CN101407740B - 快干型金属薄层防锈油 - Google Patents

快干型金属薄层防锈油 Download PDF

Info

Publication number
CN101407740B
CN101407740B CN2008102309620A CN200810230962A CN101407740B CN 101407740 B CN101407740 B CN 101407740B CN 2008102309620 A CN2008102309620 A CN 2008102309620A CN 200810230962 A CN200810230962 A CN 200810230962A CN 101407740 B CN101407740 B CN 101407740B
Authority
CN
China
Prior art keywords
reaction kettle
oil
quick
mixture
metal thin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008102309620A
Other languages
English (en)
Other versions
CN101407740A (zh
Inventor
陈蓉
陈凯
王子君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI PETROFER SPECIAL LUBRICANT CO Ltd
Original Assignee
Luoyang Bearing Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Luoyang Bearing Science and Technology Co Ltd filed Critical Luoyang Bearing Science and Technology Co Ltd
Priority to CN2008102309620A priority Critical patent/CN101407740B/zh
Publication of CN101407740A publication Critical patent/CN101407740A/zh
Application granted granted Critical
Publication of CN101407740B publication Critical patent/CN101407740B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种快干型金属薄层防锈油，将35～40％N5#机油和余量为N32#机油加入到反应釜中搅拌加热到110～120℃充分脱水，再将7～10％石油磺酸钙加入反应釜中，加热搅拌使其溶解，从反应釜底部放出少量热油，在添加剂4～8％二壬基奈磺酸钡、0.5～1.5％十八铵盐、2～4％医用羊毛脂中加入热油搅拌使其溶解为混合物，将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时，待其温度降至40℃以下时过滤装桶包装。本发明可广泛使用于轴承、机械零件的快干型薄层防锈处理。

Description

快干型金属薄层防锈油
技术领域
本发明属于防锈油技术领域，尤其是一种快干型金属薄层防锈油。
背景技术
防锈油是轴承生产行业及金属零件加工行业普遍使用的一种防锈剂。目前国内市场上销售的防锈油普遍存在以下问题：
1、防锈期为两年以上的防锈油，零件上涂油后产生较厚的油膜，影响封存包装外观，客户拆包装时会沾一手油。
2、快干型的防锈油虽然油膜较薄，但防锈期较短，湿热试验和盐雾试验数据不太理想，尤其对于出口零件来说，要经过长时间的海运，要求更加苛刻。
发明内容
为了解决轴承(零件)生产出口厂家的包装封存问题，本发明提供了一种快干型金属薄层防锈油，该防锈油可快速形成较薄的油膜，防锈时间长，易于海上运输。
为实现上述发明目的，本发明采用如下技术方案：
所述的快干型金属薄层防锈油，其配方按重量百分比构成如下：
石油磺酸钙7～10％；二壬基奈磺酸钡4～8％；医用羊毛脂2～4％；十八铵盐0.5～1.5％；N5#机油35～40％；N32#机油余量。
所述的快干型金属薄层防锈油，依据上述配方其生产工艺如下：
①将35～40％N5#机油和余量N32#机油加入到反应釜中搅拌加热到110～120℃充分脱水；
②将7～10％石油磺酸钙加入反应釜中，加热搅拌使其溶解；
③从反应釜底部放出少量热油，在添加剂4～8％二壬基奈磺酸钡、0.5～1.5％十八铵盐、2～4％医用羊毛脂中加入热油搅拌使其溶解为混合物；
④将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时；
⑤待其温度降至40℃以下时过滤装桶包装。
由于采用如上所述的技术方案，本发明具有如下优越性：
1、解决了许多轴承(零件)生产厂家的包装封存问题，保证防锈油在零件上快速形成较薄的油膜，防锈时间长。
2、对于出口运往国外的轴承(零件)，一方面满足了长时间海上运输的要求，另一方面满足了国外客户对油膜厚度的要求。
具体实施方式
以下实施例均按生产1000Kg防锈油为例。
实施例1：分别取石油磺酸钙10％，二壬基奈磺酸钡4％，医用羊毛脂3％，十八铵盐1％，N5#机油37％，N32#机油45％制取快干型金属薄层防锈油，其生产工艺如下：
①将370Kg N5#机油和450KgN32#机油加入到反应釜中搅拌加热到115～120℃充分脱水；
②将100Kg石油磺酸钙加入反应釜中，加热搅拌使其溶解；
③从反应釜底部放出100Kg热油，在40Kg二壬基奈磺酸钡、10Kg十八铵盐、30Kg医用羊毛脂中加入热油搅拌使其溶解为混合物；
④将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时；
⑤待其温度降至40℃以下时过滤装桶包装。
实施例2：分别取石油磺酸钙7％，二壬基奈磺酸钡8％，医用羊毛脂2.5％，十八铵盐0.5％，N5#机油38％，N32#机油44％制取快干型金属薄层防锈油，其生产工艺如下：
①将380Kg N5#机油和440KgN32#机油加入到反应釜中搅拌加热到115～120℃充分脱水；
②将70Kg石油磺酸钙加入反应釜中，加热搅拌使其溶解；
③从反应釜底部放出100Kg热油，在80Kg二壬基奈磺酸钡、5Kg十八铵盐、25Kg医用羊毛脂中加入热油搅拌使其溶解为混合物；
④将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时；
⑤待其温度降至40℃以下时过滤装桶包装。
实施例3：分别取石油磺酸钙9％，二壬基奈磺酸钡7％，医用羊毛脂2％，十八铵盐1.5％，N5#机油40％，N32#机油40.5％制取快干型金属薄层防锈油，其生产工艺如下：
①将400Kg N5#机油和405KgN32#机油加入到反应釜中搅拌加热到115～120℃充分脱水；
②将90Kg石油磺酸钙加入反应釜中，加热搅拌使其溶解；
③从反应釜底部放出100Kg热油，在70Kg二壬基奈磺酸钡、15Kg十八铵盐、20Kg医用羊毛脂中加入热油搅拌使其溶解为混合物；
④将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时；
⑤待其温度降至40℃以下时过滤装桶包装。
实施例4：分别取石油磺酸钙8％，二壬基奈磺酸钡5％，医用羊毛脂4％，十八铵盐1％，N5#机油35％，N32#机油47％制取快干型金属薄层防锈油，其生产工艺如下：
①将350Kg N5#机油和470KgN32#机油加入到反应釜中搅拌加热到115～120℃充分脱水；
②将80Kg石油磺酸钙加入反应釜中，加热搅拌使其溶解；
③从反应釜底部放出100Kg热油，在50Kg二壬基奈磺酸钡、10Kg十八铵盐、40Kg医用羊毛脂中加入热油搅拌使其溶解为混合物；
④将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时；
⑤待其温度降至40℃以下时过滤装桶包装。
本发明可广泛使用于轴承、机械零件的快干型薄层防锈处理。

Claims (2)

1.一种快干型金属薄层防锈油，其特征在于：该快干型金属薄层防锈油配方按重量百分比构成如下：
石油磺酸钙7～10％；二壬基奈磺酸钡4～8％；医用羊毛脂2～4％；十八胺盐0.5～1.5％；N5#机油35～40％；N32#机油余量。
2.根据权利要求1所述的快干型金属薄层防锈油，其特征在于：依据上述配方其生产工艺如下：
①将35～40％N5#机油和余量N32#机油加入到反应釜中搅拌加热到110～120℃充分脱水；
②将7～10％石油磺酸钙加入反应釜中，加热搅拌使其溶解；
③从反应釜底部放出少量热油，再添加剂4～8％二壬基奈磺酸钡、0.5～1.5％十八胺盐、2～4％医用羊毛脂中加入热油搅拌使其溶解为混合物；
④将溶解后的混合物加入反应釜中加热搅拌，在110～115℃下反应3个小时；
⑤待其温度降至40℃以下时过滤装桶包装。
CN2008102309620A 2008-11-11 2008-11-11 快干型金属薄层防锈油 Active CN101407740B (zh)