CN101565583B - 一种矿棉吊顶板用背涂涂料的配制及施工工艺 - Google Patents
一种矿棉吊顶板用背涂涂料的配制及施工工艺 Download PDFInfo
- Publication number
- CN101565583B CN101565583B CN2009100520005A CN200910052000A CN101565583B CN 101565583 B CN101565583 B CN 101565583B CN 2009100520005 A CN2009100520005 A CN 2009100520005A CN 200910052000 A CN200910052000 A CN 200910052000A CN 101565583 B CN101565583 B CN 101565583B
- Authority
- CN
- China
- Prior art keywords
- coating
- mineral cotton
- ceiling floor
- coating used
- sheet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种矿棉吊顶板用背涂涂料的配制及其施工工艺。所述矿棉吊顶板用背涂涂料为一种液体状层料。所述施工工艺包括三个工序:基层板材测试→辊涂背涂涂料→高温烘烤(交联固化)。本发明矿棉吊顶板用背涂涂料具有交联速度快、致密性高、拉伸强度大,及良好的防火防潮、增强板材拉伸强度、防霉、降低噪声的作用,同时还具有使用寿命长、耐黄变、低VOC、施工方便等特点。本发明矿棉吊顶板用背涂涂料与矿棉吊顶板配套使用,具有独特的防潮透气和防下沉效果,可保证顶棚的长久平整视觉效果,适用于各种高档建筑物吊顶饰面的装饰。
Description
技术领域:
本发明涉及矿棉吊顶板用背涂涂料及施工工艺,具体地说是一种施工在矿棉吊顶板上的矿棉吊顶板用背涂涂料及施工工艺。
背景技术:
目前市场上出现各种档次的室内顶面装饰材料,一般都是以铝材、岩棉、碳酸钙或石膏材质的吊顶板为主,其装饰效果比较单一。铝材的吊顶板表面比较光滑,成本也较高,对光线反射大,造成室内的光线效果反差大,给人的视觉效果不好;岩棉材质的吊顶板质轻,但防水效果较差,时间长后很容易受潮下垂;碳酸钙或石膏材质的吊顶板,较易破碎,造成施工不便,而且容易吸水。
发明内容:
本发明的目的是针对现有技术的不足而提供的一种与矿棉吊顶板结合使用的矿棉吊顶板用背涂涂料及施工工艺。
本发明目的可以通过以下技术方案来实现:
本发明的一方面是一种矿棉吊顶板用背涂涂料,为液体状层料,主要成分(按重量计)为:
合成树脂5-40份,分散剂0.1-1份,增稠剂0.1-1份,高岭土10-30份,碳酸钙10-20份,消泡剂0.1-0.5,水30-50份。
所述分散剂为聚丙烯酸盐分散剂、硅酸盐分散剂或缩合磷酸盐类分散剂。
所述合成树脂是固体三聚氰胺甲醛树脂或液体三聚氰胺甲醛树脂、或其它水溶性三聚氰胺类合成的固体或液体树脂或其混合物。
所述增稠剂为选自如下的纤维素醚及其衍生物:甲基纤维素、乙基纤维素、羟甲基纤维素、羟乙基纤维素、羟丙基纤维素、羧甲基纤维素或甲基羟丙基纤维素类。
所述消泡剂是硅氧烷系消泡剂或硅氧烷系消泡剂的复配。
本发明的另一方面是一种矿棉吊顶板用背涂涂料的施工工艺,包括以下三个工序:基层板材测试→辊涂背涂涂料→高温烘烤(交联固化)。
所述的施工工艺,其特征在于所述背涂涂料是用辊筒将涂料粘在基层上的,在3-10秒内经过700-900℃高温明火烘烤。
本发明矿棉吊顶板用背涂涂料具有交联速度快、致密性高、拉伸强度大,及良好的防火防潮、增强板材拉伸强度、防霉、降低噪声的作用,同时还具有使用寿命长、耐黄变、低VOC、施工方便等特点。本发明矿棉吊顶板用背涂涂料与矿棉吊顶板配套使用,具有独特的防潮透气和防下沉效果,可保证顶棚的长久平整视觉效果,适用于各种高档建筑物吊顶饰面的装饰。
本发明矿棉吊顶板用背涂涂料与传统吊顶板装饰相比,综合装饰效果更强,具有隔音降噪效果好、防火防潮性能好、使用寿命长、使室内清晰度更佳、施工装饰更加快捷等优良性能,是吊顶装饰的一大突破。经市场调查,目前国内还没有使用涂料和矿棉板配套的技术产品,本发明填补了国内本行业的空白。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
取合成固体三聚氰胺甲醛树脂8份,分散剂0.3份,增稠剂0.3份,高岭土20份,碳酸钙20份,消泡剂0.2,水51.2份。将水注入反应釜中,加入缩合磷酸盐分散剂高速分散5分钟,加入羟甲基纤维素高速分散5分钟,加入碳酸钙和高岭土高速分散35分钟,加入三聚氰胺甲醛树脂乳液慢速搅拌10分钟,加入消泡剂慢速搅拌5分钟,停止搅拌,得到背涂涂料。
本发明施工工艺包括以下三个工序:基层板材测试→辊涂背涂→高温烘烤(交联固化)。
具体施工工艺过程如下:
1、基层板材测试:
基层板材须清洁干燥,不能含有污迹、油污、浮灰等。
对基层板材的含水率、强度等性能进行测试,达到一定标准再进入施工程序。
2、辊涂背涂涂料:
利用辊筒,将背涂涂料均匀粘在板材背面。
3、高温烤干
将工序2中粘上背涂涂料的板材,在3-10秒内通过700-900℃高温的明火,将涂料烘烤(交联固化),对矿棉板材进行平整密封,加强板材的强度。
实施例2
取合成液体三聚氰胺甲醛树脂20份,分散剂0.3份,增稠剂0.3份,高岭土20份,碳酸钙20份,消泡剂0.2,水39.2份。将水注入反应釜中,加入缩合磷酸盐分散剂高速分散5分钟,加入羟甲基纤维素高速分散5分钟,加入碳酸钙和高岭土高速分散35分钟,加入三聚氰胺甲醛树脂乳液慢速搅拌10分钟,加入消泡剂慢速搅拌5分钟,停止搅拌,得到背涂涂料。
本发明施工工艺包括以下三个工序:基层板材测试→辊涂背涂→高温烘烤(交联固化)。
具体施工工艺过程如下:
1、基层板材测试:
基层板材须清洁干燥,不能含有污迹、油污、浮灰等。
对基层板材的含水率、强度等性能进行测试,达到一定标准再进入施工程序。
2、辊涂背涂涂料:
利用辊筒,将背涂涂料均匀粘在板材背面。
3、高温烤干
将工序2中粘上背涂涂料的板材,在3-10秒内通过700-900℃高温的明火,将涂料烘烤(交联固化),对矿棉板材进行平整密封,加强板材的强度。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等同物界定。
Claims (5)
1.一种矿棉吊顶板用背涂涂料,为液体状层料,各原料成分按重量比计为:
合成树脂5-40份,分散剂0.1-1份,增稠剂0.1-1份,高岭土10-30份,碳酸钙10-20份,消泡剂0.1-0.5,水30-50份;
所述合成树脂是固体三聚氰胺甲醛树脂或液体三聚氰胺甲醛树脂。
2.根据权利要求1所述的矿棉吊顶板用背涂涂料,其特征在于所述分散剂为聚丙烯酸盐分散剂、硅酸盐分散剂或缩合磷酸盐类分散剂。
3.根据权利要求1所述的矿棉吊顶板用背涂涂料,其特征在于所述增稠剂为选自如下的纤维素醚及其衍生物:甲基纤维素、乙基纤维素、羟甲基纤维素、羟乙基纤维素、羟丙基纤维素、羧甲基纤维素或甲基羟丙基纤维素类。
4.根据权利要求1所述的矿棉吊顶板用背涂涂料,其特征在于所述消泡剂是硅氧烷系消泡剂或硅氧烷系消泡剂的复配。
5.一种权利要求1所述的矿棉吊顶板用背涂涂料的施工工艺,其特征在于它包括以下三个工序:基层板材测试→辊涂背涂涂料→高温烘烤;其中基层板材测试是对基层板材的含水率、强度性能进行测试;辊涂背涂涂料是利用辊筒,将背涂涂料均匀粘在板材背面;高温烤烤是将粘上背涂涂料的板材,在3-10秒内通过700-900℃高温的明火,将涂料烘烤进行交联固化。