CN101397708A - Process for making anti-infrared multifunctional camouflaged color cloth - Google Patents
Process for making anti-infrared multifunctional camouflaged color cloth Download PDFInfo
- Publication number
- CN101397708A CN101397708A CNA2008102319849A CN200810231984A CN101397708A CN 101397708 A CN101397708 A CN 101397708A CN A2008102319849 A CNA2008102319849 A CN A2008102319849A CN 200810231984 A CN200810231984 A CN 200810231984A CN 101397708 A CN101397708 A CN 101397708A
- Authority
- CN
- China
- Prior art keywords
- temperature
- meters
- motor vehicle
- speed
- vat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a textile printing and dyeing technique, in particular to a manufacturing technique of an infrared ray resistant multi-functional camouflage fabric. The technique flow is as follows: original cloth seaming, singeing, old rolling, 180 pre-treatment, shaping, mercerizing, ground dyeing, pattern printing, baking, aging, stentering of post treatment, examination and acceptance; wherein, the ground dyeing flow is as follows: padding liquor, two groups of infrared rays and drying; a formula adopted in the ground dyeing flow comprises 2g/l to 10g/l of dispersion dyes, 5g/l to 15g/l of vat dyes and 0.01g/l to 1.0g/l of infrared ray resistant regulators; the formula of pattern printing is as follows: 2kg to 15.7kg of dispersion material, 2. kg/l to 10.5kg/l of vat material and 0.01kg to 2.5kg of infrared ray resistant regulators; post treatment has the function compatibility of multiple functions which are water proofing, oil repellence, ventilation, crease resistance and static resistance. The technique has the advantages of having short production procedure, color phase with good uniformity, stable infrared reflectivity, low cost, multiple functions, mainly using environment friendly dyes and being suitable for infrared ray resistant camouflage fabric products with different fibers and different specifications.
Description
(1) technical field
The present invention relates to a kind of textile printing and dyeing process, a kind of specifically manufacture craft of anti-infrared multifunctional camouflage fabric.
(2) background technology
Present domestic anti-infrared lining is forest land, the desert type polyester-cotton blend product that 400-1200 nanometers have the anti-infrared performance for the wavelength of organizational equipment only, its wave-length coverage is little, the equipment that making needs or the combination of kinds of processes, even the use of some special process, and production process is long, the cost height, the form and aspect uniformity is poor.
(3) summary of the invention
The object of the present invention is to provide a kind of production process short, form and aspect are disposable good, wavelength has forest land, desert type polyester-cotton blend, the bright and beautiful cotton product of anti-infrared performance for the 400-2380 nanometer, the anti-infrared reflectivity is stable, cost is low, and based on the manufacture craft of a kind of anti-infrared multifunctional camouflage fabric of environmental protection dyestuff.
The present invention is achieved like this for achieving the above object, and manufacture craft of the present invention sews up through following processing for getting former cloth: singe (1): 90-95 meters/minutes of the speed of a motor vehicle, and TWILL CLOTH, two positive one is anti-, three road burners; Plain cloth, two positive two is anti-, four road burners. (2) are cold rolling: clot, 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, working solution content: caustic soda 40-45g/L, hydrogen peroxide 8 ± 1g/L, replenish liquid: caustic soda 50-60g/L, hydrogen peroxide 20 ± 2g/L, driving before measurement pick-up 70-75%, obturage with plastic paper after the clot, normal temperature is banked up, and (its cold rolling liquid was for getting cold pad-batch additive 6kg in 24 hours, scouring agent 3kg, hydrogen peroxide 15kg, hydrogen peroxide bleaching stabilizer 5kg, chelated dispersants 2kg, it is 430L that residue adds water to solution). → (3) 180 pre-treatment oxygen move back: 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, 95-100 ℃ of crawler belt temperature are banked up 45 minutes time, wash 80-90 ℃ of the 1-5 lattice, 60-65 ℃ of flowing water of all living of the 6th lattice replenish liquid: caustic soda 40-45g/L, hydrogen peroxide 4 ± 2 g/L, working solution: caustic soda 30 ± 2g/L, hydrogen peroxide 2 ± 0.5g/L, (it is hydrogen peroxide 7 kg that its oxygen moves back liquid, scouring agent 3 kg, stabilizing agent 3 kg, to add water to solution be 500L to residue) capillary effect does first inspection more than 2cm/5 minute. (4) typing: 50 ± 1 meters/minute of the speed of a motor vehicle, temperature 1,3,185-200 ℃ of Room 8,215-220 ℃ of all the other each chambers, cropping fabric width 155-155.5cm, the cropping temperature is lower than 45 ℃, notes skew of weft, overfeeding 3%. (5) 180 mercerisings: 45 ± 1 meters/minute of the speed of a motor vehicle, fuselage 155-156cm, acetic acid content: 4 ± 1g/L, 60-65 ℃ of lixiviating oven temperature, degree, 70-80 ℃ of washing temperature, 60-65 ℃ of last lattice, the flowing water of all living, cloth cover pH value uniformity. dye at the end (6): the speed of a motor vehicle: 30 ± 1 meters/minute, soak that a padding liquor → two group infrared ray → (padding liquor is two groups of preliminary drying → oven dry croppings: DISPERSE DYES: 2-10/Lg more; Reducing dye: 5-15g/L; Anti-infrared conditioning agent: 0.02-0.1g/L). (7) stamp: the speed of a motor vehicle: 30 ± 1 meters/minute, bake out temperature: 100-105 ℃. (prescription: light green spot: disperse yellow S-6G:0.9kg; Disperse blue S-BG:0.5kg; Disperse red S-2G:0.04kg; Vat yellow 5GF:0.56kg; Reduce blue C-MG:0.13kg; Vat Brown BR: 0.02kg; Anti-infrared conditioning agent: 0.01kg; Sodium alginate: 40kg residue adds water configuration 100kg.Green statin: disperse yellow S-2R:1.6kg; Disperse blue S-BG:0.5kg; Disperse red S-2G:0.07kg; Vat yellow RK:1.2kg; Reduce blue C-MG:0.5kg; Vat brown HRR:0.1kg; Vat grey NC:0.25kg; Anti-infrared conditioning agent: 0.16kg; Sodium alginate: 40kg, residue adds water configuration 100kg.Palm fibre spot: disperse yellow S-2R:1.1kg; Disperse blue S-BG:0.2kg; Disperse red S-2G:0.15kg; Vat yellow RK:1.2kg; Vat brown HRR:1.2kg; Vat green FFB:0.8kg; Anti-infrared conditioning agent: 1.2kg; Sodium alginate: 40kg, residue adds water configuration 100kg.Blackspot: disperse black P-G:1.8kg; Disperse blue S-BG:0.8kg; Vat black G:4.9kg; Vat yellow 5GF:0.4kg; Anti-infrared conditioning agent: 1.5kg; Sodium alginate: 40kg, residue adds water configuration 100kg.(8) bake: 35 ± 1 meters/minute of the speed of a motor vehicle, 185 ± 2 ℃ of temperature, 2 minutes 40 seconds-2 minutes 45 seconds time; Evaporate → (9): 35-45 meters/minutes of the speed of a motor vehicle, 125-140 ℃ of temperature, 85-95 ℃ of soap boiling temperature, 80-85 ℃ of washing temperature, 60-65 ℃ of last lattice, flowing water all alive, replenish liquid: caustic soda 75-85g/L, working solution: caustic soda 70-85g/L, sodium hydrosulfite: replenish liquid: caustic soda 85-95g/L, working solution: caustic soda 70-85g/L, hydrogen peroxide 1.5-2.5g/L. (9) back arrangement tentering: 30-35 meters/minutes of the speed of a motor vehicle, temperature 180-185 ℃, cropping fabric width 151-151.5cm. (prescription: ventilative, anti wrinkling agent FEL:60g/l, waterproof, refuse oil, antistatic additive XQ-608A:50g/l) (10) are shrinkproof: anti-shrinkage 3%, fabric width is at 150-151 cm.
The invention has the advantages that production process is short, form and aspect are disposable good, and infrared reflectivity is stable, and cost is low, and based on the environmental protection dyestuff, the product that it is fit to higher class in the anti-infrared camouflage color product fabric panel very much uses.
(4) specific embodiment
The present invention is done the explanation of further detail below in conjunction with embodiment:
The present invention be with one or several concrete different products how to make need carry out detail respectively description-attention here be described as manufacture craft.
One, 20*20T50/C50 forest land camouflage color plaids (63 ")
This product has the anti-infrared function in the 400-2380nm wave-length coverage, have ventilative, crease-resistant, waterproof, refuse oil, anlistatig function.
Technological process of the present invention: former cloth sews up → singes → cold rolling → 180 pre-treatment → typing → mercerisings → dye the end → stamp → bake → evaporate → back arrangement tentering → examination.
1, former cloth sews up: needle gage density: 24-26 pin/10cm, sew up flat, straight, neat.
2, singe: 90-95 meters/minutes of the speed of a motor vehicle, two positive two is anti-, four road burners.
3, cold rolling: clot, 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, working solution content: caustic soda 40-45g/L, hydrogen peroxide 8 ± 1g/L replenishes liquid: caustic soda 50-60g/L, hydrogen peroxide 20 ± 2g/L, driving before measurement pick-up 70-75% is obturaged with plastic paper after the clot, and normal temperature was banked up 24 hours.(prescription: cold pad-batch additive 6kg, scouring agent 3kg, hydrogen peroxide 15kg, hydrogen peroxide bleaching stabilizer 5kg, chelated dispersants 2kg, residue adds water configuration 430L)
4,180 pre-treatment oxygen move back: 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, 95-100 ℃ of crawler belt temperature, bank up 45 minutes time, wash 80-90 ℃ of the 1-5 lattice, 60-65 ℃ of flowing water of all living of the 6th lattice replenish liquid: caustic soda 40-45g/L, hydrogen peroxide 4 ± 2g/L, working solution: caustic soda 30 ± 2g/L, hydrogen peroxide 2 ± 0.5g/L. (prescription: hydrogen peroxide 7kg, scouring agent 3kg, stabilizing agent 3kg, it is 500L that residue adds water to solution). capillary effect was done first inspection more than 2cm/5 minute.
5, typing: 50 ± 1 meters/minute of the speed of a motor vehicle, 185-200 ℃ of temperature Room 1,3,8,215-220 ℃ of all the other each chambers, cropping fabric width 155-155.5cm, the cropping temperature is lower than 45 ℃, notes skew of weft, overfeeding 3%.
6,180 mercerisings: 45 ± 1 meters/minute of the speed of a motor vehicle, fuselage 155-156cm, acetic acid content: 4 ± 1g/L, 60-65 ℃ of lixiviating oven temperature, degree, 70-80 ℃ of washing temperature, 60-65 ℃ of last lattice, the flowing water of all living, cloth cover pH value uniformity.
7, dye at the end: the speed of a motor vehicle: 30 ± 1 meters/minute, soak a padding liquor → two group infrared ray → two groups of preliminary drying → oven dry croppings more.(prescription: disperse yellow S-2R:3.4g/L; Disperse blue S-BG:1.8g/L; Vat yellow 3R:3.1kg; Vat Brown BR: 4.6g/L; Vat green FFB:4.0g/L; Anti-infrared conditioning agent: 0.01-0.05g/L)
8, stamp: the speed of a motor vehicle: 30 ± 1 meters/minute, bake out temperature: 100-105 ℃. (prescription: light green spot: disperse yellow S-6G:0.9kg; Disperse bright blue S-BG:0.5kg; Disperse red S-2G:0.04kg; Vat yellow 5GF:0.56kg; Reduce blue C-MG:0.13kg; Vat Brown BR: 0.02kg; Anti-infrared conditioning agent: 0.01kg; Sodium alginate: 40kg, residue adds water configuration 100kg.Green statin: disperse yellow S-2R:1.6kg; Disperse blue S-BG:0.5kg; Disperse red S-2G:0.07kg; Vat yellow RK:1.2kg; Reduce blue C-MG:0.5kg; Vat brown HRR:0.1kg; Vat grey NC:0.25kg; Anti-infrared conditioning agent: 0.16kg; Sodium alginate: 40kg, residue adds water configuration 100kg.Palm fibre spot: disperse yellow S-2R:1.1kg; Disperse blue S-BG:0.2kg; Disperse red S-2G:0.15kg; Vat yellow RK:1.2kg; Vat brown HRR:1.2kg; Vat green FFB:0.8kg; Anti-infrared conditioning agent: 1.2kg; Sodium alginate: 40kg, residue adds water configuration 100kg.Blackspot: disperse black P-G:1.8kg; Disperse blue S-GB:0.8kg; Vat black G:4.9kg; Vat yellow 5GF:0.4kg; Anti-infrared conditioning agent: 1.5kg; Sodium alginate: 40kg, residue adds water configuration 100kg)
9, bake: 35 ± 1 meters/minute of the speed of a motor vehicle, 185 ± 2 ℃ of temperature, 2 minutes 40 seconds-2 minutes 45 seconds time.
10, evaporate: 35-45 meters/minutes of the speed of a motor vehicle, 125-140 ℃ of temperature, 85-95 ℃ of soap boiling temperature, 80-85 ℃ of washing temperature, 60-65 ℃ of last lattice, flowing water all alive, replenish liquid: caustic soda 75-85g/L, working solution: caustic soda 70-85g/L, sodium hydrosulfite: replenish liquid: caustic soda 85-95g/L, working solution: caustic soda 70-85g/L, hydrogen peroxide 1.5-2.5g/L.
11, back arrangement tentering: 25 ± 1 meters/minute of the speed of a motor vehicle, temperature 180-185 ℃, cropping fabric width 151-151.5cm. (prescription: ventilative anti wrinkling agent FEL:60g/L)
12, shrinkproof: anti-shrinkage 3%, fabric width is at 150-151cm.
Two, 30/2*36/2T20/C80 forest land camouflage color satin drill satin (63 ")
This product has the anti-infrared function in the 700-1200nm wave-length coverage, have crease-resistant, waterproof, refuse oil, anlistatig function.
Technological process: former cloth sews up → singes → cold rolling → 180 pre-treatment → typing → mercerisings → dye the end → stamp → bake → evaporate → back arrangement tentering → examination.
Process conditions: 1, former cloth sews up: needle gage density: 24-26 pin/10cm, sew up flat, straight, neat.
2, singe: 90-95 meters/minutes of the speed of a motor vehicle, two positive one is anti-, three road burners.
3, cold rolling: clot, 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, working solution content: caustic soda 40-45g/L, hydrogen peroxide 8 ± 1g/L replenishes liquid: caustic soda 50-60g/L, hydrogen peroxide 20 ± 2g/L, driving before measurement pick-up 70-75% is obturaged with plastic paper after the clot, and normal temperature was banked up 24 hours.(prescription: cold pad-batch additive 6kg, scouring agent 3kg, hydrogen peroxide 15kg, hydrogen peroxide bleaching stabilizer 5kg, chelated dispersants 2kg, it is 430L that residue adds water to solution)
4,180 pre-treatment oxygen move back: 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, 95-100 ℃ of crawler belt temperature, bank up 45 minutes time, wash 80-90 ℃ of the 1-5 lattice, 60-65 ℃ of flowing water of all living of the 6th lattice replenish liquid: caustic soda 40-45g/L, hydrogen peroxide 4 ± 2g/L, working solution: caustic soda 30 ± 2g/L, hydrogen peroxide 2 ± 0.5g/L. (prescription: hydrogen peroxide 7kg, scouring agent 3kg, stabilizing agent 3kg, it is 500L that residue adds water to dark liquid). capillary effect was done first inspection more than 2cm/5 minute.
5, typing: 50 ± 1 meters/minute of the speed of a motor vehicle, 185-200 ℃ of temperature Room 1,3,8,215-220 ℃ of all the other each chambers, cropping fabric width 155-155.5cm, the cropping temperature is lower than 45 ℃, notes skew of weft, overfeeding 3%.
6,180 mercerisings: 45 ± 1 meters/minute of the speed of a motor vehicle, fuselage 155-156cm, acetic acid content: 4 ± 1g/L, 60-65 ℃ of lixiviating oven temperature, degree, 70-80 ℃ of washing temperature, 60-65 ℃ of last lattice, the flowing water of all living, cloth cover pH value uniformity.
7, dye at the end: the speed of a motor vehicle: 30 ± 1 meters/minute, soak a padding liquor, preliminary drying: 70-80 ℃, cropping must be done more. (prescription: disperse yellow SE-4RL:2g/L; Disperse blue E-4R:1.6g/L, disperse red E-4B:0.5g/L; Vat Yellow GCN: 5.0g/L; Reduce blue C-MG:3.0g/L; Vat Brown BR: 5.0g/L; Anti-infrared conditioning agent: 0.4-0.5g/L)
8, stamp: the speed of a motor vehicle: 30 ± 1 meters/minute, bake out temperature: 100-105 ℃. (seal slurry formula: green statin: disperse light yellow SE-4GL:0.08kg; Disperse blue E-4R:0.1kg; Vat yellow 5GF:1.35kg; Vat brown T-RN:0.7kg; Anti-infrared conditioning agent: 0.01-0.015kg; Sodium alginate: 40kg, residue adds water configuration 100kg.Palm fibre spot: disperse orange S-4RL:1.2kg; Disperse blue E-4R:0.32kg; Disperse red E-4B:0.3kg; Vat Brown BR: 1.8kg; Vat Olive R: 0.7kg; Reducing yellow G: 0.55kg; Anti-infrared conditioning agent: 0.02-0.025kg; Sodium alginate: 40kg, residue adds water configuration 100kg)
9, bake: 35 ± 1 meters/minute of the speed of a motor vehicle, 185 ± 2 ℃ of temperature, 2 minutes 40 seconds-2 minutes 45 seconds time.
10, evaporate: 35-45 meters/minutes of the speed of a motor vehicle, 125-140 ℃ of temperature, 85-95 ℃ of soap boiling temperature, 80-85 ℃ of washing temperature, 60-65 ℃ of last lattice, flowing water all alive, replenish liquid: caustic soda 75-85g/L, working solution: caustic soda 70-85g/L, sodium hydrosulfite: replenish liquid: caustic soda 85-95g/L, working solution: caustic soda 70-85g/L, hydrogen peroxide 1.5-2.5g/L.
11, back arrangement tentering: 25 ± 1 meters/minute of the speed of a motor vehicle, temperature 180-185 ℃, cropping fabric width 151-151.5cm. (prescription: antifouling, anti wrinkling agent FEL:60g/L, waterproof, refuse oil, antistatic additive XQ-608A:50g/l)
12, shrinkproof: anti-shrinkage 3%, fabric width is at 150-151cm.
Three, cotton three look desert camouflage color waterproof yarn card (63 ") of 14*14 brocade
This product has the anti-infrared function in the 400-1200nm wave-length coverage, have waterproof, refuse oil, anlistatig function.
Technological process: former cloth sews up → singes → cold rolling → 180 pre-treatments → end → stamp of finalizing the design → dye → bake → evaporate → mercerising → back arrangement → tentering → shrinkproof → check and accept.
Process conditions: 1, former cloth sews up: needle gage density: 24-26 pin/10cm, sew up flat, straight, neat.
2, singe: 90-95 meters/minutes of the speed of a motor vehicle, two positive one is anti-, three road burners.
3, cold rolling: clot, 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, working solution content: caustic soda 30-35g/l, hydrogen peroxide 4 ± 1g/L replenishes liquid: caustic soda 40-45g/L, hydrogen peroxide 7 ± 1g/L, driving before measurement pick-up 70-75% is obturaged with plastic paper after the clot, and normal temperature was banked up 24 hours.(prescription: cold pad-batch additive 6kg, scouring agent 3kg, hydrogen peroxide 10kg, hydrogen peroxide bleaching stabilizer 3kg, chelated dispersants 2kg, residue adds water configuration 430L)
4,180 pre-treatment oxygen move back: 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, 95-100 ℃ of crawler belt temperature, bank up 45 minutes time, wash 80-90 ℃ of the 1-5 lattice, 60-65 ℃ of flowing water of all living of the 6th lattice replenish liquid: caustic soda 40-45g/L, hydrogen peroxide 4 ± 2g/L, working solution: caustic soda 30 ± 2g/L, hydrogen peroxide 2 ± 0.5g/L. (prescription: hydrogen peroxide 7kg, scouring agent 3kg, stabilizing agent: 3kg, residue adds water configuration 5001).Capillary effect was done first inspection more than 2cm/5 minute.
5, typing: 50 ± 1 meters/minute of the speed of a motor vehicle, 190-195 ℃ of temperature 1-8 chamber, cropping fabric width 155-155.5cm, the cropping temperature is lower than 45 ℃, notes skew of weft, overfeeding 3%.
6, dye at the end: the speed of a motor vehicle: 30 ± 1 meters/minute, soak a padding liquor, preliminary drying: 70-80 ℃, cropping must be done more. (prescription: reduced khaki 2 G: 0.6g/L; Vat Brown BR: 0.3g/L; Reduced olive T: 0.6g/L; Anti-infrared conditioning agent: 0.001g/L)
7, stamp: the speed of a motor vehicle: 30 ± 1 meters/minute, bake out temperature: 100-105 ℃. (seal slurry formula: khaki color spot: reduced olive T: 0.03kg; Vat Brown BR: 0.18kg; Reducing yellow G: 0.02kg; Sodium alginate: 50kg, residue adds water configuration 100kg.Green statin: vat green B:0.19kg; Reducing yellow G: 0.06kg; Sodium alginate: 50kg, residue adds water configuration 100kg.Palm fibre spot: Vat Brown BR: 1.7kg; Reducing yellow G: 0.14kg; Anti-infrared conditioning agent: 0.01kg; Sodium alginate: 50kg, residue adds water configuration 100kg)
8, bake: 35 ± 1 meters/minute of the speed of a motor vehicle, temperature 160-165 ℃, 2 minutes 40 seconds-2 minutes 45 seconds time.
9, evaporate: 35-45 meters/minutes of the speed of a motor vehicle, 125-140 ℃ of temperature, 85-95 ℃ of soap boiling temperature, 80-85 ℃ of washing temperature, 60-65 ℃ of last lattice, flowing water all alive, replenish liquid: caustic soda 75-85g/L, working solution: caustic soda 70-85g/L, sodium hydrosulfite: replenish liquid: caustic soda 85-95g/L, working solution: caustic soda 70-85g/L, hydrogen peroxide 1.5-2.5g/L.
10,180 mercerisings: 45 ± 1 meters/minute of the speed of a motor vehicle, fuselage 155-156cm, acetic acid content: 4 ± 1g/L, 60-65 ℃ of lixiviating oven temperature, degree, 70-80 ℃ of washing temperature, 60-65 ℃ of last lattice, the flowing water of all living, cloth cover pH value uniformity.
11, back arrangement: the speed of a motor vehicle: 30 ± 1 meters/minute, with two groups of infrared rays, cropping must be done.(prescription: ventilative, anti wrinkling agent FEL:60g/L, waterproof, refuse oil, antistatic additive XQ-608A:50g/L).
12, tentering: the speed of a motor vehicle: 25 ± 1 meters/minute, temperature 180-185 ℃, cropping fabric width 151-151.5cm.
13, shrinkproof: anti-shrinkage 3%, fabric width is at 150-151cm.
Claims (3)
1, a kind of manufacture craft of anti-infrared multifunctional camouflage fabric, it is characterized in that getting former cloth and sew up through following processing: singe (1): 90-95 meters/minutes of the speed of a motor vehicle, TWILL CLOTH, two positive one is anti-, three road burners, plain cloth, two positive two is anti-, four road burners; (2) cold rolling: clot, 40 ± 1 meters/minute of the speed of a motor vehicle, groove normal temperature, working solution content: caustic soda 40-45g/l, hydrogen peroxide 8 ± 1g/l, replenish liquid: caustic soda 50-60g/l, hydrogen peroxide 20 ± 2g/l, driving before measurement pick-up 70-75%, obturage with plastic paper after the clot, normal temperature was banked up 24 hours, and its cold rolling liquid is: cold pad-batch additive 6kg, scouring agent 3kg, hydrogen peroxide 15kg, hydrogen peroxide bleaching stabilizer 5kg, chelated dispersants 2kg, it is that 430L. (3) 180 pre-treatment oxygen move back: 40 ± 1 meters/minute of the speed of a motor vehicle that residue adds water to solution, groove normal temperature, 95-100 ℃ of crawler belt temperature are banked up 45 minutes time, wash 80-90 ℃ of the 1-5 lattice, 60-65 ℃ of flowing water of all living of the 6th lattice, replenish liquid: caustic soda 40-45g/L, hydrogen peroxide 4 ± 2g/L, working solution: caustic soda 30 ± 2g/L, hydrogen peroxide 2 ± 0.5g/L, its oxygen moves back liquid: hydrogen peroxide 7kg, scouring agent 3kg, stabilizing agent 3kg, it is 500L that residue adds water to solution, capillary effect was done first inspection more than 2cm/5 minute. (4) typing: 50 ± 1 meters/minute of the speed of a motor vehicle, temperature 1,3,185-200 ℃ of Room 8,215-220 ℃ of all the other each chambers, cropping fabric width 155-155.5cm, the cropping temperature is lower than 45 ℃, notes skew of weft, overfeeding 3%.(5) 180 mercerisings: 45 ± 1 meters/minute of the speed of a motor vehicle, fuselage 15-156cm, acetic acid content: 4 ± 1g/L, 60-65 ℃ of lixiviating oven temperature, degree, 70-80 ℃ of washing temperature, 60-65 ℃ of last lattice, the flowing water of all living, cloth cover pH value uniformity. dye at the end (6): 30 ± 1 meters/minute of the speed of a motor vehicle, soak a padding liquor → two group infrared ray → two groups of preliminary drying → oven dry croppings more; (7) stamp: the speed of a motor vehicle: 30 ± 1 meters/minute, bake out temperature: 100-105 ℃; (8) bake: 35 ± 1 meters/minute of the speed of a motor vehicle, temperature 185-190 ℃, 2 minutes 40 seconds-2 minutes 45 seconds time. evaporate (9): 35-45 meters/minutes of the speed of a motor vehicle, 125-140 ℃ of temperature, 85-95 ℃ of soap boiling temperature, 80-85 ℃ of washing temperature, 60-65 ℃ of last lattice, the flowing water of all living replenishes liquid: caustic soda 75-85g/L, working solution: caustic soda 70-85g/L, sodium hydrosulfite: replenish liquid: caustic soda 85-95g/L, working solution: caustic soda 70-85g/L, hydrogen peroxide 1.5-2.5g/L. (10) back arrangement tentering: 30-35 meters/minutes of the speed of a motor vehicle, 180-185 ℃ of temperature, cropping fabric width 151-151.5cm; (11) shrinkproof: anti-shrinkage 3%, fabric width is at 150-151cm.
2,, it is characterized in that described end padding liquor DISPERSE DYES 2-10g/L, the reducing dye 5-15g/L of dying according to the manufacture craft of a kind of anti-infrared multifunctional camouflage fabric shown in the claim 1; Anti-infrared conditioning agent: 0.01-1.0g/L.
3,, it is characterized in that described stamp has (a) light green spot: disperse yellow S-6G:0.9kg according to the manufacture craft of a kind of anti-infrared multifunctional camouflage fabric shown in the claim 1; Disperse blue S-GB:0.5kg; Disperse red S-2G:0.04kg; Vat yellow 5GF:0.56kg; Reduce blue C-MG:0.13kg; Vat Brown BR: 0.02kg; Anti-infrared conditioning agent: 0.01kg; Sodium alginate paste: 40kg, residue adds water and disposes to 100kg.(b) green statin: disperse yellow S-2R:1.6kg; Disperse blue S-BG:0.5kg; Disperse red S-2G:0.07kg; Vat yellow RK:1.2kg; Reduce blue C-MG:0.5kg; Vat brown HRR:0.1kg; Vat grey NC:0.25kg; Anti-infrared conditioning agent: 0.16kg; (c) brown spot: disperse yellow S-2R:1.1kg; Disperse blue S-BG:0.2kg; Disperse red S-2G:0.15kg; Vat yellow RK:1.2kg; Vat brown HRR:1.2kg; Vat green FFB:0.8kg; Anti-infrared conditioning agent: 1.2kg; Sodium alginate: 40kg adds water and disposes to 100kg.(d) blackspot: disperse black P-G:1.8kg; Disperse blue S-BG:0.8kg; Vat black G:4.9kg; Vat yellow 5GF:0.4kg; Anti-infrared conditioning agent: 1.5kg; Sodium alginate: 40kg adds water and disposes to 100kg.