CN101445679A - UV-light solidifying paint having decorative effect and preparation method thereof - Google Patents
UV-light solidifying paint having decorative effect and preparation method thereof Download PDFInfo
- Publication number
- CN101445679A CN101445679A CNA2008101480250A CN200810148025A CN101445679A CN 101445679 A CN101445679 A CN 101445679A CN A2008101480250 A CNA2008101480250 A CN A2008101480250A CN 200810148025 A CN200810148025 A CN 200810148025A CN 101445679 A CN101445679 A CN 101445679A
- Authority
- CN
- China
- Prior art keywords
- decorative effect
- acrylate
- coating
- paint
- effect according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a UV-light solidifying paint having decorative effect and preparation method thereof, in particular to a light solidifying paint containing mica coated with metallic oxides as a paint. The paint is composed of the followings in proportions: the content of low polymer is 30-70wt%; the content of reactive diluent is 25-65wt%; the content of light trigger is 0.5-10wt%; the content of pearlescent pigment is 3-30wt%; the content of accessory ingredient is 0.2-8wt%; the content of solvent is 0-50wt%. As added pearlescent pigment has strong metallic performance, the prepared light solidifying paint has the character of strong pearl effect and also has very good water resisting property, higher rigidity and abrasive resistance. The paint can be applied to decoration on the surfaces of motor vehicles, electric appliance, furniture, articles for daily use, toys, walls, leather products, etc.
Description
Technical Field
The invention relates to an ultraviolet curing coating with decorative effect and a preparation method thereof, which is characterized in that pearlescent pigment is adopted to prepare the ultraviolet curing coating, and the ultraviolet curing coating has the characteristics of strong metal texture, higher hardness, higher wear resistance and the like.
Background
The pearlescent pigment is a pigment which is produced according to the physical and optical principles and is similar to the elegant luster and color of natural pearls, shells, butterflies, birds and metals, and is divided according to the functions of the pigment. The natural mica flake with a smooth surface and a low optical refractive index is used as an inner core and is coated with transparent titanium dioxide or iron oxide with a high refractive index to form a sandwich type wafer, and the color phase and luster are created by means of refraction and transmission of light, so that the natural mica flake creates a deep layering sense and a special pearl luster effect in a transparent medium, has the glittering effect of a metal pigment and has the soft color of natural pearls. In ideal applications, the pearlescent pigment is uniformly dispersed in the coating and is distributed in multiple layers parallel to the surface of the material, and incident light shows a pearlescent effect through multiple reflections and interference as in pearls. The pearlescent pigment can endow the paint with a special decorative effect, compared with aluminum powder, the pearlescent pigment has better storage stability in the paint, and the aluminum powder can generate a replacement reaction with water, so that the final luster of the paint is darkened and grayed. The excellent water resistance and chemical solvent resistance of the pearlescent pigment, excellent high temperature resistance, incombustibility, electric arc resistance, safety, non-toxicity and the like are the first choice of the decorative coating.
The ultraviolet curing coating has the advantages of high curing speed, energy conservation and environmental protection, and generally comprises an oligomer, an active diluent, a photoinitiator and other additives, wherein under the irradiation of ultraviolet light, the photoinitiator firstly absorbs the ultraviolet light and decomposes the ultraviolet light into active free radicals, and then the oligomer and the active diluent are initiated to carry out chain polymerization reaction to finally form a cross-linked cured coating. The ultraviolet curing equipment has high utilization rate, is suitable for flow line production, saves the space of a field and has high production efficiency.
Disclosure of Invention
The invention aims to provide an ultraviolet curing coating with a decorative effect and a preparation method thereof. Wherein, the pearlescent pigment in the paint has the characteristics of adjustable pearlescent effect, stable physicochemical property and the like. Meanwhile, the ultraviolet curing technology is adopted, so that the problems of large environmental hazard, high energy consumption, poor storage stability of the coating and the like in the prior art are solved, and the prepared coating has strong metal texture, higher hardness and wear resistance.
The technical scheme of the invention is as follows: the ultraviolet curing coating with decorative effect and the preparation method thereof are characterized in that the coating comprises the following components in percentage by weight:
oligomer … … … … … … … … … … … … … … … … … … … … … … … … … 30-70 wt%
Reactive diluent … … … … … … … … … … … … … … … … … … … … … … … 25-65 wt%
Photoinitiator … … … … … … … … … … … … … … … … … … … … … … … … 0.5.5-10 wt%
Pearlescent pigment … … … … … … … … … … … … … … … … … … … … … … … … 3-30 wt%
0.2 to 8 weight percent of auxiliary agent … … … … … … … … … … … … … … … … … … … … … … … … … … 0.2
Solvent … … … … … … … … … … … … … … … … … … … … … … … … … … 0-50 wt%
Wherein,
the oligomer can be selected from at least one of epoxy acrylate, polyurethane acrylate, polyester acrylate, polyether acrylate, acrylated polyacrylate or vinyl resin.
The active diluent is at least one of hydroxyethyl acrylate (HEA), hydroxyethyl methacrylate (HEMA), N-vinyl pyrrolidone (NVP), dipropylene glycol diacrylate (DPGDA), tripropylene glycol diacrylate (TPGDA), neopentyl glycol diacrylate (NPGDA), 1, 6-hexanediol diacrylate (HDDA), 1, 4-butanediol diacrylate (BDDA), phthalic acid ethylene glycol diacrylate (PDDA), trimethylolpropane triacrylate (TMPTA), pentaerythritol tetraacrylate (PETTA), dipentaerythritol pentaacrylate (DPPA), dipentaerythritol hexaacrylate (DPHA), alkoxylated acrylate, vinyl ether active diluent and methoxylated acrylate active diluent.
The photoinitiator is at least one of alpha, alpha' -dimethylbenzyl ketal, alpha-hydroxy ketone derivatives, alpha-amidoketone derivatives, acyl phosphine oxide, benzophenone + active amine and benzophenone.
The pearlescent pigment is one or more layers of mica powder coated by metal oxide, wherein: the metal oxide is at least one of titanium dioxide, ferric oxide, silicon dioxide, tin dioxide and cerium oxide, and the particle size of the metal oxide is 1-500 nm.
The auxiliary agent is at least one of a flatting agent, a defoaming agent and a wetting dispersant. Wherein the leveling agent may be selected from: polydimethyl siloxane, fluorine-containing compound, modified polysiloxane, polyether-polysiloxane copolymer, (methyl) acrylic ester polymer, fluorine modified acrylic ester or their mixture; the defoaming agent may be selected from: a silicone-free polymer solution, polydimethylsiloxane, organomodified polysiloxane, a polymer solution with siloxane end groups, or mixtures thereof; the wetting and dispersing agent may be selected from: electrically neutral polyamide and polyester mixtures, carboxyl-bearing polymer solutions, polyacrylate, polyurethane compounds or mixtures thereof.
The solvent can be at least one selected from ethyl acetate, propyl acetate, butyl acetate, isobutyl acetate, methyl ethyl ketone, ethanol, propanol, isobutyl alcohol, dicarboxylic ester, toluene, xylene, acetone, n-butanol, cyclohexanone, ethylene glycol butyl ether and propylene glycol butyl ether.
The preparation method of the ultraviolet curing coating is characterized by comprising the following steps:
(1) mixing the oligomer, the reactive diluent and the photoinitiator according to the proportion, and stirring uniformly at a certain temperature;
(2) adding pearlescent pigment into the components obtained in the step (1), adding a proper amount of wetting dispersant, flatting agent, defoaming agent or solvent according to the requirement, and stirring and mixing uniformly to obtain slurry;
(3) spraying, spin coating, dip coating or roll coating the slurry on the surface of a substrate, standing for a period of time, irradiating the coated surface with ultraviolet light, and curing to form a film.
When the ultraviolet curing coating with the decorative effect is prepared, the process is simple and convenient, only the required raw materials are mixed according to a certain proportion and are uniformly stirred, the requirement on equipment is not high, the ultraviolet curing coating is suitable for flow line production, the production efficiency is high, and the production cost is reduced. The paint prepared by the invention can be used for decorating the surfaces of automobiles, electrical appliances, furniture, daily necessities, toys, walls, leather products and the like.
Detailed Description
An ultraviolet curing coating with decorative effect and a preparation method thereof are disclosed as examples:
epoxy acrylate (CNUVE150/80, Saedoma) … … … … … … … … … … … 30g
… … … … … … … … … … 25g of aliphatic urethane acrylate (CN965, Saedoma Co., Ltd.)
… … … … … … … … … … 25g of 1, 6-hexanediol diacrylate (SR238, Saedoma Co., Ltd.)
High-purity trimethylolpropane triacrylate (SR351HP, Saedoma) … … … … … 20g
2-hydroxy-2-methyl-1-phenylpropanone (Darocur1173, Ciba Switzerland) … … … … 3g
… … … … … … … 2g of 1-hydroxycyclohexyl benzophenone (Irgacure184, Ciba Switzerland)
Leveling agent (Levelo1837, Germany modest) … … … … … … … … … … … … … … … … 0.5.5 g
Antifoaming agent (Defom2700, Germany Co., Ltd.) … … … … … … … … … … … … … … … … 0.3.3 g
Wetting and dispersing agent (Disponer912, Germany modest Co.) … … … … … … … … … … … … … … … 2g
(1) Mixing 1, 6-hexanediol diacrylate serving as an active diluent, high-purity trimethylolpropane triacrylate, Darocur1173 and Irgacur184 according to the proportion, and uniformly stirring at the constant temperature of 50 ℃; (2) and (2) uniformly stirring and mixing the components obtained in the step (1), epoxy acrylate, aliphatic polyurethane acrylate, pearlescent pigment, a flatting agent, a defoaming agent and a wetting dispersant, spin-coating the mixture on a glass plate by using a spin coater, wherein the thickness of the coating is 100 mu m, standing the glass plate at room temperature for a period of time, and then putting the glass plate into a lamp box (the power density of an ultraviolet lamp is 80w/cm, and the distance from the lamp tube is 15cm) to solidify and form a film.
And (3) testing results: the prepared paint has high curing speed, and the coating has strong pearlescent effect, high hardness and wear resistance and good water resistance.
Claims (8)
- An ultraviolet curing coating with decorative effect and a preparation method thereof are characterized in that: the coating comprises the following components in percentage by weight:oligomer … … … … … … … … … … … … … … … … … … … … … … … 30-70 wt%Reactive diluent … … … … … … … … … … … … … … … … … … … … … 25-65 wt%Photoinitiator … … … … … … … … … … … … … … … … … … … … … … 0.5.5-10 wt%Pearlescent pigment … … … … … … … … … … … … … … … … … … … … … … … 3-30 wt%0.2 to 8 weight percent of auxiliary agent … … … … … … … … … … … … … … … … … … … … … … … … 0.20-50 wt% of solvent … … … … … … … … … … … … … … … … … … … … … … … … … 0.
- The ultraviolet-curable coating material with decorative effect according to claim 1, wherein: the oligomer can be selected from at least one of epoxy acrylate, polyurethane acrylate, polyester acrylate, polyether acrylate, acrylated polyacrylate or vinyl resin.
- The ultraviolet-curable coating material with decorative effect according to claim 1, wherein: the active diluent is at least one of hydroxyethyl acrylate (HEA), hydroxyethyl methacrylate (HEMA), N-vinyl pyrrolidone (NVP), dipropylene glycol diacrylate (DPGDA), tripropylene glycol diacrylate (TPGDA), neopentyl glycol diacrylate (NPGDA), 1, 6-hexanediol diacrylate (HDDA), 1, 4-butanediol diacrylate (BDDA), phthalic acid ethylene glycol diacrylate (PDDA), trimethylolpropane triacrylate (TMPTA), pentaerythritol tetraacrylate (PETTA), dipentaerythritol pentaacrylate (DPPA), dipentaerythritol hexaacrylate (DPHA), alkoxylated acrylate, vinyl ether active diluent and methoxylated acrylate active diluent.
- The UV curable coating with decorative effect according to claim 1, wherein: the photoinitiator is at least one of alpha, alpha' -dimethylbenzyl ketal, alpha-hydroxy ketone derivatives, alpha-amidoketone derivatives, acyl phosphine oxide, benzophenone + active amine and benzophenone.
- The UV curable coating with decorative effect according to claim 1, wherein: the pearlescent pigment is one or more layers of mica powder coated by metal oxide, wherein: the metal oxide is at least one of titanium dioxide, ferric oxide, silicon dioxide, tin dioxide and cerium oxide, and the particle size of the metal oxide is 1-500 nm.
- The UV curable coating with decorative effect according to claim 1, wherein: the auxiliary agent is at least one of a flatting agent, a defoaming agent and a wetting dispersant.Wherein,the leveling agent may be selected from: polydimethyl siloxane, fluorine-containing compound, modified polysiloxane, polyether-polysiloxane copolymer, (methyl) acrylic ester polymer, fluorine modified acrylic ester or their mixture;the defoaming agent may be selected from: a silicone-free polymer solution, polydimethylsiloxane, organomodified polysiloxane, a polymer solution with siloxane end groups, or mixtures thereof;the wetting and dispersing agent may be selected from: electrically neutral polyamide and polyester mixtures, carboxyl-bearing polymer solutions, polyacrylate, polyurethane compounds or mixtures thereof.
- The ultraviolet-curable coating material with decorative effect according to claim 1, wherein: the solvent can be at least one selected from ethyl acetate, propyl acetate, butyl acetate, isobutyl acetate, methyl ethyl ketone, ethanol, propanol, isobutyl alcohol, dicarboxylic ester, toluene, xylene, acetone, n-butanol, cyclohexanone, ethylene glycol butyl ether and propylene glycol butyl ether.
- The method for preparing the ultraviolet curing coating with decorative effect according to claim 1, wherein the method comprises the following steps:(1) mixing the oligomer, the reactive diluent and the photoinitiator according to the proportion, and stirring uniformly at a certain temperature;(2) adding pearlescent pigment into the components obtained in the step (1), adding a proper amount of wetting dispersant, flatting agent, defoaming agent or solvent according to the requirement, and stirring and mixing uniformly to obtain slurry;(3) spraying, spin coating, dip coating or roll coating the slurry on the surface of a substrate, standing for a period of time, irradiating the coated surface with ultraviolet light, and curing to form a film.