CN107500701A - 一种嵌缝膏配方 - Google Patents

一种嵌缝膏配方 Download PDF

Info

Publication number
CN107500701A
CN107500701A CN201710918082.1A CN201710918082A CN107500701A CN 107500701 A CN107500701 A CN 107500701A CN 201710918082 A CN201710918082 A CN 201710918082A CN 107500701 A CN107500701 A CN 107500701A
Authority
CN
China
Prior art keywords
filleting
powder
paste formulation
latex powder
bentonite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710918082.1A
Other languages
English (en)
Inventor
王林敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang New Materials Co Ltd Gennext
Original Assignee
Zhejiang New Materials Co Ltd Gennext
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang New Materials Co Ltd Gennext filed Critical Zhejiang New Materials Co Ltd Gennext
Priority to CN201710918082.1A priority Critical patent/CN107500701A/zh
Publication of CN107500701A publication Critical patent/CN107500701A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种低成本的嵌缝膏配方，在保证产品粘结强度、有效减小干缩比、改善施工性能的前提下，能有效节约生产成本，按质量百分比由如下组分组成：重钙粉55%‑60%，灰钙粉5%‑8%，石膏30%‑35%，膨润土1.0%‑1.7%，乳胶粉1%‑1.5%，羟丙基甲基纤维素2‰‑3‰，缓凝剂1‰‑3‰，木质纤维2‰‑3.5‰。

Description

一种嵌缝膏配方
技术领域
本发明属于装饰装修建材领域，尤其涉及一种嵌缝膏配方。
背景技术
嵌缝膏通常是以精细的半水石膏粉（熟石膏）、多种添加剂混合而成的石膏板拼缝处理材料，一般要求较高的粘结强度、附着力，较小的收缩变形，较好的和易性、施工性能等特点。要做到这一点并不容易，质量好的嵌缝膏生产成本也高，市场价格高，为了节省成本，一些施工单位会用腻子替代嵌缝膏，导致接缝收缩变形后开裂。很明显，这会影响到施工质量和客户评价。
发明内容
本发明要解决的技术问题是提供一种低成本的嵌缝膏配方，保证产品粘结强度、有效减小干缩比、改善施工性能的前提下，还能有效节约生产成本，从经济角度断绝施工过程中的偷工减料利益驱动，保证建筑装饰装修质量。
本发明涉及一种嵌缝膏配方，按质量百分比由如下组分组成：重钙粉55%-60%，灰钙粉5%-8%，石膏30%-35%，膨润土1.0%-1.7%，乳胶粉1%-1.5%，羟丙基甲基纤维素2‰-3‰，缓凝剂1‰-3‰，木质纤维2‰-3.5‰。
膨润土具有良好的膨胀性、悬浮性、粘结性、润滑性，添加到嵌缝膏中能使长时间存放不脱水，刮到墙面上柔韧有光泽、厚度均匀，粘结性能好，无论是与墙面还是与罩面乳胶漆都有很好的结合力。
优选的，所述乳胶粉为可再分散乳胶粉，是水溶性可再分散粉末，分为乙烯/醋酸乙烯酯的共聚物、醋酸乙烯/属碳酸乙烯共聚物、丙烯酸共聚物等，喷雾干燥后制成的粉体粘合剂，以聚乙烯醇为保护胶体。这种粉体与水接触后可以很快再分散成乳液，具有高粘结强度和独特性能，如抗水性、施工性和隔热性等。
缓凝剂的作用是提高嵌缝膏的和易性、施工性能，延长嵌缝膏的硬化时间，避免硬化过快导致收缩变形、开裂产生新缝。
木质纤维是天然可再生木材经过化学处理、机械法加工得到的有机絮状纤维物质。由于纤维结构的毛细管作用，将系统内部的水分迅速传输到浆料表面和界面，使得浆料内部的水分均匀分布，可明显减少结皮现象，并使得粘结强度和表面强度明显提高，这个机理也由于干燥过程中张力的减少而明显起到抗裂的作用，对于防止涂层开裂、提高保水性、提高生产稳定性和施工和易性、增加强度、增强对墙面的附着力等都有良好的效果。木质纤维的尺寸稳定性和热稳定性，在外墙面保温材料中也起到了很好的保温抗裂作用。
具体实施方式
按质量百分比，取得由以下组分组成的混合物10KG：重钙粉56.5%，灰钙粉6%，石膏34%，膨润土1.5%，羟丙基甲基纤维素2.5‰，缓凝剂2‰，乳胶粉1.25%，木质纤维3‰。经检测，符合《陶瓷墙地砖填缝剂（JC/T 1004-2006）》、《建筑室内用腻子（JG/T 298-2010）》标准要求。在桶状容器内先加入干净的清水，然后将上述混合物边加入边搅拌，水灰比约0.22，均匀搅拌后搁置3分钟开始用于宽约0.5CM-2CM的水泥板拼缝处理，填补钉眼空隙，并于1小时内用完。经检验，质量合乎要求，产品成本介于普通腻子粉和普通嵌缝膏之间。

Claims (2)

1.一种嵌缝膏配方，其特征在于按质量百分比由如下组分组成：重钙粉55%-60%，灰钙粉5%-8%，石膏30%-35%，膨润土1.0%-1.7%，乳胶粉1%-1.5%，羟丙基甲基纤维素2‰-3‰，缓凝剂1‰-3‰，木质纤维2‰-3.5‰。
2.如权利要求1所述的一种嵌缝膏配方，其特征在于：所述乳胶粉为可再分散乳胶粉。
CN201710918082.1A 2017-09-30 2017-09-30 一种嵌缝膏配方 Pending CN107500701A (zh)