CN101549448A - 钢网架螺栓球节点用高强度螺栓的加工工艺 - Google Patents

钢网架螺栓球节点用高强度螺栓的加工工艺 Download PDF

Info

Publication number
CN101549448A
CN101549448A CNA2008100200892A CN200810020089A CN101549448A CN 101549448 A CN101549448 A CN 101549448A CN A2008100200892 A CNA2008100200892 A CN A2008100200892A CN 200810020089 A CN200810020089 A CN 200810020089A CN 101549448 A CN101549448 A CN 101549448A
Authority
CN
China
Prior art keywords
bolt
time
cold extrusion
temperature
forming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008100200892A
Other languages
English (en)
Other versions
CN101549448B (zh
Inventor
李俭
李玉叶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGDU SHIHE HIGH STRENGTH BOLT CO Ltd
Original Assignee
JIANGDU SHIHE HIGH STRENGTH BOLT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGDU SHIHE HIGH STRENGTH BOLT CO Ltd filed Critical JIANGDU SHIHE HIGH STRENGTH BOLT CO Ltd
Priority to CN2008100200892A priority Critical patent/CN101549448B/zh
Publication of CN101549448A publication Critical patent/CN101549448A/zh
Application granted granted Critical
Publication of CN101549448B publication Critical patent/CN101549448B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

钢网架螺栓球节点用高强度螺栓的加工工艺。本发明涉及一种高强度连接件的加工工艺。采用40Cr为坯料，它的加工方式为：采用少无切削加工，其中包括三次冷挤压成型、一次热锻成型，即第一次冷挤压成型为螺杆成型、第二次冷挤压成型为螺杆上螺纹段成型、第三次冷挤压成型为螺纹成型，热锻成型为螺栓冒头成型。本发明主要采用冷挤压工艺进行螺栓生产，提高了螺栓的强度，优化了其生产工艺，解决了高强度下螺栓的延迟断裂和疲劳断裂，使用过程中不易折断，连接可靠，提高了螺栓的使用寿命，能更加满足现今社会对钢网架螺栓球节点用高强度螺栓的使用需要。

Description

钢网架螺栓球节点用高强度螺栓的加工工艺
技术领域
本发明涉及一种高强度连接件的加工工艺，尤其涉及一种钢网架螺栓球节点用高强度螺栓的加工工艺。
背景技术
钢网架螺栓球节点用高强度螺栓是机械行业中常用的紧固件，目前的加工方式一般采用车削方式加以成型，其强度往往难以保证，当抗拉强度超过一定值时，在缺口集中的地方如杆与头部的过渡处或螺纹根部容易造成延迟断裂和疲劳断裂，对工程质量造成严重影响，严重时会由于其连接强度的不够而导致安全事故的发生，故需要对传统的高强度螺栓的生产工艺加以研究和改进，以在确保其质量的前提下能高效的进行大批量生产，满足社会对钢网架螺栓球节点用高强度螺栓的广泛需要。
发明内容
本发明针对上述缺陷，目的在于提供一种加工工艺简单、且能生产出高质量钢网架螺栓球节点用高强度螺栓的钢网架螺栓球节点用高强度螺栓的加工工艺。
本发明的技术方案是：本发明采用40Cr为坯料，它的加工方式为：采用少无切削加工，其中包括三次冷挤压成型、一次热锻成型，即第一次冷挤压成型为螺杆成型、第二次冷挤压成型为螺杆上螺纹段成型、第三次冷挤压成型为螺纹成型，热锻成型为螺栓冒头成型。
本发明的具体加工步骤按以下进行：
(1)备料：选用40Cr为坯料，并按照螺栓的规格大小车下坯料。
(2)软化退火：在钟罩炉内进行等温球化退火，软化退火温度取780℃±15℃，保温时间为8-12小时，其硬度控制在HB100-120之间。
(3)热锻冒头：在热锻炉内以900℃-1000℃的温度对螺栓冒头进行热锻，后冷却。
(4)坯料表面处理及润滑：对螺杆段进行磷化处理和涂MoS2的表面处理工艺，其工艺流程为：碱洗→水洗→酸洗→水洗→磷化→清洗→震荡机上涂MoS2。
(5)第一次冷挤压成型：在室温下对螺杆段进行挤压，选用150-200吨气位冲床。
(6)第二次挤压成型：在室温下对螺杆上螺纹段进行挤压，选用70-90吨气位冲床。
(7)第三次挤压成型，在室温下进行螺纹成型，选用Z-28滚丝机。
(8)淬火：在盐浴炉内对成型件进行淬火，其温度控制在850℃±10℃，升温时间4min-6min，保温时间25min-40min，淬火完成后，用油冷却，其冷却温度小于80℃。
(9)检验：用HR-150A洛式硬度计对其进行检验，以HRC不小于50为合格件。
(10)回火：在硝盐炉内对合格件进行回火，其温度控制在530℃±15℃，升温时间为25min-35min，保温时间为50min-70min，回火完成后，用水在室温条件下进行冷却。
(11)二次检验：用HR-150A洛式硬度计对其进行检验，以HRC在32-37内为合格件。
(12)发兰：对上述合格件进行发兰处理，以确保其不生锈。
(13)入库。
本发明主要采用冷挤压工艺进行螺栓生产，提高了螺栓的强度，优化了其生产工艺，解决了高强度下螺栓的延迟断裂和疲劳断裂，使用过程中不易折断，连接可靠，提高了螺栓的使用寿命，能更加满足现今社会对钢网架螺栓球节点用高强度螺栓的使用需要。
具体实施方式
下面结合实施方式对本发明做进一步的阐述：
实施方式一：
本发明采用40Cr为坯料，它的加工方式为：采用少无切削加工，其中包括三次冷挤压成型、一次热锻成型，即第一次冷挤压成型为螺杆成型、第二次冷挤压成型为螺杆上螺纹段成型、第三次冷挤压成型为螺纹成型，热锻成型为螺栓冒头成型。
本发明的具体加工步骤按以下进行：
(1)备料：选用40Cr为坯料，并按照螺栓的规格大小车下坯料。
(2)软化退火：在钟罩炉内进行等温球化退火，软化退火温度取765℃，保温时间为12小时，其硬度控制在HB100-120之间。
(3)热锻冒头：在热锻炉内以900℃的温度对螺栓冒头进行热锻，后冷却。
(4)坯料表面处理及润滑：对螺杆段进行磷化处理和涂MoS2的表面处理工艺，其工艺流程为：碱洗→水洗→酸洗→水洗→磷化→清洗→震荡机上涂MoS2。
(5)第一次冷挤压成型：在室温下对螺杆段进行挤压，选用160吨气位冲床。
(6)第二次挤压成型：在室温下对螺杆上螺纹段进行挤压，选用80吨气位冲床。
(7)第三次挤压成型，在室温下进行螺纹成型，选用Z-28滚丝机。
(8)淬火：在盐浴炉内对成型件进行淬火，其温度控制在840℃，升温时间6min，保温时间40min，淬火完成后，用油冷却，其冷却温度小于80℃。
(9)检验：用HR-150A洛式硬度计对其进行检验，以HRC不小于50为合格件。
(10)回火：在硝盐炉内对合格件进行回火，其温度控制在515℃，升温时间为35min，保温时间为70min，回火完成后，用水在室温条件下进行冷却。
(11)二次检验：用HR-150A洛式硬度计对其进行检验，以HRC在32-37内为合格件。
(12)发兰：对上述合格件进行发兰处理，以确保其不生锈。
(13)入库。
由于热轧状态下的40Cr各部位的硬度不均匀，塑性差，变形抗力大，若不经软化退火处理而直接进行冷挤压加工，则成形困难、模具容易损坏、挤压件容易产生裂纹，因此在冷挤压成形前需对坯料进行软化退火处理。本发明采用球化退火使其具有较低的硬度和较好的塑性，为了进一步提高材料的机械性能，本发明也可采用正火工艺对材料软化。
为了减少材料的残余应力和提高材料的表面质量，在对材料冷挤压之前本发明要对材料进行润滑处理，主要是磷化处理，经研究进行磷化处理会显著降低材料的疲劳性能，也更利于对其进行冷挤压加工。
本发明进行三次冷挤压成型，充分提高了螺栓各段的强度其，螺栓质量好、精度高、其强度性能也好；冷挤压属于少、无切削加工，节省原材料；冷挤压是利用模具来成形的，其生产效率很高；据统计材料利用率大为提高，达到99.5％-99.7％，加工效率约为传统切削工艺的1.8倍，单位成本大为降低，因其属于少无切削加工工艺，使得螺栓的材料纤维方向在螺栓本体上体现了整体性，大大提高了其抗拉强度。
本发明的热处理采用调质处理，即淬火加上回火的处理，以得到具有良好综合性能的螺栓，本发明的淬火方法可采用高温淬火、高频循环快速加热淬火和亚共析钢的亚温淬火等现代淬火方式，使本发明的螺栓具有更好的力学综合性能。
具体实施方式二：
本发明采用40Cr为坯料，它的加工方式为：采用少无切削加工，其中包括三次冷挤压成型、一次热锻成型，即第一次冷挤压成型为螺杆成型、第二次冷挤压成型为螺杆上螺纹段成型、第三次冷挤压成型为螺纹成型，热锻成型为螺栓冒头成型。
本发明的具体加工步骤按以下进行：
(1)备料：选用40Cr为坯料，并按照螺栓的规格大小车下坯料。
(2)软化退火：在钟罩炉内进行等温球化退火，软化退火温度取795℃，保温时间为8小时，其硬度控制在HB100-120之间。
(3)热锻冒头：在热锻炉内以1000℃的温度对螺栓冒头进行热锻，后冷却。
(4)坯料表面处理及润滑：对螺杆段进行磷化处理和涂MoS2的表面处理工艺，其工艺流程为：碱洗→水洗→酸洗→水洗→磷化→清洗→震荡机上涂MoS2。
(5)第一次冷挤压成型：在室温下对螺杆段进行挤压，选用190吨气位冲床。
(6)第二次挤压成型：在室温下对螺杆上螺纹段进行挤压，选用85吨气位冲床。
(7)第三次挤压成型，在室温下进行螺纹成型，选用Z-28滚丝机。
(8)淬火：在盐浴炉内对成型件进行淬火，其温度控制在860℃，升温时间4min，保温时间30min，淬火完成后，用油冷却，其冷却温度小于80℃。
(9)检验：用HR-150A洛式硬度计对其进行检验，以HRC不小于50为合格件。
(10)回火：在硝盐炉内对合格件进行回火，其温度控制在545℃，升温时间为25min，保温时间为50min，回火完成后，用水在室温条件下进行冷却。
(11)二次检验：用HR-150A洛式硬度计对其进行检验，以HRC在32-37内为合格件。
(12)发兰：对上述合格件进行发兰处理，以确保其不生锈。
(13)入库。
由于热轧状态下的40Cr各部位的硬度不均匀，塑性差，变形抗力大，若不经软化退火处理而直接进行冷挤压加工，则成形困难、模具容易损坏、挤压件容易产生裂纹，因此在冷挤压成形前需对坯料进行软化退火处理。本发明采用球化退火使其具有较低的硬度和较好的塑性，为了进一步提高材料的机械性能，本发明也可采用正火工艺对材料软化。
为了减少材料的残余应力和提高材料的表面质量，在对材料冷挤压之前本发明要对材料进行润滑处理，主要是磷化处理，经研究进行磷化处理会显著降低材料的疲劳性能，也更利于对其进行冷挤压加工。
本发明进行三次冷挤压成型，充分提高了螺栓各段的强度其，螺栓质量好、精度高、其强度性能也好；冷挤压属于少、无切削加工，节省原材料；冷挤压是利用模具来成形的，其生产效率很高；据统计材料利用率大为提高，达到99.5％-99.7％，加工效率约为传统切削工艺的1.8倍，单位成本大为降低，因其属于少无切削加工工艺，使得螺栓的材料纤维方向在螺栓本体上体现了整体性，大大提高了其抗拉强度。
本发明的热处理采用调质处理，即淬火加上回火的处理，以得到具有良好综合性能的螺栓，本发明的淬火方法可采用高温淬火、高频循环快速加热淬火和亚共析钢的亚温淬火等现代淬火方式，使本发明的螺栓具有更好的力学综合性能。

Claims (2)

1、钢网架螺栓球节点用高强度螺栓的加工工艺，采用40Cr为坯料，其特征在于，它的加工方式为：采用少无切削加工，其中包括三次冷挤压成型、一次热锻成型，即第一次冷挤压成型为螺杆成型、第二次冷挤压成型为螺杆上螺纹段成型、第三次冷挤压成型为螺纹成型，热锻成型为螺栓冒头成型。
2、根据权利要求1所述的钢网架螺栓球节点用高强度螺栓的加工工艺，其特征在于，它的具体加工步骤按以下进行：
(1)备料：选用40Cr为坯料，并按照螺栓的规格大小车下坯料。
(2)软化退火：在钟罩炉内进行等温球化退火，软化退火温度取780℃±15℃，保温时间为8-12小时，其硬度控制在HB100-120之间。
(3)热锻冒头：在热锻炉内以900℃-1000℃的温度对螺栓冒头进行热锻，后冷却。
(4)坯料表面处理及润滑：对螺杆段进行磷化处理和涂MoS2的表面处理工艺，其工艺流程为：碱洗→水洗→酸洗→水洗→磷化→清洗→震荡机上涂MoS2。
(5)第一次冷挤压成型：在室温下对螺杆段进行挤压，选用150-200吨气位冲床。
(6)第二次挤压成型：在室温下对螺杆上螺纹段进行挤压，选用70-90吨气位冲床。
(7)第三次挤压成型，在室温下进行螺纹成型，选用Z-28滚丝机。
(8)淬火：在盐浴炉内对成型件进行淬火，其温度控制在850℃±10℃，升温时间4min-6min，保温时间25min-40min，淬火完成后，用油冷却，其冷却温度小于80℃。
(9)检验：用HR-150A洛式硬度计对其进行检验，以HRC不小于50为合格件。
(10)回火：在硝盐炉内对合格件进行回火，其温度控制在530℃±15℃，升温时间为25min-35min，保温时间为50min-70min，回火完成后，用水在室温条件下进行冷却。
(11)二次检验：用HR-150A洛式硬度计对其进行检验，以HRC在32-37内为合格件。
(12)发兰：对上述合格件进行发兰处理，以确保其不生锈。
(13)入库。
CN2008100200892A 2008-03-31 2008-03-31 钢网架螺栓球节点用高强度螺栓的加工工艺 Expired - Fee Related CN101549448B (zh)