：35份，乙酸乙烯酯：2份，丙烯酸羟乙酯：1份，丙烯酸：3份，溶剂：60份。
3.一种生产权利要求1或2所述的PE保护膜压敏胶的方法，其特征在于：该方法包括如下步骤：
1)：按比例称取各种原料；
2)：在溶剂内加入丙烯酸2-乙基己酯，乙酸乙烯酯，丙烯酸羟乙酯，丙烯酸后加热至80℃进行搅拌8小时即可。