CN101357398A - 双液双金属复合铸造颚板生产工艺方法 - Google Patents

双液双金属复合铸造颚板生产工艺方法 Download PDF

Info

Publication number
CN101357398A
CN101357398A CNA2007100725858A CN200710072585A CN101357398A CN 101357398 A CN101357398 A CN 101357398A CN A2007100725858 A CNA2007100725858 A CN A2007100725858A CN 200710072585 A CN200710072585 A CN 200710072585A CN 101357398 A CN101357398 A CN 101357398A
Authority
CN
China
Prior art keywords
double
metal composite
lining
composite casting
interface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100725858A
Other languages
English (en)
Inventor
荣守范
郭继伟
黄志求
李俊刚
朱永长
张敬强
于峰
江丽炜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2007100725858A priority Critical patent/CN101357398A/zh
Publication of CN101357398A publication Critical patent/CN101357398A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种双液双金属复合铸造颚板生产工艺方法。采用两个浇注系统(见附图)，先在工作层浇口处浇入高铬铸铁(或高碳贝氏体钢、高铬钢)，当金属液达到复合界面或稍下一点时，根据铸件大小，间隔3－120秒，之后，再在衬层浇口处浇入低合金钢，并在耐磨工作层处放置激冷材料，同时，衬层采用雨淋式浇注系统，防止后浇注的金属液对结合界面的过渡冲刷，以保证结晶界面与基体具有一定的温度梯度和一定厚度及均匀、完整的结合界面。双液双金属复合铸造颚板生产工艺方法，由于耐磨工作层表面采用了高铬铸铁，衬层用低合金钢材质制作，即发挥了工作层高铬铸铁耐磨性好的作用，也发挥了衬层材料韧性强的特长，使鄂板的使用寿命明显增加。

Description

双液双金属复合铸造颚板生产工艺方法
所属技术领域
本发明涉及一种双液双金属复合铸造颚板生产工艺方法。尤其是通过在复合材料先浇注的金属耐磨工作层处放置激冷材料，以保证结晶界面与基体具有一定的温度梯度和完整结合界面的一种双液双金属复合铸造颚板的生产工艺方法。
背景技术：
鄂板是鄂式破碎机上的重要零件，也是破碎机上消耗最大、最容易损坏的零件。目前，国内破碎机使用的各种型号的传统鄂板，大多都是采用中碳合金钢、高锰钢或高铬铸铁。中碳合金钢和高锰钢韧性虽好，但硬度低，抗磨性相对较差，锤头使用寿命低；高铬铸铁虽然抗磨性好，但因其韧性较差，使用过程中容易在产生断裂现象。
双液双金属复合铸造颚板生产工艺方法，由于耐磨工作层表面采用了高铬铸铁，衬层用低合金钢材质制作，即发挥了工作层高铬铸铁耐磨性好的作用，也发挥了衬层材料韧性强的特长，使鄂板的使用寿命明显增加。
发明内容：
为了克服现有鄂板材质耐磨性相对较差，和高铬铸铁在使用过程中容易发生断裂等不足，本发明提供一种双液双金属复合铸造颚板的生产工艺方法。
本发明的技术方案是：采用两个浇注系统，先浇入工作表面金属液，达到工艺要求的复合界面或稍下一点时，根据铸件大小，间隔3-120秒，之后，再浇入衬层金属液，并在复合材料的高铬铸铁处放置激冷材料，同时，衬层采用雨淋式浇注系统，防止后浇注的金属液对结合界面的过渡冲刷，以保证结晶界面与基体具有一定的温度梯度和一定厚度及均匀、完整的结合界面。
本发明的有益效果是，由于采用双液双金属复合铸造方法生产鄂板，使工作面具有很高的耐磨性，衬层部分具有良好的冲击韧性，充分发挥了各种材料的特长。同时雨淋式浇注系统的使用，确保了复合材料界面的均匀和完整，使鄂板的使用性能得以优化。
附图说明
下面是结合附图对本发明作详细的说明。
附图是双液双金属复合铸造鄂板的铸造工艺示意图，图中1是复合材料工作层，其材质为高碳贝氏体钢、高铬铸铁或高铬钢，在耐磨工作层处放置激冷材料，用于加速金属液的冷却，为了防止混料现象，激冷材料应放置在双液结合面以下，根据铸件大小，可以放置在鄂板结合部位以下的两侧或四周；图中2是衬层，材质为低合金钢，以保证鄂板的整体强度；图中3是工作层的浇注系统，用于浇铸或补缩高铬铸铁或高合金钢液体；图中4是用于浇注衬层的雨淋式浇注系统，用于浇注或补缩衬层的金属液，并防止后浇注的金属液对结合界面的过渡冲刷，确保结合界面的均匀和完整；图中5是双金属复合界面。
具体实施方式
采用两个浇注系统，先在工作层浇口处浇入高铬铸铁(或高碳贝氏体钢、高铬钢)，当金属液达到复合界面或稍下一点时，根据铸件大小，间隔3-120秒，之后，再在衬层浇口处浇入低合金钢，并在耐磨工作层处放置激冷材料，同时，衬层采用雨淋式浇注系统，防止后浇注的金属液对结合界面的过渡冲刷，以保证结晶界面与基体具有一定的温度梯度和一定厚度及均匀、完整的结合界面。

Claims (6)

1.双液双金属复合铸造颚板生产工艺方法，其特征是采用两个浇注系统，并在复合材料的工作表面放置激冷材料的一种双液双金属复合铸造颚板的生产工艺方法。
2.根据权利要求1所述的双液双金属复合铸造颚板生产工艺方法，其特征是采用高铬铸铁(或高碳贝氏体钢、高铬钢)与低合金钢双液双金属复合铸造的方法，并在耐磨材料工作面处放置激冷材料，以保证结晶界面与基体具有一定的温度梯度，和一定厚度及完整的结合界面。
3.根据权利要求1所述的双液双金属复合铸造颚板生产工艺方法，其特征是采用两个浇注系统，先浇入工作层液体，根据铸件大小，间隔3-120秒后再浇入衬层材料，使双金属复合界面得到良好的补缩。
4.根据权利要求1所述的双液双金属复合铸造颚板生产工艺方法，其特征是衬层采用雨淋式浇注系统，防止后浇注的金属液对结合界面的过渡冲刷，以保证界面的均匀和完整。
5.根据权利要求1所述的双液双金属复合铸造颚板生产工艺方法，其特征是根据零件工作环境的不同，工作面可以采用高铬铸铁、高合金钢、高碳贝氏体钢等材质。
6.根据权利要求1所述的双液双金属复合铸造颚板生产工艺方法，其特征是衬层部分采用的是低合金钢材质，以保证鄂板具有良好的整体强度。
CNA2007100725858A 2007-07-30 2007-07-30 双液双金属复合铸造颚板生产工艺方法 Pending CN101357398A (zh)