CN101824258A - 一种水性建筑反射隔热涂料 - Google Patents

一种水性建筑反射隔热涂料 Download PDF

Info

Publication number
CN101824258A
CN101824258A CN 201010159219 CN201010159219A CN101824258A CN 101824258 A CN101824258 A CN 101824258A CN 201010159219 CN201010159219 CN 201010159219 CN 201010159219 A CN201010159219 A CN 201010159219A CN 101824258 A CN101824258 A CN 101824258A
Authority
CN
China
Prior art keywords
percent
coating
reflective heat
insulating building
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010159219
Other languages
English (en)
Inventor
王晓莉
羡永彪
杨胜
朱志远
董洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU WATERPROOF RESEARCH INSTITUTE CHINA BUILDING MATERIALS ACADEMY
Original Assignee
SUZHOU WATERPROOF RESEARCH INSTITUTE CHINA BUILDING MATERIALS ACADEMY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU WATERPROOF RESEARCH INSTITUTE CHINA BUILDING MATERIALS ACADEMY filed Critical SUZHOU WATERPROOF RESEARCH INSTITUTE CHINA BUILDING MATERIALS ACADEMY
Priority to CN 201010159219 priority Critical patent/CN101824258A/zh
Publication of CN101824258A publication Critical patent/CN101824258A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种水性建筑反射隔热涂料,按重量份计,所述涂料包括丙烯酸乳液40%~60%;硅丙乳液10%~20%;钛白粉5%~15%;平均粒径10μm~30μm的空心微珠1%~8%;纳米级过渡金属氧化物1%~2%;滑石粉5%~15%;分散剂0.3%~1%;消泡剂0.3%~0.8%;增塑剂0.2%~0.5%以及水10%~30%。本发明综合性能特别是反射隔热性能优异,且成本较低,制备工艺简单,适于推广应用。

Description

一种水性建筑反射隔热涂料
技术领域
[0001] 本发明涉及一种水性建筑反射隔热涂料,特别涉及一种建筑外墙体用涂料。 背景技术
[0002] 外墙反射隔热涂料可以保持室内温度恒定,增大室内外的温差,在夏季减少降温能耗,在冬季降低取暖费用。现有的隔热涂料,如中国发明专利申请200510028388. 7和 200610034700. 8的反射隔热涂料,采用对可见光和近红外辐射具有高反射的功能填料,尽 管这种涂层具有相当好的太阳反射率,但是红外辐射率较差;在阳光下,由于能量的积累, 涂层的内部环境温度还是会高于外部大气温度,涂层无法通过散射辐射热来提高隔热效 果。中国专利申请200810038491. 3公开了一种水性反射隔热涂料,其中添加了大量的纳米 材料,造价十分高昂,不适于建筑外墙上的大面积涂刷使用;而且由于仅添加纳米材料,未 能有效降低热传导,其隔热保温效果不理想。
发明内容
[0003] 本发明所要解决的技术问题是克服现有技术的不足,提供一种改进的水性建筑反 射隔热涂料,其成本低且反射隔热效果好。
[0004] 为解决以上技术问题,本发明采取如下技术方案:
[0005] 一种水性建筑反射隔热涂料,按重量份计,所述涂料包括丙烯酸乳液40%〜60%; 硅丙乳液10%〜20% ;钛白粉5%〜15% ;平均粒径10 μ m〜30 μ m的空心微珠1 %〜8% ; 纳米级过渡金属氧化物1 %〜2 % ;滑石粉5 %〜15 % ;分散剂0. 3 %〜1 % ;消泡剂0. 3 %〜 0. 8% ;增塑剂0. 2%〜0. 5%以及水10%〜30%。
[0006] 根据本发明,所述空心微珠可以为陶瓷微珠或玻璃微珠。所述纳米级过渡属氧化 物可以为选自纳米氧化锌、纳米氧化钛、纳米氧化铝及纳米氧化钴中的一种或几种的组合。 所述分散剂优选为聚丙烯酸盐类分散剂。所述消泡剂优选为有机硅消泡剂。所述增塑剂优 选为邻苯二甲酸类化合物例如邻苯二甲酸丁二酯。
[0007] 根据本发明的进一步实施方案,所述涂料还包括有机硅改性聚硅氧烷类抗污剂 0. 2%〜0. 5%以进一步提高涂料的抗污能力,防止涂料因沾污而致使反射隔热效果变差。
[0008] 根据本发明,所述涂料还可以进一步包括防腐杀菌剂0. 01%〜0. 5%。
[0009] 由于上述技术方案的运用,本发明与现有技术相比具有如下优点:
[0010] 本发明选择透明度高、不含吸热基团且对可见光和近红外光吸收小的丙烯酸乳液 为主要成膜物质,辅以抗污性优异的硅丙乳液,并通过添加钛白粉来提高反射率、遮盖率、 膜层强度、耐老化性和耐磨性;添加具有中空结构的空心微珠减缓热量传递,更好的达到降 温节能的目的;添加少量具有高发射率的纳米级过渡金属氧化物,提高热辐射。同时,选择 合适的助剂进行配比优化,在保证良好反射隔热功能的基础上突出涂膜的耐候性、耐水性、 耐温变性、防水性、抗开裂性,以最低成本获得综合性能最佳的涂膜性能。本发明成本低,综 合性能优异,适于推广应用。具体实施方式
[0011] 下面结合具体实施例对本发明做进一步详细的说明,但本发明并不限于以下实施 例。
[0012] 实施例1
[0013] 一种水性建筑反射隔热涂料,以重量含量计,其由如下组分组成:丙烯酸乳液 50 %、硅丙乳液12 %、钛白粉10 %、滑石粉10 %、空心微珠5 %、纳米氧化钴1 %、分散剂聚丙 烯酸钠1%、有机硅改性聚硅氧烷抗污剂0. 2%、有机硅消泡剂0. 3%、增塑剂邻苯二甲酸二 丁酯 0. 5%、水 10%。
[0014] 涂料的制备过程如下:
[0015] (1)、在低速搅拌下依次加入配方量的蒸馏水、分散剂、一部分消泡剂、增塑剂和抗 污剂等充分混合均勻,然后添加钛白粉,研磨分散30分钟,使粉体粒子在高剪切速率作用 下,分散成原级粒子,并达到分散稳定状态得到色浆;
[0016] (2)、将步骤(1)所得色浆缓慢加入到丙烯酸乳液和硅丙乳液的混合乳液中,再低 速搅拌30〜40分钟;
[0017] (3)、在低速状态下,向经过步骤(2)的分散液中加入空心微珠,搅拌过程中滴加 剩余的消泡剂,并调到合适的粘度,过滤,出料即得所述隔热涂料。
[0018] 实施例2
[0019] 一种水性建筑反射隔热涂料,以重量含量计,其由如下组分组成:丙烯酸乳液 60 %、硅丙乳液10 %、钛白粉6 %、滑石粉5 %、空心微珠5 %、纳米氧化钴2 %、分散剂聚丙烯 酸钠1%、有机硅改性聚硅氧烷抗污剂0. 2%、有机硅消泡剂0. 3%、增塑剂邻苯二甲酸二丁 酯0.4%、防腐杀菌剂0. 1%、水10%。
[0020] 制备工艺同实施例。
[0021] 实施例3
[0022] 一种水性建筑反射隔热涂料,以重量含量计,其由如下组分组成:丙烯酸乳液 40 %、硅丙乳液20 %、钛白粉12 %、滑石粉8 %、空心微珠6 %、纳米氧化钴2 %、分散剂聚丙 烯酸钠1%、有机硅改性聚硅氧烷抗污剂0. 2%、有机硅消泡剂0. 3%、增塑剂邻苯二甲酸二 丁酯 0. 5%、水 10%。
[0023] 制备工艺同实施例1。
[0024] 根据JC/T 235-2008《建筑反射隔热涂料》标准进行检测,实施例1〜3提供的涂 料的太阳反射比大于等于0. 90,半球发射率大于等于0. 87,隔热温差高达12°C,隔热温差 衰减在6°C以下。
[0025] 另外,经检测,实施例1〜3提供的涂料的对比率(遮盖率)彡0. 93,耐沾污 性< 15%,耐人工气候老化性(》600h),耐水性(》96h)、耐碱性(》48h),耐洗刷性 (彡2000次),满足GB/T 9755-2001《合成树脂乳液外墙涂料》“优等品”要求。
[0026] 综上,本发明提供的涂料不仅综合性能优异,且成本低,可通过常规的涂料制备工 艺生产,适于推广应用。
[0027] 上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内 。

Claims (7)

  1. 一种水性建筑反射隔热涂料,其特征在于:按重量份计,所述涂料包括丙烯酸乳液40%~60%;硅丙乳液10%~20%;钛白粉5%~15%;平均粒径10μm~30μm的空心微珠1%~8%;纳米级过渡金属氧化物1%~2%;滑石粉5%~15%;分散剂0.3%~1%;消泡剂0.3%~0.8%;增塑剂0.2%~0.5%以及水10%~30%。
  2. 2.根据权利要求1所述的水性建筑反射隔热涂料,其特征在于:所述纳米级过渡属氧 化物为选自纳米氧化锌、纳米氧化钛、纳米氧化铝及纳米氧化钴中的一种或几种的组合。
  3. 3.根据权利要求1所述的水性建筑反射隔热涂料,其特征在于:所述分散剂为聚丙烯 酸盐。
  4. 4.根据权利要求1所述的水性建筑反射隔热涂料,其特征在于:所述消泡剂为有机硅 消泡剂。
  5. 5.根据权利要求1所述的水性建筑反射隔热涂料,其特征在于:所述增塑剂为邻苯二 甲酸类化合物。
  6. 6.根据权利要求1所述的水性建筑反射隔热涂料,其特征在于:所述涂料还包括有机 硅改性聚硅氧烷类抗污剂0. 2%〜0. 5%。
  7. 7.根据权利要求1或6所述的水性建筑反射隔热涂料,其特征在于:所述涂料还包括 防腐杀菌剂0.01%〜0.5%。
CN 201010159219 2010-04-23 2010-04-23 一种水性建筑反射隔热涂料 Pending CN101824258A (zh)