CN101311320A - 一种装饰性镀镍新工艺 - Google Patents
一种装饰性镀镍新工艺 Download PDFInfo
- Publication number
- CN101311320A CN101311320A CNA2008100207410A CN200810020741A CN101311320A CN 101311320 A CN101311320 A CN 101311320A CN A2008100207410 A CNA2008100207410 A CN A2008100207410A CN 200810020741 A CN200810020741 A CN 200810020741A CN 101311320 A CN101311320 A CN 101311320A
- Authority
- CN
- China
- Prior art keywords
- washing
- nickel
- grams
- grams per
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种装饰性镀镍新工艺。本发明解决其技术问题所采用制作工艺、流程及配是:工艺流程:除油-酸洗除锈-水洗-钢丝轮抛光-除油-酸洗-水洗-镀锌-水洗-硝酸出光-水洗-镀中性镍-水洗-纯水-干燥;镀中性镍的工艺及配方:硫酸镍100克-250克/升;柠檬酸钠100克-250克/升;三乙醇胺5克-40克/升;氯化镍20克-80克/升;硼酸20克-80/升;操作温度为20-25℃常温;阳极:镍板或不锈钢板,pH值:5~10,电流密度:0.5-1A/分米2;该装饰性镀镍工艺,可省去镀铜、镍及铬贵金属,可降低成本60%~70%,并且可确保产品的装饰性电镀的质量。
Description
技术领域
本发明涉及一种装饰性电镀工艺,尤其是一种装饰性镀镍新工艺。
背景技术
目前,传统的装饰性镀镍,绝大部分的制作工艺要经过镀铜-镀酸性镍-镀铬三个过程,目前,由于全球镍的产量严重不足,近年来,镍的价格由每吨8万元,已上升到了每吨46万元,铜也由每吨1.7万元上涨到37.5万元,所以寻求一种既能降低成本又能保持住质量的新工艺势在必行。
发明内容
为了解决目前装饰性电镀成本过高的问题,本发明提供出了一种装饰性镀镍工艺,该工艺可省去镀铜、镍及铬贵金属,可降低成本60%~70%,并且还可确保产品装饰性电镀的质量。
本发明解决其技术问题所采用的制作工艺配方及流程方案是:(1)工艺流程:除油-酸洗除锈-水洗-钢丝轮抛光-除油-酸洗-水洗-镀锌-水洗-硝酸出光-水洗-镀中性镍-水洗-纯水-干燥;(2)镀中性镍的工艺及配方:硫酸镍100克-250克/升;柠檬酸钠100克-250克/升;三乙醇胺5克-40克/升;氯化镍20克-80克/升;硼酸20克-80/升;操作温度为20℃~25℃;阳极:镍板或不锈钢板,PH值:5~10,电流密度:0.5-1A/分米2;(3)纯化:重铬酸钾8克-10克/升;PH值:3-5;时间:1-2分钟;温度:20-25℃。
其有益效果是:该装饰性镀镍工艺,可省去镀铜、镍及铬贵金属,可降低成本60%~70%,并且可确保产品装饰性电镀的质量。
具体实施方式
实施例1:所采用的制作工艺、配方及流程特征是:(1)工艺流程:除油-酸洗除锈-水洗-钢丝轮抛光-除油-酸洗-水洗-镀锌-水洗-硝酸出光-水洗-镀中性镍-水洗-纯水-干燥;(2)镀中性镍的工艺及配方:硫酸镍100克/升;柠檬酸钠100克/升;三乙醇胺5克/升;氯化镍20克/升;硼酸20克/升;操作温度为25℃;阳极:镍板,P H值:10,电流密度:1A/分米2;(3)纯化:重铬酸钾10克/升;P H值:3;时间:2分钟;温度:20℃。
实施例2:所采用制作工艺过程的具体方案是:(1)工艺流程:除油-酸洗除锈-水洗-钢丝轮抛光-除油-酸洗-水洗-镀锌-水洗-硝酸出光-水洗-镀中性镍-水洗-纯水-干燥;(2)镀中性镍的工艺及配方:硫酸镍250克/升;柠檬酸钠250克/升;三乙醇胺40克/升;氯化镍80克/升;硼酸80/升;操作温度为20℃;阳极:不锈钢板,P H值:5,电流密度:0.5A/分米2;(3)纯化:重铬酸钾8克/升;P H值:3;时间:1分钟;温度:25℃。
其中,镀锌为公知的镀锌工艺。
Claims (1)
1.一种装饰性镀镍新工艺所采用的制作工艺、配方及流程的具体特征是:(1)工艺流程:除油-酸洗除锈体方案是:(1)工艺流程:除油-酸洗除锈-水洗-钢丝轮抛光-除油-酸洗-水洗-镀锌-水洗-硝酸出光-水洗-镀中性镍-水洗-纯水-干燥;(2)镀中性镍的工艺及配方:硫酸镍100克-250克/升;柠檬酸钠100克-250克/升;三乙醇胺5克-40克/升;氯化镍20克-80克/升;硼酸20克-80/升;操作温度为20-25℃;阳极:镍板或不锈钢板,PH值:5~10,电流密度:0.5-1A/分米2;(3)纯化:重铬酸钾8克-10克/升;PH值:3-5;时间:1-2分钟;温度:20-25℃。