CN101462846A - 装饰材料及其生产方法 - Google Patents

装饰材料及其生产方法 Download PDF

Info

Publication number
CN101462846A
CN101462846A CNA200910102406XA CN200910102406A CN101462846A CN 101462846 A CN101462846 A CN 101462846A CN A200910102406X A CNA200910102406X A CN A200910102406XA CN 200910102406 A CN200910102406 A CN 200910102406A CN 101462846 A CN101462846 A CN 101462846A
Authority
CN
China
Prior art keywords
pvc
production method
powder
decorative material
finishing material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA200910102406XA
Other languages
English (en)
Inventor
李运华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUIZHOU YINJIANG AUTONOMOUS COUNTY JUCHUANG DECORATIVE MATERIAL CO Ltd
Original Assignee
GUIZHOU YINJIANG AUTONOMOUS COUNTY JUCHUANG DECORATIVE MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUIZHOU YINJIANG AUTONOMOUS COUNTY JUCHUANG DECORATIVE MATERIAL CO Ltd filed Critical GUIZHOU YINJIANG AUTONOMOUS COUNTY JUCHUANG DECORATIVE MATERIAL CO Ltd
Priority to CNA200910102406XA priority Critical patent/CN101462846A/zh
Publication of CN101462846A publication Critical patent/CN101462846A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种装饰材料及其生产方法，其特征在于：由碳酸重钙粉6－8份、秸秆粉0.5－1份、PVC1.5－3份混合，烘干到物料中水份含量低于0.1％，在190－220℃下造粒，然后在190－220℃下挤压成型而得。PVC为新料、废料PVC或两者的混合物。本发明具有防水、阻燃、抗腐、防蛀、脚感弹性良，触觉性佳，隔音隔热、使用寿命长的特点。

Description

装饰材料及其生产方法
技术领域
本发明涉及材料技术领域，具体来说涉及装饰材料，同时还涉及其生产方法。
背景技术
目前地板装饰材料(地砖除外)主要有两种类型；一是以原木为原料，经加工生产的实木材料；二是以木塑粉为原料，加入粘合剂，通过压制而成的复合材料。实木材料的生产，需消耗大量天然的森林资源，不利于生态环境保护，综合利用木质粉、秸秆粉等废渣生产的复合材料，需加入粘合剂，至使产品内含甲醛，且存在耐磨性不足、涂装后开槽边缘易进白等质量缺陷。
发明内容
本发明的目的在于克服上述缺点而提供的一种防水、阻燃、抗腐、防蛀、脚感弹性良，触觉性佳，隔音隔热、使用寿命长的装饰材料。
本发明的另一目的还在于提供该装饰材料的生产方法。
本发明的装饰材料，由碳酸重钙粉6-8份、的桔杆粉0.5-1份、PVC1.5-3份混合，烘干到物料中水份含量低于0.1％，在190-220℃下造粒，然后在190-220℃下挤压成型而得。
其中：PVC为新料、废料PVC或两者的混合物。
一种装饰材料的生产方法，包括下述步骤：
(1)配料：将400-800目的碳酸重钙粉6-8份、800-2000目的桔杆粉0.5-1份、PVC1.5-3份混合；
(2)挤压：将物料烘干至其水份含量低于0.1％，在190-220℃下造粒，然后在190-220℃下挤压成型；
(3)冷却、切割、打磨、上色即得。
其中：切割后的边角废料经粉碎后返回配料。
其中：PVC为新料G-5、300-500目的废料PVC或两者的混合物。
本发明与现有技术的相比，从以上技术方案可知，主要有以下优点：以石代木，可有效节约木材资源，保护生态环境；生产中采用物理高温挤压成型，不需粘合剂。可采用回收废料PVC，从而更进一步降低成本；生产中的边角废物，可回收粉碎后参与配料，材料可循环使用。由于采用碳酸重钙粉为主料，废料PVC和秸秆粉(农作物)为辅料。因而生产成本低，仅为强化地板的50％。同时具有：、防水、阻燃、抗腐、防蛀、不长真菌、耐潮湿、耐酸碱、无毒害、无污染、脚感弹性良，触觉性佳，隔音隔热、耐磨度高，使用寿命更长。由于可用水洗，因而可用于室内外。
以下通过具体实施方式，进一步说明本发明的有益效果。
具体实施方式
实施例1：
装饰材料的生产方法，包括下述步骤：
(1)配料：将400目的碳酸重钙粉80kg、800目的桔杆粉5kg、PVC(G-5)15kg份混合；
(2)挤压：将物料烘干至其水份含量低于0.1％，在190℃下造粒，然后在190℃下挤压成型；
(3)冷却、切割、打磨、上色即得。
切割后的边角废料经过粉碎、与收集的生产中产生的粉尘一并返回到配料。
实施例2：
装饰材料的生产方法，包括下述步骤：
(1)配料：将500目的碳酸重钙粉70kg、1000目的桔杆粉10kg、PVC(G-5)粉5kg、粉碎成500目的废料PVC粉15kg混合；
(2)挤压：将物料烘干至其水份含量低于0.1％，在190℃下造粒，然后在190℃下挤压成型；
(3)冷却、切割、打磨、上色即得。
切割后的边角废料经过粉碎、与收集的生产中产生的粉尘一并返回到配料。
实施例3：
装饰材料的生产方法，包括下述步骤：
(1)配料：将800目的碳酸重钙粉60kg、2000目的桔杆粉10kg、粉碎成300目的废料PVC粉30kg混合；
(2)挤压：将物料烘干至其水份含量低于0.1％，在220℃下造粒，然后在220℃下挤压成型；
(3)冷却、切割、打磨、上色即得。
切割后的边角废料经过粉碎、与收集的生产中产生的粉尘一并返回到配料。
本发明生产的地板与传统地板比较表
 
本发明的地板         免漆实木地板 免漆竹木地板 免漆多层实木复合地板 强化地板 实木地板紫板     地砖
 
耐磨性 7160MPa  1000～1500MPa        1000～1500MPa        1000～1500MPa        1000～6000MPa        无 ≥6000MPa
木纹逼真性 良 优 优 优 良 优 一般
防虫防腐性 不需防虫防腐         需作防虫预处理       需防虫预处理         需防虫预处理         需防虫预处理         需防虫预处理         不需防虫处理        
二次变形 无 易发生 易发生 会发生轻微变形   不易发生变形     易发生 无
是否可回收 可回收 无 无 无 无 无 无
物理承载性 韧性好、强度略差     优 良 优 一般 优 易脆裂
总成本 60～80元/m2        ≥250元/m2 130～180元/m2         150～300元//m2        40～180元/m2         品种不同价不同       30～100元/m2        
施工繁简 简单 简单 简单 简单 简单 繁琐，周期长         较简单
安装性能 直接在地面上垫一层弹性膜即可开始铺装，无需防潮处理。       需作地平、打龙骨，需作防虫、防潮预处理。 需作地平、打龙骨，需作防虫、防潮预处理   需作地平、打龙骨，需作防虫、防潮预处理   不需打龙骨，但需作防潮处理 需作地平、打龙骨，需作防虫、防潮预处理   用水泥粘接在地面即可
防水性 完全防水、可用湿拖把拖地。     禁遇水，否则会变形。 禁遇水，否则会变形，散片。     禁遇水，否则会变形。 不可长期浸水     禁遇水，否则会变形。 完全防水。
防火性 阻燃材质烟头烫表面无任何变化，80℃以下不起烟。     易燃物，烟头烫后，漆面有鼓泡，龟裂，发黄发黑。     易燃物，烟头烫后，漆面有鼓泡，龟裂，发黄发黑。     易燃物，烟头烫后，漆面有鼓泡，龟裂，发黄发黑。     易燃物，惧烟头烫。 易燃物，烟头烫后，漆面有鼓泡，龟裂，发黄发黑。     易燃物，不惧烟头烫。
环保性能 无任何TV0C，健康、环保 无任何TV0C，健康、环保 基材含胶质，长期有甲醛等有害气体释放，影响人体健康。       基材含胶质，长期有甲醛等TV0C释放，影响人体健康。 基材含胶质，长期有甲醛TVOC释放，影响人体健康。 基材含胶质，长期有甲醛TV0C释放，影响人体健康。 在某些类型的地砖中可能具有放射性，对人体健康有潜在的威胁。  
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，任何未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (5)

1、一种装饰材料，其特征在于：由碳酸重钙粉6-8份、的桔杆粉0.5-1份、PVC1.5-3份混合，烘干到物料中水份含量低于0.1％，在190-220℃下造粒，然后在190-220℃下挤压成型而得。
2、如权利要求1所述的装饰材料，其特征在于：PVC为新料、废料PVC或两者的混合物。
3、一种装饰材料的生产方法，包括下述步骤：
(1)配料：将400-800目的碳酸重钙粉6-8份、800-2000目的桔杆粉0.5-1份、PVC1.5-3份混合；
(2)挤压：将物料烘干至其水份含量低于0.1％，在190-220℃下造粒，然后在190-220℃下挤压成型；
(3)冷却、切割、打磨、上色即得。
4、如权利要求3所述的装饰材料的生产方法，其特征在于：PVC为新料G-5、300-500目的废料PVC或两者的混合物。
5、如权利要求3或4所述的装饰材料的生产方法，其特征在于：切割后的边角废料经粉碎后返回配料。
CNA200910102406XA 2009-01-05 2009-01-05 装饰材料及其生产方法 Pending CN101462846A (zh)