CN101386720A - 一种防水防腐腻子 - Google Patents
一种防水防腐腻子 Download PDFInfo
- Publication number
- CN101386720A CN101386720A CNA2007100499946A CN200710049994A CN101386720A CN 101386720 A CN101386720 A CN 101386720A CN A2007100499946 A CNA2007100499946 A CN A2007100499946A CN 200710049994 A CN200710049994 A CN 200710049994A CN 101386720 A CN101386720 A CN 101386720A
- Authority
- CN
- China
- Prior art keywords
- percent
- putty
- water
- parts
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防水防腐腻子,该腻子由以下重量配比的原料组成:灰钙粉 100-400、重质碳酸钙 50-200、轻质碳酸钙 30-10、滑石粉 100-400、立德粉 50-150、钛白粉 30-100、聚乙烯醇 10-35、食用植物油 2-6、机油1-5、95%工业酒精 2-8、10%酰胺溶液 1-10、水 280-480所组成。本发明所涉及的腻子在聚乙烯醇溶液中加入了食用植物油、机油、工业酒精,确保了有较高含量灰钙粉的填料仍能均匀地分散于粘结材料中,使得本发明的腻子在提高防水防腐性能的同时保持了良好的施工性。
Description
技术领域
本发明涉及建筑材料技术领域,具体地说涉及一种用于刮涂墙体的腻子。
背景技术
通常墙壁在刷涂料之前都要刮涂腻子,腻子又叫批灰,主要由粘接材料和填料混合调制而成,它可以平整墙面的凹凸不平、龟裂缝或孔隙,同时平整的腻子层,不但可以节省涂料,还能提高涂料的光滑性。腻子的性能如粘接强度、耐水性等,是影响表面涂料耐久性的重要因素。传统的腻子是由滑石粉等填料和粘结材料组成,在施工时加入一定比例的水混合后刮于墙体上,这类腻子粘结强度低,耐水性、防腐性较差,在长期的使用过程中,容易产生空鼓、脱落、龟裂、发霉等现象,墙体表面涂料也随着腻子的脱落而起皮、脱落,影响到建筑物装修工程的质量。现在市场上出现了一些以灰钙粉为主要活性填料的新型腻子,灰钙粉是一种气硬性胶凝材料,随着腻子的刮涂,其主要成分Ca(OH)2会与空气中的CO2反应生成CaCO3晶体而产生强度,进而在腻子层中能够为其他填料组分提供一定的粘结性,并赋予腻子层显著的耐水性;同时由于消耗了空气中的CO2,涂装后能改善室内的空气质量;并且灰钙粉所提供的高碱性环境,使得霉菌和微生物无法生存,能提高腻子的防腐性。但由于灰钙粉添加到腻子会发生增稠的现象,若灰钙粉的含量过高,会使得填料难以均匀地分散到粘结材料中,腻子产生结块,影响其施工刮涂,因而现有腻子中灰钙粉的用量较低(一般不能超过腻子总量的5%),使得这类腻子的防水防腐性能受到了限制。
发明内容
本发明的目的是克服现有技术中存在的缺点和不足,提供一种灰钙粉含量较高,成本低、防水和防腐性能优良、不龟裂的高性能腻子。
本发明的腻子由以下重量配比的原料组成:
灰钙粉100—400、重质碳酸钙50—200、轻质碳酸钙30—100、滑石粉100—400、立德粉50—150、钛白粉30—100、聚乙烯醇10—35、食用植物油2—6、机油1—5、95%工业酒精2—8、10%酰胺溶液1—10、水280—480。
本发明腻子的优选配比为:
灰钙粉100—200、重质碳酸钙80—100、轻质碳酸钙50—80、滑石粉200—400、立德粉80—100、钛白粉50—80、聚乙烯醇20—30、食用植物油3—6、机油3—5、95%工业酒精5—8、10%酰胺溶液3—5、水300—400。
本发明腻子的最佳配比为:
灰钙粉150、重质碳酸钙100、轻质碳酸钙50、滑石粉300、立德粉80、钛白粉60、聚乙烯醇20、食用植物油3、机油3、95%工业酒精5、10%酰胺溶液3、水350。
制备本发明腻子组合物的方法为常规方法,即在常温常压下按规定比例将聚乙烯醇和水混合后加热,搅拌使其溶解,搅拌下加入食用植物油、润滑油、酒精、酰胺溶液,再按规定比例加入各种填料。本发明的腻子可采用常规方法进行刮涂。
与现有技术相比,本发明的有益效果是:本发明的腻子含有较高含量的灰钙粉,由于灰钙粉的特性,使得本发明的腻子具有明显的防水防腐性能;本发明在聚乙烯醇溶液中加入了食用植物油、机油、酒精,使得含有较高含量灰钙粉的填料仍能均匀地分散于粘结材料中,保持良好的施工性;同时本发明利用灰钙粉具有增稠的性质,在增加其用量的同时减少了增稠剂酰胺溶液的用量,使增稠剂对腻子防水性的不良影响降到最低。参照JG/T3049—1998技术指标对本发明的腻子进行性能测试,结果表明上述组合以及用量配比可使本发明的腻子组合物具有良好的施工性、耐水性、防腐性、洁白性,可以达到理想的效果而且成本很低。
具体实施方式
下面结合具体实施例对本发明作进一步的详细描述。
实施例1
在常温常压下将20份聚乙烯醇和350份水混合后加热,搅拌使其溶解,搅拌下加入3份食用植物油、3份机油、5份95%工业酒精、3份10%酰胺溶液,再加入150份灰钙粉、100份重质碳酸钙、50份轻质碳酸钙、300份滑石粉、80份立德粉、60份钛白粉,搅拌均匀后即可制得建筑用腻子。
实施例2
在常温常压下将10份聚乙烯醇和280份水混合后加热,搅拌使其溶解,搅拌下加入3份食用植物油、3份机油、5份95%工业酒精、1份10%酰胺溶液,再加入400份灰钙粉、50份重质碳酸钙、30份轻质碳酸钙、100份滑石粉、50份立德粉、60份钛白粉,搅拌均匀后即可制得建筑用腻子。
实施例3
在常温常压下将30份聚乙烯醇和480份水混合后加热,搅拌使其溶解,搅拌下加入2份食用植物油、1份机油、2份95%工业酒精、5份10%酰胺溶液,再加入200份灰钙粉、80份重质碳酸钙、80份轻质碳酸钙、200份滑石粉、100份立德粉、80份钛白粉,搅拌均匀后即可制得建筑用腻子。
实施例4
在常温常压下将35份聚乙烯醇和300份水混合后加热,搅拌使其溶解,搅拌下加入6份食用植物油、5份机油、8份95%工业酒精、10份10%酰胺溶液,再加入100份灰钙粉、80份重质碳酸钙、100份轻质碳酸钙、400份滑石粉、150份立德粉、100份钛白粉,搅拌均匀后即可制得建筑用腻子。
实施例5
将以上配制的腻子刮涂于瓷板砖上,观察施工情况,并参照JG/T3049—1998技术指标对本发明的腻子进行性能测试,其结果如下:
腻子在容器中无结块、腻子干燥后表面光滑、细腻及无裂缝,刮涂性能优异;
耐水性试验:用水磨砂纸打磨瓷板砖上刮涂的腻子后用水冲洗,腻子底层不软化、不脱落,再在常温下浸入水中浸泡30天,腻子不起泡、不脱落;
耐碱性试验:将刮涂了腻子的瓷板砖在常温下浸入饱和Ca(OH)2浸泡30天不起泡,不脱落,无变化;
耐洗刷性实验:用0.5%皂液洗刷刮涂了腻子的瓷板砖,腻子表面不起粉;
干燥循环性试验:将刮涂了腻子的瓷板砖在常温浸泡水中1h,取出后干燥1h,再浸泡入水中,如此循环20次,腻子表面无异常;
天然老化腻子耐候性实验:将样板放在天然曝晒架上进行自然老化实验,经过200天后,观察样板表面,除去样板表面比较脏外,无其他变化。
Claims (3)
1、一种防水防腐腻子,其特征在于由按重量配比的以下原料组成:
灰钙粉100—400、重质碳酸钙50—200、轻质碳酸钙30—100、滑石粉100—400、立德粉50—150、钛白粉30—100、聚乙烯醇10—35、食用植物油2—6、机油1—5、95%工业酒精2—8、10%酰胺溶液1—10、水280—480。
2、根据权利要求1所述的防水防腐腻子,其特征在于各原料的重量配比为:
灰钙粉100—200、重质碳酸钙80—100、轻质碳酸钙50—80、滑石粉200—400、立德粉80—100、钛白粉50—80、聚乙烯醇20—30、食用植物油3—6、机油3—5、95%工业酒精5—8、10%酰胺溶液3—5、水300—400。
3、根据权利要求1所述的防水防腐腻子,其特征在于各原料的重量配比为:
灰钙粉150、重质碳酸钙100、轻质碳酸钙50、滑石粉300、立德粉80、钛白粉60、聚乙烯醇20、食用植物油3、机油3、95%工业酒精5、10%酰胺溶液3、水350。