CN101462766B - 一种四氯化钛炉气的冷却工艺 - Google Patents

一种四氯化钛炉气的冷却工艺 Download PDF

Info

Publication number
CN101462766B
CN101462766B CN2007102032257A CN200710203225A CN101462766B CN 101462766 B CN101462766 B CN 101462766B CN 2007102032257 A CN2007102032257 A CN 2007102032257A CN 200710203225 A CN200710203225 A CN 200710203225A CN 101462766 B CN101462766 B CN 101462766B
Authority
CN
China
Prior art keywords
cooling
titanic chloride
gas
cooler
furnace gas
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2007102032257A
Other languages
English (en)
Other versions
CN101462766A (zh
Inventor
丁子文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guiyang Aluminum Magnesium Design and Research Institute Co Ltd
Original Assignee
Guiyang Aluminum Magnesium Design and Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guiyang Aluminum Magnesium Design and Research Institute Co Ltd filed Critical Guiyang Aluminum Magnesium Design and Research Institute Co Ltd
Priority to CN2007102032257A priority Critical patent/CN101462766B/zh
Publication of CN101462766A publication Critical patent/CN101462766A/zh
Application granted granted Critical
Publication of CN101462766B publication Critical patent/CN101462766B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种四氯化钛炉气的冷却工艺，该工艺包含以下工序：出炉气依次进入旋风除尘器(1)中除尘，1#冷却器(2)中冷却，喷雾冷凝塔(3)中降温，袋式过滤器(4)过滤，前淋洗塔(5)、后淋洗塔(6)、2#冷却器(7)进一步冷凝，再进入冷却筒(8)，经冷却筒后废气进入尾气洗涤系统，排放达标后排入大气，液体进入粗四氯化钛储槽(9)。此工艺合理的利用了高温四氯化钛出炉气中的热量，提高了TiCl4的收率，减少了尾气中的有害气体的排放量，有利于环境保护，符合建设节约能源资源和保护生态环境的产业结构的要求。

Description

一种四氯化钛炉气的冷却工艺 
技术领域
本发明涉及一种炉气的冷却工艺，具体地说涉及一种四氯化钛炉气的冷却工艺。 
背景技术
四氯化钛是一种用途广泛的化工原料，可用于制备有机钛化合物、含钛电子陶瓷、钛氧宝石等，另外在玻璃、硬质合金、皮革、印染工业等方面也有特殊的用途。到目前为止，我国主要是用钛铁矿(TiFeO3)经过电炉冶炼变成高钛渣(TiO2)，再在氯化炉里，加油焦，通氯气生成粗四氯化钛(TICl4)，同时也生成了大量的高温的炉气，国内现有的炉气处理工艺设备体积庞大、笨重(沉降室)，技术落后，温度难以控制；有些虽在工程设计中某项目的原料采用了进口天然金红石，但沸腾氯化系统的冷却冷凝系统仍是落后的工艺，无法充分利用能源以达到节能减排的目的。 
在现有技术中，申请号为200510022528.X的中国专利公布了硫酸生产中沸腾炉后废热利用方法，虽然该工艺利用了出炉气的废热，可它是用高温烟气加热空气，再用空气加热水和冷空气，而不是用高温炉气直接加热水和冷空气，工序繁琐，很难使高温炉气中的热量很好利用。申请号为89102481.6的中国专利公布了一种炉气干法净化方法，该方法中出炉气冷却冷凝系统方法落后，无法很好的适用于四氯化钛炉气充分冷却及节能减排。 
发明内容
本发明所要解决的技术问题是提供一种四氯化钛炉气的冷却工艺，该工艺一方面合理的利用了高温四氯化钛出炉气中的热量，另一方面提高了TiCl4的收率，减少了尾气中的氯化物的排放，有利于环境保护。 
为了解决以上问题，本发明提供了一种四氯化钛炉气的冷却工艺，该工艺包含以下工序：出炉气依次进入旋风除尘器1中除尘，1#冷却器2中冷却，喷雾冷凝塔3中降温，袋式过滤器4过滤，前淋洗塔5、后淋洗塔6、2#冷却器7进一步冷凝，再进入冷却筒8，经冷却筒后废气进入尾气洗涤系统，排放达标后排入大气，液体进入粗四氯化钛储槽9。 
出炉气经过旋风除尘器1产生的粉尘返回氯化炉，循环处理。 
出炉气经1#冷却器2冷却后温度由950～650℃降至400～380℃；1#冷却器2用水冷却可得到热水，得到的热水可起余热锅炉的作用，使热能得到回收利用。 
喷雾冷凝塔3中采用的喷淋剂为粗四氯化钛；出炉气经过喷雾冷凝塔3温度降至180～171 ℃，此时出炉气体中的氯化物的沸点与FeCl3的沸点(315℃)相近者(ZrCl4、CrCl3、NbCl5、AlCl3等)都能在400～171℃之间变成固态。 
出炉气经前淋洗塔5和后淋洗塔6冷却后，气体四氯化钛变成液体四氯化钛。 
出炉气经2#冷却器7深度冷凝后温度降至0～-12℃，减少了尾气中的氯化物，再经过冷却筒8的冷却(也是用冷冻盐水深度冷却)，冷却筒8收集气体中夹杂的四氯化钛，冷却筒8也起到气液分离的作用。收集下来的四氯化钛进入粗四氯化钛储槽9，尾气进入尾气洗涤系统，排放达标后排入大气。 
进入粗四氯化钛储槽9中的粗四氯化钛既可用于四氯化钛精制工序又可作为喷雾冷凝塔3中的喷淋剂。 
与现有技术相比，本发明提供的四氯化钛炉气的冷却工艺，合理的利用了高温四氯化钛出炉气中的热量，提高了TiCl4的收率，减少了尾气中的有害气体的排放量，有利于环境保护，符合建设节约能源资源和保护生态环境的产业结构的要求。 
附图说明
图1为本发明的工艺流程图。 
附图中的标记分别为：1-旋风除尘器，2-1#冷却器，3-喷雾冷凝塔，4-袋式过滤器，5-前淋洗塔，6-后淋洗塔，7-2#冷却器，8-冷却筒，9-粗四氯化钛储槽。 
具体实施方式
实施例：四氯化钛出炉气体温度高约950℃～650℃并含有粉尘，先进入旋风除尘器1除尘，粉尘返回氯化炉继续氯化。高温气体出旋风除尘器1以后进入1#冷却器2使气体降温至400℃，1#冷却器2用水夹套冷却可得到热水，使热能得到回收利用。出炉气体再进入用粗四氯化钛喷淋的喷雾冷凝塔3。在喷雾冷凝塔3内喷入的粗四氯化钛被蒸发，使出炉气体温度被降到180～171℃，此时出炉气体中的氯化物的沸点与FeCl3的沸点(315℃)相近者(ZrCl4、CrCl3、NbCl5、AlCl3等)都能在400～171℃之间变成固态。再经袋式过滤器4除去氯化物渣。比较清洁的气体(含TiCl4、SiCl4、VoCl3、CO、CO2)可用冷却过的粗四氯化钛液体在前淋洗塔5和后淋洗塔6分别喷淋冷凝，使气体中的四氯化钛变成液体四氯化钛。少量未冷凝的氯化物和非冷凝气体再经2#冷却器7冷凝使绝大多数的氯化物全部冷凝。液体四氯化钛流入冷却筒8，经冷却筒8再次深度冷却后，废气进入尾气洗涤系统，排放达标后排入大气，液体四氯化钛最后流入粗四氯化钛储槽9中，粗四氯化钛既可用于四氯化钛精制工序又可作为喷雾冷凝塔3中的喷淋剂。此工艺提高了金属钛的实收率和减少了氯化物的排放。 

Claims (7)

1.一种四氯化钛炉气的冷却工艺，其特征在于：该工艺包含以下工序：出炉气依次进入旋风除尘器(1)中除尘，1#冷却器(2)中冷却，喷雾冷凝塔(3)中降温，袋式过滤器(4)过滤，前淋洗塔(5)、后淋洗塔(6)、2#冷却器(7)进一步冷凝，再进入冷却筒(8)，经冷却筒后废气进入尾气洗涤系统，排放达标后排入大气，液体进入粗四氯化钛储槽(9)。
2.根据权利要求1所述的四氯化钛炉气的冷却工艺，其特征在于：出炉气经过旋风除尘器(1)产生的粉尘返回氯化炉，循环处理。
3.根据权利要求1所述的四氯化钛炉气的冷却工艺，其特征在于：出炉气经1#冷却器(2)冷却后温度由950～650℃降至400～380℃。
4.根据权利要求1所述的四氯化钛炉气的冷却工艺，其特征在于：出炉气经过喷雾冷凝塔(3)温度降至180～171℃。
5.根据权利要求1所述的四氯化钛炉气的冷却工艺，其特征在于：出炉气经2#冷却器(7)深度冷凝后温度降至0～-12℃。
6.根据权利要求1所述的四氯化钛炉气的冷却工艺，其特征在于：喷雾冷凝塔(3)中采用的喷淋剂为粗四氯化钛。
7.根据权利要求1或6所述的四氯化钛炉气的冷却工艺，其特征在于：进入粗四氯化钛储槽(9)中的粗四氯化钛作为喷雾冷凝塔(3)中的喷淋剂。
CN2007102032257A 2007-12-19 2007-12-19 一种四氯化钛炉气的冷却工艺 Active CN101462766B (zh)