CN114891424A - 一种隔热外墙涂料 - Google Patents
一种隔热外墙涂料 Download PDFInfo
- Publication number
- CN114891424A CN114891424A CN202210559735.2A CN202210559735A CN114891424A CN 114891424 A CN114891424 A CN 114891424A CN 202210559735 A CN202210559735 A CN 202210559735A CN 114891424 A CN114891424 A CN 114891424A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- resin
- exterior wall
- insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种隔热外墙涂料，涉及涂料生产技术领域。本发明包括以下重量份的原料：树脂28‑35份、活性稀释剂1‑3份、玻璃短纤维5‑8份、醇类溶剂4‑6份、去离子水30‑40份、隔热助剂一5‑8份、隔热助剂二5‑8份、抗紫外线添加剂3‑5份、消泡剂1‑2份和阻燃剂1‑3份。本发明以合成树脂和天然树脂为基料，与玻璃短纤维、纳米级高分子微球、空心陶瓷微珠、空心玻璃微珠及各种功能性助剂等配制而成，涂覆在建筑物外墙和屋顶，具有隔热、防晒、附着力好等优点，空心陶瓷微珠能反射掉太阳光中大部分的能量，进入涂层的另一部分能量经玻璃短纤维、纳米级高分子微球、玻璃微珠等的阻隔可避免光线的穿透，消耗掉大部分能量，从而使得该外墙涂料的隔热性能得到大大提高。
Description
技术领域
本发明属于涂料生产技术领域，特别是涉及一种隔热外墙涂料。
背景技术
涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体，涂料属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型，按照现代通行的化工产品的分类，涂料属于精细化工产品，现代的涂料正在逐步成为一类多功能性的工程材料，是化学工业中的一个重要行业，随着涂料行业的不断发展，人们除对涂料的环保性、经济性有越来越高的要求外，对涂料的其他性能，如耐碱、耐水、耐人工老化等要求更为严格，外墙涂料已成为外墙装饰的主流，近年来人们生活水平的提高，对外墙涂料也提出了更高的要求，节约资源、节能减排、生态环保、低碳循环经济是我国经济发展的基本模式，开发隔热涂料，降低建筑物、设备表面温度是一种被动利用太阳能的方法，对节约能源、保护环境、创造人与自然的和谐关系具有重要意义。
现有的外墙涂料在使用时存在以下不足之处：
1.现有的外墙涂料隔热措施单一，整个涂料的隔热效果难以满足更高水平的要求；
2.现有的外墙涂料功能单一，附着性差，容易老化。
因此有必要对现有技术进行改进，以解决上述问题。
发明内容
本发明的目的在于提供一种隔热外墙涂料，以合成树脂和天然树脂为基料，与玻璃短纤维、纳米级高分子微球、空心陶瓷微珠、空心玻璃微珠及各种功能性助剂等配制而成，涂覆在建筑物外墙和屋顶，具有隔热、防晒、附着力好等优点，空心陶瓷微珠能反射掉太阳光中大部分的能量，进入涂层的另一部分能量经玻璃短纤维、纳米级高分子微球、玻璃微珠等的阻隔可避免光线的穿透，消耗掉大部分能量，从而使得该外墙涂料的隔热性能得到大大提高，解决了现有的外墙涂料隔热措施单一，整个涂料的隔热效果难以满足更高水平的要求的问题。
为解决上述技术问题，本发明是通过以下技术方案实现的：
本发明为一种隔热外墙涂料，包括以下重量份的原料：树脂28-35份、活性稀释剂1-3份、玻璃短纤维5-8份、醇类溶剂4-6份、去离子水30-40份、隔热助剂一5-8份、隔热助剂二5-8份、抗紫外线添加剂3-5份、消泡剂1-2份和阻燃剂1-3份，其中抗紫外线添加剂可设置为RQT-X-1，RQT-X-1具有吸附紫外线辐射的功能，从而延长外墙涂料的寿命，阻燃剂可设置为三氧化二锑。
进一步地，包括以下重量份的原料：树脂28份、活性稀释剂3份、玻璃短纤维6份、醇类溶剂6份、去离子水40份、隔热助剂一5份、隔热助剂二5份、抗紫外线添加剂5份、消泡剂1份和阻燃剂1份。
进一步地，包括以下重量份的原料：树脂30份、活性稀释剂1份、玻璃短纤维5份、醇类溶剂6份、去离子水39份、隔热助剂一7份、隔热助剂二7份、抗紫外线添加剂3份、消泡剂1份和阻燃剂1份。
进一步地，包括以下重量份的原料：树脂35份、活性稀释剂1份、玻璃短纤维5份、醇类溶剂6份、去离子水31份、隔热助剂一8份、隔热助剂二8份、抗紫外线添加剂3份、消泡剂2份和阻燃剂1份。
进一步地，所述树脂设置为改性树脂和天然树脂的混合物，且改性树脂的重量份数为20-25份，天然树脂的重量份数为8-10份，改性树脂设置为有机硅类改性醇酸树脂，天然树脂设置为紫胶。
进一步地，所述活性稀释剂设置为多官能团丙烯酸酯类稀释剂。
进一步地，所述玻璃短纤维设置为纳米级玻璃短纤维，所述玻璃短纤维的粒径设置为100-1000nm。
进一步地，所述隔热助剂一设置为纳米级高分子微球，所述纳米级高分子微球的粒径设置为100-1000nm。
进一步地，所述隔热助剂二设置为空心陶瓷微珠、玻璃微珠、硫酸钡、云母粉和消光粉的混合物，所述空心陶瓷微珠和玻璃微珠的粒径均设置为2000-3000nm，硫酸钡应用在粉末涂料方面能增强粉末涂料的流平性和保光性，并且与所有的色料有较好的兼容性，可使粉末涂料在喷涂工艺中达到理想的涂膜厚度，且上粉率高，云母粉应用于涂料中，可大幅提高涂膜的耐候性，抗透水性，增强涂膜的附着力和强度，改善涂膜的表观，消光粉应用在涂料、油漆中，能均衡的控制涂膜表面光泽，增加涂膜的耐磨性和抗划痕性，去湿、除臭、净化空气，隔音、防水和隔热、通透性。
本发明具有以下有益效果：
该外墙涂料以合成树脂和天然树脂为基料，与玻璃短纤维、纳米级高分子微球、空心陶瓷微珠、空心玻璃微珠及各种功能性助剂等配制而成，涂覆在建筑物外墙和屋顶，具有隔热、防晒、附着力好等优点，空心陶瓷微珠能反射掉太阳光中大部分的能量，进入涂层的另一部分能量经玻璃短纤维、纳米级高分子微球、玻璃微珠等的阻隔可避免光线的穿透，消耗掉大部分能量，从而使得该外墙涂料的隔热性能得到大大提高。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明为一种隔热外墙涂料，包括以下重量份的原料：树脂28-35份、活性稀释剂1-3份、玻璃短纤维5-8份、醇类溶剂4-6份、去离子水30-40份、隔热助剂一5-8份、隔热助剂二5-8份、抗紫外线添加剂3-5份、消泡剂1-2份和阻燃剂1-3份。
树脂设置为改性树脂和天然树脂的混合物，且改性树脂的重量份数为20-25份，天然树脂的重量份数为8-10份，改性树脂设置为有机硅类改性醇酸树脂，天然树脂设置为紫胶，有机硅类涂料具有优异的电绝缘性能、耐高温和耐腐烛性能，利用有机硅改性醇酸树脂能显著提高醇酸树脂的耐候性和耐热性，通过冷拼的方法用有机硅改性后的醇酸树脂，有优异的户外耐候性和耐紫外性能，紫胶树脂粘着力强，光泽好，对紫外线稳定，电绝缘性能良好，兼有热塑性和热固性。
活性稀释剂设置为多官能团丙烯酸酯类稀释剂，具体可设置为1，6-己二醇二丙烯酸酯。
玻璃短纤维设置为纳米级玻璃短纤维，玻璃短纤维的粒径设置为100-1000nm，玻璃短纤维具有绝缘性好，耐高温，抗腐蚀能力好、隔热的特性，纳米级的玻璃短纤维其隔热性能更加的优越，应用在外墙涂料上，能使得该外墙涂料的隔热性能得到大大提高。
隔热助剂一设置为纳米级高分子微球，纳米级高分子微球的粒径设置为100-1000nm，且隔热助剂一可设置为纳米级丙烯酸酯自交联高分子微球，高分子微球内部具有三维空间立体孔结构，当太阳光照射涂料表面上，多孔结构可有效反射、吸收太阳光，该材料具有重量轻、隔热、保温和降噪的作用，适合应用在外墙涂料上。
隔热助剂二设置为空心陶瓷微珠、玻璃微珠、硫酸钡、云母粉和消光粉的混合物，空心陶瓷微珠和玻璃微珠的粒径均设置为2000-3000nm，通过添加空心陶瓷微珠去反射太阳光中的能量，提高该涂料的隔热效果，玻璃微珠设置为空心玻璃微珠，空心玻璃微珠是一种微小、中空的圆球状粉末，具有重量轻、体积大、导热系数低、抗压强度高、绝缘、自润滑、隔音、不吸水、耐火、耐腐蚀、防辐射、无毒，以及分散性、流动性、稳定性好等优点，空心玻璃微珠可直接填充于绝大部分类型的热固性、热塑性树脂产品中，在粉末涂料中应用时，空心玻璃微珠可以起到隔热、绝缘的作用，可改善粉末涂层的物理机械性能，空心玻璃微珠填料可增加粉末涂料的硬度和刚度。
实施例一
一种隔热外墙涂料，包括以下重量份的原料：树脂28份、活性稀释剂3份、玻璃短纤维6份、醇类溶剂6份、去离子水40份、隔热助剂一5份、隔热助剂二5份、抗紫外线添加剂5份、消泡剂1份和阻燃剂1份。
实施例二
一种隔热外墙涂料，包括以下重量份的原料：树脂30份、活性稀释剂1份、玻璃短纤维5份、醇类溶剂6份、去离子水39份、隔热助剂一7份、隔热助剂二7份、抗紫外线添加剂3份、消泡剂1份和阻燃剂1份。
实施例三
一种隔热外墙涂料，包括以下重量份的原料：树脂35份、活性稀释剂1份、玻璃短纤维5份、醇类溶剂6份、去离子水31份、隔热助剂一8份、隔热助剂二8份、抗紫外线添加剂3份、消泡剂2份和阻燃剂1份。
在本说明书的描述中，参考术语“一个实施例”、“示例”、“具体示例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或者特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不一定指的是相同的实施例或示例。而且，描述的具体特征、结构、材料或者特点可以在任何的一个或多个实施例或示例中以合适的方式结合。
以上公开的本发明优选实施例只是用于帮助阐述本发明。优选实施例并没有详尽叙述所有的细节，也不限制该发明仅为所述的具体实施方式。显然，根据本说明书的内容，可作很多的修改和变化。本说明书选取并具体描述这些实施例，是为了更好地解释本发明的原理和实际应用，从而使所属技术领域技术人员能很好地理解和利用本发明。本发明仅受权利要求书及其全部范围和等效物的限制。
Claims (9)
1.一种隔热外墙涂料，其特征在于：包括以下重量份的原料：树脂28-35份、活性稀释剂1-3份、玻璃短纤维5-8份、醇类溶剂4-6份、去离子水30-40份、隔热助剂一5-8份、隔热助剂二5-8份、抗紫外线添加剂3-5份、消泡剂1-2份和阻燃剂1-3份。
2.根据权利要求1所述的一种隔热外墙涂料，其特征在于，包括以下重量份的原料：树脂28份、活性稀释剂3份、玻璃短纤维6份、醇类溶剂6份、去离子水40份、隔热助剂一5份、隔热助剂二5份、抗紫外线添加剂5份、消泡剂1份和阻燃剂1份。
3.根据权利要求1所述的一种隔热外墙涂料，其特征在于，包括以下重量份的原料：树脂30份、活性稀释剂1份、玻璃短纤维5份、醇类溶剂6份、去离子水39份、隔热助剂一7份、隔热助剂二7份、抗紫外线添加剂3份、消泡剂1份和阻燃剂1份。
4.根据权利要求1所述的一种隔热外墙涂料，其特征在于，包括以下重量份的原料：树脂35份、活性稀释剂1份、玻璃短纤维5份、醇类溶剂6份、去离子水31份、隔热助剂一8份、隔热助剂二8份、抗紫外线添加剂3份、消泡剂2份和阻燃剂1份。
5.根据权利要求1-4任意一项所述的一种隔热外墙涂料，其特征在于，所述树脂设置为改性树脂和天然树脂的混合物，且改性树脂的重量份数为20-25份，天然树脂的重量份数为8-10份，改性树脂设置为有机硅类改性醇酸树脂，天然树脂设置为紫胶。
6.根据权利要求1-4任意一项所述的一种隔热外墙涂料，其特征在于，所述活性稀释剂设置为多官能团丙烯酸酯类稀释剂。
7.根据权利要求1-4任意一项所述的一种隔热外墙涂料，其特征在于，所述玻璃短纤维设置为纳米级玻璃短纤维，所述玻璃短纤维的粒径设置为100-1000nm。
8.根据权利要求1-4任意一项所述的一种隔热外墙涂料，其特征在于，所述隔热助剂一设置为纳米级高分子微球，所述纳米级高分子微球的粒径设置为100-1000nm。
9.根据权利要求1-4任意一项所述的一种隔热外墙涂料，其特征在于，所述隔热助剂二设置为空心陶瓷微珠、玻璃微珠、硫酸钡、云母粉和消光粉的混合物，所述空心陶瓷微珠和玻璃微珠的粒径均设置为2000-3000nm。