CN101460548B - 高分子量聚(α-烯烃)溶液和由其制造的制品 - Google Patents

高分子量聚(α-烯烃)溶液和由其制造的制品 Download PDF

Info

Publication number
CN101460548B
CN101460548B CN2007800202228A CN200780020222A CN101460548B CN 101460548 B CN101460548 B CN 101460548B CN 2007800202228 A CN2007800202228 A CN 2007800202228A CN 200780020222 A CN200780020222 A CN 200780020222A CN 101460548 B CN101460548 B CN 101460548B
Authority
CN
China
Prior art keywords
uhmw
extruder
solvent
temperature
slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2007800202228A
Other languages
English (en)
Chinese (zh)
Other versions
CN101460548A (zh
Inventor
谭耀泰
Q·周
J·A·杨
C·R·阿内特
J·D·布罗迪
C·J·托米
L·L·沃纳
S·卡韦什
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Honeywell International Inc
Original Assignee
Honeywell International Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Honeywell International Inc filed Critical Honeywell International Inc
Publication of CN101460548A publication Critical patent/CN101460548A/zh
Application granted granted Critical
Publication of CN101460548B publication Critical patent/CN101460548B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/02—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D01F6/04—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyolefins
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/022—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the choice of material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
    • B29C48/05—Filamentary, e.g. strands
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
    • B29C48/07—Flat, e.g. panels
    • B29C48/08—Flat, e.g. panels flexible, e.g. films
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/25—Component parts, details or accessories; Auxiliary operations
    • B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
    • B29C48/395—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders
    • B29C48/40—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders using two or more parallel screws or at least two parallel non-intermeshing screws, e.g. twin screw extruders
    • B29C48/405—Intermeshing co-rotating screws
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/02—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques
    • C08J3/09—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in organic liquids
    • C08J3/091—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in organic liquids characterised by the chemical constitution of the organic liquid
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D1/00—Treatment of filament-forming or like material
    • D01D1/02—Preparation of spinning solutions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/25—Component parts, details or accessories; Auxiliary operations
    • B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
    • B29C48/395—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders
    • B29C48/40—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders using two or more parallel screws or at least two parallel non-intermeshing screws, e.g. twin screw extruders
    • B29C48/41—Intermeshing counter-rotating screws
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/25—Component parts, details or accessories; Auxiliary operations
    • B29C48/88—Thermal treatment of the stream of extruded material, e.g. cooling
    • B29C48/919—Thermal treatment of the stream of extruded material, e.g. cooling using a bath, e.g. extruding into an open bath to coagulate or cool the material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/04—Polymers of ethylene
    • B29K2023/06—PE, i.e. polyethylene
    • B29K2023/0658—PE, i.e. polyethylene characterised by its molecular weight
    • B29K2023/0683—UHMWPE, i.e. ultra high molecular weight polyethylene
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2323/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
    • C08J2323/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Health & Medical Sciences (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Textile Engineering (AREA)
  • General Chemical & Material Sciences (AREA)
  • Dispersion Chemistry (AREA)
  • Artificial Filaments (AREA)
  • Processes Of Treating Macromolecular Substances (AREA)
  • Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
  • Extrusion Moulding Of Plastics Or The Like (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Pharmaceuticals Containing Other Organic And Inorganic Compounds (AREA)
  • Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
CN2007800202228A 2006-03-30 2007-03-28 高分子量聚(α-烯烃)溶液和由其制造的制品 Active CN101460548B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US11/393,218 2006-03-30
US11/393,218 US8444898B2 (en) 2006-03-30 2006-03-30 High molecular weight poly(alpha-olefin) solutions and articles made therefrom
PCT/US2007/065333 WO2007118008A2 (en) 2006-03-30 2007-03-28 High molecular weight poly(alpha-olefin) solutions and articles made therefrom

Publications (2)

Publication Number Publication Date
CN101460548A CN101460548A (zh) 2009-06-17
CN101460548B true CN101460548B (zh) 2012-02-01

Family

ID=38509798

Family Applications (1)

Application Number Title Priority Date Filing Date
CN2007800202228A Active CN101460548B (zh) 2006-03-30 2007-03-28 高分子量聚(α-烯烃)溶液和由其制造的制品

Country Status (15)

Country Link
US (2) US8444898B2 (enExample)
EP (1) EP1999190B1 (enExample)
JP (1) JP5144641B2 (enExample)
KR (1) KR101390161B1 (enExample)
CN (1) CN101460548B (enExample)
AT (1) ATE543858T1 (enExample)
BR (1) BRPI0709652B1 (enExample)
CA (1) CA2648212C (enExample)
ES (1) ES2379505T3 (enExample)
IL (1) IL194448A (enExample)
MX (1) MX2008012312A (enExample)
MY (1) MY149308A (enExample)
RU (1) RU2008142849A (enExample)
TW (1) TWI417322B (enExample)
WO (1) WO2007118008A2 (enExample)

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8747715B2 (en) 2007-06-08 2014-06-10 Honeywell International Inc Ultra-high strength UHMW PE fibers and products
US9365953B2 (en) 2007-06-08 2016-06-14 Honeywell International Inc. Ultra-high strength UHMWPE fibers and products
BRPI0910444B1 (pt) * 2008-04-11 2018-11-27 Dsm Ip Assets Bv fios de multifilamento de polietileno com peso molecular ultra elevado, e processo para produção dos mesmo
US20120192339A1 (en) * 2010-07-28 2012-08-02 Honeywell International Inc. Flexible Body Armor Vest with Breast Plate
US8791217B2 (en) 2011-12-28 2014-07-29 Chevron Phillips Chemical Company Lp Catalyst systems for production of alpha olefin oligomers and polymers
US8785576B2 (en) 2011-12-28 2014-07-22 Chevron Phillips Chemical Company Lp Catalyst compositions for the polymerization of olefins
US9169581B2 (en) 2012-02-24 2015-10-27 Honeywell International Inc. High tenacity high modulus UHMW PE fiber and the process of making
US9273418B2 (en) 2012-05-17 2016-03-01 Honeywell International Inc. Hybrid fiber unidirectional tape and composite laminates
WO2014058513A2 (en) 2012-08-06 2014-04-17 Honeywell International Inc. Multidirectional fiber-reinforced tape/film articles and the method of making the same
US9243354B2 (en) 2013-03-15 2016-01-26 Honeywell International Inc. Stab and ballistic resistant articles
EP3584357A1 (en) * 2013-10-29 2019-12-25 Braskem S.A. Continuous system and method for producing at least one polymeric yarn
US9834872B2 (en) 2014-10-29 2017-12-05 Honeywell International Inc. High strength small diameter fishing line
US10612189B2 (en) 2015-04-24 2020-04-07 Honeywell International Inc. Composite fabrics combining high and low strength materials
US10272640B2 (en) 2015-09-17 2019-04-30 Honeywell International Inc. Low porosity high strength UHMWPE fabrics
US20170297295A1 (en) 2016-04-15 2017-10-19 Honeywell International Inc. Blister free composite materials molding
CN109640854B (zh) * 2016-07-07 2022-12-13 直观外科手术操作公司 用于电通量输送器械的电通量输送及返回配置
CN109610027B (zh) * 2018-01-08 2021-01-19 江苏恒辉安防股份有限公司 石墨烯复合超高分子量聚乙烯纤维及其制备方法
US11306432B2 (en) 2018-11-05 2022-04-19 Honeywell International Inc. HMPE fiber with improved bending fatigue performance

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4413110A (en) * 1981-04-30 1983-11-01 Allied Corporation High tenacity, high modulus polyethylene and polypropylene fibers and intermediates therefore
CN85107352A (zh) * 1985-02-15 1986-10-01 斯塔米卡本公司(Dsm附属公司) 连续制备均匀的高分子聚合物溶液的方法
US4784820A (en) * 1986-08-11 1988-11-15 Allied-Signal Inc. Preparation of solution of high molecular weight polymers
US5032338A (en) * 1985-08-19 1991-07-16 Allied-Signal Inc. Method to prepare high strength ultrahigh molecular weight polyolefin articles by dissolving particles and shaping the solution
CN1160093A (zh) * 1997-01-02 1997-09-24 中国纺织科学研究院 超高分子量聚乙烯纤维连续制备方法和设备

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3119704A (en) * 1961-12-04 1964-01-28 Dow Chemical Co Preparation of aerated cementitious products
NL177759B (nl) 1979-06-27 1985-06-17 Stamicarbon Werkwijze ter vervaardiging van een polyetheendraad, en de aldus verkregen polyetheendraad.
US4405399A (en) * 1981-09-30 1983-09-20 Colgate-Palmolive Company Method and apparatus for manufacturing dentifrice containing dispersed speckles
US4440711A (en) 1982-09-30 1984-04-03 Allied Corporation Method of preparing high strength and modulus polyvinyl alcohol fibers
US4883628A (en) 1983-12-05 1989-11-28 Allied-Signal Inc. Method for preparing tenacity and modulus polyacrylonitrile fiber
NL8402961A (nl) * 1984-09-28 1986-04-16 Stamicarbon Werkwijze voor het bereiden van hoogverstrekbare polymere gelvoorwerpen.
KR870001724B1 (ko) * 1984-09-28 1987-09-25 스태미카본 베 · 뷔 고분자폴리머의 균질용액을 연속적으로 제조하는 방법
DE3577110D1 (de) 1984-09-28 1990-05-17 Stamicarbon Verfahren zur kontinuierlichen herstellung von homogenen loesungen von hochmolekularen polymeren.
US4778601A (en) * 1984-10-09 1988-10-18 Millipore Corporation Microporous membranes of ultrahigh molecular weight polyethylene
US4663101A (en) 1985-01-11 1987-05-05 Allied Corporation Shaped polyethylene articles of intermediate molecular weight and high modulus
JPS62263307A (ja) * 1986-05-06 1987-11-16 Toyobo Co Ltd 高強力繊維またはフイルムの製造法
KR910005573B1 (ko) * 1986-10-13 1991-07-31 아사히 가세이 고오교 가부시끼가이샤 고밀도 폴리에틸렌 망상섬유, 이 섬유로 구성된 부직포 및 이들의 제조방법
JP3277233B2 (ja) * 1990-07-18 2002-04-22 ジ・オーストラリアン・ナショナル・ユニバーシティー 多孔性材料の形成
US6506695B2 (en) * 1998-04-21 2003-01-14 Rheinische Kunststoffewerke Gmbh Breathable composite and method therefor
EP1177231B1 (en) * 1999-04-09 2009-08-19 Invitrogen Dynal AS Process for the preparation of monodisperse polymer particles
EP1118275B1 (en) * 1999-08-03 2006-05-17 Morinaga Milk Industry Co., Ltd. Production method for soybean processed food and heating-deaerating device for mashed soybean soup
DK1126052T3 (da) * 1999-08-11 2004-01-12 Toyo Boseki Højstyrke-polyethylenfiber og anvendelse deraf
US6448359B1 (en) * 2000-03-27 2002-09-10 Honeywell International Inc. High tenacity, high modulus filament
CN100410431C (zh) * 2002-12-10 2008-08-13 帝斯曼知识产权资产管理有限公司 制造和转化聚烯烃纤维的方法
JP4578483B2 (ja) 2004-01-01 2010-11-10 ディーエスエム アイピー アセッツ ビー．ブイ． 高性能ポリエチレンマルチフィラメント糸の製造方法
DK1699954T3 (da) 2004-01-01 2012-02-06 Dsm Ip Assets Bv Fremgangsmåde til fremstilling af multifilament polyethylengarn med høj ydeevne
US7147807B2 (en) 2005-01-03 2006-12-12 Honeywell International Inc. Solution spinning of UHMW poly (alpha-olefin) with recovery and recycling of volatile spinning solvent

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4413110A (en) * 1981-04-30 1983-11-01 Allied Corporation High tenacity, high modulus polyethylene and polypropylene fibers and intermediates therefore
CN85107352A (zh) * 1985-02-15 1986-10-01 斯塔米卡本公司(Dsm附属公司) 连续制备均匀的高分子聚合物溶液的方法
US5032338A (en) * 1985-08-19 1991-07-16 Allied-Signal Inc. Method to prepare high strength ultrahigh molecular weight polyolefin articles by dissolving particles and shaping the solution
US4784820A (en) * 1986-08-11 1988-11-15 Allied-Signal Inc. Preparation of solution of high molecular weight polymers
CN1160093A (zh) * 1997-01-02 1997-09-24 中国纺织科学研究院 超高分子量聚乙烯纤维连续制备方法和设备

Also Published As

Publication number Publication date
BRPI0709652A2 (pt) 2011-07-19
EP1999190A2 (en) 2008-12-10
WO2007118008A3 (en) 2007-11-29
US8444898B2 (en) 2013-05-21
KR20090004960A (ko) 2009-01-12
CA2648212C (en) 2013-10-01
EP1999190B1 (en) 2012-02-01
US8506864B2 (en) 2013-08-13
MY149308A (en) 2013-08-30
BRPI0709652B1 (pt) 2018-08-28
WO2007118008A2 (en) 2007-10-18
MX2008012312A (es) 2008-10-31
TW200804471A (en) 2008-01-16
KR101390161B1 (ko) 2014-05-13
ATE543858T1 (de) 2012-02-15
CN101460548A (zh) 2009-06-17
US20110049753A1 (en) 2011-03-03
IL194448A0 (en) 2009-08-03
US20070231572A1 (en) 2007-10-04
CA2648212A1 (en) 2007-10-18
JP2009532528A (ja) 2009-09-10
RU2008142849A (ru) 2010-05-10
IL194448A (en) 2015-05-31
ES2379505T3 (es) 2012-04-26
JP5144641B2 (ja) 2013-02-13
TWI417322B (zh) 2013-12-01

Similar Documents

Publication Publication Date Title
CN101460548B (zh) 高分子量聚(α-烯烃)溶液和由其制造的制品
EP0183285B1 (en) Process for the continuous preparation of homogeneous solutions of high-molecular polymers
JP5093126B2 (ja) ポリフェニレンサルファイド繊維の製造方法
JPS61167010A (ja) 中間分子量および高モジュラスのポリエチレン付形物の製造法
CN114134590B (zh) 一种高性能液晶聚芳酯纤维及其制备方法和生产设备
TW201126036A (en) Process for producing shaped articles of poly (trimethylene arylate)/polystyrene
CN115559018B (zh) 一种高强聚烯烃纤维及其制备方法
TW201120132A (en) Poly(trimethylene arylate)/polystyrene composition and process for preparing
CN116043360B (zh) 一种具有表面凹凸结构的羟基聚丙烯共聚物纤维及其制备方法
CN112095172B (zh) 一种高强高模细旦化聚芳酯纤维及其制备方法
JPS61143439A (ja) 高分子量ポリマ−原液の連続調製法
JPH0655839B2 (ja) 粒子を溶解し、溶液を成形することによる高強力、高モジュラスポリオレフィン成形品の製法
JPH05230732A (ja) 高分子量ポリオレフィンの多段延伸方法及び延伸装置
JP2024546718A (ja) 超微細デニールｕｈｍｗ ｐｅ繊維
JPS6173743A (ja) 高分子量ポリオレフイン原液の連続調整法
JPH05140816A (ja) 高分子量ポリオレフイン延伸物の製造方法
JPH0482909A (ja) 高分子量ポリオレフィン繊維の製造方法
JPH01314717A (ja) ポリビニルアルコール繊維の製造法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant