CN101255289A - 一种紫外光固化加硬液 - Google Patents

一种紫外光固化加硬液 Download PDF

Info

Publication number
CN101255289A
CN101255289A CNA2008100272547A CN200810027254A CN101255289A CN 101255289 A CN101255289 A CN 101255289A CN A2008100272547 A CNA2008100272547 A CN A2008100272547A CN 200810027254 A CN200810027254 A CN 200810027254A CN 101255289 A CN101255289 A CN 101255289A
Authority
CN
China
Prior art keywords
ultraviolet light
hardening liquid
aliphatic urethane
light curing
urethane acrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008100272547A
Other languages
English (en)
Other versions
CN101255289B (zh
Inventor
何吉刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huizhou Changrunfa Coating Co Ltd
Original Assignee
Huizhou Changrunfa Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huizhou Changrunfa Coating Co Ltd filed Critical Huizhou Changrunfa Coating Co Ltd
Priority to CN2008100272547A priority Critical patent/CN101255289B/zh
Publication of CN101255289A publication Critical patent/CN101255289A/zh
Application granted granted Critical
Publication of CN101255289B publication Critical patent/CN101255289B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种紫外光固化加硬液，它的重量百分组成为高官能脂肪族聚氨酯丙烯酸酯5～40wt％，环状单官能丙烯酸酯单体5～15wt％，二官能脂肪族聚氨酯丙烯酸酯5～10wt％，二官能丙烯酸酯5～25wt％，光引发剂1～5wt％，稀释剂20～60wt％，助剂0.01～1wt％，上述紫外光固化加硬液应用于光学薄膜、光学级别的PMMA、PS、PC、CR、PVC等树脂镜片上，液晶显示屏、汽车太空与防爆膜、眼镜镜片等，由于高交联密度提供极高的硬度；环状单官能丙烯酸酯单体既具有很低的粘度，提供流平性，又具有环状结构，保证了光学薄膜等树脂镜片具有良好的硬度。

Description

一种紫外光固化加硬液
技术领域
本发明涉及一种紫外光固化涂料，尤其涉及光学薄膜、光学级别的PMMA、PS、PC、CR、PVC等树脂镜片上加硬的保护涂料。
背景技术
便携式电子产品已成为快速消费品，越来越成为人们生活的一部分，对外观要求也越来越高，而大都数码产品都有各种各样象LCD视窗、PMMA、PC、PS等镜片，这些视察镜片很容易摔破、刮花等缺点，目前还未发现有类似的专利技术，国内实际使用大多采用进口日韩的产品，市场前景广阔。
发明内容
本发明解决数码产品LCD视窗口、光学薄膜、光学级别的PMMA、PS、PC、CR、PVC等树脂镜片易摔伤、刮花、不耐磨与不防雾、不防静电等问题。
本发明所采用的技术方案是：一种紫外光固化加硬液，其重量百分组成为高官能脂肪族聚氨酯丙烯酸酯5～40wt％、环状单官能丙烯酸酯单体5～15wt％、二官能脂肪族聚氨酯丙烯酸酯5～10wt％、二官能丙烯酸酯5～25wt％、光引发剂1～5wt％、稀释剂20～60wt％、助剂0.01～1wt％。
进一步：上述紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，所述的光引发剂是苯基亚膦酸二乙酯、二苯甲酮、α一羟基异丙基苯甲酮、α一羟基环己基苯甲酮中的一种或几种，这些光引发剂具有较高的光敏性和热稳定性；所述的稀释剂是己二醇二丙烯酸酯、新戊二醇二丙烯酸酶、三羟甲基丙烷三丙烯酸酯中的一种或几种；常用的助剂有阻聚剂、消泡剂、流平剂和颜填料等助剂，它们的主要作用是改善涂料性能，增加紫外光敏感性，降低施工难度。
上述配方中优选的配方是它们的重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯10～35wt％、环状单官能丙烯酸酯单体8～12wt％、二官能脂肪族聚氨酯丙烯酸酯6～9wt％、二官能丙烯酸酯8～20wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％。
将上述紫外光固化加硬液应用于光学薄膜、光学级别的PMMA、PS、PC、CR、PVC等树脂镜片上，液晶显示屏、汽车太空与防爆膜、眼镜镜片等，由于高交联密度提供极高的硬度；环状单官能丙烯酸酯单体既具有很低的粘度，提供流平性，又具有环状结构，保证了良好的硬度，起到防刮花、耐磨与防雾、防静电等作用。
用上述紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
具体实施方式
以下实施例是紫外光固化加硬液优选的配方，这些配方为非限定性实施方式，其只是用于具体说明本发明，本领域的技术人员完全可以根据本发明的思路和选料配比筛选出的配方均为本发明的保护范围。
实施例1
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯15wt％、环状单官能丙烯酸酯单体12wt％、二官能脂肪族聚氨酯丙烯酸酯9wt％、二官能丙烯酸酯20wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，所述的光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例2
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯35wt％、环状单官能丙烯酸酯单体8wt％、二官能脂肪族聚氨酯丙烯酸酯6wt％、二官能丙烯酸酯10wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是二苯甲酮，稀释剂是新戊二醇二丙烯酸酶，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例3
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯32wt％、环状单官能丙烯酸酯单体10wt％、二官能脂肪族聚氨酯丙烯酸酯7wt％、二官能丙烯酸酯10wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是α一羟基异丙基苯甲酮，稀释剂是三羟甲基丙烷三丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例4
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯20wt％、环状单官能丙烯酸酯单体10wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、二官能丙烯酸酯12wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是苯基亚膦酸，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例5
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯20wt％、环状单官能丙烯酸酯单体10wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、二官能丙烯酸酯14wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例6
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯25wt％、环状单官能丙烯酸酯单体11wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、二官能丙烯酸酯16wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例7
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯28wt％、环状单官能丙烯酸酯单体11wt％、二官能脂肪族聚氨酯丙烯酸酯7wt％、二官能丙烯酸酯15wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。
实施例8
一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯30wt％、环状单官能丙烯酸酯单体10wt％、二官能脂肪族聚氨酯丙烯酸酯8wt％、二官能丙烯酸酯18wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％，在该紫外光固化加硬液中，高官能脂肪族聚氨酯丙烯酸酯具有16官能团，光引发剂是苯基亚膦酸二乙酯，稀释剂是己二醇二丙烯酸酯，再加上常用助剂。
用上述配方的紫外光固化加硬液处理过的光学薄膜树脂镜片具有以下优点：
1、很好解决了涂层与PMMA、PC、PS等树脂的附着力；
2、高耐磨、防刮花，硬度达到6H以上。

Claims (4)

1、一种紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯5～40wt％、环状单官能丙烯酸酯单体5～15wt％、二官能脂肪族聚氨酯丙烯酸酯5～10wt％、二官能丙烯酸酯5～25wt％、光引发剂1～5wt％、稀释剂20～60wt％、助剂0.01～iwt％。
2、如权利要求1所述的紫外光固化加硬液，其特征在于：高官能脂肪族聚氨酯丙烯酸酯具有16官能团。
3、如权利要求2所述的紫外光固化加硬液，其特征在于：所述的光引发剂是苯基亚膦酸二乙酯、二苯甲酮、α一羟基异丙基苯甲酮、α一羟基环己基苯甲酮中的一种或几种；
所述的稀释剂是己二醇二丙烯酸酯、新戊二醇二丙烯酸酶、三羟甲基丙烷三丙烯酸酯中的一种或几种。
4、如权利要求3所述的紫外光固化加硬液，其重量百分组成为：高官能脂肪族聚氨酯丙烯酸酯10～35wt％、环状单官能丙烯酸酯单体8～12wt％、二官能脂肪族聚氨酯丙烯酸酯6～9wt％、二官能丙烯酸酯8～20wt％、光引发剂2～4wt％、稀释剂30～50wt％、助剂0.1～0.8wt％。
CN2008100272547A 2008-04-03 2008-04-03 一种紫外光固化加硬液 Expired - Fee Related CN101255289B (zh)