CN101255313B - 用于汽车反光层涂料 - Google Patents

用于汽车反光层涂料 Download PDF

Info

Publication number
CN101255313B
CN101255313B CN2007101914908A CN200710191490A CN101255313B CN 101255313 B CN101255313 B CN 101255313B CN 2007101914908 A CN2007101914908 A CN 2007101914908A CN 200710191490 A CN200710191490 A CN 200710191490A CN 101255313 B CN101255313 B CN 101255313B
Authority
CN
China
Prior art keywords
coating
reflecting layer
layer according
automobile reflecting
paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2007101914908A
Other languages
English (en)
Other versions
CN101255313A (zh
Inventor
吕建平
王京甫
洪本飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHU LITEL PAINT MANUFACTURING Co Ltd
Original Assignee
WUHU LITEL PAINT MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHU LITEL PAINT MANUFACTURING Co Ltd filed Critical WUHU LITEL PAINT MANUFACTURING Co Ltd
Priority to CN2007101914908A priority Critical patent/CN101255313B/zh
Publication of CN101255313A publication Critical patent/CN101255313A/zh
Application granted granted Critical
Publication of CN101255313B publication Critical patent/CN101255313B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了用于汽车反光层涂料，包括底漆、面漆，所述的面漆包括有机硅丙酸酯乳液、氟丙烯酸脂乳液、偏苯三酸三辛酯、轻质碳酸钙、滑石粉、钛白粉、六偏磷酸钠、反光粉、消泡剂、增稠剂、水，本发明与现有技术相比，所形成涂层的反光率达到90-100％，同时涂层也有较好的耐水、耐磨性能。

Description

用于汽车反光层涂料
技术领域
本发明属于反光涂料，特别属于用于汽车反光层涂料。
背景技术
随着物流的发展，及中国公路建设滞后等深层次的原因，为了提高公路的利用率，夜间行车量在不断增加，目前市场上汽车用反光层由面漆和底漆组成，面漆为反光层涂料，主要为溶剂型聚氨酯涂料，溶剂型聚氨酯涂膜具有硬度高、附着力强、耐磨性高、耐溶剂性好的特点，但其反光率为60％，反光率较差，容易导致夜间行车事故的发生。
发明内容
本发明所要解决的技术问题是提供一种反光率好的用于汽车反光层涂料。
本发明解决技术问题的技术方案为：用于汽车反光层涂料，包括底漆、面漆，所述的面漆包括以下物质及重量份：
有机硅丙酸酯乳液    40-50
氟丙烯酸脂乳液      40-50
偏苯三酸三辛酯      1-10
轻质碳酸钙          200-250
滑石粉              40-60
钛白粉              3-6
六偏磷酸钠          2-5
反光粉              10-15
消泡剂              3-6
增稠剂        3-6
水            300-350
所述的有机硅丙酸酯乳液由国民淀粉化学公司生产，型号为：NaPoly KD8。
所述的氟丙烯酸脂乳液由四川华高化工有限公司生产。
所述的反光粉为玻璃微珠，其粒度为40-60目。
所述的消泡剂为二甲基硅油。
所述的增稠剂为羟乙基纤维素钠、羧甲基纤维素钠。
所述的底漆为现有的水性电泳漆。
为了提高涂料的耐腐蚀性，还可在涂料中增加防腐剂，所述的防腐剂最好为纳米防腐剂。
本发明通过偏苯三酸三辛酯将有机硅丙酸酯乳液和氟丙烯酸酯乳液有机的结合起来，形成稳定的乳液，并将反光粉均匀的包裹在乳液中，提高涂料形成的反光涂层的反光率。
本发明与现有技术相比，所形成涂层的反光率达到90-100％，同时涂层也有较好的耐水、耐磨性能。
具体实施方式
下面结合实施例对本发明做详细的说明。
本发明的制备方法为现有有机涂料的制备方法。
所述面漆的具体配比见表1，表1中各物质的单位均为重量份。
表1：
  实施例1   实施例2   实施例3
  有机硅丙酸酯乳液   40   45   50
  氟丙烯酸脂乳液   40   43   50
  偏苯三酸三辛酯   1   5   10
  轻质碳酸钙   200   220   250
  滑石粉   40   50   60
  钛白粉   3   4   6
  六偏磷酸钠   2   3   5
  玻璃微珠   10   12   15
  二甲基硅油   3   5   6
  羧甲基纤维素钠   3   5   6
  纳米防腐剂   0   0   1
  水   350   340   350
实施例1-3中，涂料的不挥发物含量≥60％，细度≤15μm，遮盖力(白色)(g/m2)≤100，表面干燥时间≤3.5小时；
将实施例1-3喷涂到汽车玻璃上，所形成涂层的反光率≥90％，光泽(60度)≥90，划格试验≤1级，弯曲≤2毫米，硬度≥0.8，耐水性：在水中72小时不起泡，不起皱，不脱落，耐磨性：(750g/500r)≤0.02。

Claims (6)

1.用于汽车反光层的涂料，包括底漆、面漆，其特征在于：所述的面漆包
括以下物质及重量份：
有机硅丙烯酸酯乳液    40-50
氟丙烯酸酯乳液        40-50
偏苯三酸三辛酯        1-10
轻质碳酸钙            200-250
滑石粉                40-60
钛白粉                3-6
六偏磷酸钠            2-5
反光粉                10-15
消泡剂                3-6
增稠剂                3-6
水                    300-350。
2.根据权利要求1所述的用于汽车反光层的涂料，其特征在于：所述的有机硅丙烯酸酯乳液由国民淀粉化学公司生产，型号为：NaPoly KD8。
3.根据权利要求1所述的用于汽车反光层的涂料，其特征在于：所述的反光粉为玻璃微珠，其粒度为40-60目。
4.根据权利要求1所述的用于汽车反光层的涂料，其特征在于：所述的消泡剂为二甲基硅油。
5.根据权利要求1所述的用于汽车反光层的涂料，其特征在于：所述的增稠剂为羟乙基纤维素钠、羧甲基纤维素钠。
6.根据权利要求1所述的用于汽车反光层的涂料，其特征在于：所述的底漆为水性电泳漆。
CN2007101914908A 2007-12-18 2007-12-18 用于汽车反光层涂料 Expired - Fee Related CN101255313B (zh)