CN101250388A - 一种环保型特效万能胶 - Google Patents

一种环保型特效万能胶 Download PDF

Info

Publication number
CN101250388A
CN101250388A CNA2008100870574A CN200810087057A CN101250388A CN 101250388 A CN101250388 A CN 101250388A CN A2008100870574 A CNA2008100870574 A CN A2008100870574A CN 200810087057 A CN200810087057 A CN 200810087057A CN 101250388 A CN101250388 A CN 101250388A
Authority
CN
China
Prior art keywords
environment
friendly type
purpose adhesive
reactor
type effective
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100870574A
Other languages
English (en)
Inventor
陈炳强
陈炳耀
张意田
陈炳江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGSHAN SANVO AEROSOL CO Ltd
Original Assignee
ZHONGSHAN SANVO AEROSOL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHONGSHAN SANVO AEROSOL CO Ltd filed Critical ZHONGSHAN SANVO AEROSOL CO Ltd
Priority to CNA2008100870574A priority Critical patent/CN101250388A/zh
Publication of CN101250388A publication Critical patent/CN101250388A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保型特效万能胶,其配方配比为:SBS热塑性弹性体10~15、萜烯树脂10~15、C9石油树脂6~12、松香甘油脂2~6、乙酸乙酯8~12、乙酸丁酯0.5~2、环保溶剂油30~50、BHT 0.2~1.0、环烷油0.1~3、苯甲酸0.1~0.4。本发明具有1.环保,不含"三苯"、卤代烃,符合《HJ/T220-2005环境标志产品技术要求胶粘剂》标准要求;2.气味清,刺激性小;3.表干速度快,初粘力强;4.粘性保持时间长;5.粘度低,流动性好,方便施工。

Description

一种环保型特效万能胶
技术领域
本发明是一种应用于家庭装修,家具生产制造所应用的环保型特效万能胶,无苯低毒,可广泛用于粘贴铝塑板、防火板、实木面板。
技术背景
目前应用于家庭装修的万能胶有两种,分别是氯丁型万能胶和SBS型万能胶,万能胶主要由橡胶、增粘树脂、混合溶剂、助剂组成,橡胶决定了粘接的强度,是影响万能胶品质的主要因素,增粘树脂同橡胶混配,改变了体系的弹性模量,提供粘性,混合溶剂影响到万能胶的施工性能,提供流动性,使胶水便于施工,助剂的作用在于改变产品的物理机械性能。
现有的万能胶都不同比例的含有“三苯”(苯、甲苯、二甲苯)及卤代烃类等高毒性溶剂,长时间接触会造成人体的慢性中毒,同时也会给周围环境造成严重污染。随着人们生活水平的提高,在人们的生活条件不断改善的同时,对环境的要求越来越高,同时随着社会的发展,胶粘剂的使用越来越广泛,不接触胶粘剂或周围的生活、工作环境中没有胶粘剂已经越来越困难,开发环保型胶粘剂是社会的需要,也是国家环境保护政策的要求。继2001年国家推出强制性的国标GB18583,对装修用胶市场进行规范,2005年颁布的《HJ/T 220-2005环境标志产品技术要求胶粘剂》,对万能胶的环保性能提出了更高的要求。
发明内容
本发明的目的是提供一种环保型特效万能胶,环保,不含“三苯”、卤代烃,符合《HJ/T 220-2005环境标志产品技术要求胶粘剂》标准要求,气味清、刺激性小,表干速度快,初粘力强,粘性保持时间长,粘度低,流动性好,方便施工。
本发明是这样实现的:一种环保型特效万能胶,其特殊之处在于,配方配比:(重量份)
SBS热塑性弹性体  10~15  萜烯树脂    10~15
C9石油树脂       6~12   松香甘油脂  2~6
乙酸乙酯         8~12   乙酸丁酯    0.5~2
环保溶剂油       30~50  BHT         0.2~1.0
环烷油           0.1~3  苯甲酸      0.1~0.4
一种环保型特效万能胶的生产方法,其特殊之处在于,其生产方法包括以下步骤:
(1)将乙酸乙酯、乙酸丁酯、环保溶剂油加入反应釜中;
(2)开动电机搅拌,将萜烯树脂、C9石油树脂、松香甘油酯加入反应釜中,搅拌15~60分钟至完全溶解;
(3)将SBS热塑性弹性体加入反应釜中,搅拌2~4小时至完全溶解;
(4)将BHT、环烷油、苯甲酸加入反应釜中,搅拌半小时后出料。
本发明与现有技术相比有如下特点:
1.环保,不含“三苯”、卤代烃,符合环境标志要求;2.气味清,刺激性小;3.表干速度快,初粘力强;4.粘性保持时间长;5.粘度低,流动性好,方便施工。
具体实施方式
实施例1
按比例称取原料,将乙酸乙酯9Kg、乙酸丁酯1Kg、环保溶剂油47.9Kg加入反应釜中,开动电机高速搅拌,将萜烯树脂15Kg、C9石油树脂8Kg、松香甘油脂3Kg加入反应釜中,搅拌30分钟后,加入SBS热塑性弹性体14Kg,搅拌2小时后,加入BHT 1Kg、环烷油1Kg,苯甲酸0.1Kg,搅拌30分钟,即制成成品。
实施例2
按比例称取原料,将乙酸乙酯10Kg、乙酸丁酯1Kg、环保溶剂油48.3Kg加入反应釜中,开动电机高速搅拌,将萜烯树脂14Kg、C9石油树脂9Kg、松香甘油脂2Kg加入反应釜中,搅拌30分钟后,加入SBS热塑性弹性体13Kg,搅拌2小时后,加入BHT 0.5Kg、环烷油2Kg、苯甲酸0.2Kg,搅拌30分钟,即制成成品。
实施例3
按比例称取原料,将乙酸乙酯12Kg、乙酸丁酯2Kg、环保溶剂油43.8Kg加入反应釜中,开动电机高速搅拌,将萜烯树脂12Kg、C9石油树脂8Kg、松香甘油脂5Kg加入反应釜中,搅拌30分钟后,加入SBS热塑性弹性体13.5Kg,搅拌2小时后,加入BHT 0.3Kg、环烷油3Kg、苯甲酸0.4Kg,搅拌30分钟,即制成成品。
主要原材料名称、技术指标:
1.SBS热塑性弹性体
外观:白色多孔柱状或粒状固体;
比重(g/cm3):0.92~0.95;
结构:线型;
嵌段比(S/B):40/60;
2.萜烯树脂
外观:淡黄色脆固体,片状,块状;
软化点(环球法,℃):≥100;
色号(铁钴法):≤4;
皂化值(mgKOH/g):≤1.5
碘值:40-75;
甲苯不溶物(%):≤0.05
3.C9石油树脂
外观:黄色脆固体,片状,块状;
软化点(环球法,℃):110~120;
色号(铁钴法):≤10;
酸值(mgKOH/g):≤0.5;
灰分(%):≤0.1
4.松香甘油酯
外观:淡黄色脆固体,片状,块状;
软化点(环球法,℃):≥100;
色号(铁钴法):≤4;
5.乙酸乙酯,工业级;
6.乙酸丁酯,工业级;
7.环保溶剂油
外观:无色透明液体;
馏程(℃):60~100;
比重(g/cm3,20℃):0.72~0.74;
8.BHT
化学名称:2,6-二叔丁基对甲酚,试剂级;
9.环烷油
外观:无色透明粘稠液体;
运动粘度(100℃,m2/s):24~32;
凝点(℃):≤-15;
折光率(nD 20):≥1.4800
10.苯甲酸,试剂级;
产品经抽样检验,符合《(HJ/T 220-2005环境标志产品技术要求胶粘剂》标准,其主要性能指标如下表。
  序号   项目   标准要求   检验结果
  1   外观   黄色均匀粘稠液体   符合
  2   粘度(mPa·s)   150~400   220
  3   固含量(%)   ≥30   40.5
  4   初粘强度(MPa)   ≥0.7   0.85
  5   拉伸剪切强度(MPa)   ≥1.56   1.6
  6   游离甲醛(mg/Kg)   ≤500   未检出
  7   苯(mg/Kg)   ≤2000   未检出
  8   甲苯+二甲苯(mg/Kg)   ≤2000   未检出
  9   丙酮(mg/Kg)   ≤750   未检出
  10   卤代烃(mg/Kg)   ≤2000   未检出
  11   总挥发性有机物(g/L)   ≤750   480

Claims (5)

1. 一种环保型特效万能胶,其特殊之处在于,配方配比:(重量份)
SBS热塑性弹性体 10~15   萜烯树脂    10~15
C9石油树脂      6~12    松香甘油脂  2~6
乙酸乙酯        8~12    乙酸丁酯    0.5~2
环保溶剂油      30~50   BHT         0.2~1.0
环烷油          0.1~3   苯甲酸      0.1~0.4
2. 如权利要求1所述的一种环保型特效万能胶,其特征在于,该重量配比各组分之和为100。
3. 如权利要求1所述的一种环保型特效万能胶,其特征在于,使用苯甲酸作为增强剂,增加初粘力和剥离强度,用量为0.1~0.4。
4. 如权利要求1所述的一种环保型特效万能胶,其特征在于,其生产方法包括以下步骤:
(1)将乙酸乙酯、乙酸丁酯、环保溶剂油加入反应釜中;
(2)开动电机搅拌,将萜烯树脂、C9石油树脂、松香甘油酯加入反应釜中,搅拌15~60分钟至完全溶解;
(3)将SBS热塑性弹性体加入反应釜中,搅拌2~4小时至完全溶解;
(4)将BHT、环烷油、苯甲酸加入反应釜中,搅拌半小时后出料。
5. 如权利要求1所述的一种环保型特效万能胶生产方法,生产时采用的是带分散盘的高速搅拌。
CNA2008100870574A 2008-03-31 2008-03-31 一种环保型特效万能胶 Pending CN101250388A (zh)