CN101434707B - 一种纤维素基荧光膜的制备方法 - Google Patents

一种纤维素基荧光膜的制备方法 Download PDF

Info

Publication number
CN101434707B
CN101434707B CN2008102367857A CN200810236785A CN101434707B CN 101434707 B CN101434707 B CN 101434707B CN 2008102367857 A CN2008102367857 A CN 2008102367857A CN 200810236785 A CN200810236785 A CN 200810236785A CN 101434707 B CN101434707 B CN 101434707B
Authority
CN
China
Prior art keywords
cellulose
preparation
solution
film
based fluorescent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008102367857A
Other languages
English (en)
Other versions
CN101434707A (zh
Inventor
张俐娜
祁海松
常春雨
杨全岭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University WHU
Original Assignee
Wuhan University WHU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University WHU filed Critical Wuhan University WHU
Priority to CN2008102367857A priority Critical patent/CN101434707B/zh
Publication of CN101434707A publication Critical patent/CN101434707A/zh
Application granted granted Critical
Publication of CN101434707B publication Critical patent/CN101434707B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种纤维素基荧光膜的制备方法。该制备方法是将含6～8wt％NaOH和10～14wt％尿素的组合水溶液溶解纤维素制备纤维素湿膜，在有机荧光染料中浸泡吸附后干燥即得纤维素基荧光膜。本发明中纤维素的溶解、与颜料的共混和再生都是物理过程，未发生化学反应。本发明工艺过程简单，操作方便，对环境无污染。这类复合膜将在包装、信息技术、防伪和光学材料等领域具有广泛的应用前景。

Description

一种纤维素基荧光膜的制备方法
技术领域
本发明涉及一种纤维素基荧光膜的制备方法。
背景技术
当前塑料等白色污染日趋严重，必须开发可再生材料以取代传统石化产品。因此，生物质原料显得越来越重要。纤维素作为一种最丰富的天然高聚物有广泛应用前景。由于它价格低廉且可生物降解，可用于制备包装膜和功能材料，以解决环境污染问题。另外，由于纤维素薄膜具有良好的透光性，可用作发光材料的基质，和其它荧光物质或发光物质复合，制备发光膜、发光板及发光纤维。这类发光材料既有良好的发光性能，也有高分子材料的易加工性和力学性能，而且比一般的共轭高分子发光材料稳定性更好，可用于发光、显示和高能探测等领域。
发明内容
本发明的目的是提供一种纤维素基荧光膜的制备方法，通过该方法制备的发光膜工艺过程简单，不发生化学反应，无污染，易于工业化。
为实现上述目的，本发明所采用的技术方案如下：
一种纤维素基荧光膜的制备方法，将含6～8wt％NaOH和10～14wt％尿素的组合水溶液预冷到-12～-13℃，加入纤维素，搅拌均匀得到纤维素溶液；将纤维素溶液流延，经含有硫酸或者硫酸/硫酸钠的凝固浴凝固成形得到纤维素湿膜，将制备的纤维素湿膜浸入含0.05～5wt％有机荧光染料的溶液中，浸泡30分钟以上，取出干燥后即得到纤维素基荧光膜。
上述的纤维素溶液的比例为2～8wt％。
上述的有机荧光染料在膜中的含量为0.01～1wt％。
与已有技术相比较，本发明的创新如下：
本发明中纤维素的溶解、与颜料的共混和再生都是物理过程，未发生化学反应。整个工艺对设备要求不高，有利于工业化生产，废液容易回收循环使用。本发明以氢氧化钠、尿素、水为原料，价格便宜，操作简单方便，对环境无污染。而且产品纤维素基荧光膜安全无毒，在一定条件下易生物降解，属环境友好材料。
具体实施方式
以下结合具体的实例对本发明的技术方案作进一步说明：
实施例1
将190克含6～8wt％NaOH和10～14wt％尿素的混合水溶液中预冷至-12℃，立即取棉短绒浆(粘均分子量Mη＝8×104)10克投入其中，在0℃下充分搅拌均匀(约3分钟)，即可制得的纤维素透明溶液。将纤维素溶液流延，经含有5％硫酸的凝固浴凝固成形得到纤维素湿膜，将制备的纤维素湿膜浸入含1％荧光素的溶液中，浸泡30分钟，取出干燥后即得到纤维素荧光膜。其中按重量计有机荧光染料在膜中的含量为0.1％。
该实施例中的有机染料溶液也可以换成0.5％吖啶橙溶液或者1％罗丹明溶液等，同样可以得到纤维素基荧光膜。这类荧光膜在紫外光下依染料的不同可以发出不同的颜色。
实施例2
196克含6～8wt％NaOH和10～14wt％尿素的混合水溶液中预冷至-12℃，立即取棉短绒浆(粘均分子量Mη＝13×104)4克投入其中，在0℃下充分搅拌均匀(约3分钟)，即可制得的纤维素透明溶液。将纤维素溶液流延，经含有5％硫酸的凝固浴凝固成形得到纤维素湿膜，将制备的纤维素湿膜浸入含0.5％荧光素的溶液中，浸泡30分钟，取出干燥后即得到纤维素荧光膜。其中按重量计有机荧光染料在膜中的含量为0.05％。
实施例3
184克含6～8wt％NaOH和10～14wt％尿素的混合水溶液中预冷至-12℃，立即取棉短绒浆(粘均分子量Mη＝4×104)16克投入其中，在0℃下充分搅拌均匀(约3分钟)，即可制得的纤维素透明溶液。将纤维素溶液流延，经含有5％硫酸的凝固浴凝固成形得到纤维素湿膜，将制备的纤维素湿膜浸入含0.1％荧光素的溶液中，浸泡30分钟，取出干燥后即得到纤维素荧光膜。其中按重量计有机荧光染料在膜中的含量为0.01％。
实施例4
190克含6～8wt％NaOH和10～14wt％尿素的混合水溶液中预冷至-12℃，立即取棉短绒浆(粘均分子量Mη＝8×104)10克投入其中，在0℃下充分搅拌均匀(约3分钟)，即可制得的纤维素透明溶液。将纤维素溶液流延，经含有5％硫酸的凝固浴凝固成形得到纤维素湿膜，将制备的纤维素湿膜浸入含0.75％荧光素的溶液中，浸泡30分钟，取出干燥后即得到纤维素荧光膜。其中按重量计有机荧光染料在膜中的含量为0.08％。

Claims (3)

1.一种纤维素基荧光膜的制备方法，将含6～8wt％ NaOH和10～14wt％尿素的组合水溶液预冷到-12～-13℃，加入纤维素，搅拌均匀得到纤维素溶液；将纤维素溶液流延，经含有硫酸的凝固浴凝固成形得到纤维素湿膜，将制备的纤维素湿膜浸入含0.05～5wt％有机荧光染料的溶液中，浸泡30分钟以上，取出干燥后即得到纤维素基荧光膜。
2.根据权利要求1所述的纤维素基荧光膜的制备方法，其特征在于：所述纤维素溶液的比例为2～8wt％。
3.根据权利要求1所述的纤维素基荧光膜的制备方法，其特征在于：所述的有机荧光染料在膜中的含量为0.01～1wt％。
CN2008102367857A 2008-12-11 2008-12-11 一种纤维素基荧光膜的制备方法 Expired - Fee Related CN101434707B (zh)