CN101357842A - Technique of preparing artificial stone - Google Patents
Technique of preparing artificial stone Download PDFInfo
- Publication number
- CN101357842A CN101357842A CNA2008102120356A CN200810212035A CN101357842A CN 101357842 A CN101357842 A CN 101357842A CN A2008102120356 A CNA2008102120356 A CN A2008102120356A CN 200810212035 A CN200810212035 A CN 200810212035A CN 101357842 A CN101357842 A CN 101357842A
- Authority
- CN
- China
- Prior art keywords
- mould
- artificial stone
- sand
- product
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a preparation process of an artificial stone, relates to a decorative material of the artificial stone and belongs to the technical field of artificial stone material used in decoration. The invention more particularly relates to a preparation method of the artificial stone with high intensity. The product of the invention is prepared in a way that inorganic substances of cement, gypsum, siliceous dust, industrial lithium carbonate, ferric oxide pigment, a special water reducing agent, an inner-mixing waterproofing agent, quartz sand, white sand, river sand, other colored sand, and the like, which are harmless to human body are mixed and a wire gauze is added, thus improving the surface strength, tensile strength and earthquake resistant strength. The prepared product has the advantages of no smell, no toxicity, no radiation, fire protection, high surface strength, high tensile strength and good earthquake resistance.
Description
Technical field:
The present invention relates to a kind of rostone finishing material, belong to decorating and use artificial stone-like material's technical field, be specifically related to a kind of preparation method of high-intensity artificial stone.
Background technology:
At present, the inside of most of inorganic compounding class rostones all adds grid cloth (glass fiber mesh), grid cloth bonds together each component of rostone closely, improved the tensile strength of rostone, but for larger-size artificial slabstone and mould, the grid cloth role is just very little, the characteristic that does not possess very strong wear-resisting, withstand voltage, folding, shock resistance is also poor, for the higher project under construction of ask for something, security incident takes place easily.
Summary of the invention:
The preparation technology who the purpose of this invention is to provide a kind of rostone, it can solve the existing problem of background technology, and it adds wire netting and reinforcing bar by the inside at inorganic compounding class rostone, has increased surface strength and tensile strength, has also increased shock strength.
In order to solve the existing problem of background technology, the present invention adopts following scheme to realize, preparation method of the present invention: (a) go into mould: after uniformly mixing according to weight percent cement 20-25%, gypsum 5-10%, silicon ash 10-15%, Quilonum Retard 0.1-0.5%, extraordinary water reducer 1-3%, water-resisting agent 1-2%, pigment 5-10%, sand 40-55%, the water that adds 15-20% stirs once more, gets mixture; (b) add wire netting: mixture 1/2nd is poured in the mould, the wire netting that is slightly less than the mould size is put into, compress, wire netting and mixture are sticked together, remaining 1/2nd mixtures are poured in the mould, by vibrating, bubble is drawn, get work in-process; (c) demoulding: after work in-process are placed 1-2 hour, molding semi product, with molding semi product and mould separating; (d) maintenance: molding semi product was carried out maintenance 1-3 days under temperature 20-25 ℃, humidity 90-95%, make high-strength panel; (e) cutting aftertreatment: with the high-strength panel excision forming, clean up then, carry out surface waterproofing, dry, packing is made product.
The present invention mixes by cement, gypsum, silicon ash, industrial lithium carbonate, iron oxide pigment, extraordinary water reducer, internal doping type water-resisting agent, quartz sand, white sand, river sand being also had harmless inorganicss such as other color sand, by adding wire netting, surface strength and tensile strength have been increased, also increased shock strength, make product, have tasteless, nontoxic, radiationless, fire prevention, surface and tensile strength height, shock resistance is good.
Embodiment:
Embodiment one: this embodiment preparation method of the present invention: (a) go into mould: after uniformly mixing according to weight percent cement 20-25%, gypsum 5-10%, silicon ash 10-15%, Quilonum Retard 0.1-0.5%, extraordinary water reducer 1-3%, water-resisting agent 1-2%, pigment 5-10%, sand 40-55%, the water that adds 15-20% stirs once more, gets mixture; (b) add wire netting: mixture 1/2nd is poured in the mould, the wire netting that is slightly less than the mould size is put into, compress, wire netting and mixture are sticked together, remaining 1/2nd mixtures are poured in the mould, by vibrating, bubble is drawn, get work in-process; (c) demoulding: after work in-process are placed 1-2 hour, molding semi product, with molding semi product and mould separating; (d) maintenance: molding semi product was carried out maintenance 1-3 days under temperature 20-25 ℃, humidity 90-95%, make high-strength panel; (e) cutting aftertreatment: with the high-strength panel excision forming, clean up then, carry out surface waterproofing, dry, packing is made product.
Described wire netting can be to be welded into by Φ 2 iron wires, the degree zinc-iron silk screen of the whole specification 550X1150 of mesh 50X50.
Embodiment two: different is with embodiment one: make the wire netting that adds into reinforcing bar, other step is identical with embodiment one.
The present invention mixes by cement, gypsum, silicon ash, industrial lithium carbonate, iron oxide pigment, extraordinary water reducer, internal doping type water-resisting agent, quartz sand, white sand, river sand being also had harmless inorganicss such as other color sand, by adding wire netting, surface strength and tensile strength have been increased, also increased shock strength, make product, have tasteless, nontoxic, radiationless, fire prevention, surface and tensile strength height, shock resistance is good.
Specific embodiments of the invention: at first take by weighing cement 700 grams, 1.4 kilograms of sands, wollastonite powder 140 grams, water reducer 3 grams, water-resisting agent 50 grams, pigment 2 grams, peptizer 1 gram.With above-mentioned material thorough mixing, add water 600-900 gram, after stirring, get mixture; A mixture of/2nd is poured in the mould, ready wire netting (or reinforcing bar) is put into mould, after compressing, pour the mixture of residue 1/2nd into, after vibrating, scrape moulding; Place after 1-2 hour, carry out the demoulding; With the sheet material after the demoulding (mould), and under this condition (temperature: 20-25 ℃, humidity: 90-95%), placed 1-3 days; The sheet material that maintenance is good can be polished, the cutting, carry out WATER REPELLENT after, promptly get product.
The good effect of this specific embodiment:
1, the present invention adopts a large amount of inorganic material to be composited, and is a kind of Environmentally-sound technology.
2, material source of the present invention is extensive, is easy to promotion and implementation.
3, the product of made of the present invention is radiationless, and is corrosion-resistant, and the intensity height preferably can have Processability.
4, the invention provides a kind of sheet material of production high strength large-size and the method for mould.
Claims (1)
1, a kind of preparation technology of rostone, it is characterized in that preparation method of the present invention: (a) go into mould: after uniformly mixing according to weight percent cement 20-25%, gypsum 5-10%, silicon ash 10-15%, Quilonum Retard 0.1-0.5%, extraordinary water reducer 1-3%, water-resisting agent 1-2%, pigment 5-10%, sand 40-55%, the water that adds 15-20% stirs once more, gets mixture; (b) add wire netting: mixture 1/2nd is poured in the mould, the wire netting that is slightly less than the mould size is put into, compress, wire netting and mixture are sticked together, remaining 1/2nd mixtures are poured in the mould, by vibrating, bubble is drawn, get work in-process; (c) demoulding: after work in-process are placed 1-2 hour, molding semi product, with molding semi product and mould separating; (d) maintenance: molding semi product was carried out maintenance 1-3 days under temperature 20-25 ℃, humidity 90-95%, make high-strength panel; (e) cutting aftertreatment: with the high-strength panel excision forming, clean up then, carry out surface waterproofing, dry, packing is made product.