CN101417224A - 一种多功能新型干燥剂 - Google Patents
一种多功能新型干燥剂 Download PDFInfo
- Publication number
- CN101417224A CN101417224A CNA200810072157XA CN200810072157A CN101417224A CN 101417224 A CN101417224 A CN 101417224A CN A200810072157X A CNA200810072157X A CN A200810072157XA CN 200810072157 A CN200810072157 A CN 200810072157A CN 101417224 A CN101417224 A CN 101417224A
- Authority
- CN
- China
- Prior art keywords
- stalk core
- hemp stalk
- industrial hemp
- core powder
- auxiliary material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种多功能新型干燥剂，由工业大麻秆芯粉和根据需要添加的辅料组成，辅料为易潮解物质或吸水性物质或功能性试剂中的一种或多种的混合物。该干燥剂具有抗菌防腐、安全无毒、可生物降解、可重复利用、成本低廉等优点。
Description
技术领域
本发明涉及一种干燥剂，具体涉及一种以廉价的工业大麻秆芯粉为基本原料的多功能新型干燥剂。
技术背景
干燥剂通过吸附特定环境中的水分，使物品在较长时间内保持相对干燥，从而调控微生物生存和化学反应、光解反应以及酶促反应的水分条件，达到防潮、防霉、防虫、防锈、抗氧化、延长产品保存期的目的。传统干燥剂如活性炭、生石灰、氯化钙、硅胶等存在着各自的缺点。活性炭的吸附能力比较低，且易污染被干燥物品。生石灰干燥剂中氧化钙在遇水变成氢氧化钙的过程中释放热量，误食会灼伤口腔或食道。氯化钙吸湿性强，但由于易潮解性，使其在实际应用中也受到了限制。硅胶干燥剂为物理吸水方式，吸水量很易达到饱和，易出现崩裂和水分的逆吸附现象，有效作用时间短。此外，硅胶中加入的用于颜色变化的氯化钴(俗称蓝胶)已被欧盟于1998年列为二类致癌物，会对生产和使用者的健康产生危害，且对环保不利。新兴的干燥剂如以海泡石、沸石、膨润土、蒙脱石、凹凸棒石、鸡窝岩矿石等为原料的天然岩石基干燥剂及以淀粉、魔芋飞粉和椰子外皮等为原料的生物基干燥剂，又有着或成本相对较高，或工艺复杂，或产品性能不稳定、功能相对单一等缺点。
工业大麻是全球较为广泛种植的一种作物，“崇尚绿色、返璞归真”的消费潮流使大麻产品的消费呈日趋增长的趋势。大麻韧皮纤维具有强度高、比重轻、吸湿透气、凉爽快干、抑菌防腐、保健卫生、吸波消音和防紫外等独特功能，是理想的高档纺织原料和复合材料的增强纤维。经研究发现大麻秆芯同样具有上述优点，但因其为短纤维，而通常被用作造纸和加工粘胶纤维、活性炭的原料，其优良性能(特别如：吸湿、抗菌、可降解)未能得到充分利用。
发明内容
本发明的目的在于提供一种具有吸湿能力可调、天然抗菌、可重复利用、可降解、安全无毒、成本低廉等优点的新型多功能干燥剂。
本发明可通过以下技术方案实现：一种多功能新型干燥剂，由工业大麻秆芯粉和根据需要添加的辅料组成，上述辅料为易潮解物质或吸水性物质或功能性试剂中的一种或多种的混合物。
上述工业大麻秆芯粉与上述辅料的重量百分比为：
工业大麻秆芯粉 10％～100％
辅 料 0％～90％
上述工业大麻秆芯粉与上述辅料的重量百分比为：
工业大麻秆芯粉 25％～85％
辅 料 15％～75％
上述工业大麻秆芯粉与上述辅料的重量百分比为：
工业大麻秆芯粉 40％～70％
辅 料 30％～60％
上述工业大麻秆芯粉系将工业大麻秆芯粉碎后的产品，其粒度范围为：10目～500目。
上述工业大麻秆芯粉的粒度范围为：20目～300目。
上述工业大麻秆芯粉的粒度范围为：30目～200目。
上述辅料中的易潮解物质为硫酸镁、氯化镁、氯化锌、氯化锂、氯化钙、硫酸锌中的一种或多种混合物。
上述辅料中的吸水性物质为X或[X-接枝-Y]或[X-接枝-Y]-盐中的一种或多种的混合物；其中，X为淀粉、改性淀粉、纤维素、改性纤维素、甲壳素、改性甲壳素、魔芋粉、改性魔芋粉中的一种或多种的混合物；Y为丙烯酸、丙烯晴、丙烯酸酯、醋酸乙烯酯、丙烯酰胺、环氧化物等中的一种或多种的混合物。
上述辅料中的功能性试剂为吸湿变色指示剂、驱虫剂、抗菌剂、异味吸附剂、有毒气体吸附剂、香料等中的一种或多种的混合物。
本发明的吸湿机理：大麻秆芯的主要成分为纤维素，含有大量羟基，可与水形成分子间氢键，使大麻秆芯具有良好的吸湿能力。再者，大麻秆芯的形态为中空结构，中腔呈线形或椭圆形，常与外形不一，纤维横截面有许多微细孔隙，这种结构能产生优异的毛细效应，这又会进一步增强其吸湿能力。大麻秆芯粉经辅料改性后，一部分辅料被固定于大麻秆芯的孔洞结构中，使用过程中大麻秆芯在吸湿的同时又起到保水作用。大麻秆芯粉与其他辅料的协同作用，可使该干燥剂产生良好的吸湿能力，且吸湿能力可通过辅料及其用量来进行调整。
本发明的抗菌防腐机理：日常生活经验证明，工业大麻作物生长无需任何完化学药物，自身既可抵御各种病虫害，是典型的绿色环保作物。工业大麻秆芯本身含有微量特殊的化学物质——四氢大麻酚(THC)，在加工过程中经光照和空气氧化会产生大麻酚(Cannabinol)，该物质与麻醉性物质一样具有杀菌能力。大麻制品对大肠秆菌，金黄色葡萄球菌、绿脓秆菌，白色念珠菌、青霉、曲霉等有明显的杀灭、抑制作用，护肤保健之效明显。另外，大麻秆芯特殊的孔洞结构使得大麻秆芯富含氧气，使厌氧菌无法生存，因而其抗霉防腐作用更加突出。
与现有技术相比，本发明的干燥剂采用工业大麻产业的副产品—大麻秆芯为基本原料，具有优良的天然抗菌防腐性能，且可根据需要通过添加辅料而得到不同吸湿能力及功能的产品，工艺简单，成本低廉，产品安全无毒，可重复使用，可生物降解。本发明应用领域广泛，可在食品包装、精密仪器、电子产品、医药保健品、种子保存、鞋服皮革、工艺美术品保藏等行业中使用。本发明首次将工业大麻秆芯应用作为干燥剂的材料，对大麻产业的综合发展及新型多功能干燥剂的开发具有非常积极的意义。
具体实施方式
实施例1：
选取粒度为20目～30目的工业大麻秆芯粉，烘干后，冷却，包装。
实施例2：
选取粒度为100目的工业大麻秆芯粉，烘干后，冷却，包装。
实施例3：
选取粒度为40目的工业大麻秆芯粉，按MgSO4:工业大麻秆芯粉＝1:1的质量比将其与硫酸镁直接在混合机中混合均匀后加水膨化，烘干后，冷却，包装。
实施例4：
选取粒度为40目的工业大麻秆芯粉，按MgSO4:秆芯粉＝1:2的质量比将其与硫酸镁直接在混合机中混合均匀后加水膨化，烘干后，冷却，包装。
实施例5：
选取粒度为40目的工业大麻秆芯粉，按MgCl2:秆芯粉＝1:1的质量比将其与氯化镁直接在混合机中混合均匀后加水膨化，烘干后，冷却，包装。
实施例6：
选取粒度为40目的工业大麻秆芯粉，按MgCl2:秆芯粉＝1:2的质量比将其与氯化镁直接在混合机中混合均匀后加水膨化，烘干后，冷却，包装。
实施例7：
选取粒度为40目的工业大麻秆芯粉，按CaCl2:秆芯粉＝1:1的质量比将其与氯化钙直接在混合机中混合均匀后加水膨化，再烘干，冷却，包装。
实施例8：
选取粒度为40目的工业大麻秆芯粉，按CaCl2:秆芯粉＝1:2的质量比将其与氯化钙直接在混合机中混合均匀后加水膨化，再烘干，冷却，包装。
实施例9：
选取粒度为40目的工业大麻秆芯粉，按CaCl2:秆芯粉＝1:3的质量比将其与氯化钙直接在混合机中混合均匀后加水膨化，再烘干，冷却，包装。
实施例10：
选取粒度为80目的工业大麻秆芯粉，按工业大麻秆芯粉:淀粉接枝丙烯酸盐＝1:1的质量比将物料在混合机中混合均匀，再烘干，冷却，包装。
实施例11：
选取粒度为200目的工业大麻秆芯粉，按工业大麻秆芯粉:淀粉接枝丙烯酸盐＝1:1的质量比将物料在混合机中混合均匀后加水膨化，造粒后再烘干，冷却，包装。
实施例12：
选取粒度为200目的工业大麻秆芯粉，按工业大麻秆芯粉：淀粉接枝丙烯酸盐:CaCl2＝1:1:1的质量比将物料在混合机中混合均匀后加水膨化，造粒后再烘干，冷却，包装。
实施例13：
选取粒度为200目的工业大麻秆芯粉，按工业大麻秆芯粉:淀粉接枝丙烯酸盐＝1:1的质量比将物料在混合机中，同时加入少量的驱虫剂，混合均匀后加水膨化，再造粒，烘干，冷却，包装。
本发明的上述各个实施例中，不同配方的干燥剂有着不同的吸湿能力或附加功能，除上述实施例外，本发明还可以由其它实施方式实现。凡是将工业大麻秆芯作为干燥剂原料或组分的技术方案，均在本发明的保护范围内。
Claims (10)
1、一种多功能新型干燥剂，其特征在于：由工业大麻秆芯粉和根据需要添加的辅料组成，上述辅料为易潮解物质或吸水性物质或功能性试剂中的一种或多种的混合物。
2、根据权利要求1所述的一种多功能新型干燥剂，其特征在于：上述工业大麻秆芯粉与上述辅料的重量百分比为：
工业大麻秆芯粉 10％～100％
辅 料 0％～90％。
3、根据权利要求2所述的一种多功能新型干燥剂，其特征在于：上述工业大麻秆芯粉与上述辅料的重量百分比为：
工业大麻秆芯粉 25％～85％
辅 料 15％～75％。
4、根据权利要求3所述的一种多功能新型干燥剂，其特征在于：上述工业大麻秆芯粉与上述辅料的重量百分比为：
工业大麻秆芯粉 40％～70％
辅 料 30％～60％。
5、根据权利要求1所述的一种多功能新型干燥剂，其特征在于：上述工业大麻秆芯粉系将工业大麻秆芯粉碎后的产品，其粒度范围为：10目～500目。
6、根据权利要求5所述的一种多功能新型干燥剂，其特征在于：上述工业大麻秆芯粉的粒度范围为：20目～300目。
7、根据权利要求6所述的一种多功能新型干燥剂，其特征在于：上述工业大麻秆芯粉的粒度范围为：30目～200目。
8、根据权利要求1所述的一种多功能新型干燥剂，其特征在于：上述辅料中的易潮解物质为硫酸镁、氯化镁、氯化锌、氯化锂、氯化钙、硫酸锌中的一种或多种混合物。
9、根据权利要求1所述的一种多功能新型干燥剂，其特征在于：上述辅料中的吸水性物质为X或[X-接枝-Y]或[X-接枝-Y]-盐中的一种或多种的混合物；其中，X为淀粉、改性淀粉、纤维素、改性纤维素、甲壳素、改性甲壳素、魔芋粉、改性魔芋粉中的一种或多种的混合物；Y为丙烯酸、丙烯晴、丙烯酸酯、醋酸乙烯酯、丙烯酰胺、环氧化物等中的一种或多种的混合物。
10、根据权利要求1所述的一种多功能新型干燥剂，其特征在于：上述辅料中的功能性试剂为吸湿变色指示剂、驱虫剂、抗菌剂、异味吸附剂、有毒气体吸附剂、香料等中的一种或多种的混合物。