CN101327627A - 一种车辆内饰件表皮的搪塑方法 - Google Patents
一种车辆内饰件表皮的搪塑方法 Download PDFInfo
- Publication number
- CN101327627A CN101327627A CNA2007100422569A CN200710042256A CN101327627A CN 101327627 A CN101327627 A CN 101327627A CN A2007100422569 A CNA2007100422569 A CN A2007100422569A CN 200710042256 A CN200710042256 A CN 200710042256A CN 101327627 A CN101327627 A CN 101327627A
- Authority
- CN
- China
- Prior art keywords
- slush molding
- molding method
- slush
- inner decoration
- epidermis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开的一种车辆内饰件表皮的搪塑方法，包括现有搪塑工艺步骤，其特征在于，其搪塑模具采用高温导热油进行加热，其加热的温度为70－225℃。本发明采用高温导热油进行加热，使得模具加热更加均匀，搪出来的表皮档次高、表面花纹粗细均匀，深浅一致，强度高，耐摩擦，不易开裂，寿命长。
Description
技术领域
本发明涉及一种车辆内饰件表皮的加工方法，特别是一种车辆内饰件表皮的搪塑方法。
背景技术
目前国内外汽车内装饰件，尤其是仪表板生产技术主要有两种：一种是真空吸塑成型技术，采用ABS/PVC合金表皮吸塑成型，然后与骨架发泡为一体而成，但产品档次低、易开裂，表面花纹在拉伸后粗细不一，深浅不均匀，质感差，寿命短，仅在低挡经济车型使用，正逐渐被淘汰。一种是搪塑技术，中高挡汽车使用，表皮材料采用PVC粉末，装入搪塑模具中进行急剧加热，模具快速翻转，然后急剧冷却，形成表皮，再与骨架发泡为一体而成，优点是产品档次高、表面花纹粗细均匀，深浅一致，强度高，耐摩擦，不易开裂，寿命长。但是目前的搪塑的加热方式一般采用的是在搪塑模具中插入电加热丝进行加热，这样的加热方法容易造成加热不均匀，搪塑的质量不高。
发明内容
本发明的所要解决的技术问题在于提供一种车辆内饰件表皮的搪塑方法，该搪塑方法能获得很好的汽车内装饰件表皮。
本发明的所要解决的技术问题可以通过以下技术方案来实现：
一种车辆内饰件表皮的搪塑方法，包括现有搪塑工艺步骤，其特征在于，其搪塑模具采用高温导热油进行加热，其加热的温度为70-225℃。
本发明采用高温导热油进行加热，使得的模具加热更加均匀，搪出来的表皮档次高、表面花纹粗细均匀，深浅一致，强度高，耐摩擦，不易开裂，寿命长。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
一种车辆内饰件表皮的搪塑方法，包括现有搪塑工艺步骤，其搪塑模具采用高温导热油进行加热，其加热的温度为70-225℃。
下面以左、右前门上饰板表皮搪皮工艺为例来进一步说明本发明
材料为PVC粉末，质量为270-330g。左、右前门上饰板表皮搪皮的高温导热油循环温度设定在220-240℃，高温导热油有效温度设定在210-230℃，辐射板走行减速设定在1500转/分钟，辐射板走行温度设定在800转/分钟。
冷却油调整时间为70-90秒，冷却油迂回时间为60-70秒，主轴手动速度设定在200-1000转/分钟，辐射板上升延迟时间200秒，脱型告知时间为20秒。
加热过程中：1回目阶段正转/逆转2次，回转角390°，回转速度为300-500转/分钟，停止时间为3-5秒。加热时间为45秒，开始温度160-180℃，加热温度200-220℃。2回目阶段正转/逆转1次，回转角400°-420°，回转速度为800-1000转/分钟，停止时间为3-5秒。3回目阶段和4回目阶段各参数均为0，原点正转/逆转2次，反转原点正转/逆转2次
烧入阶段中：1回目阶段正转/逆转0次，回转角0°，停止时间为0秒。烧入时间为20秒，烧入时间20秒，取出时间为999秒，烧入温度205-215℃，冷却温度60-70℃。2回目阶段、3回目阶段、4回目阶段各参数均为零。取出阶段正转/逆转2次。
本发明采用高温导热油进行加热，使得的模具加热更加均匀，搪出来的表皮档次高、表面花纹粗细均匀，深浅一致，强度高，耐摩擦，不易开裂，寿命长。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1、一种车辆内饰件表皮的搪塑方法，包括现有搪塑工艺步骤，其特征在于，其搪塑模具采用高温导热油进行加热，其加热的温度为70-225℃。
2、根据权利要求1所述的一种车辆内饰件表皮的搪塑方法，其特征在于，采用的材料为PVC。
3、根据权利要求1所述的一种车辆内饰件表皮的搪塑方法，其特征在于，所述高温导热油循环温度设定在220-240℃