CN101289586A - 快干亮光胶版油墨 - Google Patents
快干亮光胶版油墨 Download PDFInfo
- Publication number
- CN101289586A CN101289586A CN 200710172396 CN200710172396A CN101289586A CN 101289586 A CN101289586 A CN 101289586A CN 200710172396 CN200710172396 CN 200710172396 CN 200710172396 A CN200710172396 A CN 200710172396A CN 101289586 A CN101289586 A CN 101289586A
- Authority
- CN
- China
- Prior art keywords
- ink
- oil
- quick
- printing ink
- offset printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明为一种快干亮光胶版油墨，其重量配比为：连接料50－70％；颜料13－20％；油墨油5－15％；以及助剂5－15％，其中该连接料为松香改性酚醛树脂，通过以下步骤制成：酚醛缩合；将缩合的酚醛加成；酯化反应制得半成品；检验半成品是否合格；以及使用合格的半成品进行炼油制成成品。本发明油墨的密度高、飞墨少、纸张干燥时间快、耐磨效果也好，这样的油墨转移性能良好，能达到快干亮光的效果，适合高速印刷。
Description
技术领域
本发明涉及一种快干亮光胶版油墨，其适用于单张进纸的单色机、双色或多色胶印印刷机。
背景技术
近年来，包装印刷市场得到快速的发展，中高速印刷机越来越受到客户的认可，当前海德堡、罗兰、小森、三菱等公司的主流印刷机的印刷速度都在11000-14000张/小时之间，长、短版都可适应。而目前的普通胶印油墨大多只能适应11000张/小时以下，如果高速印刷机采用此类油墨，会由于转移性差而导致印刷质量下降，甚至无法完成印刷。
现有油墨的连接料主要是酚醛树脂制成，其生产工艺主要包括以下步骤：
酚醛缩合；
将缩合的酚醛加成；
酯化反应制得半成品；
对半成品进行检验；
将合格的半成品切片包装；
使用半成品切片进行炼油制成连接料成品。
上述步骤中，从半成品检验合格之后，还需要进行切片包装和炼油两个步骤才能制成连接料。其中的切片包装具体是指：待酯化反应生成的连接料半成品冷却成块后，将其切成片状作后续的炼油加工。
带来的问题是由于需要等半成品冷却，加工工时较长、工艺复杂、采用这样制得的连接料制造出油墨也不能适应高速印刷的要求。
发明内容
本发明的目的在于提供一种用于适合高速印刷的快干亮光胶印油墨的连接料及其制造工艺，以及由该连接料制成的快干亮光胶印油墨。
为达成上述目的，本发明提供一种油墨的连接料制造工艺，该连接料为松香改性酚醛树脂，其特征在于该制造工艺包括以下步骤：
a.酚醛缩合；
b.将缩合的酚醛加成；
c.酯化反应制得半成品；
d.检验半成品是否合格；以及
e.使用合格的半成品进行炼油制成成品。
本发明还提供了一种通过上述工艺制成的油墨连接料。
本发明还提供了一种快干亮光胶版油墨，其重量配比为：
连接料50-70％；
颜料13-20％；
油墨油5-15％；以及
助剂5-15％，
其中该连接料为采用上述工艺制成的油墨连接料。
较佳地，上述颜料为有机颜料；所述油墨油为240-320度的高沸点石油馏分；所述助剂为蜡、干燥剂或抗氧剂。
下面本发明的洋红油墨为例并结合印刷效果的对比来说明本发明优点：
洋红油墨配比为：
连接料 67％
洋红颜料为PR57:1(科莱恩) 18％
油墨油 8％
助剂 7％
其中本发明的油墨采用上述省略冷却步骤的工艺进行制造的连接料；而对照例仍使用原来的先冷却再进行切片的工艺进行制造。
表一：印刷效果对比表
| 本发明 | 对照例 | |
| 粘性/800rpm | 13.4 | 15 |
| 色浓度 | 100％ | 100％ |
| 光泽 | 73 | 73 |
| 密度 | 1.93 | 1.83 |
| 固着 | 6’ | 7’ |
| 飞墨 | 微飞 | 飞 |
| AST/70℃ | 20’-30’ | 20’-30’ |
| 纸张干燥 | 2-3h | 3-4h |
| 耐磨性 | 2级 | 1级 |
从上表可看出，本发明油墨的密度高、飞墨少、纸张干燥时间快、耐磨效果也好，这样的油墨转移性能良好，能达到快干亮光的效果，适合高速印刷。
具体实施方式
本发明为一种快干亮光胶版油墨，其重量配比为：
连接料50-70％，较佳为67％；
颜料13-20％，较佳为18％；
油墨油5-15％，较佳为8％；以及
助剂5-15％，，较佳为7％。
其中所述的连接料可以是松香改进酚醛树脂，其制造工艺包括以下步骤：
a.酚醛缩合；
b.将缩合的酚醛加成；
c.进行酯化反应制得半成品；
d.检验半成品；
e.使用合格的半成品进行炼油制成连接料成品。
在上述的油墨中，所述的颜料可以是有机颜料；所述的油墨油可以是240-320度的高沸点石油馏分；所述的助剂可以是蜡、干燥剂或者抗氧剂。
上述的快干亮光胶版油墨的制造工艺为：
1.在配料桶中加入颜料、连接料、部分油墨油(例如40％、50％或60％，)；
2.以转速：500-1000RPM，搅拌分散40-60分钟；
3.将搅拌充分的物料进入三辊机研磨，压力：30-60Mpa，温度：50-70度，经过三次研磨，将油墨的细度控制在10μ以下；
4.加入剩余的油墨油(例如60％、50％或40％)和助剂，将油墨调整到预定的指标范围内；
5.用灌装机进行灌装。
Claims (6)
1.一种油墨的连接料制造工艺，该连接料为松香改性酚醛树脂，其特征在于该制造工艺包括以下步骤：
a.酚醛缩合；
b.将缩合的酚醛加成；
c.酯化反应制得半成品；
d.检验半成品是否合格；以及
e.使用合格的半成品进行炼油制成成品。
2.一种采用如权利要求1所述的工艺制成的油墨连接料。
3.一种快干亮光胶版油墨，其重量配比为：
连接料50-70％；
颜料13-20％；
油墨油5-15％；以及
助剂5-15％，
其特征在于，该连接料为采用如权利要求1所述的工艺制成的油墨连接料。
4.如权利要求3所述的快干亮光胶版油墨，其特征在于：所述颜料为有机颜料。
5.如权利要求3所述的快干亮光胶版油墨，其特征在于：所述油墨油为240-320度的高沸点石油馏分。
6.如权利要求3所述的快干亮光胶版油墨，其特征在于：所述助剂为蜡、干燥剂或抗氧剂。