CN101338153B - 一种耐高温泡沫胶粘剂及其制备方法 - Google Patents

一种耐高温泡沫胶粘剂及其制备方法 Download PDF

Info

Publication number
CN101338153B
CN101338153B CN2008100219884A CN200810021988A CN101338153B CN 101338153 B CN101338153 B CN 101338153B CN 2008100219884 A CN2008100219884 A CN 2008100219884A CN 200810021988 A CN200810021988 A CN 200810021988A CN 101338153 B CN101338153 B CN 101338153B
Authority
CN
China
Prior art keywords
percent
high temperature
temperature resistant
resistant foam
foam glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100219884A
Other languages
English (en)
Other versions
CN101338153A (zh
Inventor
高延敏
张天财
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Nanjing Normal University Development Research Institute Co Ltd
Original Assignee
Jiangsu University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu University of Science and Technology filed Critical Jiangsu University of Science and Technology
Priority to CN2008100219884A priority Critical patent/CN101338153B/zh
Publication of CN101338153A publication Critical patent/CN101338153A/zh
Application granted granted Critical
Publication of CN101338153B publication Critical patent/CN101338153B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐高温泡沫胶粘剂及其制备方法，该胶粘剂由组分及质量百分含量为：环氧树脂50-85％，固化剂4.3-14％，发泡剂4.5-20％，促进剂0.5-4％，填料1-30％组成。制备过程中，将上所述的组分按比例混合、搅拌均匀，包装封存。使用时胶体在140℃的温度下反应30分钟，并在实施部位90℃下保温2小时。本发明因采用线性联苯基团的胺类固化剂，所以，具有优良的耐高温性能，无氟发泡、环保无污染等优点，且剪切力高达12Mpa以上，导热系数为4.0×10-3w/(m·℃)以下。本发明应用前景广阔。

Description

一种耐高温泡沫胶粘剂及其制备方法
技术领域
本发明属于胶粘剂领域，具体地说，是涉及一种耐高温泡沫胶粘剂及其制备方法，可应用于复合材料夹心粘接，高温蒸汽保温管道修复。
背景技术
目前，在航天航空以及保温管和夹心保温材料安装过程中所使用的粘合剂能够满足胶结施工的需要，但因粘合剂不能直接发泡，一定程度上影响了绝热保温效果。
发明内容
本发明的目的是为了克服现有技术所存在的缺陷，解决粘合剂导热系数大，绝热性差的技术问题，提供一种耐高温泡沫胶粘剂及其制备方法。
为了实现上述的目的，本发明的一种耐高温泡沫胶粘剂是由环氧树脂，固化剂，促进剂，发泡剂，填料组成，其各组分的质量百分含量为：
环氧树脂   50-85％，
固化剂     4.3-14％，
发泡剂    4.5-20％，
促进剂    0.5-4％，
填料      1-30％。
上述的环氧树脂为双酚A型环氧树脂E-44；
上述的固化剂为萘胺类化合物，其结构式为：
式中：L为烷基；n取值范围为1～2；
上述的发泡剂为偶氮二甲酰胺或丙酮或环己酮的任一种；
上述的促进剂为甲基咪唑或三乙醇胺的任一种；
上述的填料为硅微粉。
为了实现上述的目的，本发明的一种耐高温泡沫胶粘剂的制备方法是：先将上述诸物按比例混合、搅拌均匀，包装封存。使用时胶体在140℃的温度下反应30分钟，并在实施部位90℃下保温2小时。
本发明的一种耐高温泡沫胶粘剂因采用线性联苯基团的胺类固化剂，所以，具有优良的耐高温性能(瞬时耐温可达400℃)，无氟发泡、环保无污染，且剪切力高达12Mpa以上，导热系数为4.0×10-3w/(m·℃)以下。
具体实施方式
实施例1：
本发明的一种耐高温泡沫胶粘剂按如下组分配比制备而成(质量百分含量)：
1、双酚A型环氧树脂E-44，其用量是胶体整体质量的63％，
2、固化剂为萘胺，其用量是胶体整体质量的11％，
3、发泡剂为偶氮二甲酰胺，其用量是胶体整体质量的20％，
4、促进剂为甲基咪唑，其用量是胶体整体质量2.5％，
5、填料为硅微粉，其用量是胶体整体质量3.5％，
将以上5种物质按比例混合、搅拌均匀，包装封存。使用时胶体在140℃的温度下反应30分钟，并在实施部位90℃下保温2小时。
其有益效果为：在300℃的高温下仍有良好力学性能，剪切力可达12Mpa，该温度下使用时间为15h，导热系数为2.5×10-3w/(m·℃)。
实施例2：
本发明耐高温泡沫胶粘剂按如下组分配比制备而成(质量百分含量)：
1、双酚A型环氧树脂E-44，其用量是胶体整体质量的85％，
2、固化剂为萘胺，其用量是胶体整体质量的12％，
3、发泡剂为丙酮，其用量是胶体整体质量的1.5％，
4、促进剂为甲基咪唑，其用量是胶体整体质量0.5％，
5、填料为硅微粉，其用量是胶体整体质量1％。
制备方法与使用与实施例1相同。
其有益效果为：在300℃高温下剪切力可达15Mpa，使用时间30小时，导热系数为3.5×10-3w/(m·℃)。
实施例3：
本发明耐高温泡沫胶粘剂按如下组分配比制备而成(质量百分含量)：
1、双酚A型环氧树脂E-44，其用量是胶体整体质量的50％，
2、固化剂为萘胺，其用量是胶体整体质量的4.3％，
3、发泡剂为丙酮，其用量是胶体整体质量的11.7％，
4、促进剂为甲基咪唑，其用量是胶体整体质量4％，
5、填料为硅微粉，其用量是胶体整体质量30％。
制备方法与使用与实施例1相同。
其有益效果在于，泡沫体柔韧性好，抗冲击力强，施工方便。可耐300℃高温，剪切力可达13Mpa，使用时间40小时，导热系数为4.0×10-3w/(m·℃)。
实施例4：
本发明耐高温泡沫胶粘剂按如下组分配比制备而成(质量百分含量)：
1、双酚A型环氧树脂E-44，其用量是胶体整体质量的60％，
2、固化剂为萘胺，其用量是胶体整体质量的10.4％，
3、发泡剂为环己酮，其用量是胶体整体质量的10％，
4、促进剂为三乙醇胺，其用量是胶体整体质量4％，
5、填料为硅微粉，其用量是胶体整体质量15.6％。
制备方法与使用与实施例1相同。
其有益效果在于，泡沫体硬，具有高耐温性能，在300℃的高温下剪切力可达12Mpa，使用时间14小时，导热系数为3.2×10-3w/(m·℃)。
所述实施例仅用于说明本发明技术方案，并不用于限制本发明。

Claims (6)

1.一种耐高温泡沫胶粘剂，其特征是：由环氧树脂，固化剂，促进剂，发泡剂，填料组成，其各组分的质量百分含量为：
环氧树脂                    50-85％，
固化剂                      4.3-14％，
发泡剂                      4.5-20％，
促进剂                      0.5-4％，
填料                        1-30％；
其中固化剂为萘胺类化合物，其结构式为：
Figure FSB00000175562100011
式中：L为烷基；n取值范围为1～2。
2.根据权利要求1所述的一种耐高温泡沫胶粘剂，其特征是：所述的环氧树脂为双酚A型环氧树脂E-44。
3.根据权利要求1所述的一种耐高温泡沫胶粘剂，其特征是：所述的发泡剂为偶氮二甲酰胺或丙酮或环己酮的任一种。
4.根据权利要求1所述的一种耐高温泡沫胶粘剂，其特征是：所述的促进剂为甲基咪唑或三乙醇胺的任一种。
5.根据权利要求1所述的一种耐高温泡沫胶粘剂，其特征是：所述的填料为硅微粉。
6.如权利要求1所述的一种耐高温泡沫胶粘剂的制备方法，其特征是：先将各组分按权利要求1的比例配方，然后进行混合、搅拌均匀，最后包装封存；使用时胶体在140℃的温度下反应30分钟，并在实施部位90℃下保温2小时。
CN2008100219884A 2008-08-20 2008-08-20 一种耐高温泡沫胶粘剂及其制备方法 Expired - Fee Related CN101338153B (zh)