CN101269933A - High-negative ion function verdelite grain entity plane materiel and preparation method thereof - Google Patents
High-negative ion function verdelite grain entity plane materiel and preparation method thereof Download PDFInfo
- Publication number
- CN101269933A CN101269933A CNA2008100735661A CN200810073566A CN101269933A CN 101269933 A CN101269933 A CN 101269933A CN A2008100735661 A CNA2008100735661 A CN A2008100735661A CN 200810073566 A CN200810073566 A CN 200810073566A CN 101269933 A CN101269933 A CN 101269933A
- Authority
- CN
- China
- Prior art keywords
- verdelite
- grain
- negative ion
- plane materiel
- tourmalinite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses tourmaline crystal-grain solid surfacing material with high anion function and a preparation method of the solid surfacing material. Crystal grains that are sieved from the crushed tourmaline is uniformly mixed with adhesive, and then the mixture is injected into a forming die to pump the vacuum and to be heated for solidification, and the mixture is cut to obtain the finished product of ecological environmental building material in different specifications. The present invention has the advantages that the tourmaline crystal-grain solid surfacing material is provided with a permanent static electrostatic field at the normal state, which can continuously generates the anion and the radiation infrared ray, thereby facilitating the activation of the water molecular to melt the favorable mineral elements, and having the healthcare functions such as improving the blood circulation, improving the lymph circulation, promoting the fat metabolism, etc. The tourmaline crystal-grain solid surfacing material is very suitable to be used as the materials for the healthcare facilities such as the bedrock bath, the sauna room, the sauna bath, etc. and the household bathtub, the cabinet, the indoor decoration.
Description
Technical field:
The present invention relates to building and ornament materials, specifically is a kind of high-negative ion function verdelite grain entity plane materiel and preparation method thereof.
Background technology:
" tourmalinite " (English name Tourmaline, transliteration Tourmaline) is a kind of functional mineral material with natural energy extremely rare in the global environment.French physicist Curie brothers in 1880 study the physical phenomenon of " tourmalinite is added that heat or pressure can produce electric charge ", have proved that tourmalinite can continue to take place faint electric current under the state of nature.Over more than 100 year, state scholars such as Japan have confirmed that by test tourmalinite has a series of uniquenesses such as piezoelectricity, pyroelectricity, spontaneous electrode, ir radiation and important properties, for tourmalinite at the application start of industrial circle and medical field wide prospect.In recent years, along with people surging to the consciousness of healthy and environment, countries in the world have started and used tourmalinite is that basic raw material is made upsurge various and environment and healthy related products.
Because tourmalinite has special pyroelectricity and piezoelectricity, excite Shi Douhui to produce electric charge being subjected to heat, pressure, bump, vibration, friction and other outside energy, discharge a large amount of negative ion and radiation infrared, have and excite potential energy and electromagnetic protection function especially.Therefore, Tourmaline Mineral Material can be widely used in industries such as environmental protection, electronics, daily use chemicals, weaving, pottery, building materials.
The negative ion that tourmalinite produces under the excitation of universe natural energy can make airborne water molecules generation electrolytic action, a lot of negative ion group that forms in air.Negative ion has good biological activity.It mainly is after entering blood by the approach of breathing, to emit electric charge to the effect of human body, acts on cell, protein, and reflex irritation enteroception organ by the neural system conduction, acts on brain nervus centralis and vegetative nervous system, and function affects the nerves.
After negative ion is inhaled into human body, can increase the oxygen delivery capacity of respiratory system, enhance metabolism, improve blood circulation, the enhancing immunity system capability can be regulated neural state of excitation, increases work efficiency or the like.Negative ion has certain prevention and assisting therapy effect to hypertension, insomnia, asthma, sacroiliitis, multiple disease such as allergic, so people call airborne negative ion " air VITAMIN ".
Tourmalinite is a kind of typical high temperature pneumatogenic mineral that the earth volcanic explosion of age in time immemorial forms, and also is a kind of function far infrared radiation function material of excellent property therefore.It is close that tourmalinite gives off the far infrared rays wavelength that far infrared rays that wavelength is 4 ~ 14 μ m and human body natural take place, and has a penetrating quality, can make human inner cell's water molecules produce the most effective " resonance ", impel the temperature of subcutaneous deep to rise, make Marjoram Extract, stimulate circulation, strengthen the vigor of cell effectively, reach the purpose of activation histocyte, strengthening immune system.So the multiple disease that far infrared rays causes for blood circulation and microcirculation disturbance all has control and assisting therapy effect, is of value to HUMAN HEALTH.Therefore, people call the far infrared rays of this section wavelength " life light ".
By retrieval, do not see the patent application that verdelite grain entity plane materiel is arranged.
Summary of the invention:
The objective of the invention is to provide verdelite grain entity plane materiel of a kind of high-negative ion release, high far-infrared radiation, high strength with health role, shock resistance, resistance to compression, anti-folding, impermeabilisation, corrosion-resistant, high temperature resistant, fire-retardant fireproof, antibacterial and mouldproof, "dead", toxicological harmless and preparation method thereof.
Verdelite grain entity plane materiel of the present invention is a crystal grain of selecting the tourmalinite crushing and screening of high-negative ion release for use, with the bonding agent mixing and stirring, be injected into to vacuumize in the pattern and heat and make its curing, obtaining finished product through cutting mill again, the weight percent of each component raw material consumption is: particle diameter is the 0.1%-1% that verdelite grain 55%-95%, unsaturated polyester resin or the unsaturated polyester resin of 0.05-5mm and 0.25-5mm and methyl-prop diluted acid formicester blended resin or methyl-prop diluted acid formicester 5%-45%, modified silane coupler account for weight resin.
The verdelite grain of 0.25-5mm particle diameter accounts for the 50%-60% of tourmalinite total amount in the described verdelite grain, and the verdelite grain of 0.05-0.25mm particle diameter accounts for the 40%-50% of tourmalinite total amount.
The preparation method of verdelite grain entity plane materiel of the present invention: comprise the steps:
1, with EB-15 type anion test instrument the crude tourmaline raw mineral materials is tested screening, choose static negative ion numerical value 〉=500ions/cm
3, dynamic negative ion numerical value 〉=50000ions/g.s, the tourmalinite raw material for standby of far-infrared radiation rate 〉=90%;
2, will be processed into the verdelite grain that particle size range is 0.05 ~ 5mm through detecting the tourmalinite raw ore of selecting for use with crusher;
3, in the ratio of product specification definition verdelite grain, unsaturated polyester resin or unsaturated polyester resin and methymethacrylate blended resin or methymethacrylate material and modified silane coupler are put into the container mixing and stirring;
4, above-mentioned mixing raw material is put into forming mould, the gas of extracting out in the feed particles gap reaches-0.1Mpa vacuum tightness, enters drying room again and is heated to 120-180 ℃ raw material is solidified, and becomes the waste material of entity plane materiel;
5, with processing of stone machinery the entity plane materiel famine is expected section, flour milling, side cut, chamfering, maintenance, obtain the various sizes verdelite grain entity plane materiel.
The invention has the beneficial effects as follows:
Because tourmalinite has and has permanent electrostatic field under normal conditions, continue generating negative ions and radiation infrared, can make the useful unique functions such as mineral element of water molecules sensitization stripping, entity plane materiel is especially suitable for use as slabstone heating health-care facilities, family's kitchen cabinet, bathtubs such as laccolite bath, sweat-steaming house, sauna bath and decorates and the interior decoration material.
The health-care facilities that the entity plane materiel that uses the present invention to prepare is made can produce following various body-building effect to human body:
1, improves blood circulation, increase blood flow, improve the oxygen level of blood, promote cytoactiveization;
2, improve lymph fluid circulation, promote sweat secretion, accelerate to get rid of harmful toxins in the body, improve immune function of human body;
3, promote metabolism of fat, get rid of the superfluous fat of human body accumulation, blood fat reducing and cholesterol reach the weight-reducing effect;
4, improve allergic dermatitis, keep skin wet, smooth exquisiteness, increase elasticity;
5, slow down joint, muscle, neuralgia, sacroiliitis, scapulohumeral periarthritis, cervical spondylosis, cold hands and feet are had auxiliary curative effect;
6, Ginseng Extract improves sleep, slows down the vegetative dystonie shape, discharges the stress of work strain;
7, keep hair gloss to moisten, suppress dandruff, alopecia;
8, slow down the climacterium obstacle, prevented presenility.
Description of drawings:
Fig. 1 is the manufacturing process flow block diagram of high-negative ion function verdelite grain entity plane materiel of the present invention.
Embodiment:
Below in conjunction with embodiment content of the present invention is further elaborated:
Embodiment 1:
The method for preparing inferior light polyester type high-negative ion far infrared verdelite grain plane materiel:
1) with EB-15 type anion test instrument the crude tourmaline raw mineral materials is tested screening, choose static negative ion numerical value 〉=500ions/cm
3The tourmalinite raw mineral materials standby;
2) will be processed into verdelite grain through detecting the tourmalinite crushing raw ore of selecting for use with crusher, screening is two kinds of specifications of particle diameter 0.25-5mm (account for verdelite grain weight 60%) and 0.05-0.25mm (account for verdelite grain weight 40%), and tourmalinite raw ore crystal grain weight accounts for 90% of product weight;
3) in verdelite grain, add unsaturated polyester resin (account for product weight 10%) and modified silane coupler (accounting for the 0.1%-1% of weight resin);
4) above kind raw material is mixed the stirring back and inject mould, in vacuum chamber, extract the gas between feed particles out, vacuum tightness is reached-0.1Mpa, enter drying room again, be heated to 120-180 ℃, raw material is solidified, become entity plane materiel famine material;
5) with processing of stone machinery with the waste material section of entity plane materiel, surface grinding to 18 degree, side cut then, chamfering, maintenance obtain the verdelite grain plane materiel of various sizes.
Embodiment 2:
The method for preparing light polyester type high-negative ion far infrared verdelite grain plane materiel:
1) with EB-15 type anion test instrument the crude tourmaline raw mineral materials is tested screening, choose static negative ion numerical value 〉=500ions/cm
3The tourmalinite raw mineral materials standby;
2) will be processed into verdelite grain through detecting the tourmalinite crushing raw ore of selecting for use with crusher, the screening particle diameter is two kinds of specifications of 0.25 ~ 5mm (account for verdelite grain weight 80%) and 0.05 ~ 0.25mm (account for verdelite grain weight 20%), and tourmalinite raw ore crystal grain weight accounts for 80% of product weight;
3) in verdelite grain, add unsaturated polyester resin (account for product weight 20%) and modified silane coupler (accounting for the 0.1%-1% of weight resin);
4) above kind raw material is mixed the stirring back and inject mould, in vacuum chamber, extract the gas between feed particles out, vacuum tightness is reached-0.1Mpa, enter drying room again, be heated to 120-180 ℃, raw material is solidified, become entity plane materiel famine material;
5) with processing of stone machinery with the waste material section of entity plane materiel, surface grinding to 68 degree, side cut then, chamfering, maintenance obtain the verdelite grain plane materiel of various sizes.
Embodiment 3:
The method for preparing inferior photorecombination acrylic type high-negative ion far infrared verdelite grain plane materiel:
1) with EB-15 type anion test instrument the crude tourmaline raw mineral materials is tested screening, choose static negative ion numerical value 〉=500ions/cm
3The tourmalinite raw mineral materials standby;
2) will be processed into verdelite grain through detecting the tourmalinite crushing raw ore of selecting for use with crusher, the screening particle diameter is two kinds of specifications of 0.25 ~ 5mm (account for verdelite grain weight 60%) and 0.05 ~ 0.25mm (account for verdelite grain weight 40%), and tourmalinite raw ore crystal grain weight accounts for 70% of product weight;
3) in verdelite grain, add unsaturated polyester resin (account for product weight 15%), methymethacrylate (account for product weight 15%) and modified silane coupler (accounting for the 0.1%-1% of weight resin);
4) above kind raw material is mixed the stirring back and inject mould, in vacuum chamber, extract the gas between feed particles out, vacuum tightness is reached-0.1Mpa, enter drying room again, be heated to 120-180 ℃, raw material is solidified, become entity plane materiel famine material;
5) with processing of stone machinery with the waste material section of entity plane materiel, surface grinding to 18 degree, side cut then, chamfering, maintenance obtain the verdelite grain plane materiel of various sizes.
Embodiment 4:
The method for preparing light acrylic type high-negative ion far infrared verdelite grain plane materiel:
1) with EB-15 type anion test instrument the crude tourmaline raw mineral materials is tested screening, choose static negative ion numerical value 〉=500ions/cm
3The tourmalinite raw mineral materials standby;
2) will be processed into verdelite grain through detecting the tourmalinite crushing raw ore of selecting for use with crusher, the screening particle diameter is two kinds of specifications of 0.25 ~ 5mm (account for verdelite grain weight 80%) and 0.05-0.25mm (account for verdelite grain weight 20%), and tourmalinite raw ore crystal grain weight accounts for 50% of product weight;
3) in verdelite grain, add methymethacrylate (account for product weight 50%) and modified silane coupler (accounting for the 0.1%-1% of weight resin);
4) above kind raw material is mixed the stirring back and inject mould, in vacuum chamber, extract the gas between feed particles out, vacuum tightness is reached-0.1Mpa, enter drying room again, be heated to 120-180 ℃, raw material is solidified, become entity plane materiel famine material;
5) with processing of stone machinery with the waste material section of entity plane materiel, surface grinding to 68 degree, side cut then, chamfering, maintenance obtain the verdelite grain plane materiel of various sizes.
Claims (4)
1, a kind of high-negative ion function verdelite grain entity plane materiel, it is characterized in that: the tourmalinite that it is discharged by high-negative ion is through the crystal grain of crushing and screening, with the bonding agent mixing and stirring, be injected in the pattern and vacuumize, and heating makes its curing, grind through cutting again, each component raw material consumption weight percent is: particle diameter is the verdelite grain 55%-95% of 0.05-5mm and 0.25-5mm, unsaturated polyester resin or unsaturated polyester resin and methyl-prop diluted acid formicester blended resin or methyl-prop diluted acid formicester 5%-45%, modified silane coupler (accounting for the 0.1%-1% of weight resin).
2, a kind of high-negative ion function verdelite grain entity plane materiel according to claim 1, it is characterized in that: the verdelite grain of 0.25-5mm particle diameter accounts for the 50%-60% of tourmalinite total amount in the described verdelite grain, and the verdelite grain of 0.05-0.25mm particle diameter accounts for the 40%-50% of tourmalinite total amount.
3, a kind of high-negative ion function verdelite grain entity plane materiel according to claim 1 is characterized in that, used tourmalinite raw ore, its static negative ion numerical value 〉=500ions/cm
3, dynamic negative ion numerical value 〉=50000ions/g.s, far infrared radiation rate 〉=90%.
4, the preparation method of the brilliant entity plane materiel of a kind of high-negative ion function verdelite, it is characterized in that: this method comprises the steps:
(1), the crude tourmaline raw mineral materials is tested screening, choose static negative ion numerical value 〉=500ions/cm with EB-15 type anion test instrument
3The tourmalinite raw material for standby;
(2), will be processed into the verdelite grain that particle size range is 0.05-5mm through detecting the tourmalinite raw ore of selecting for use with crusher;
(3), in the ratio of product specification definition verdelite grain, unsaturated polyester resin or unsaturated polyester resin and methymethacrylate blended resin or methymethacrylate material and modified silane coupler are put into the container mixing and stirring;
(4), with mixing raw material injection moulding mould, extract the gas in the feed particles gap out, vacuum tightness is reached-0.1Mpa, enter drying room again, be heated to 120-180 ℃, raw material is solidified, become the waste material of entity plane materiel;
(5), with processing of stone machinery with the section of the waste material of entity plane materiel, flour milling, side cut, chamfering, maintenance, obtain the various sizes verdelite grain entity plane materiel.