CN101306958B - Method of making crystal fancy glaze - Google Patents
Method of making crystal fancy glaze Download PDFInfo
- Publication number
- CN101306958B CN101306958B CN2008100316583A CN200810031658A CN101306958B CN 101306958 B CN101306958 B CN 101306958B CN 2008100316583 A CN2008100316583 A CN 2008100316583A CN 200810031658 A CN200810031658 A CN 200810031658A CN 101306958 B CN101306958 B CN 101306958B
- Authority
- CN
- China
- Prior art keywords
- percent
- glaze
- oxide
- coat enamel
- ground
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A method for making crystal fancy glaze is characterized in that: the compositions in percentage by weight of ground glaze and surface glaze are: 25 to 35 percent of potash feldspar, 8 to 15 percent of quartz, 15 to 25 percent of calcite, 15 to 25 percent of clay, 3 to 8 percent of barium carbonate, 3 to 7 percent of titanium oxide and 3 to 7 percent of copper oxide, as well as 45 to 55 percent of fusion cake, 15 to 25 percent of potash feldspar, 8 to 12 percent of clay, 8 to 12 percent of titanium oxide, 3 to 7 percent of ferric oxide and 3 to 7 percent of zinc oxide; the ground glaze and the surface glaze undergo wet method ball milling and sieving so as to be made into glaze slurry of 34 to 45 baume degree; the ground glaze is applied to a briquette so as to carry out natural drying; surface glaze slurry is drawn on the opening edges of dried ground glaze cup or dish which undergo firing at a temperature of between 1,160 and 1,200 DEG C; and the fired fancy glaze has strong tree-dimensional perception and higher artistic appeal and unique charm.
Description
Technical field
The present invention relates to the making method of crystal fancy glaze.
Background technology
Can crystal fancy glaze be with glittering and translucent, and stereoscopic sensation is loved by the people by force, use it on the porcelain industry, allows it combine with porcelain, allow it bring into play its exclusive artistic appeal and glamour?
Summary of the invention
Purpose of the present invention just provides a kind of making method of crystal fancy glaze, and it is got close to nature, and has stronger infectivity.
Crystal fancy glaze of the present invention is characterized in that:
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 25～35 quartz 8～15
Calcite 15～25 clays 15～25
Barium carbonate 3～8 titanium oxide 3～7
Cupric oxide 3～7
B, cover-coat enamel
Frit 45～55 potassium felspar sands 15～25
Clay 8～12 titanium oxide 8～12
Ferric oxide 3～7 zinc oxide 3～7
(2) with ground-coat enamel by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, and the glaze behind the ball milling is crossed 200 mesh sieves, and the glaze slip of furnishing 34～45 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake by hand again, and is stand-by after the seasoning;
(3) with cover-coat enamel by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, glaze behind the ball milling is crossed 200 mesh sieves, the glaze slip of furnishing 34～45 degree Beaume again, be painted on rim of a cup edge or dish mouth edge with cover-coat enamel caiquejee worker, fire through 1160～1200 ℃ of temperature, when the high temperature, flow formation crystal decorative pattern naturally mouthful along cover-coat enamel.
According to this crystal fancy glaze that above technical scheme proposes, it is strong to fire the back stereoscopic sensation, has higher artistic appeal and unique charm.
Embodiment
Embodiment one
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 33 quartz 12
Calcite 20 clays 20
Barium carbonate 5 titanium oxide 5
Cupric oxide 5
B, cover-coat enamel
Frit 50 potassium felspar sands 20
Clay 10 titanium oxide 10
Ferric oxide 5 zinc oxide 5
(2) with ground-coat enamel by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, and the glaze behind the ball milling is crossed 200 mesh sieves, and the glaze slip of furnishing 34～45 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake by hand again, and is stand-by after the seasoning;
(3) with cover-coat enamel by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, glaze behind the ball milling is crossed 200 mesh sieves, the glaze slip of furnishing 34～45 degree Beaume again, be painted on rim of a cup edge or dish mouth edge with cover-coat enamel caiquejee worker, fire through 1160～1200 ℃ of temperature, when the high temperature, flow formation crystal decorative pattern naturally mouthful along cover-coat enamel.
Embodiment two
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 30 quartz 15
Calcite 15 clays 25
Barium carbonate 7 titanium oxide 3
Cupric oxide 5
B, cover-coat enamel
Frit 45 potassium felspar sands 25
Clay 8 titanium oxide 12
Ferric oxide 7 zinc oxide 3
(2) with ground-coat enamel by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, and the glaze behind the ball milling is crossed 200 mesh sieves, and the glaze slip of furnishing 34～45 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake by hand again, and is stand-by after the seasoning;
(3) with cover-coat enamel by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, glaze behind the ball milling is crossed 200 mesh sieves, the glaze slip of furnishing 34～45 degree Beaume again, be painted on rim of a cup edge or dish mouth edge with cover-coat enamel caiquejee worker, fire through 1160～1200 ℃ of temperature, when the high temperature, flow formation crystal decorative pattern naturally mouthful along cover-coat enamel.
Frit among the present invention program is the general a kind of material of the industry, from professional production producer, its constitutive material is: silicon-dioxide 64%, aluminium sesquioxide 7%, ferric oxide 1%, calcium oxide 8%, magnesium oxide 0.5%, potassium oxide 4%, sodium oxide 4%, boron trioxide 11%, zinc oxide 0.5%.
Claims (1)
1. the making method of a crystal fancy glaze is characterized in that:
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 25～35 quartz 8～15
Calcite 15～25 clays 15～25
Barium carbonate 3～8 titanium oxide 3～7
Cupric oxide 3～7
B, cover-coat enamel
Frit 45～55 potassium felspar sands 15～25
Clay 8～12 titanium oxide 8～12
Ferric oxide 3～7 zinc oxide 3～7
Wherein: the constitutive material of frit is: silicon-dioxide 64%, aluminium sesquioxide 7%, ferric oxide 1%, calcium oxide 8%, magnesium oxide 0.5%, potassium oxide 4%, sodium oxide 4%, boron trioxide 11%, zinc oxide 0.5%;
(2) ground-coat enamel is by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, and the glaze behind the ball milling is crossed 200 mesh sieves, and the glaze slip of furnishing 34～45 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake by hand again, and is stand-by after the seasoning;
(3) cover-coat enamel is by material: ball: water equals to carry out wet ball grinding 18～20 hour at 1: 2: 0.6, glaze behind the ball milling is crossed 200 mesh sieves, the glaze slip of furnishing 34～45 degree Beaume is painted on rim of a cup edge or dish mouth edge with cover-coat enamel caiquejee worker again, fires finished product through 1160～1200 ℃ of temperature.