CN101555142A - 纳米碳化硅增韧氧化铝防弹陶瓷的制备方法 - Google Patents
纳米碳化硅增韧氧化铝防弹陶瓷的制备方法 Download PDFInfo
- Publication number
- CN101555142A CN101555142A CNA2009100152395A CN200910015239A CN101555142A CN 101555142 A CN101555142 A CN 101555142A CN A2009100152395 A CNA2009100152395 A CN A2009100152395A CN 200910015239 A CN200910015239 A CN 200910015239A CN 101555142 A CN101555142 A CN 101555142A
- Authority
- CN
- China
- Prior art keywords
- silicon carbide
- preparation
- aluminum oxide
- bulletproof ceramic
- toughened aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)